Influence of enamel wetness on resin composite restorations using various dentine bonding agents: part I-effects on marginal quality and enamel microcrack formation |
| |
Authors: | Chuang Shu-Fen Chang Chih-Han Yaman Peter Chang Li-Tung |
| |
Affiliation: | Institute of Biomedical Engineering, National Cheng Kung University, Tainan, Taiwan, ROC. sfchuang@mail.ncku.edu.tw |
| |
Abstract: | OBJECTIVES: To investigate the influence of enamel wetness on marginal quality and enamel microcrack formation using various dentine bonding adhesives; and to determine the changes of marginal quality and enamel microcracks over time. METHODS: Forty extracted molars were each prepared with a cylindrical cavity and divided into five groups. Groups 1-4 were acid-etched and treated separately with either an ethanol-based adhesive (Single Bond) or an acetone-based adhesive (Prime&Bond NT) on either dry or wet enamel. Teeth in Group 5 were treated with a self-etching adhesive (Clearfil SE Bond). Epoxy replicas of different stages were taken after cavity preparation, after restoration, after 24 h storage, and after thermocycling test. These replicas were examined under a scanning electron microscope for their restorative marginal quality and enamel microcrack. Quantitative measurement was performed to measure the length ratio of different margin patterns, and enamel microcracks. RESULTS: There was no difference in the marginal quality when ethanol-base adhesive was applied on dry or wet dentin. The group using acetone-based adhesive on the dry enamel presented higher intact margin ratio than the group on wet enamel did only after restoration. Using self-etching primer led to higher open margin ratio at all stages. Enamel microcracks were found in all five groups and were higher in groups using acetone-based adhesives. CONCLUSION: Enamel wetness did not show a significantly adverse effect on the marginal quality of the restorations using either acetone- or ethanol-based adhesive. Using self-etching adhesive may lead to high incidence of margin deterioration. |
| |
Keywords: | Enamel Marginal quality Enamel microcrack Dentine bonding adhesive Thermocycling test Scanning electron microscope |
本文献已被 ScienceDirect PubMed 等数据库收录! |