牛骨形态发生蛋白复合微孔钛与骨界面疲劳损伤机理研究

观察微孔涂层假体与骨界面疲劳行为及影响因素，方法：将牛骨形态发生蛋白复合微孔涂层的钛合金假体植入犬股骨近侧，４，８周后取标本，干燥，在配置产皮劳台的扫描电镜下动态观察在周胶变载吓界面损伤机理。结论：微孔内骨组织改建状态对于界面疲劳损伤过程具有重要的影响。     

医用微孔钛界面内锁性生物固定机理的实验研究

微孔钛的特点是容许新生骨小梁组织直接长入其孔隙内,形成内锁性生物固定,达到人工关节长期稳定的目的。作者采用球形钛粉末和钛纤维,分别植入24只犬股骨内。孔径是0.24mm,孔隙度是40％～50％。3月后测得界面剪切强度是4.6±0.36 MPa,扫描电镜显示微孔内有新骨成分,光镜显示新生骨细胞,新骨长入深度为3 mm。界面剪切性能可以满足人体应力负荷需要。研究表明:钛纤维表面结构的稳定性优于球形钛粉末。微孔钛研制成人工关节,可预防假体松动,并有助于临床开展新业务。     

羟基磷灰石涂层的钛-75合金种植体的犬骨内种植实验

目的：观察评体羟基磷灰石（ＨＡ）烧结涂层的钛０７５（Ｔｉ－７５）合金种植体（ＨＡＴＩ）的生物学性能与生物力学特性。方法：应用穿皮质骨种植模型,以纯钛种植体（ＰＴＩ）作对照,在双侧犬股骨内种植ＨＡＴＩ和ＰＴＩ共３２ 术后３个月和６个月处死动物取村。应用组织学、定量组织学、推出试验、扫描电镜等方法,观察种植体骨界面的结合情况和剪切强度。结果：ＨＡＴＩ与ＰＴＩ均与骨组织形成了骨性结合,ＨＡＴＩ的骨性结合     

羟基磷灰石涂层加速种植体－骨界面骨融合的形成

以成年杂种犬为实验对象，以未涂层纯钛种植体为对照，用定量组织学方法研究两种羟基磷灰石（ＨＡ１和ＨＡ２）涂层种植体穿骨皮质种植１、３、６个月后，种植体－骨组织界面骨融合形成的情况。结果表明：两种羟基磷灰石涂层种植体均能在种植早期加速界面骨融合的形成，其中ＨＡ２涂层种植体的骨融合指数在各种植程期均高于ＨＡ１涂层和未涂层纯钛种植体，显示出良好的生物活性。     

羟基磷灰石涂层加速种植体—骨界面骨融合的形成

以成年杂种犬为实验对象，以示涂层纯钛种植体为对照，用定量组织学方法研究两种羟基磷灰石涂层种植体穿骨皮质种植１、３、６个月后，种植体－骨组织办面骨融合形成的情况。结果表明：两种羟基磷灰石涂层种植体均能在种植早期加速界面骨融合的形成，其中ＨＡ２涂层种植体的骨融合指数在各种樾程期均高于ＨＡ１涂层和未涂层纯钛种植体，显示出良好的生物活性。     

四环素标记的钛-75犬股骨内种植实验

目的;研究肽－７５（钛铝钼锆）合金的组织相容性。方法：成年杂种犬６只,于其双侧后腿股骨内侧手术植入种植体,一侧为纯钛,另一侧为钛－７５合金。分别于术后３,６,１２个月处死动物,并于处死前１４ｄ及３ｄ给动物肌注四环素各一次。取与种植体接触的皮质骨制成磨片,在荧光显微镜下观察骨－种植体界面,并摄取照片,通过计算机图像分析系统计算四环素荧光标记区占全视野骨面积的百分比。结果：五四素－荧光标记区所占骨面积     

