Comparative evaluation of effects of different surface treatment methods on bond strength between fiber post and composite core

PURPOSE

Debonding of a composite resin core of the fiber post often occurs at the interface between these two materials. The aim of this study was to evaluate the effects of different surface treatment methods on bond strength between fiber posts and composite core.

MATERIALS AND METHODS

Sixty-four fiber posts were picked in two groups (Hetco and Exacto). Each group was further divided into four subgroups using different surface treatments: 1) silanization; 2) sandblasting; 3) Treatment with 24% H₂O₂, and 4) no treatment (control group). A cylindrical plexiglass matrix was placed around the post and filled with the core resin composite. Specimens were stored in 5000 thermal cycles between 5℃ and 55℃. Tensile bond strength (TBS) test and evaluation using stereomicroscope were performed on the specimen and the data were analyzed using two-way ANOVA, Post Hoc Scheffe tests and Fisher''s Exact Test (α=.05).

RESULTS

There was a significant difference between the effect of different surface treatments on TBS (P<.001) but different brands of post (P=.743) and interaction between the brand of post and surface treatment (P=.922) had no significant effect on TBS. Both silanization and sandblasting improved the bonding strength of fiber posts to composite resin core, but there were not any significant differences between these groups and control group.

CONCLUSION

There was not any significant difference between two brands of fiber posts that had been used in this study. Although silanization and sandblasting can improve the TBS, there was not any significant differences between surface treatments used.     

In vitro study of fracture strength of provisional crown materials

PURPOSE

The purpose of this report was to evaluate the effect of the fabrication method and material type on the fracture strength of provisional crowns.

MATERIALS AND METHODS

A master model with one crown (maxillary left second premolar) was manufactured from Cr-Co alloy. The master model was scanned, and the data set was transferred to a CAD/CAM unit (Yenamak D50, Yenadent Ltd, Istanbul, Turkey) for the Cercon Base group. For the other groups, temporary crowns were produced by direct fabrication methods (Imident, Temdent, Structur Premium, Takilon, Systemp c&b II, and Acrytemp). The specimens were subjected to water storage at 37℃ for 24 hours, and then they were thermocycled (TC, 5000×, 5-55℃) (n=10). The maximum force at fracture (Fmax) was measured in a universal test machine at 1 mm/min. Data was analyzed by non-parametric statistics (α=.05).

RESULTS

Fmax values varied between 711.09-1392.1 N. In the PMMA groups, Takilon showed the lowest values (711.09 N), and Cercon Base showed the highest values (959.59 N). In the composite groups, Structur Premium showed the highest values (1392.1 N), and Acrytemp showed the lowest values (910.05 N). The composite groups showed significantly higher values than the PMMA groups (P=.01).

CONCLUSION

Composite-based materials showed significantly higher fracture strengths than PMMA-based materials. The CAD-CAM technique offers more advantages than the direct technique.     

In vitro antimicrobial effect of the tissue conditioner containing silver nanoparticles

PURPOSE

The aim of this study was to identify in vitro antimicrobial activity of the tissue conditioner containing silver nanoparticles on microbial strains, Staphylococcus aureus, Streptococcus mutans and Candida albicans.

MATERIALS AND METHODS

Experimental disc samples (20.0×3.0 mm) of tissue conditioner (GC Soft-Liner, GC cooperation, Tokyo, Japan) containing 0.1 - 3.0% silver nanoparticles (0%: control) were fabricated. Samples were placed on separate culture plate dish and microbial suspensions (100 µL) of tested strains were inoculated then incubated at 37℃. Microbial growth was verified at 24 hrs and 72 hrs and the antimicrobial effects of samples were evaluated as a percentage of viable cells in withdrawn suspension (100 µL). Data were recorded as the mean of three colony forming unit (CFU) numerations and the borderline of the antimicrobial effect was determined at 0.1% viable cells.

