目的 通过微拉伸粘接强度实验,探讨激光对全酸蚀粘接剂处理后的非龋性硬化牙本质与复合树脂粘接强度的影响.方法 选择牙本质视觉分级为3级以上的(牙合)面磨损后牙10颗,每颗牙以低速锯垂直于牙本质表面,将硬化牙本质分为面积相等的两部分(约12 mm2),按随机数字表法将这两部分分为实验组和对照组,实验组经Nd∶YAG激光(1 W,10 Hz)处理后,使用Scotchbond (STB)酸蚀、涂布粘接剂Adper Single bond 2(ASB)联合Z350复合树脂充填,对照组使用STB酸蚀、涂布粘接剂ASB联合Z350复合树脂充填.置于37 ℃生理盐水中24 h后,制作微拉伸试件并测试微拉伸粘接强度,体视显微镜下观察断裂模式并分类.采用SPSS13.0软件对微拉伸粘接强度值做t检验.结果 实验组粘接强度[(26.11±1. 62)Mpa]显著高于对照组[(22.27±2.16)Mpa],差异有统计学意义(P=0.006).体视显微镜下可见断裂多发生于牙本质-树脂粘接面.结论 Nd∶YAG激光能够提高硬化牙本质与全酸蚀粘接系统的粘接强度.

Effects of Nd: YAG laser on micro-tensile bond strength of single bond adhesive system for noncarious sclerotic dentin

Objective To investigate the effect of Nd: YAG laser on microtensile bond strength of single bond adhesive system for non-carious sclerotic dentin. Methods Ten human molars with occlusal wearing were cut into equal halves ( nearly 12 mm2 ), and randomly divided into experimental group and control group. The teeth in experimental group were processed with Nd: YAG laser( 1 W,10 Hz) ,and then applied with Scotchbond and filled with Z350 resin. In control group, the teeth were processed with single bond and filled with Z350 resin. The specimens were sectioned, and the microtensile bond strengths of each sample was tested by a universal testing machine. Results The bond strength of the experimental group [ (26. 11 ±1.62) MPa] was significantly higher than that of the control group[ (22. 27 ±2. 16) MPa],P＜0. 05. Stero-microscope examination indicated that most of the fractures occurred in dentin-resin interface. Conclusions Nd: YAG laser can increase the rnicrotensile bond strength of single bond adhesive system in non-carious sclerotic dentin.