Analysis of Carbonation Behavior of Cracked Concrete |
| |
| Authors: | Qun Guo Lexin Jiang Jianmin Wang Junzhe Liu |
| |
| Affiliation: | 1.College of Architecture Engineering, Qingdao Agricultural University, Qingdao 266109, China;2.College of Civil and Environmental Engineering, Ningbo University, Ningbo 315211, China; |
| |
| Abstract: | The crack and carbonation of concrete pose a great challenge to its durability. Therefore, this paper studies the effect of cracks on the carbonation depth of cement paste under different factors. The relationship between carbonation and cracks was determined, and the carbonation mechanism of cement paste with cracks was clarified. The results show that a small water–binder ratio can effectively inhibit the carbonation process. The bidirectional carbonation enlarged the carbonation area around the crack. Within 21 days of the carbonation, the carbonation depth increased with carbonation time, and the Ca(OH)2 on the surface of the specimen was sufficient, allowing for a convenient chemical reaction with CO2. The influence of crack width on the carbonation process at the crack was greater than the influence of the crack depth. Carbonation influenced the hydration of cement-based materials, altering the types and quantities of hydration products. In conclusion, accurately predicting the regularity of carbonation in cracked structures is critical for improving the durability of concrete. |
| |
| Keywords: | carbonation cracks durability cement paste |
|
|