RESULTS

A 0.1% silver nanoparticles combined to tissue conditioner displayed minimal bactericidal effect against Staphylococcus aureus and Streptococcus mutans strains, a 0.5% for fungal strain. Control group did not show any microbial inhibitory effect and there were no statistical difference between 24 hrs and extended 72 hrs incubation time (P > .05).

CONCLUSION

Within the limitation of this in vitro study, the results suggest that the tissue conditioner containing silver nanoparticles could be an antimicrobial dental material in denture plaque control. Further mechanical stability and toxicity studies are still required.     

Comparison of light transmittance in different thicknesses of zirconia under various light curing units

PURPOSE

The objective of this study was to compare the light transmittance of zirconia in different thicknesses using various light curing units.

MATERIALS AND METHODS

A total of 21 disc-shaped zirconia specimens (5 mm in diameter) in different thicknesses (0.3, 0.5 and 0.8 mm) were prepared. The light transmittance of the specimens under three different light-curing units (quartz tungsten halogen, light-emitting diodes and plasma arc) was compared by using a hand-held radiometer. Statistical significance was determined using two-way ANOVA (α=.05).

RESULTS

ANOVA revealed that thickness of zirconia and light curing unit had significant effects on light transmittance (P<.001).

CONCLUSION

Greater thickness of zirconia results in lower light transmittance. Light-emitting diodes light-curing units might be considered as effective as Plasma arc light-curing units or more effective than Quartz-tungsten-halogen light-curing units for polymerization of the resin-based materials.     

The effect of two artificial salivas on the adhesion of Candida albicans to heat-polymerized acrylic resin

PURPOSE

Xerostomia can diminish the quality of life, leads to changes in normal chemical composition of saliva and oral microbiata, and increases the risk for opportunistic infections, such as Candida albicans. Various artificial salivas have been considered for patients with xerostomia. However, the knowledge on the antifungal and antiadhesive activity of artificial saliva substitutes is limited. The aim of the present study was to evaluate influence of two artificial salivas on the adhesion of Candida albicans to the polymethylmethacrylate disc specimens.

MATERIALS AND METHODS

Two commercial artificial salivas (Saliva Orthana and Biotene Oral Balance Gel) were selected. 45 polymethylmethacrylate disc specimens were prepared and randomly allocated into 3 groups; Saliva Orthana, Biotene-Oral Balance gel and distilled water. Specimens were stored in the artificial saliva or in the sterile distilled water for 60 minutes at 37℃. Then they were exposed to yeast suspensions including Candida albicans. Yeast cells were counted using ×40 magnification under a light microscope and data were analysed.

RESULTS

Analysis of data indicated statistically significant difference in adhesion of Candida albicans among all experimental groups (P=.000). Findings indicated that Saliva Orthana had higher adhesion scores than the Biotene Oral Balance gel and distilled water (P<.05).

CONCLUSION

In comparison of Saliva Orthana, the use of Biotene Oral Balance Gel including lysozyme, lactoferrin and peroxidase may be an appropriate treatment method to prevent of adhesion of Candida albicans and related infections in patients with xerostomia.     

Bond strength of veneer ceramic and zirconia cores with different surface modifications after microwave sintering

PURPOSE

To evaluate the effects of surface treatments on shear bond strength (SBS) between microwave and conventionally sintered zirconia core/veneers.

MATERIALS AND METHODS

96 disc shaped Noritake Alliance zirconia specimens were fabricated using YenaDent CAM unit and were divided in 2 groups with respect to microwave or conventional methods (n=48/group). Surface roughness (Ra) evaluation was made with a profilometer on randomly selected microwave (n=10) and conventionally sintered (n=10) cores. Specimens were then assessed into 4 subgroups according to surface treatments applied (n=12/group). Groups for microwave (M) and conventionally (C) sintered core specimens were as follows; M_C,C_C: untreated (control group), M₁,C₁:Al₂O₃ sandblasting, M₂,C₂:liner, M₃,C₃:Al₂O₃ sandblasting followed by liner. Veneer ceramic was fired on zirconia cores and specimens were thermocycled (6000 cycles between 5°-55℃). All specimens were subjected to SBS test using a universal testing machine at 0.5 mm/min, failure were evaluated under an optical microscope. Data were statistically analyzed using Shapiro Wilk, Levene, Post-hoc Tukey HSD and Student''s t tests, Two-Way-Variance-Analysis and One-Way-Variance-Analysis (α=.05).