钛涂层317L接骨板螺钉骨界面的扫描电镜观察

报告了钛涂层３１７Ｌ接骨板螺钉和３１７Ｌ接骨板螺钉骨界面扫描电镜观察结果。钛涂层３１７Ｌ接骨板螺钉表面粗糙，植入后与狗下颌骨紧密结合，达到生物整合骨界面。未喷钛３１７Ｌ接骨板间钉植入后亦形成骨整合界面，但存在微小间隙。结果表明，钛涂层３１７Ｌ接骨板螺钉组织相容性优于３１７Ｌ接骨板螺钉。     

等梯度羟基磷灰石涂层结构对狗骨-植入体间隙愈合的增强作用

目的：观察等梯度羟基磷灰石－骨界面间隙内成骨反应。方法：应用经皮骨植入体模式，在１２条狗的双侧股骨上共植入９６个等梯度羟磷灰石（ＨＡ）表面涂层及非涂层钛合金栓。术中在植入体周围预置１ｍｍ间隙。分别于术后６、１２及１８周处死取材。测定界面抗剪强度并作组织学观察。结果：术后每一时间段涂层植入体界面抗剪强度均显著高于非涂层者。涂层植入体表面间隙内充满新生骨，骨与涂层结合紧密，而非涂层植入体表面与骨组织间常见纤维组织存在。结论：这种等梯度ＨＡ涂层结构具有增强骨－植入体界面间隙骨性愈合的作用。     

生物陶瓷／微孔钛混合烧结的口腔种植体复合骨形成蛋白骨界面结合的机理探讨

作者将钛（Ｔｃ＿４），羟基磷灰石（ＨＡ）和生物活性玻璃陶瓷（ＢＧＣ）颗粒混合烧结成生物活性微孔复合种植体复合骨形成蛋白（ＢＭＰ）移植于２０只成年杂种狗颌骨和股骨内，对１～１２周标本进行检测、观察和成骨量的测定．证明种植体与骨界面结合在于界面存在三相性（钛氧化膜：ＴｉＯ，Ｔｉ＿２Ｏ，Ｔｉ＿２Ｏ＿３，ＨＡ晶相和ＢＧＣ晶相），使钙、磷富集层形成，生物陶瓷降解产物再沉积，蛋白多糖、粘多糖类细胞外基质和天然骨粘合物粘连沉积并引导钙盐沉积在界面上，测得该种植体各项技术指标优于目前单一材料种植体技术指标．     

四环素标记的钛-75犬股骨内种植实验

目的：研究钛-75（钛铝钼锆）合金的组织相容性。方法：成年杂种犬6只,于其双侧后腿股骨内侧手术植入种植体,一侧为纯钛,另一侧为钛-75合金。分别于术后3,6,12个月处死动物,并于处死前14d及3d给动物肌注四环素各一次。取与种植体接触的皮质骨制成磨片,在荧光显微镜下观察骨-种植体界面,并摄取照片,通过计算机图像分析系统计算四环素荧光标记区占全视野骨面积的百分比。结果：四环素-荧光标记区所占骨面积在两种材料间比较无显著差异(P>0.05);同种材料不同程期间四环素-荧光标记区所占骨面积的比较也无显著学差异(P>0.05)。结论：钛-75合金具有与纯钛相近的组织相容性。     

深低温冷冻与常温储骨对皮质骨生物力学特性影响的研究

目的：研究深低温冷冻法和常温法储骨对皮质骨生物力学特性的影响。方法：用深低温冷冻法和常温酒精浸泡法储存相同时间的股骨皮质作标本,分别将其修成弯瞳及压缩试件,在Instron1195型电子拉伸试验机上测试两组的极限弯曲强度,弹性模量及极限压缩强度,所得数据进行组间t检验。结果：两组间极限弯曲强度、弹性模量、极限压缩强度差异均不明显（P〉0．05）。结论：深低温冷冻及常温法储骨对皮质骨生物力学特性无影响,在无深低温冷冻储骨条件的地方,如有合适的骨源,也可积极取骨用常温法储存,以免骨源浪费。     

Binding mechanism of interface of porous coated titanium alloy prostheses

ＢｉｎｄｉｎｇｍｅｃｈａｎｉｓｍｏｆｉｎｔｅｒｆａｃｅｏｆｐｏｒｏｕｓｃｏａｔｅｄｔｉｔａｎｉｕｍａｌｌｏｙｐｒｏｓｔｈｅｓｅｓＺｏｕＨｏｎｇｅｎ（邹宏思）；ＹｅＪｕｎ（叶军）；ＴａｎｇＮｏｎｇｘｕａｎ（唐农轩）；ＹｕａｎＣｕｎｈｕａ（袁存华）（Ｄｅ...     

