Wear-Resistant TiC Strengthening CoCrNi-Based High-Entropy Alloy Composite
Authors:Yanlin Cai  Yonggang Tong  Yongle Hu  Hongfeng Huang  Xiancheng Zhang  Manyu Hua  Shan Xu  Yongbing Mei  Chengbiao Ma  Zhifeng Li
Abstract:In order to improve the wear resistance of CoCrNi alloy, TiC was introduced into the alloy and wear-resistant CoCrNi/(TiC)x composites were designed. The effects of TiC contents on the microstructure, mechanical properties, and wear resistance of CoCrNi matrix were investigated, respectively. It was found that the TiC produced dissolution and precipitation process in CoCrNi alloy, and a large number of needled and blocky TiC particles were precipitated in the composites. The compressive yield strength of CoCrNi/(TiC)x composites increased with the increasing TiC content. Compared with the CoCrNi alloy, the yield strength of CoCrNi/(TiC)x composites increased from 108 to 1371 MPa, and the corresponding strengthening mechanism contributed to the second phase strengthening. The wear resistance of CoCrNi/(TiC)x composites was also greatly improved due to the strengthening of TiC. Compared with the CoCrNi alloy, the specific wear rate of CoCrNi/(TiC)1.0 alloy was reduced by about 77%. The wear resistance of CoCrNi/(TiC)x composites was enhanced with the increasing content of TiC addition.
Keywords:high-entropy alloy   microstructure   TiC   wear resistance   mechanical properties
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号