Effect of bisphosphonates on anodized and heat-treated titanium surfaces: an animal experimental study

Background: Recent investigations reported that osseointegration of titanium implants can be significantly reinforced with a nanostructure treated with anodic oxidation and heat treatment. This experimental study investigates the effect of bisphosphonates on the nanotubular implant surface in rats. Methods: Thirty‐six titanium implants were divided into three groups: 1) machine‐turned (MT), 2) anodized and heat‐treated (AH), and 3) anodized and heat‐ and bisphosphonate‐treated (AHB) groups. The 36 implants were randomly placed in both tibias of 18 male Wistar rats. After 2 and 4 weeks, the levels of osseointegration of the implants were evaluated by a removal torque test and microcomputerized tomography (μCT). Peri‐implant bone tissue on the extracted region was examined for the expression of type I collagen and osteocalcin. Results: The AHB group showed the highest removal torque at 2 and 4 weeks (13.92 ± 1.51 Ncm and 18.10 ± 2.15 Ncm, respectively) followed, in order, by the AH group (11.63 ± 1.58 Ncm at 2 weeks and 14.80 ± 2.34 Ncm at 4 weeks) and MT group (4.30 ± 0.76 Ncm at 2 weeks and 6.20 ± 1.33 Ncm at 4 weeks) with statistically significant differences between the MT and other two groups at both time points. μCT images also revealed a denser appearance around implants in the AHB group than in the other groups. Levels of type I collagen and osteocalcin expression were similar between the MT and AH groups; however, the values were significantly higher in the AHB group compared to the other groups, which were 220.85% ± 71.09% and 363.04% ± 100.21%, respectively (P <0.05). Conclusion: Within the limits of this experiment, it was concluded that surface loading with bisphosphonates significantly improved the degree of osseointegration of titanium implants with a nanostructure.