Bacterial adhesion and growth on a polymer brush-coating

Biomaterials-related infections pose serious problems in implant surgery, despite the development of non-adhesive coatings. Non-adhesive coatings, like polymer brush-coatings, have so far only been investigated with respect to preventing initial bacterial adhesion, but never with respect to effects on kinetics of bacterial growth. Here, we compare adhesion and 20h growth of three bacterial strains (Staphylococcus aureus, Staphylococcus epidermidis and Pseudomonas aeruginosa) on pristine and brush-coated silicone rubber in a parallel plate flow chamber. Brush-coatings were made using a tri-block copolymer of polyethylene oxide (PEO) and polypropylene oxide (PPO). Brush-coatings prevented adhesion of staphylococci to below 5x10(5)cm(-2) after 30min, which is a 10-fold reduction compared to pristine silicone rubber. Biofilms grew on both brush-coated and pristine silicone rubber, while the viability of biofilms on brush-coatings was higher than on pristine silicone rubber. However, biofilms on brush-coatings developed more slowly and detached almost fully by high fluid shear. Brush-coating remained non-adhesive after S. epidermidis biofilm formation and subsequent removal whereas a part of its functionality was lost after removal of S. aureus biofilms. Adhesion, growth and detachment of P. aeruginosa were not significantly different on brush-coatings as compared with pristine silicone rubber, although here too the viability of biofilms on brush-coatings was higher. We conclude that polymer brush-coatings strongly reduce initial adhesion of staphylococci and delay their biofilm growth. In addition, biofilms on brush-coatings are more viable and easily removed by the application of fluid shear.