RESULTS

Conventionally sintered specimens (1.06 ± 0.32 µm) showed rougher surfaces compared to microwave sintered ones (0.76 ± 0.32 µm)(P=.046), however, no correlation was found between SBS and surface roughness (r=-0.109, P=.658). The statistical comparison of the shear bond strengths of C₃ and C₁ group (P=.015); C_C and M_C group (P=.004) and C₃ and M₃ group presented statistically higher (P=.005) values. While adhesive failure was not seen in any of the groups, cohesive and combined patterns were seen in all groups.

CONCLUSION

Based on the results of this in-vitro study, Al₂O_3- sandblasting followed by liner application on conventionally sintered zirconia cores may be preferred to enhance bond strength.     

Influence of surface modification techniques on shear bond strength between different zirconia cores and veneering ceramics

PURPOSE

Veneering porcelain might be delaminated from underlying zirconia-based ceramics. The aim of this study was the evaluation of the effect of different surface treatments and type of zirconia (white or colored) on shear bond strength (SBS) of zirconia core and its veneering porcelain.

MATERIALS AND METHODS

Eighty zirconia disks (40 white and 40 colored; 10 mm in diameter and 4 mm thick) were treated with three different mechanical surface conditioning methods (Sandblasting with 110 µm Al₂O₃ particle, grinding, sandblasting and liner application). One group had received no treatment. These disks were veneered with 3 mm thick and 5 mm diameter Cercon Ceram Kiss porcelain and SBS test was conducted (cross-head speed = 1 mm/min). Two and one way ANOVA, Tukey''s HSD Past hoc, and T-test were selected to analyzed the data (α=0.05).

RESULTS

In this study, the factor of different types of zirconia ceramics (P=.462) had no significant effect on SBS, but the factors of different surface modification techniques (P=.005) and interaction effect (P=.018) had a significant effect on SBS. Within colored zirconia group, there were no significant differences in mean SBS among the four surface treatment subgroups (P=0.183). Within white zirconia group, "Ground group" exhibited a significantly lower SBS value than "as milled" or control (P=0.001) and liner (P=.05) groups.

CONCLUSION

Type of zirconia did not have any effect on bond strength between zirconia core and veneer ceramic. Surface treatment had different effects on the SBS of the different zirconia types and grinding dramatically decreased the SBS of white zirconia-porcelain.     

Mechanical analysis of conventional and small diameter conical implant abutments

PURPOSE

The aim of the present study was to evaluate if a smaller morse taper abutment has a negative effect on the fracture resistance of implant-abutment connections under oblique compressive loads compared to a conventional abutment.

MATERIALS AND METHODS

Twenty morse taper conventional abutments (4.8 mm diameter) and smaller abutments (3.8 mm diameter) were tightened (20 Ncm) to their respective implants (3.5 × 11 mm) and after a 10 minute interval, implant/abutment assemblies were subjected to static compressive test, performed in a universal test machine with 1 mm/min displacement, at 45° inclination. The maximum deformation force was determined. Data were statistically analyzed by student t test.

RESULTS

Maximum deformation force of 4.8 mm and 3.8 mm abutments was approximately 95.33 kgf and 95.25 kgf, respectively, but no fractures were noted after mechanical test. Statistical analysis demonstrated that the evaluated abutments were statistically similar (P=.230).

CONCLUSION

Abutment measuring 3.8 mm in diameter (reduced) presented mechanical properties similar to 4.8 mm (conventional) abutments, enabling its clinical use as indicated.     