Effect of morselized bones on binding of the canine hydroxyapatite-coated femoral stem

Background Non-cement femoral stems are recognized in clinical use, but there are still some problems. The aim of this research was to make non-cement femoral stems to be press-fit with the medullary cavity. Methods Twenty-four healthy adult mongrel dogs were randomly divided into experimental and control groups. In the right hip joint, an artificial femoral bone replacement surgery was conducted. For the experimental group, the replacement surgery of hydroxyapatite （HA）-coated femoral stems was done, while autogeneous morselized bone was implanted into the medullary cavity. For the control group, morselized bone was not implanted. At postoperative 1, 3, 6 months, a test for interfacial shear characteristics was conducted in the MTS810 Tester. The comparison between the two groups＇ bone-prostheses in shear strength for their interface from shearing destruction was made. A histological observation to check prosthesis-bone interface contact ratios and bone growth was carried out. Results For the experimental group, shear strength was 0.317 MPa in 1 month, 1.447 MPa in 3 months, and 1.621 MPa in 6 months. For the control group, shear strength was 0.195 MPa in 1 month, 1.023 MPa in 3 months, and 1.483 MPa in 6 months. The difference was statistically significant. Stereomicroscope-based observation showed that the number of trabecular bones in the experimental group was larger than that of the control group, and bone growth of the former group was better than that of the latter group. Inverted microscopic observation showed that the binding degree between the prosthesis and trabecular bone of the experimental group was higher than that of the control group. Comparatively, the experimental group＇s trabecular bone had more stromal cells. Conclusions The morselized bones can effectively improve the biological bonding strength and bone-contact ratios in the short term for the HA-coated femoral stem and accelerate the bonding process. The use of morselized autogenous bones played a good role in bone in-growth of the femoral bone stem surface.     

动静态下仿生型钛种植体界面应力 与疲劳行为的有限元分析

目的：研究静态与动态加载下仿生型种植体骨界面应力分布状况和疲劳行为,为研发能有效地转移应力至周围骨组织的新型种植体提供理论依据。方法：采用CAD（Pro/E Widefire 2.0）软件建立颌骨和钛种植体的三维有限元模型,设置全致密型（1号）和仿生型（2号）两种结构钛种植体,采用Ansys Workbench 10.0软件分析静态与动态加载下种植体骨界面应力分布状况,并对2号种植体进行疲劳行为分析。结果：在相同载荷下,1号和2号种植体在皮质骨区均为高应力区,2号种植体界面最大应力值、高应力区域面积、根端区最大应力值均低于1号种植体,从上至下种植体骨界面应力呈均匀递减趋势。动态加载的界面应力比静态的界面应力高17.15%。两种加载方式下,两种种植体在皮质骨区界面最大应力值无差别;在松质骨区, 1号的界面最大应力值比2号高75.97%;在根端区,1号的界面最大应力值比2号高22.46%,种植体界面最大应力远小于纯钛的屈服强度。2号种植体颈部皮质骨边缘的最大应力值比1号高7.85%,皮质骨边缘的最大应力值未达到皮质骨的屈服强度。预载50~300 N动态载荷,致密芯的安全系数均在10以上,随载荷加大,多孔层的界面应力呈线性增加,动态加载轴向300 N 和颊舌向45°25 N时,多孔层界面最大应力为11.38 MPa。结论：仿生型种植体有利于松质骨区及根端区界面应力转移到周围骨组织,其几何结构设计能耐受正常咀嚼的疲劳载荷,是安全的设计。     

