Dimethacrylate based on cycloaliphatic epoxide for dental composite.

OBJECTIVES: The aim of this study was to investigate the kinetics and mechanical properties of dimethacrylate monomer based on cycloaliphatic epoxide for dental restorative composite. METHODS: Dimethacrylate based on cycloaliphatic epoxide (EPCDMA) was copolymeirzed with TEGDMA by varying the curing conditions: monomer composition and light intensity. A real-time near FTIR technique was employed to monitor the double bond conversion and the rate of polymerization. Dynamic mechanical analysis was performed on a dynamic mechanical analyzer, and volume shrinkage of the cured samples was determined by pycnometric method. RESULTS: The results of kinetics showed that, two peaks of maximum rate of polymerization (Rpmax) occurred when the amount of TEGDMA was more than 30wt%. Increasing the amount of TEGDMA, the final double bond conversion and polymerization shrinkage both increased, while the glass transition temperature (Tg) decreased. All EPCDMA/TEGDMA mixtures had slightly higher storage modulus at body temperature (37 degrees C). When compared with Bis-GMA/TEGDMA (70/30), the EPCDMA/TEGDMA (70/30) system assumed similar reactivity and volume shrinkage but higher Tg. SIGNIFICANCE: EPCDMA had comparable mechanical properties to those of Bis-GMA.