The effect of low temperature aging on the mechanical property & phase stability of Y-TZP ceramics

STATEMENT OF PROBLEM

Recently Yttrium-stabilized tetragonal zirconia polycrystal (Y-TZP) has been introduced due to superior flexural strength and fracture toughness compared to other dental ceramic systems. Although zirconia has outstanding mechanical properties, the phenomenon of decrease in the life-time of zirconia resulted from degradation in flexural strength after low temperature aging has been reported.

PURPOSE

The objective of this study was to investigate degradation of flexural strength of Y-TZP ceramics after various low temperature aging treatments and to evaluate the phase stability and micro-structural change after aging by using X-ray diffraction analysis and a scanning electron microscope (SEM).

MATERIAL AND METHODS

Y-TZP blocks of Vita In-Ceram YZ (Vita Zahnfabrik, Bad Säckingen, Germany) were prepared in 40 mm (length) × 4 mm (width) × 3 mm (height) samples. Specimens were artificially aged in distilled water by heat-treatment at a temperature of 75, 100, 125, 150, 175, 200, and 225℃ for 10 hours, in order to induce the phase transformation at the surface. To measure the mechanical property, the specimens were subjected to a four-point bending test using a universal testing machine (Instron model 3365; Instron, Canton, Mass, USA). In addition, X-ray diffraction analysis (DMAX 2500; Rigaku, Tokyo, Japan) and SEM (Hitachi s4700; Jeol Ltd, Tokyo, Japan) were performed to estimate the phase transformation. The statistical analysis was done using SAS 9.1.3 (SAS institute, USA). The flexural strength data of the experimental groups were analyzed by one-way analysis of variance and to detect statistically significant differences (α= .05).

RESULTS

The mean flexural strength of sintered Vita In-Ceram YZ without autoclaving was 798 MPa. When applied aging temperature at below 125℃ for 10 hours, the flexural strength of Vita In-Ceram YZ increased up to 1,161 MPa. However, at above 150℃, the flexural strength started to decrease. Although low temperature aging caused the tetragonal-to-monoclinic phase transformation related to temperature, the minimum flexural strength was above 700 MPa.

CONCLUSION

The monoclinic phase started to appear after aging treatment above 100℃. With the higher aging temperature, the fraction of monoclinic phase increased. The ratio of monoclinic/tetragonal + monoclinic phase reached a plateau value, circa 75% above 175℃. The point of monoclinic concentration at which the flexural strength begins to decrease was between 12% and 54%.     

Prosthetic misfit of implant-supported prosthesis obtained by an alternative section method

PURPOSE

Adequate passive-fitting of one-piece cast 3-element implant-supported frameworks is hard to achieve. This short communication aims to present an alternative method for section of one-piece cast frameworks and for casting implant-supported frameworks.

MATERIALS AND METHODS

Three-unit implant-supported nickel-chromium (Ni-Cr) frameworks were tested for vertical misfit (n = 6). The frameworks were cast as one-piece (Group A) and later transversally sectioned through a diagonal axis (Group B) and compared to frameworks that were cast diagonally separated (Group C). All separated frameworks were laser welded. Only one side of the frameworks was screwed.

RESULTS

The results on the tightened side were significantly lower in Group C (6.43 ± 3.24 µm) when compared to Groups A (16.50 ± 7.55 µm) and B (16.27 ± 1.71 µm) (P<.05). On the opposite side, the diagonal section of the one-piece castings for laser welding showed significant improvement in the levels of misfit of the frameworks (Group A, 58.66±14.30 µm; Group B, 39.48±12.03 µm; Group C, 23.13±8.24 µm) (P<.05).

CONCLUSION

Casting diagonally sectioned frameworks lowers the misfit levels. Lower misfit levels for the frameworks can be achieved by diagonally sectioning one-piece frameworks.     

