稀土氧化物着色钇稳定四方多晶氧化锆陶瓷与饰面瓷匹配性的研究

目的:探讨通过添加稀土氧化物着色剂而制备的钇稳定四方多晶氧化锆陶瓷与饰面瓷的匹配性。方法:以稀土氧化物(Pr6O11,CeO2,Er2O3)和过渡元素氧化物(MnO2)为着色剂,采用粉体掺杂方法,在四方多晶氧化锆陶瓷粉体中添加不同质量分数的着色剂,制备出6组钇稳定四方多晶氧化锆陶瓷,测定其与Vita VM9饰面瓷的抗热震性能及界面结合强度。采用SAS6.12软件包对数据进行单因素方差分析。结果:6组钇稳定四方多晶氧化锆陶瓷与Vita-VM9饰面瓷烧结后,各组在60℃～240℃测试过程未发现径向或层间开裂或裂纹现象,加热温度>240℃。6组钇稳定四方多晶氧化锆陶瓷与VitaVM9饰面瓷界面的抗剪切强度值为(36.03±3.82)～(37.98±4.89)MPa,均高于纯四方氧化锆陶瓷组的剪切强度值,但各组与纯四方氧化锆陶瓷的抗剪切强度值无显著差异(P>0.05)。结论:稀土氧化物着色钇稳定四方多晶氧化锆陶瓷与饰面瓷的匹配性达到临床应用水平。

Interface compatibility between tooth-like yttria-stabilized tetragonal zirconia polycrystal by adding rare-earth oxide and Vita VM9 veneering porcelain

PURPOSE: To evaluate the interface compatibility between tooth-like yttria-stabilized tetragonal zirconia polycrystal(Y-TZP) by adding rare-earth oxide and Vita VM9 veneering porcelain.METHODS: Six kinds(S1,S2,S3,S4,S5,S6) of tooth-like yttria stabilized tetragonal zirconia polycrystal were made by introducing internal colorating technology to detect the thermal shock resistance and interface bonding strength with Vita VM9 Bsaedentin.Statistical analysis was performed using SAS6.12 software package.RESULTS:...