Particulate endocytosis mediates biological responses of human mesenchymal stem cells to titanium wear debris.

Continual loading and articulation cycles undergone by metallic (e.g., titanium) alloy arthroplasty prostheses lead to liberation of a large number of metallic debris particulates, which have long been implicated as a primary cause of periprosthetic osteolysis and postarthroplasty aseptic implant loosening. Long-term stability of total joint replacement prostheses relies on proper integration between implant biomaterial and osseous tissue, and factors that interfere with this integration are likely to cause osteolysis. Because multipotent mesenchymal stem cells (MSCs) located adjacent to the implant have an osteoprogenitor function and are critical contributors to osseous tissue integrity, when their functions or activities are compromised, osteolysis will most likely occur. To date, it is not certain or sufficiently confirmed whether MSCs endocytose titanium particles, and if so, whether particulate endocytosis has any effect on cellular responses to wear debris. This study seeks to clarify the phenomenon of titanium endocytosis by human MSCs (hMSCs), and investigates the influence of endocytosis on their activities. hMSCs incubated with commercially pure titanium particles exhibited internalized particles, as observed by scanning electron microscopy and confocal laser scanning microscopy, with time-dependent reduction in the number of extracellular particles. Particulate endocytosis was associated with reduced rates of cellular proliferation and cell-substrate adhesion, suppressed osteogenic differentiation, and increased rate of apoptosis. These cellular effects of exposure to titanium particles were reduced when endocytosis was inhibited by treatment with cytochalasin D, and no significant effect was seen when hMSCs were treated only with conditioned medium obtained from particulate-treated cells. These findings strongly suggest that the biological responses of hMSCs to wear debris are triggered primarily by the direct endocytosis of titanium particulates, and not mediated by secreted soluble factors. In this manner, therapeutical approaches that suppress particle endocytosis could reduce the bioreactivity of hMSCs to particulates, and enhance long-term orthopedic implant prognosis by minimizing wear-debris periprosthethic osteolysis.     

医用钛合金在三种不同生理电解液中的耐腐蚀行为研究

利用电化学方法研究医用钛合金在0.9%NaCl生理盐水，模拟人工唾液，模拟人工体液中的腐蚀情况，分析腐蚀电位和腐蚀电流密度，扫面电镜观察腐蚀表面形貌，CA-A型接触角测试仪测试钛合金表面被腐蚀后接触角的变化。实验表明：钛合金在三种生理电解液中的腐蚀情况依次是：模拟人工唾液〉模拟人工体液〉0.9%NaCl生理盐水。扫面电镜观察表明，医用钛合金在0.9% NaCl生理盐水腐蚀后，表面出现了许多腐蚀孔，经模拟人体体液腐蚀后，表面变得粗糙不平整，腐蚀孔数目变化不大，钛合金经人工唾液腐蚀后，腐蚀孔数目增多，部分腐蚀孔孔径明显增大。经三种生理电解液腐蚀后，钛合金表面接触角都减小。结论：医用钛合金在人工唾液中的腐蚀最严重，在临床应用中应给予相应的防范措施。     

复合矫治弓丝接头的力学性能及接头组织观察

目的　测试复合矫治弓丝接头的机械性能及分析接头、接头断口变化。方法　测试复合矫治弓丝接头的拉伸强度、剪切强度、扭转强度、弯曲形变残余角,TiNi形状记忆合金丝超弹性,扫描电镜观察及分析接头、断口组织变化。结果　复合矫治弓丝接头抗拉伸强度为32 0～36 0MPa ,剪切强度为2 2 0～2 5 0MPa ,抗扭转强度为30～4 0N·m、断裂时扭转角度不小于1 4 4 0°,弯曲形变残余角为1 2～1 7°;钎焊异质接头中TiNi形状记忆合金丝超弹性几乎没有破坏;接头钎料与TiNi形状记忆合金界面不存在扩散层,与不锈钢丝界面之间有一较宽的扩散层,接头断裂多发生在钎料与TiNi形状记忆合金超弹界面处,部分发生在钎缝中心。结论　复合矫治弓丝机械性能符合正畸临床要求,可应用于临床。     

An XPS and SEM evaluation of six chemical and physical techniques for cleaning of contaminated titanium implants

