义齿PMMA基托表面粗糙度影响的实验研究

目的：研究技工操作因素对义齿树脂基托表面粗糙度的影响。方法：在不同粉液比、充填时期、聚合温度、混合方式以及出盒温度成型的上颌半口义齿基托上选取1.5cm^2范围，按照统一的打磨顺序，由粗到细打磨抛光完成，浸入冷水中，7天后进行粗糙度测试，所得数据经t检验统计处理。结果：在单体含量降低组、丝状期充填组．热处理时直接放入70℃水中维持9h组与对照组相比，均存在显著差异（P〈0．05）。结论：影响PMMA树脂表面粗糙度的制作工艺因素有单体含量降低、丝状期充填和未经100℃高温热处理。     

A 2‐year report on maxillary and mandibular fixed partial dentures supported by Astra Tech dental implants. A comparison of 2 implants with different surface textures.

In 50 partially edentulous patients, 133 (48 maxillary; 85 mandibular) Astra Tech dental implants of 2 different surface textures (machined; TiO‐blasted) were alternately installed, supporting 52 fixed partial dentures (FPDs). Before abutment connection 2 machined implants (1 mandibular; 1 maxillary) were found to be non-osseointegrated and were replaced. Another implant could not be restored due to a technical complication. Two FPDs were remade because of technical complications, both because of abutment fractures. Thus, after 2 years in function, the cumulative survival rates were 97.7% and 95.7% for implants and prostheses, respectively. There was no statistically significant difference in survival rate between the 2 types of implants, 100%(TiO‐blasted) vs 95.3%(machined), P =0.24. After 2 years in function, when both jaw and type of implants were combined, the mean (SD) marginal bone loss was 0.24 (0.69) mm. No statistically significant difference in bone loss was found between the 2 tvues of implant after 2 years of loading, 0.04 (0.82) mm, P >0.30.     

Sources of unwanted variability in measurement and description of skin surface topography

Background/aims: Quantitative measurement of skin roughness has proved to be a valuable tool in the efficacy-control of external applications, but it suffers from not yielding easily comparable results. The most important sources of inter-observer variability are high-pass filters used to separate roughness and waviness, and low-pass filters which result from the finite resolution of the instrument or from the finite sampling interval of digital measurement. In the present study, the effects of high-pass filters and sampling intervals on the roughness measured were investigated. Methods: Dynamically focusing optical profilometry was used to measure the surfaces of negative replicas of healthy human skin. High-pass cut-off wavelengths and sampling intervals were varied systematically. Results/conclusions: Virtually unbiased estimates for the roughness parameters K, Sk, R_q, and R_a can be obtained using sampling intervals of 40 or even 80 μm. Regarding these roughness parameters, it is far better to do more scans than to shorten the sampling interval. The roughness parameters R_z, R_p, R_t, R_pm, R_max, P_t, on the other hand are very sensitive to the influence of the sampling interval; to achieve satisfying estimates, the sampling interval should be no longer than 2 to 5 urn; as an important parameter’of the measurement, it is worthy of remark and should always be indicated. The way the mean square roughness R_q depends on the cut-off wavelength is not well described by the Sayles-Thomas-relation R_q～λ_c^0.5. If the power-spectrum |h*(v)|² approximates sufficiently to a power law, |h*(v)|²～v^δ, a better estimate is given by R_q～λ_c^γ with γ=-(δ+1)/2. In many cases, γ=1 or R_q～λ_c will suffice.     

