A facile method for the preparation of black TiO2 by Al reduction of TiO2 and their visible light photocatalytic activity

Black TiO₂ has attracted widespread attention due to its visible light absorption and wide range of applications. However, the currently reported preparation methods for black TiO₂ are not suitable for large-scale production due to its being prepared under high vacuum and over a long time. We have successfully prepared black TiO₂ under normal pressure and short time conditions. The as-prepared black titanium dioxide was characterized by XRD, XPS, TEM, UV-visible absorption spectrum and other characterization methods. The result shows that the as prepared black titanium dioxide had a disordered structure and oxygen vacancy defects on the surface, and exhibits excellent visible and near infrared absorption performance. The black TiO₂ sample was prepared under 650 °C 60 min exhibits excellent visible light photocatalytic performance, and can degrade 56% MO after visible light irradiation for 120 min.

Black TiO₂ has attracted widespread attention due to its visible light absorption and wide range of applications.