Metal-ceramic bond strength of Co-Cr alloy fabricated by selective laser melting |
| |
Authors: | Xiang Nan Xin Xian-Zhen Chen Jie Wei Bin |
| |
Institution: | Department of Prosthodontics, Ninth People's Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai Key Laboratory of Stomatology, Shanghai, China. |
| |
Abstract: | ObjectivesThis study was to evaluated the metal–ceramic bond strength of a Co–Cr dental alloy prepared using a selective laser melting (SLM) technique.MethodsTwo groups comprised of twenty Co–Cr metal bars each were prepared using either a SLM or traditional lost-wax casting method. Ten bars from each group were moulded into standard ISO 9693:1999 dimensions of 25 mm × 3 mm × 0.5 mm with 1.1 mm of porcelain fused onto an 8 mm × 3 mm rectangular area in the centre of each bar. Metal–ceramic bonding was assessed using a three-point bending test. Fracture mode analysis and area fraction of adherence porcelain (AFAP) were determined by measuring Si content of specimens by SEM/EDS.ResultsStudent's t-test within the groups demonstrated no significant difference for the mean bond strength between the SLM and traditional cast sample groups. While SEM/EDS analysis indicated a mixed fracture mode on the debonding interface of both the SLM and the cast groups, the SLM group showed significantly more porcelain adherence than the control group (p < 0.05).ConclusionsThe SLM metal–ceramic system exhibited a bonding strength that exceeds the requirement of ISO 9691:1999(E) and it even showed a better behaviour in porcelain adherence test comparable to traditional cast methods. |
| |
Keywords: | |
本文献已被 ScienceDirect PubMed 等数据库收录! |