BOND STRENGTH OF HARD CHAIRSIDE RELINE RESINS TO A RAPID POLYMERIZING DENTURE BASE RESIN BEFORE AND AFTER THERMAL CYCLING

Purpose:

This study assessed the shear bond strength of 4 hard chairside reline resins (Kooliner, Tokuso Rebase Fast, Duraliner II, Ufi Gel Hard) to a rapid polymerizing denture base resin (QC-20) processed using 2 polymerization cycles (A or B), before and after thermal cycling.

Materials and Methods:

Cylinders (3.5 mm x 5.0 mm) of the reline resins were bonded to cylinders of QC-20 polymerized using cycle A (boiling water–20 minutes) or B (boiling water; remove heat-20 minutes; boiling water–20 minutes). For each reline resin/polymerization cycle combination, 10 specimens (groups CAt e CBt) were thermally cycled (5 and 55 °C; dwell time 30 seconds; 2,000 cycles); the other 10 were tested without thermal cycling (groups CAwt ad CBwt). Shear bond tests (0.5 mm/min) were performed on the specimens and the failure mode was assessed. Data were analyzed by 3-way ANOVA and Newman-Keuls post-hoc test (α=.05).

Results:

QC-20 resin demonstrated the lowest bond strengths among the reline materials (P<.05) and mainly failed cohesively. Overall, the bond strength of the hard chairside reline resins were similar (10.09±1.40 to 15.17±1.73 MPa) and most of the failures were adhesive/cohesive (mixed mode). However, Ufi Gel Hard bonded to QC-20 polymerized using cycle A and not thermally cycled showed the highest bond strength (P<.001). When Tokuso Rebase Fast and Duraliner II were bonded to QC-20 resin polymerized using cycle A, the bond strength was increased (P=.043) after thermal cycling.

Conclusions:

QC-20 displayed the lowest bond strength values in all groups. In general, the bond strengths of the hard chairside reline resins were comparable and not affected by polymerization cycle of QC-20 resin and thermal cycling.     

Effect of different veneering techniques on the fracture strength of metal and zirconia frameworks

PURPOSE

To determine whether the fracture strengths and failure types differed between metal and zirconia frameworks veneered with pressable or layering ceramics.

MATERIALS AND METHODS

A phantom molar tooth was prepared and duplicated in 40 cobalt-chromium abutments. Twenty metal (IPS d.SIGN 15, Ivoclar, Vivadent, Schaan, Liechtenstein) and 20 zirconia (IPS e.max ZirCAD, Ivoclar) frameworks were fabricated on the abutments. Each framework group was randomly divided into 2 subgroups according to the veneering material: pressable and layering ceramics (n=10). Forty molar crowns were fabricated, cemented onto the corresponding abutments and then thermocycled (5-55℃, 10,000 cycles). A load was applied in a universal testing machine until a fracture occurred on the crowns. In addition, failure types were examined using a stereomicroscope. Fracture load data were analyzed using one-way ANOVA and Tukey HSD post-hoc tests at a significance level of 0.05.

RESULTS

The highest strength value was seen in metal-pressable (MP) group, whereas zirconia-pressable (ZP) group exhibited the lowest one. Moreover, group MP showed significantly higher fracture loads than group ZP (P=.015) and zirconia-layering (ZL) (P=.038) group. No significant difference in fracture strength was detected between groups MP and ML, and groups ZP and ZL (P>.05). Predominant fracture types were cohesive for metal groups and adhesive for zirconia groups.

CONCLUSION

Fracture strength of a restoration with a metal or a zirconia framework was independent of the veneering techniques. However, the pressing technique over metal frameworks resisted significantly higher fracture loads than zirconia frameworks.     

Relationship of tooth mortality and implant treatment in Type 2 diabetes mellitus patients in Korean adults

PURPOSE

The purpose of this study was to to analyze the effect of Type 2 diabetes on tooth mortality, implant treatment and prosthetic status.

