Improvement of low-temperature NH3-SCR catalytic performance over nitrogen-doped MOx–Cr2O3–La2O3/TiO2–N (M = Cu,Fe, Ce) catalysts

A series of MO_x–Cr₂O₃–La₂O₃/TiO₂–N (M = Cu, Fe, Ce) catalysts with nitrogen doping were prepared via the impregnation method. Comparing the low-temperature NH₃-SCR activity of the catalysts, CeCrLa/Ti–N (xCeO₂–yCr₂O₃–zLa₂O₃/TiO₂–N) exhibited the best catalytic performance (NO conversion approaching 100% at 220–460 °C). The physico-chemical properties of the catalysts were characterized by XRD, BET, SEM, XPS, H₂-TPR, NH₃-TPD and in situ DRIFTS. From the XRD and SEM results, N doping affects the crystalline growth of anatase TiO₂ and MO_x (M = Cu, Fe, Ce, Cr, La) which were well dispersed over the support. Moreover, the doping of N promotes the increase of the Cr⁶⁺/Cr ratio and Ce³⁺/Ce ratio, and the surface chemical adsorption oxygen content, which suggested the improvement of the redox properties of the catalyst. And the surface acid content of the catalyst increased with the doping of N, which is related to CeCrLa/TiO₂–N having the best catalytic activity at high temperature. Therefore, the CeCrLa/TiO₂–N catalyst exhibited the best NH₃-SCR performance and the redox performance of the catalysts is the main factor affecting their activity. Furthermore, in situ DRIFTS analysis indicates that Lewis-acid sites are the main adsorption sites for ammonia onto CeCrLa/TiO₂–N and the catalyst mainly follows the L–H mechanism.

A series of MO_x–Cr₂O₃–La₂O₃/TiO₂–N (M = Cu, Fe, Ce) catalysts with nitrogen doping were prepared via the impregnation method.