The purpose of the present study was to analyse clinically failed and retrieved implants prior to and after cleaning by means of scanning electron microscopy (SEM) and X-ray induced photoelectron spectroscopy (XPS) as compared to unused controls. Six different chemical and physical techniques for cleaning of contaminated titanium implants were evaluated: 1) rinsing in absolute ethanol for 10 min, 2) cleaning in ultrasonic baths containing trichloroethylene (TRI) and absolute ethanol, 10 min in each solution, 3) abrasive cleaning for 30 s, 4) cleaning in supersaturated citric acid for 30 s, 5) cleaning with continuous CO2-laser in dry conditions at 5 W for 10 s, 6) cleaning with continuous CO2-laser in wet conditions (saline) at 5 W for 10 s. SEM of failed implants showed the presence of contaminants of varying sizes and XPS showed almost no titanium but high carbon signals. XPS of unused titanium implants showed lower levels of titanium as previously reported, probably due to contamination of carbon which increased with time in room air. Cleaning of used implants in citric acid followed by rinsing with deionized water for 5 min followed by cleaning in ultrasonic baths with TRI and absolute ethanol gave the best results with regard to macroscopical appearance and surface composition. However, as compared to the unused implants the results from an element composition point of view were still unsatisfactory. It is concluded that further development and testing of techniques for cleaning of organically contaminated titanium is needed.     

微波等离子体化学气相沉积合成TiN超细颗粒

热力学计算表明，Ｈ２，Ｎ２的过量有助于提高ＴｉＮ的产率，但能耗也相应增加。为此考察了温度，流量，ＴｉＣｌ４携带量，混合方式对产物性能的影响。结果表明，流量增加，温度升高，ＴｉＣｌ４携带量增加，混合愈好，则产物粒径愈小。在此基础上采用微波等离子体化学气相沉积法，合成了粒径为１２３－２８４ｎｍ的ＴｉＮ超细颗粒     

新型胫骨髓内钉的研制与生物力学研究

目的　研制新型胫骨串孔型髓内钉并对其进行生物力学研究。方法　用TAMZ合金制造远端锁孔由一个三个同样直径的串孔所替代的 9根新型胫骨髓内钉。将髓内钉安装在自行设计的夹具中 ,先将 3根新钉进行静态垂直压缩实验 ,根据静态实验结果 ,分别测试 6根新钉的动态疲劳强度。结果　新钉的静态压缩破坏载荷为 2 1 33N ,是人平均体重的 3倍多 ;通过 5 0万次压缩循环的条件疲劳强度为 1 2 0 0N ,约是人体重的 2倍。结论　新钉不仅能够方便临床使用 ,而且拥有较好的力学特性     

钛板联合羟基磷灰石人工骨眼眶重建

目的：探讨应用钛板联合羟基磷灰石人工骨矫正眼眶骨折眼球内陷的手术方法和疗效。方法：根据术前CT诊断明确的14例14眼眼眶骨折患者，术中用钛钉、钛板将复位的眶缘骨折进行坚强内固定．重建正常的眶缘，然后用羟基磷灰石人工骨材料植入眼眶，以填补眶腔容积的缺损，同时修复重建眶壁。结果：术后随访3～36个月，CT水平和冠状位扫描复查，10例眼球内陷的患者中，8例获得矫正，2例仍存中度内陷；8例复视患者中，7例获得满意改善，1例无效。无植人物感染、移位和脱出，未见视力丧失者。结论：钛板和复合羟基磷灰石人工骨具有很好的生物相容性，在眶壁重建手术中可获得满意的疗效。是眶壁重建术良好的替代材料。     

形状记忆合金环抱接骨板治疗锁骨骨折

目的 探讨形状记忆合金环抱接骨板治疗锁骨骨折的手术方法及疗效。方法 采用西脉记忆合金环抱接骨板治疗锁骨骨折54例。结果 54例病人全部获得随访，优良率96.3％。结论 形状记忆合金环抱接骨板治疗锁骨骨折是一种方便有效的方法，具有手术操作简便、内固定确实等优点，但应加强术后管理。     

新型记忆合金节段内固定器治疗腰椎峡部裂的实验研究

目的 :设计一种治疗腰椎峡部裂的新型记忆合金节段内固定器 ,测试其材料力学特性 ,并评价其生物力学稳定性。方法 :测量 2 0具干燥完整成人腰椎标本获得数据 ,按数据采用镍钛记忆合金设计固定器并行材料力学测试。取 6具新鲜成人腰椎标本 ,先后形成正常脊柱组、峡部裂组、横突棘突钢丝捆绑组、钩螺钉固定组、Buck螺钉固定组、新研制记忆合金固定器固定组 6组实验模型。利用脊柱三维运动实验机 ,分别测试 6组的前屈 /后伸、左 /右侧弯及左 /右轴向旋转 6种运动的活动范围。结果 :材料力学测试表明其形态记忆功能良好 ,体温状态下会产生稳定可靠的回复力。 6组在前屈、后伸及左右旋转状态 ,峡部裂组稳定性最差 ,同其他 5组差别明显。而使用新研制记忆合金内固定器组可明显恢复腰椎稳定性 ,同正常脊柱组及其他 3种内固定组均无显著差别。另两种状态左右侧弯 6组均无显著性差别。结论 :新设计的内固定器符合腰椎的生物力学要求 ,较先前的半环状内固定器优势明显 ,具有很好应用前景