MATERIALS AND METHODS

275 Type 2 diabetics and 300 non-diabetics, aged 40-80 years were selected for analysis. The assessment of number of teeth, missing teeth, fixed prostheses (bridge pontics), implants using panoramic radiographs and dental records were carried out.

RESULTS

Diabetes mellitus (DM) patients had a higher number of missing teeth (P<.05) and placed implants (P=.074), age (P<.05), male gender percentage (P=.042), smoker percentage (P<.05) than non-DM patients. In univariate analysis, the patients in older group showed significantly higher number of tooth loss rate at the first dental examination than the patients in younger group. Tooth loss rate of smokers did not show higher value than that of non-smokers. When multiple variables including DM, age, smoking, gender were considered together, diabetics and older group patients showed significantly higher tooth loss rate at the first dental examination than non-diabetics and younger group patients, respectively. Smokers and male group did not show a significant difference than non-smokers and female group, respectively.

CONCLUSION

Tooth mortality and implant treatment rate were significantly higher in the DM group as indicated by univariate and multivariate logistic regression analysis. Old age groups showed significantly higher odds ratios and tooth loss rate. As diabetics showed the higher tooth loss rate than non-diabetics, diabetics also had more implant restorations than non-diabetics.     

Influence of cement thickness on resin-zirconia microtensile bond strength

PURPOSE

The aim of this study was to evaluate the influence of resin cement thickness on the microtensile bond strength between zirconium-oxide ceramic and resin cement.

MATERIALS AND METHODS

Thirty-two freshly extracted molars were transversely sectioned at the deep dentin level and bonded to air-abraded zirconium oxide ceramic disks. The specimens were divided into 8 groups based on the experimental conditions (cement type: Rely X UniCem or Panavia F 2.0, cement thickness: 40 or 160 µm, storage: thermocycled or not). They were cut into microbeams and stored in 37℃ distilled water for 24 h. Microbeams of non-thermocycled specimens were submitted to a microtensile test, whereas those of thermocycled groups were thermally cycled for 18,000 times immediately before the microtensile test. Three-way ANOVA and Sheffe''s post hoc tests were used for statistical analysis (α=95%).

RESULTS

All failures occurred at the resin-zirconia interface. Thermocycled groups showed lower microtensile bond strength than non-thermocycled groups (P<.001). Differences in cement thickness did not influence the resin-zirconia microtensile bond strength given the same resin cement or storage conditions (P>.05). The number of adhesive failures increased after thermocycling in all experimental conditions. No cohesive failure was observed in any experimental group.

CONCLUSION

When resin cements of adhesive monomers are applied over air-abraded zirconia restorations, the degree of fit does not influence the resin-zirconia microtensile bond strength.     

Elastic modulus and flexural strength comparisons of high-impact and traditional denture base acrylic resins

Background

Fractures of acrylic resin dentures are a common occurrence in clinical dentistry. The denture may be fractured accidentally when dropped or while in service in the mouth due to flexural fatigue.

Objectives

The aim of this study was to compare the elastic modulus and the flexural strength between two heat-cured acrylic resins used in denture bases: a high-impact resin (Lucitone 199) and a traditional resin (Rodex).

Materials and methods

Rectangular strips of Lucitone 199 and Rodex (10 samples each) were fabricated and stored in artificial saliva at 37 °C for 2 weeks. The specimens were subjected to a three-point flexural test. The data were statistically analysed with Student’s t-test (p ⩽ .05).

Results

The high-impact acrylic resin had a lower elastic modulus (p = .000) and higher flexural strength (p = .001) compared to the traditional acrylic resin.

Conclusion

Within the limitations of this study, it can be concluded that the high-impact acrylic resin is a suitable denture base material for patients with clinical fracture of the acrylic denture.     

Effect of abutment angulation in the retention and durability of three overdenture attachment systems: An in vitro study

PURPOSE

This in vitro study investigated and compared the durability and retention of three types of attachments.

