| Abstract: | Poly(3-hexylthiophene) (PT6), poly(3-octylthiophene) (PT8), poly(3-decylthiophene) (PT10) and poly(3-dodecylthiophene) (PT12) were synthesized by electrochemical and chemical polymerization. Investigation of these polymers by means of gel permeation chromatography indicates that the polymers prepared from the different monomers under similar conditions do not differ substantially considering molecular weight and molecular weight distribution. Bimodal distributions were found for electropolymerized polymers, and with increasing polymerization time, the high-molecular-weight and probably highly branched fraction increased relatively to the low-molecular-weight fraction. The microstructure of the polymers was investigated by nuclear magnetic resonance, and it has been found that the polymers exhibit more types of structural units than expected from a simple coupling of adjacent thiophene moieties in 2,5′-positions. Chemical oxidation with iron trichloride in chloroform gave soluble, high-molecular-weight poly(3-alkyl-thiophene)s with a rather low amount of irregular couplings, and these more regular polymers exhibited a higher degree of crytallinity. Room temperature conductivities of the oxidized polymers were between 0,1 and 30 S/cm depending on the polymerization conditions, but these values were rather independent of the length of the alkyl substituent. |