Young’s Modulus and Vickers Hardness of the Hydroxyapatite Bioceramics with a Small Amount of the Multi-Walled Carbon Nanotubes

The Vickers hardness and Young’s modulus of the hydroxyapatite (HA) bioceramics with a small amount of the multi-walled carbon nanotubes (MWCNTs) were studied by using ultramicrotester Shimadzu for dynamic tests DUH-211. Small concentrations of MWCNTs were from 0.05 to 0.5 wt.%. The argon inert atmosphere and vacuum condition were taken for the prevention of the MWCNTs oxidation. The Brunauer–Emmett–Teller (BET) surface area S_BET of the HA-MWCNTs composites was determined by thermal adsorption-desorption of nitrogen. It was found that for HA-MWCNTs sintered in the Ar atmosphere, an increase in the concentration of nanotubes up to 0.5 wt.% leads to a decrease in porosity near 3 times in comparison to HA without MWCNTs additives. The small amount of additives of multi-walled carbon nanotubes leads to an increase in hardness of 1.3 times and compression strength of composite and compression strength of composite that is comparable in absolute values with the literature data of enamel hardness (3–5 GPa) and compression strength (95–370 MPa). The absolute values increase close to linearly with the increase of nanotube concentrations. The Young’s modulus of sintered composite slightly changes with the variation of concentrations of nanotubes and close to the enamel (75–100 GPa). The ratio of plastic work to total work and the ratio of elastic (reversible) work to the total work of deformation of composite HA/MWCNTs are practically constant at a studied range of MWCNTs concentration. The additives of the multi-walled carbon nanotubes lead to both an increase in the elasticity index of ~1.5 times and an increase in the resistance to plastic deformation of ~3 times, which improved the tribological performance of the surface. Plastic and elastic (reversible) work slightly changed.