桩核材料对牙本质应力分布的影响

目的 研究6种不同材料行桩核修复前后牙本质的应力分布情况,为临床桩材料的选择提供理论依据。方法 采用螺旋CT扫描数据建立上颌中切牙烤瓷桩核冠的三维有限元模型,在此模型上对用铸造Ni-Cr合金、铸造钛合金、铸造金合金、玻璃纤维树脂、聚乙烯纤维树脂及普通复合树脂6种材料行桩核修复前后的牙本质应力分布情况进行数值分析。结果 在6种材料中,与桩修复前的烤瓷熔附金属冠修复牙相比较,临床最常用的铸造Ni-Cr合金桩修复使桩尖周围牙本质的最大主应力和Von Mises应力分别升高了152％和162％;聚乙烯纤维树脂桩修复后,牙本质中的应力分布情况无明显改变。其他材料行桩修复后牙本质中应力分布的差异较大。桩植入后对牙本质应力分布模式的影响与桩的弹性模量密切相关。结论 与牙本质弹性模量接近的聚乙烯纤维树脂更适合用于桩修复。

Effects of post material on stress distribution in dentine

Objective To investigate stress distribution of different material restored post-cores in dentine and provide a theoretical guidance for clinical use. Methods A three-dimensional finite element model of maxillary central incisor restored with post-core and PFM crown was constructed by SCT scan technology. Based on this model, stress distribution in dentine was analyzed before and after post-core restorations with 6 different materials, including cast Ni-Cr alloy, cast titanium alloy, cast gold alloy, glass fiber reinforced composite, polythene fiber reinforced composite, and common composite resin. Results When the tooth was restored with cast Ni-Cr alloy post and PFM crown, the maximum tensile stress and Von Mises stress in dentin at post apex increased 152 % and 162 % respectively, compared with a tooth restored only with PFM crown. If polythene fiber reinforced composite was used as post material, the stress distribution did not significantly change. When the other materials were used for the post, the stress distribution changed greatly. The elastic modulus of post-core materials affected the stress distribution pattern in dentine. Conclusion The materials with elastic modulus similar to that of dentin, such as polythene fiber reinforced composite, may be suitable for post restoration.