口腔修复陶瓷材料的磨损性能北大核心

背景:陶瓷材料因具有优良的机械性能、与口腔组织良好的生物相容性及高度美观性广泛应用于口腔修复领域,良好的磨损性能对修复体临床应用有重要意义。目的:综述口腔修复陶瓷材料磨损性能机制及临床研究,以期为临床选择适宜的陶瓷材料提供思路。方法:应用计算机在PubMed和Web of Science数据库检索在2016年1月至2021年4月期间涉及口腔修复陶瓷材料磨损性能的相关研究。英文检索词为“dental ceramic material,wear property”,最终共纳入36篇文献进行分析。结果与结论:①全瓷材料自身耐磨性均高于树脂陶瓷复合材料,全瓷材料中氧化锆陶瓷磨损性能最佳,美学性能较弱。②玻璃陶瓷中氧化锆加强型硅酸锂玻璃陶瓷磨损性能较好,但应用时间较短,长期疗效还有待更多的研究证实。③树脂陶瓷复合材料中树脂纳米陶瓷材料磨损性能优于聚合物渗透陶瓷。④在后牙区全冠修复可选择氧化锆陶瓷,前牙区全冠修复可以根据患者的美学需求选择高透性氧化锆陶瓷或玻璃陶瓷。⑤贴面、嵌体和高嵌体修复可选择长石瓷、玻璃陶瓷和树脂陶瓷复合材料,但树脂陶瓷复合材料耐磨性差,需避免用于高应力承载区。⑥对牙本质暴露、氟斑牙和牙齿酸蚀症患者可考虑树脂纳米陶瓷材料,但这类患者适宜的陶瓷材料相关研究较少。⑦表面粗糙度对陶瓷材料的磨损性能有显著影响,临床口腔修复应用中采用良好的抛光表面可提高陶瓷材料磨损性能,而且对修复体进行定期复查也至关重要。     

Contact-Free Support Structures for the Direct Metal Laser Melting Process

Although Direct Metal Laser Melting (DMLM), a powder bed fusion (PBF) Additive Manufacturing (AM) for metallic materials, provides many advantages over conventional manufacturing such as almost unlimited design freedom, one of its main limitations is the need for support structures beneath overhang surfaces. Support structures are generally in contact with overhang surfaces to physically prop them up; therefore, they need to be removed after manufacturing due to not constituting a part of the main component design. The removal of supports is a process sequence adding extra time and cost to the overall manufacturing process and could result in damaging the main component. In this study, to examine the feasibility of contact-free supports for overhang surfaces in the DMLM process, coupons with these novel types of supports were prepared from CoCrMo alloy powder. This study aims to understand the effect of two parameters: the gap distance between supports and overhang surfaces and the inclination angle of overhang surfaces, on the surface topography and microstructural properties of these surfaces. Visual inspection, roughness measurements, and optical microscopy were utilized as characterization methods The roughness parameters (Ra, Rq, and Rz) were obtained using the focus variation method, and optical microscope analysis was performed on the cross-sections of the overhang surfaces to investigate the sub-surface microstructure and surface topology. Results showed that contact-free supports have a positive effect on decreasing surface roughness at all build angles when the gap distance is correctly set to avoid sintering of the powder in between the overhang and supports or to avoid too large gaps eliminating the desired effect of the higher thermal conductivity.     

Wettability and Surface Roughness of Parylene C on Three-Dimensional-Printed Photopolymers

The use of poly-(para-chloro-xylylene) (Parylene C) in microelectromechanical systems and medical devices has increased rapidly. However, little research has been conducted on the wettability and surface roughness of Parylene C after being soaked in solutions. In this study, the contact angle and surface roughness (arithmetic average of roughness) of Parylene C on three-dimensional (3D)-printed photopolymer in 10% sodium hydroxide, 10% ammonium hydroxide, and 100% phosphate-buffered saline (PBS) solutions were investigated using a commercial contact angle measurement system and laser confocal microscope, respectively. The collected data indicated that 10% ammonium hydroxide had no major effect on the contact angle of Parylene C on a substrate, with a Shore A hardness of 50. However, 10% sodium hydroxide, 10% ammonium hydroxide, and 100% PBS considerably affected the contact angle of Parylene C on a substrate with a Shore A hardness of 85. Substrates with Parylene C coating exhibited lower surface roughness than uncoated substrates. The substrates coated with Parylene C that were soaked in 10% ammonium hydroxide exhibited high surface roughness. The aforementioned results indicate that 3D-printed photopolymers coated with Parylene C can offer potential benefits when used in biocompatible devices.     

