Improved osteoblast compatibility of medical-grade polyetheretherketone using arc ionplated rutile/anatase titanium dioxide films for spinal implants

Titanium dioxide (TiO(2) ), known to exhibit good biocompatibility, is applied in this study as a thin film formed onto polyetheretherketone (PEEK) substrate, which has been widely used in spinal interbody fusion cages. For successful deposition, an arc ionplating (AIP) technique was applied to deposit TiO(2) at low deposition temperature without damaging PEEK substrate, while providing satisfactory film adhesion. This study systematically investigates the effects of TiO(2) thin film phase composition and surface characteristics, controlled by using different target current and substrate bias, on osteoblast compatibility. Experimental results showed that anatase phase (A-TiO(2) ) and/or rutile phase (R-TiO(2) ) TiO(2) coatings, respectively, can be prepared in appropriate deposition conditions. Overall, the TiO(2) -coated PEEK presented better osteoblast compatibility than the bare PEEK material in terms of cell adhesion, cell proliferation, and cell differentiation abilities, as well as osteogenesis performance (as determined by levels of osteopontin, osteocalcin, and calcium content). Surface roughness and hydrophilicity of the AIP-TiO(2) films were found to be responsible for significant osteoblast cell growth. It is also noticeable that the R-TiO(2) exhibited better osteoblast compatibility than the A-TiO(2) due to the presence of negatively charged hydroxyl groups on R-TiO(2) (110) surface in nature. ? 2012 Wiley Periodicals, Inc. J Biomed Mater Res Part A 100A:2787-2792, 2012.