Synthesis and characterization of some poly[nitrilo-bis(phenylamino)phosphoranetriyl]s

Polynitrilo-bis(phenylamino)phosphoranetriyl]s ( 3a–d ) were synthesized and characterized in dilute solution and in the solid state. The synthesis was accomplished by thermal polymerization of of 2,2,4,4,6,6-hexachloro--triazatriphosphorane ( 1 ) at 240°C, followed by the reaction of the soluble product, poly(nitrilodichlorophosphoranetriyl) ( 2 ), with aniline or its derivatives. Elemental analyses show the presence of some residual chlorine, which, according to the IR spectra, does not seem to be ascribed to an incomplete substitution. All the polymers have intrinsic viscosities in tetrahydrofuran higher than 100ml g^?1, and high weight average molecular weights (M _w ≥ 7 · 10⁵). The molecular weight distribution is very broad (M _w/M _n ≥ 13,4) which could suggest either a branched structure or a complex mechanism of polymerization. From DSC measurements the glass transition temperatures are found to be between 70 and 98°C and the related values of specific heat increments, ΔC_,p, are between 0,13 J g^?1 K^?1 and 0,27 J g^?1 K^?1; the densities are in the order of 1,3 g ml^?1.