A series of four novel alkaline earth metal–organic frameworks constructed of Ca(ii), Sr(ii), Ba(ii) ions and tetrahedral MTB linker: structural diversity,stability study and low/high-pressure gas adsorption properties

A series of four novel microporous alkaline earth metal–organic frameworks (AE-MOFs) containing methanetetrabenzoate linker (MTB) with composition {[Ca₄(μ₈-MTB)₂]·2DMF·4H₂O}_n (UPJS-6), {[Ca₄(μ₄-O)(μ₈-MTB)_3/2(H₂O)₄]·4DMF·4H₂O}_n (UPJS-7), {[Sr₃(μ₇-MTB)_3/2]·4DMF·7H₂O}_n (UPJS-8) and {[Ba₃(μ₇-MTB)_3/2(H₂O)₆]·2DMF·4H₂O}_n (UPJS-9) (UPJS = University of Pavol Jozef Safarik) have been successfully prepared and characterized. The framework stability and thermal robustness of prepared materials were investigated using thermogravimetric analysis (TGA) and high-energy powder X-ray diffraction (HE-PXRD). MOFs were tested as adsorbents for different gases at various pressures and temperatures. Nitrogen and argon adsorption showed that the activated samples have moderate BET surface areas: 103 m² g⁻¹ (N₂)/126 m² g⁻¹ (Ar) for UPJS-7′′, 320 m² g⁻¹ (N₂)/358 m² g⁻¹ (Ar) for UPJS-9′′ and UPJS-8′′ adsorbs only a limited amount of N₂ and Ar. It should be noted that all prepared compounds adsorb carbon dioxide with storage capacities ranging from 3.9 to 2.4 wt% at 20 °C and 1 atm, and 16.4–13.5 wt% at 30 °C and 20 bar. Methane adsorption isotherms show no adsorption at low pressures and with increasing pressure the storage capacity increases to 4.0–2.9 wt% of CH₄ at 30 °C and 20 bar. Compounds displayed the highest hydrogen uptake of 3.7–1.8 wt% at −196 °C and 800 Torr among MTB containing MOFs.

Four novel microporous alkaline earth metal–organic frameworks (AE-MOFs) containing methanetetrabenzoate linker (MTB): UPJS-6, UPJS-7, UPJS-8 and UPJS-9 have been successfully prepared, characterized and tested as adsorbents for different gases.