Preparation and characterization of superparamagnetic iron oxide nanoparticles stabilized by alginate |
| |
Authors: | Ma Hui-li Qi Xian-rong Maitani Yoshie Nagai Tsuneji |
| |
Affiliation: | Department of Pharmaceutics, School of Pharmaceutical Sciences, Peking University, Beijing 100083, China. |
| |
Abstract: | SPION with appropriate surface chemistry have been widely used experimentally for numerous in vivo applications. In this study, SPION stabilized by alginate (SPION-alginate) were prepared by a modified coprecipitation method. The structure, size, morphology, magnetic property and relaxivity of the SPION-alginate were characterized systematically by means of XRD, TEM, ESEM, AFM, DLS, SQUID magnetometer and MRI, respectively, and the interaction between alginate and iron oxide (Fe(3)O(4)) was characterized by FT-IR and AFM. The results revealed that typical iron oxide nanoparticles were Fe(3)O(4) with a core diameter of 5-10 nm and SPION-alginate had a hydrodynamic diameter of 193.8-483.2 nm. From the magnetization curve, the Ms of a suspension of SPION-alginate was 40 emu/g, corresponding to 73% of that of solid SPION-alginate. This high Ms may be due to the binding of Fe(3)O(4) nanoparticles to alginate macromolecule strands as visually confirmed by AFM. SPION-alginate of several hundred nanometers was stable in size for 12 months at 4 degrees C. Moreover, T1 relaxivity and T2 relaxivity of SPION-alginate in saline (1.5 T, 20 degrees C) were 7.86+/-0.20 s(-1) mM(-1) and 281.2+/-26.4 s(-1) mM(-1), respectively. |
| |
Keywords: | |
本文献已被 PubMed 等数据库收录! |
|