The Effect of Dentifrice on Micro-Hardness,Surface Gloss,and Micro-Roughness of Nano Filled Conventional and Bulk-Fill Polymer Composite—A Micro Indentation and Profilometric Study

The aim of the present study was to evaluate the effect of brushing with two whitening dentifrices (Colgate Optic White (COW) and Colgate Optic White Charcoal (COC)) on surface gloss, micro-roughness, and micro-hardness of nanostructured hybrid conventional (Z350) and bulk-fill (Tetric N Ceram bulk-fill) polymer composite. In total, 96 disk samples using two nano-hybrid composite polymers (Z350 and Tetric N Ceram Bulk-fill) were prepared. All specimens were exposed to two different dentifrices (COW and COC), resulting in four main subgroups in the study. Specimens were assessed for surface gloss, micro-roughness (Ra), and micro-hardness using standardized methodology. Means and standard deviations of properties compared using paired t-test, one-way and two-way ANOVA, and post hoc test. The presence of dentifrices did not show any significant difference in micro-hardness values of Z350 (p > 0.05), whereas micro-hardness of bulk-fill composite significantly reduced on dentifrices exposure (p ≤ 0.05). Bulk-fill polymer composite showed significant reduction in gloss after dentifrice exposure (p < 0.05), however, Z350 showed no significant loss of gloss due to dentifrices (p > 0.05). A significant increase in Ra was observed for both resin materials after exposure to dentifrices (COC and COW). Conventional resin composite (Z350) showed comparable surface hardness and gloss before and after dentifrice exposure, however, micro-roughness increased significantly due to dentifrice exposure. Bulk-fill resin (Tetric N Ceram) showed significant loss of micro-hardness and gloss and increase in micro-roughness on dentifrice exposure. Conventional nano-hybrid composite polymer showed better durability in resisting loss of surface properties compared to bulk-fill resin polymer in the present experiment.     

Study on Milling Force and Surface Quality during Slot Milling of Plain-Woven CFRP with PCD Tools

Carbon-fiber-reinforced polymers (CFRPs) have been widely used in many industrial fields, such as automobile, aerospace and so on, because of their excellent mechanical properties. However, due to their anisotropy and inhomogeneity, machining CFRPs is a great challenge. In this paper, the slot milling of a plain-woven CFRP with PCD tools is carried out, and the effects of cutting parameters and tool rake angle on cutting force and surface roughness are studied. The results show that the 4° rake angle PCD tool has smaller cutting force than the 0° rake angle PCD tool, but the effect of rake angle on surface roughness is not significant. The concept of equivalent cutting area is introduced to study the variation law of cutting force and surface roughness. It is found that the cutting force and surface roughness increase with the increase in equivalent cutting area, and decrease with the decrease in equivalent cutting area. The removal mechanism of surface materials under different equivalent cutting areas is different, which leads to the difference in surface roughness. Finally, the causes of delamination on the top layer after milling are explained.     

Assessment of Surface Treatment Degree of Steel Sheets in the Bonding Process

The aim of the paper is to determine the influence of the surface treatment on the adhesive properties of steel sheet surfaces and the strength of the adhesive joints of steel sheets. The paper also aims to assess the degree of steel sheets’ surface treatment in the bonding process. Due to the many methods of surface treatment and types of materials, the assessment of the surface treatment method is extremely important in adhesive processes. Two variants of the surface treatment were used: without a paint coating and with a paint coating, divided into two groups (without degreasing and with degreasing). Additionally, in the case of the analysis of the steel samples without the paint coating, mechanical treatment was applied. Two-component epoxy adhesive, prepared on the basis of bisphenol A and a polyamide curing agent, was used to prepare the single-lap adhesive joints of the steel sheets. The tests determined: (i) the adhesive properties of the steel sheets’ surface based on the measurement of the contact angle of polar and apolar liquids (including wettability, work of adhesion, and surface free energy), (ii) surface roughness parameters (PN EN ISO 4287), and (iii) mechanical properties (load capacity and shear strength) of the steel sheets’ adhesive joints (EN DIN 1465). Contact angle measurements of the steel sheet surfaces showed that the polar liquid better reflects the obtained strength results of the analyzed adhesive joints than the apolar liquid. Furthermore, better wettability of the surface of steel sheets with both polar and apolar liquids was obtained for samples whose surface was subjected to degreasing. It can also be concluded that the wettability of the surface can be used as one of the indicators of the degree of the surface treatment for the bonding process.