Microtensile bond strength of quartz fiber posts to different composite cores

The aim of this in vitro study was to assess the microtensile bond strength of quartz fiber posts to different composites, and to composite combinations used as core materials. Thirty fiber posts were treated with a 24% hydrogen peroxide solution and silanized. The posts were divided into 5 groups according to the resin composite used as follows (n = 6): G1 - ?lite Flow (Bisco, Inc), G2 - Filtek Z250 (3M ESPE), G3 - Biscore (Bisco, Inc), G4 - ?lite Flow + Filtek Z250, G5 - ?lite Flow + Biscore. The resin composites were placed around the posts to produce cylindrical specimens. Two 1-mm2 thick sticks containing the post in the center and composite cores on both ends were provided from each cylinder and tested for microtensile strength with a crosshead speed of 0.5 mm/min. One-way ANOVA and Tukey HSD tests were used for statistical analysis. Fractured surfaces were observed using a stereomicroscope with 20× magnification. Scanning electron microscopy (SEM) was used to evaluate the interface of the fractured sticks. The results showed that G2 had the highest bond strength values, and the lowest values were seen with G3. There were significant differences between groups 1, 2, 4 and groups 3, 5 (p < 0.05). Under the stereomicroscope, most of the failures were adhesive between the post and core material. Under SEM, ?lite and Z250 had smoother surfaces than Biscore, containing less porosities and voids.