Effect of light-curing methods on resin cement Knoop hardness at different depths |
| |
Authors: | Sinhoreti Mário Alexandre Coelho Manetta Izabella Paola Tango Rubens Nisie Iriyama Nelson Tetsu Consani Rafael Leonardo Xediek Correr-Sobrinho Lourenço |
| |
Affiliation: | Dental Materials Area, Department of Restorative Dentistry, School of Dentistry of Piracicaba, State University of Campinas, Piracicaba, SP, Brazil. |
| |
Abstract: | This study evaluated, using Knoop hardness test, the polymerization depth of Rely-X dual-cured resin cement activated by chemical reaction alone (control group) or by chemical/physical mode with light curing through a 1.5-mm-thick ceramic layer (HeraCeram). Bovine incisors had their buccal surface flattened and hybridized. On this surface, a rubber mould (5 mm diameter; 1 mm high) was bulk filled with cement. Either a polyester strip or a 1.5-mm-thick disc of the veneering material was seated over this set. Light curing was performed with either conventional halogen light (QTH; XL2500) for 40 s, light-emitting diode (LED; Ultrablue Is) for 40 s or xenon plasma arc (PAC; Apollo 95E) for 3 s. In a control group, cement setting occurred by chemical reaction alone. After storage dry in dark (24 h/37 masculineC), the specimens (n=5) were sectioned for hardness (KHN) measurements at three depths in a microhardness tester (50 gf load/15 s). Data were submitted to ANOVA and Tukey's test (a = 0.05). Rely-X cement presented higher Knoop hardness values when the QTH and LED LCUs were used, compared to the control group and PAC. Light curing with PAC resulted in lower hardness compared to the control group. Cement hardness was significantly lower in deeper regions. |
| |
Keywords: | |
本文献已被 PubMed 等数据库收录! |
|