预浸润玻璃纤维强化复合树脂的力学性能

大学口腔医院　修复科;2.北京大学口腔医院　材料教研室,北京100081) 摘要]　目的　研究预浸润玻璃纤维对不同复合树脂的强化效果。方法　制作Sinfony和belleGlass两种复合树脂的加入和不加预浸润玻璃纤维的标准试件(25 mm×2 mm×2 mm),于(37±1)℃的蒸馏水环境中保存24 h后,在万能力学试验机上测试弯曲强度和弹性模量。结果　Sinfony复合树脂加入纤维后弯曲强度和弹性模量显著提高,分别为(555·76±67·31)MPa和(12·59±3·06)GPa,较不加玻璃纤维试件平均提高了4·9和2·5倍(P=0);belleGlass复合树脂加入纤维后弹性模量有提高,为(14·10±2·88)Gpa,较不加玻璃纤维试件平均提高了0·9倍(P=0),而弯曲强度提高不明显。结论　预浸润玻璃纤维可以显著提高复合树脂的力学性能,但对不同复合树脂的强化效果有明显差别。

Mechanical Properties of Preimpregnated Glass Fiber Reinforced Composite Resins

OBJECTIVE: To study the mechanical properties of two kinds of composite resins reinforced by preimpregnated glass fibers. METHODS: Sinfony and belleGlass composite resins were used to make standard samples (25 mm x 2 mm x 2 mm) with and without glass fibers. After all specimens were stored for 24 hours in distilled water at (37 +/- 1) degrees C, the flexural strength and flexural modulus were measured on a universal test machine. RESULTS: Both flexural strength and flexural modulus of Sinfony composite reinforced by the glass fibers became significantly increased, which were (555.76 +/- 67.31) MPa and (12.59 +/- 3.06) GPa respectively, and 4.5 and 2.5 times much more than those of the specimens without glass fibers (P = 0); the flexural modulus of belleGlass composite became significantly increased, which was (14.10 +/- 2.88) GPa, and 0.9 time much more than the specimens without glass fibers (P = 0), but the improvement of flexural strength was not significant. CONCLUSION: Glass fibers can improve the mechanical properties of composite resins, but the reinforcement effect is different between different resins.