CBCT评价儿童上后牙颊侧微种植体支抗植入部位的骨皮质厚度

目的：通过对恒牙列初期安氏Ⅱ类1分类错?儿童的上颌后牙区微种植体支抗植入区域进行分析,测量骨皮质厚度,为儿童临床种植体支抗植入提供理论依据,对植入点的选择提供一定参考。方法选取40例恒牙列初期安氏Ⅱ类1分类儿童患者的锥束CT影像资料,男、女各20例,分别测量双侧上颌第二前磨牙与第一恒磨牙根间区距牙槽嵴顶3～9mm处,共7个平面的骨皮质厚度,对结果进行统计分析。结果上颌第二前磨牙与第一恒磨牙根间区的骨皮质厚度在7个测量平面中,距牙槽嵴顶高度4mm处最小（P＜0．05）,5mm以上的骨皮质厚度随距牙槽嵴顶距离的增加而增大,男女对象在7、8、9mm处差异均有统计学意义,男大于女（P＜0．05）。结论恒牙列初期安氏Ⅱ类1分类儿童患者的后牙区颊侧骨皮质厚度随垂直向位置的增加而增大,微种植体支抗植入时应尽可能选择距牙槽嵴顶5mm以上的位置,以提高植入的成功率。     

钛生物陶瓷涂层种植体的实验研究

目的 :比较溶胶 -凝胶烧结法制作的钛 -羟基磷灰石生物陶瓷种植体与纯钛种植体在动物骨中的骨性结合 ,为临床提供制作简单、造价低且与骨结合好的牙种植体。方法 :混种家兔 2 0只 ,均为雄性 ,体重 2～ 3kg,随机分成实验组和对照组 ,每组 1 0只。将溶胶 -凝胶烧结法制作的钛 -羟基磷灰石生物陶瓷种植体与纯钛种植体分别植入家兔胫骨内 ,分别在术后 1、4、8、1 2、1 6周后镜下观察种植体与骨结合情况。结果 :实验组术后 8周时种植体与骨形成良好骨性结合 ,而对照组则为1 2周 ,术后 1 6周对照组和实验组均显示良好的骨性结合。结论 :溶胶 -凝胶烧结法制作的生物陶瓷涂层种植体具有良好的生物性能 ,可供临床应用     

多孔金属植入材料在骨科的应用

因外伤、肿瘤、感染等原因造成的骨缺损是骨科临床常见疾患,目前解决这一问题的主要方法为自体骨移植或同种异体骨移植.自体骨移植主要存在取骨量有限,造成附加损伤,感染,出血等缺陷.同种异体骨存在价格昂贵,免疫排斥反应等问题.此外,多种骨材料替代物也越来越多地应用于研究和临床,比如羟基磷灰石,生物陶瓷等.近年来,多孔金属材料由于其良好的生物相容性,较好的抗压强度和与骨接近的弹性模量等优点逐渐成为研究热点.本文针对多孔镁、多孔铁、多孔镍、多孔钽、多孔钛等不同材质的多孔金属材料,对其构建方法、理化特性、基础研究、临床应用等方面进行综述.     

冲顶式上颌窦底提升植骨同期牙种植的实验研究

[目的]探讨用Summer's骨凿冲顶提升上颌窦底后窦底骨质和黏骨膜改变情况以及种植体与周围组织结合生物学变化,为临床应用该项技术提供进一步可靠的实验依据.[方法]16只狗随机分为提升高度不同(2 mm、4 mm)2组,每只狗植入种植体4枚,一侧植骨,一侧不植骨,在不同时间(3、6、12、24周)取材.标本经大体观察,放射检查,组织学检查,四环素荧光检查,抗BMP-2免疫组化检测.[结果]移植骨愈合良好,种植体形成骨结合,提升4 mm不植骨种植体顶端无骨形成.[结论]上颌窦提升2 mm种植体顶端有骨存在,提升4 mm时,植入种植体顶端多数情况下无骨存在.