Structural and Photoluminescence Investigations of Tb3+/Eu3+ Co-Doped Silicate Sol-Gel Glass-Ceramics Containing CaF2 Nanocrystals

In this work, the series of Tb³⁺/Eu³⁺ co-doped xerogels and derivative glass-ceramics containing CaF₂ nanocrystals were prepared and characterized. The in situ formation of fluoride crystals was verified by an X-ray diffraction technique (XRD) and transmission electron microscopy (TEM). The studies of the Tb³⁺/Eu³⁺ energy transfer (ET) process were performed based on excitation and emission spectra along with luminescence decay analysis. According to emission spectra recorded under near-ultraviolet (NUV) excitation (351 nm, ⁷F₆ → ⁵L₉ transition of Tb³⁺), the mutual coexistence of the ⁵D₄ → ⁷F_J (J = 6–3) (Tb³⁺) and the ⁵D₀ → ⁷F_J (J = 0–4) (Eu³⁺) luminescence bands was clearly observed. The co-doping also resulted in gradual shortening of a lifetime from the ⁵D₄ state of Tb³⁺ ions, and the ET efficiencies were varied from η_ET = 11.9% (Tb³⁺:Eu³⁺ = 1:0.5) to η_ET = 22.9% (Tb³⁺:Eu³⁺ = 1:2) for xerogels, and from η_ET = 25.7% (Tb³⁺:Eu³⁺ = 1:0.5) up to η_ET = 67.4% (Tb³⁺:Eu³⁺ = 1:2) for glass-ceramics. Performed decay analysis from the ⁵D₀ (Eu³⁺) and the ⁵D₄ (Tb³⁺) state revealed a correlation with the change in Tb³⁺–Eu³⁺ and Eu³⁺–Eu³⁺ interionic distances resulting from both the variable Tb³⁺:Eu³⁺ molar ratio and their partial segregation in CaF₂ nanophase.