MATERIALS AND METHODS

Three commercially available attachments were investigated: Clix®, Dalbo-Plus® and Locator®. In total, 72 samples of these attachments were placed in the acrylic resin forms and subjected to mechanical testing (5400 cycles of insertion and removal) over the respective ball or Locator abutments immersed in artificial saliva at pH 7 and 37℃. The abutments were placed at angulations of 0°, 10° and 20°. The retention force was recorded at the beginning and after 540, 1080, 2160, 3240, 4320 and 5400 insertion-removal cycles.

RESULTS

The results revealed that there were significant differences in the average values of the insertion/removal force due to angulation (F _(2.48) = 343619, P<.05) and the type of attachment (F _(7.48) = 23.220, P<.05).

CONCLUSION

Greater angulation of the abutments was found to influence the retention capacity of the attachments, and the fatigue test simulating 5 years of denture insertion and removal did not produce wear in the metal abutments.     

Occlusal scheme in a group of Thais

PURPOSE

To study the distribution of various occlusal schemes as well as associated static occlusal relationship among Thais.

MATERIALS AND METHODS

The subjects'' occlusal schemes on the left and right sides were classified as canine protected occlusion, group function, or unclassified according to the definition from Glossary of Prosthodontic Terms (8^th edition). In addition, the presence of occlusal interferences during mandibular excursions were recorded. The measurement of the horizontal overlap and vertical overlap was also performed. Chi-square, One-way ANAVA and Mann-Whitney U statistical tests were used with level of significance set at P=.05.

RESULTS

Total of 104 subjects were included in this study. The ratio for male to female was 1.8 to 1. Average age of the population was 25.01±6.87 years old. The mean vertical overlap and horizontal overlap were 1.94±1.20 and 2.41±1.32 mm respectively. The majority of the populations (68.3%) possessed group function occlusal scheme. For the remaining, 17.3% possess canine protected occlusion and 12.5% possess combination of both occlusal schemes. We also found that occlusal interference was presented in 20.2% of the population. The most common was protrusive interference (57.14%), the second was balancing interference (38.1%) and the third was working interference (4.1%).

CONCLUSION

Among Thais, the most common occlusal scheme was group function, however there were no significant occlusal factors related to any particular occlusal scheme.     

The effect of ceramic thickness and number of firings on the color of a zirconium oxide based all ceramic system fabricated using CAD/CAM technology

PURPOSE

Ceramics have a long history in fixed prosthodontics for achieving optimal esthetics and various materials have been used to improve ceramic core strength. However, there is a lack of information on how color is affected by fabrication procedure. The purpose of this study was to evaluate the effects of various dentin ceramic thicknesses and repeated firings on the color of zirconium oxide all-ceramic system (Lava™) fabricated using CAD/CAM technology.

MATERIALS AND METHODS

Thirty disc-shaped cores, 12 mm in diameter with a 1 mm thickness were fabricated from zirconium oxide based all ceramic systems (Lava™, 3M ESPE, St Paul, MN, USA) and divided into three groups (n = 10) according to veneering with dentin ceramic thicknesses: as 0.5, 1, or 1.5 mm. Repeated firings (3, 5, 7, or 9) were performed, and the color of the specimens was compared with the color after the initial firing. Color differences among ceramic specimens were measured using a spectrophotometer (VITA Easyshade, VITA Zahnfabrik, Bad Säckingen, Germany) and data were expressed in CIELAB system coordinates. A repeated measures ANOVA and Bonferroni post hoc test were used to analyze the data (n = 10, α=.05).

RESULTS

L*a*b* values of the ceramic systems were affected by the number of firings (3, 5, 7, or 9 firings) (P<.001) and ceramic thickness (0.5, 1, or 1.5 mm) (P<.001). Significant interactions were present in L*a*b* values between the number of firings and ceramic thickness (P<.001). An increase in number of firings resulted in significant increase in L* values for both 0.5 mm and 1.5 mm thicknesses (P<.01, P=.013); however it decreased for 1 mm thickness (P<.01). The a* values increased for 1 mm and 1.5 mm thicknesses (P<.01), while it decreased for 0.5 mm specimens. The b* values increased significantly for all thicknesses (P<.01, P=.022). As the dentin ceramic thickness increased, significant reductions in L* values (P<.01) were recorded. There were significant increases in both a* and b* values (P<.01) as the dentin ceramic thickness increased.

