Analysis of the shelf life of a two-solution bone cement |
| |
Authors: | Shim J B Warner S J Hasenwinkel J M Gilbert J L |
| |
Affiliation: | Department of Bioengineering and Neuroscience, Syracuse University, Syracuse, NY 13244-5290, USA. jashim@syr.edu |
| |
Abstract: | Two-solution bone cement consists of methyl methacrylate monomer and poly(methyl methacrylate) polymer dissolved together to yield a viscous solution. Two solutions are used such that the initiator, benzoyl peroxide (BPO), is placed in one solution and the activator, N,N, dimethyl-para-toluidine, is placed in the other. This approach to bone cement provides for a simplified use during surgery and eliminates some of the sources of porosity formation. However, the BPO-containing solution cement will spontaneously polymerize over time and will limit the useful shelf life of this component of the system. The activator-containing component is much more stable and is not as susceptible to spontaneous polymerization. In making two-solution cements, it is envisioned that antibiotics may be incorporated and that the polymer may be sterilized using gamma(gamma)-irradiation. Therefore, this study investigated the shelf life of the initiator-containing solution bone cement and studied the effects of initiator concentration, gamma-irradiation, gentamicin addition, and the role of storage temperature. Isothermal differential scanning calorimetry (Iso-DSC) techniques were used to monitor the polymerization of BPO-containing solutions. It was found that the shelf life was highly temperature dependent and followed an Arrhenius expression where refrigeration storage (4 degrees C) yielded approximately a 12-month storage time, while 70 degrees C storage results in setting in about 5-7 min. gamma-irradiation and gentamicin addition did not significantly affect the shelf life. Initiator concentration affected storage time with higher levels resulting in shorter shelf life. |
| |
Keywords: | |
本文献已被 PubMed 等数据库收录! |
|