张应力对小鼠蝶枕软骨联合细胞增殖及低氧诱导因子- 1α表达的影响

目的:了解循环张应力对小鼠颅底蝶枕软骨联合细胞(SOSCs)增殖及低氧诱导因子-1α表达的影响。方法:采集1 d龄小鼠的SOSCs进行体外培养,对第三代细胞加载牵张形变率分别为3%、6%、9%,频率为1 Hz,持续时间为1 h的循环张应力;用流式细胞术测算细胞增殖指数,用蛋白免疫印迹技术分析Hif-1α的表达水平。用按相同条件培养但不加力的细胞作为对照。结果:各实验组细胞的增殖指数和Hif-1α相对表达量都高于对照组(P<0.05);其中,6%牵张形变率组的细胞增殖指数和Hif-1α相对表达量较对照组增加最多。结论:适宜强度的循环张应力对体外培养小鼠SOSCs的增殖和Hif-1α表达具有促进作用。     

Incisional healing in rats treated with diethyl maleate

Diethyl maleate (DEM) which binds and thus depletes tissue glutathione levels was used to aggravate the injury and to determine its effect on incisional healing. A 5 cm dorsal midline skin incision was performed on 40 albino Wistar rats in two groups and then closed by interrupted sutures. Groups received 0.9% NaCl and DEM at a dosage of 1 mg/kg/day intraperitoneally for seven days, respectively. On postoperative days 7 and 14, histopathological assessment and tensile strengths were measured. The DEM treated group had a marked inflammation with poorly defined collagen formation and the tensile strength measurements revealed a significant decrease (p <0.001) on the 7t day. On the other hand, the first group showed better collagenization and a lesser degree of inflammation. However, on the 14th day, there was no noticeable histopathological difference between the two groups; but, tensile strength values of the second group were still lower (p <0.05). In this animal model, DEM postponed the healing process and reduced the tensile strength.     

N—酰化壳聚糖膜性能的研究

讨论了一系列N-酰化壳聚糖膜的抗张强度、透水性、VB_(12)的透过性、透氧性以及血液相容性。N-已酰化壳聚糖膜具有良好的血液相容性。在制膜过程中,加入分子量为1500的聚乙二醇为致孔剂,则可使N-己酰化壳聚糖膜的渗透性有较大提高。同时保持较好的血液相容性和强度。     

关节镜下经皮张力带钢丝固定治疗髌骨骨折

目的探索髌骨骨折错位在关节镜下复位、内固定的新方法。方法对56例新鲜闭合性横断型髌骨骨折病例,在关节镜下冲洗关节腔积血,清除骨折断端凝血块,去除小的骨碎片,进行髌骨复位,直接观察关节面复位对合情况。应用胥氏张力带钢丝固定原理,经皮穿入克氏针及钢丝,针孔做1cm小切口,完成内固定。结果术后2周绝大部分患者屈膝可达90°以上,骨折在6～10周达到临床愈合,出现针尾触痛者8例,克氏针松动上移2例,无钢丝断裂及脱落。治疗效果按膝关节损伤患者的功能评定法,优良率为96.4%。结论本术式两枚克氏针各有一根钢丝固定,在关节镜导引下,经皮穿针钢丝固定,不会因两根针位置不对称而产生扭距。操作方法简便、有效,有利于术后早期功能锻炼,为髌骨骨折提供了一种新的手术方法。     

The application of percolation theory to the compaction of pharmaceutical powders

Based on the concepts of percolation theory the compaction process is interpreted as a site-bond percolation phenomenon. The combination of the Heckel equation with an equation derived earlier yields a simple relationship between the tensile strength σ_t, or the deformation hardness P and the relative density. This mathematical model is identical with the fundamental law of percolation theory i.e., X = s(p − p_c)^q with X= system property equivalent to tensile strength or deformation hardness, S = scaling factor, p = site occupation or bond formation probability corresponding to the relative density p,p_c = percolation threshold and critical exponent q = 1 according to percolation on a Bethe lattice. In the case of the tensile strength σ_t and the deformation hardness p, two percolation thresholds p_c(1) and p_c(2) corresponding to p_c(1) and p_c(2) could be identified. The relative density p_c(1) which is close to the relative poured or relative tapped density can be interpreted as a bond percolation threshold. The particles are bonded by weak interparticulate forces and form only loose compacts as used for filling of capsules. The relative density p_c(2) is the relative density where the first stable pharmaceutical compact is achieved which can no longer be disintegrated mechanically into its primary particles. It is of special interest that the above equation is also valid for the elastic modulus with the only percolation threshold p_c(1) = p_c(1).     