CONCLUSION

The number of firings and dentin ceramic thickness have a definite effect on the final color of all ceramic system tested. The mean ΔE value increased as the dentin ceramic thicknesses increased for zirconium-oxide based all ceramic specimens tested. However, the mean ΔE values were less than 3.7ΔE units which is rated as a match in the oral environment.     

Evaluation of the bond strength between aged composite cores and luting agent

PURPOSE

The aim of this study was to evaluate effect of different surface treatment methods on the bond strength between aged composite-resin core and luting agent.

MATERIALS AND METHODS

Seventy-five resin composites and also seventy-five zirconia ceramic discs were prepared. 60 composite samples were exposed to thermal aging (10,000 cycles, 5 to 55℃) and different surface treatment. All specimens were separated into 5 groups (n=15): 1) Intact specimens 2) Thermal aging-air polishing 3) Thermal aging- Er:YAG laser irradiation 4) Thermal aging- acid etching 5) Thermal-aging. All specimens were bonded to the zirconia discs with resin cement and fixed to universal testing machine and bond strength testing loaded to failure with a crosshead speed of 0.5 mm/min. The fractured surface was classified as adhesive failure, cohesive failure and adhesive-cohesive failure. The bond strength data was statistically compared by the Kruskal-Wallis method complemented by the Bonferroni correction Mann-Whitney U test. The probability level for statistical significance was set at α=.05.

RESULTS

Thermal aging and different surface treatment methods have significant effect on the bond strength between composite-resin cores and luting-agent (P<.05). The mean baseline bond strength values ranged between 7.07 ± 2.11 and 26.05 ± 6.53 N. The highest bond strength of 26.05 ± 6.53 N was obtained with Group 3. Group 5 showed the lowest value of bond strength.

CONCLUSION

Appropriate surface treatment method should be applied to aged composite resin cores or aged-composites restorations should be replaced for the optimal bond strength and the clinical success.     

Comparative evaluation of sodium hypochlorite and microwave disinfection on dimensional stability of denture bases

PURPOSE

To compare the effect of sodium hypochlorite and microwave disinfection on the dimensional stability of denture bases without and with relining.

MATERIALS AND METHODS

A brass die was prepared by simulating an edentulous maxillary arch. It was used to fabricate 1.5 mm and 3 mm of thickness denture bases (n = 40). The 1.5 mm of thickness-specimens (n = 20) were relined with 1.5 mm of autopolymerizing relining resin. Five holes were prepared over crest of ridge of brass die with intimately fitting stainless steel pins which were transferred to the intaglio surface of specimens during fabrication of denture bases. For calculation of dimensional changes in denture bases, differences between the baseline area before and after disinfection of the specimens were used. The denture bases without and with relining were divided into 2 groups (each n = 20). Data were analyzed using student paired ''t'' and unpaired ''t'' test.

RESULTS

Microwave disinfection produces significant shrinkage in both denture bases without relining (t = 17.16; P<.001) and with relining (t = 14.9; P<.001). Denture bases without relining showed more shrinkage when compared with relined denture bases after microwave disinfection (t = 6.09; P<.001). The changes in dimensional stability after sodium hypochlorite disinfection were not significant for both denture bases without relining (t = 2.19; P=.056) and denture bases with relining (t = 2.17; P=.058).

CONCLUSION

Microwave disinfection leads to increased shrinkage of denture bases without and with relining. Chemical disinfection with sodium hypochlorite seems to be a safer method of disinfection with regards to physical properties such as changes in dimensional stability.