Lead (Pb2+) sorptive removal using chitosan-modified biochar: batch and fixed-bed studies

Chitosan-Modified fast pyrolysis BioChar (CMBC) was used to remove Pb²⁺ from water. CMBC was made by mixing pine wood biochar with a 2% aqueous acetic acid chitosan (85% deacylated chitin) solution followed by treatment with NaOH. The characterizations of both CMBC and Non-Modified BioChar (NMBC) were done using diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS), scanning electron microscopy (SEM), surface area measurements (S_BET), elemental analysis, thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and ζ-potential measurements. Elemental analysis indicated that chitosan accounts for about 25% weight of the CMBC. The Langmuir maximum adsorption capacity of CMBC at pH 5 was 134 mg g⁻¹versus 48.2 mg g⁻¹ for NMBC at 318 K. CMBC column adsorption studies resulted in a capacity of 5.8 mg g⁻¹ (Pb²⁺ conc. 150 mg L⁻¹; pH 5; column dia 1.0 cm; column length 20 cm; bed height 5.0 cm; flow rate 2.5 mL min⁻¹). CMBC removed more Pb²⁺ than NMBC suggesting that modification with chitosan generates amine groups on the biochar surface which enhance Pb²⁺ adsorption. The modes of Pb²⁺ adsorption on CMBC were studied by comparing DRIFTS and X-ray photoelectron spectroscopy spectra before and after Pb²⁺ adsorption.

Batch and fixed-bed column studies for the removal of lead (Pb²⁺) from aqueous solution by chitosan-modified pinewood biochar.