Laser welded vascular anastomosis

Summary A comparative study was undertaken to investigate the application of a specially adapted microsurgical Neodymium Yag Laser system with a wavelength of 1,319 m and a CO₂ laser system for laser assisted microvascular end-to-end anastomosis (LAMA) of the rat femoral artery. Conventionally sutured anastomoses served as controls. Postoperative investigations included patency tests, light microscopy and tensile strength measurements. Both laser systems seem to be equally suitable for LAMA: The patency rates do not differ from those of sutured anstomoses and formation of microscopically small aneurysms occurred predominantly in control animals and only once in laser groups. The clamp time needed for LAMA was half the time that was needed for sutured anastomoses. Wound healing in all groups was similar with less fibrotic reactions and less foreign body granulomas in laser groups. At all intervals tensile strength was significantly higher for sutured anastomoses while differences between the CO₂- and the ND: Yag-laser groups were not statistically significant. Potential applications in urology include microvascular anastomoses in erectile dysfunction, pediatric and reconstructive urology.Contains parts of a dissertation     

羟基磷灰石与骨界面抗张强度测试及扫描电镜观察

本文测试了孔隙率为１４％，孔径小于２μｍ的纯羟基磷灰石（ＨＡ）与兔胫骨皮质骨之间界面的抗张强度，２周时为０．７２ＭＰａ；４、８、１６周之间强度无明显差异平均为１．５ＭＰａ。扫描电镜观察表明，２周时拉伸断裂位于ＨＡ－骨界面，４周以后多在ＨＡ晶体颗粒之间。ＨＡ与骨生物适应性好，矿化组织可以直接沉着于ＨＡ表面或ＨＡ内部，近界面处的ＨＡ发生了一定的生物降解反应，且骨矿化与ＨＡ的降解可能达到某种平衡。     

人体肠道生物力学特性的研究

为探讨人体肠道的生物力学特性，采用电子拉伸机对人体肠道进行一维拉伸试验。结果表明，人体肠道应力-应变关系为指数函数关系。人体肠道各段的指数系数a值接近，但材料常数C有一定的差异，说明肠道各段应力-应变趋势是一致的。在一定应力下，肠道各段轴向与环向的相对伸长率是不同的，表明人体肠道具有各向异性的特性。在一定应变下，肠道各段的增量弹性模量不同，结肠增量弹性模量相对较小，因而更容易发生变形。本研究为肠道内窥镜机器人的研制提供了理论基础。     

聚D,L-乳酸/羟基磷灰石复合纤维的力学性能研究

采用熔融纺丝法制备PDLLA／HA复合纤维，探讨PDLLA／HA复合纤维的力学性能及影响因素和性能变化规律。实验结果表明：在分子量为12万的PDLLA中，加入一定量4～20μm的HA颗粒能提高复合纤维的力学性能。在PDLLA基体中添加HA的质量分数以10％为宜，以此配比制备的复合纤维的断裂强度高于其它配比复合纤维的断裂强度。采用分子量为20～30万的PDLLA制备的复合纤维断裂强度高，性能优异。复合纤维断裂强度随纤维直径的增加而下降，在直径为40～60μm时，复合纤维断裂伸长率高，弹性好。     

人体寰椎横韧带拉伸性能的实验研究

目的：研究人体寰椎横韧带的拉伸性能。方法：新鲜寰椎标本８例,制备成拉伸试件,进行定速率单向拉伸至横韧带断裂。结果：寰椎横韧带平均最大载荷为３１１．６Ｎ,最大变形量为６．０ｍｍ,刚度为７２．９Ｎ／ｍｍ。结论：寰椎侧块间的分离超过６．０ｍｍ,就可存在横韧带断裂。