New digital method for quantitative assessment of nasal morphology.

Our aim was to develop and validate a new method to assess objectively and quantitatively the morphology of the nostrils after nasal or nasolabial surgery. We used digital analysis using specific mathematical algorithms to assess several geometric measurements, particularly of facial asymmetry, expressed in adimensional units. Forty-five patients with no facial anomalies (control group) were used initially to evaluate the method and to obtain variables for statistical reference. Thirty-five patients operated on for unilateral cleft lip and palate (cleft group) were then analysed and compared with the control group. Individual scores were obtained for each patient, computed, and correlated with those established by a lay panel. Statistical analysis showed good sensitivity and reliability (R>0.8).     

Dynamic and static moduli of elasticity of resin-based materials.

OBJECTIVES: The purpose of this study was to assess and compare the elastic moduli of 34 resin-based materials using a dynamic and a static method. The effect of water storage was also studied up to 6 months. METHODS: Five samples of each material were prepared according to ISO-4049. The dynamic moduli were first determined non-destructively from the fundamental period of the vibrating specimen, then the static moduli were determined by a three-point bending test. The percentages of fillers by weight were determined by ashing in air at 900 degrees C. RESULTS: Low values were obtained with flowable composites as well as with two packable resin composites. Correlations were found between the static and the dynamic modulus of elasticity (r = 0.94; p = 0.0001) as well as between the weight percentage of fillers and the moduli of elasticity (r = 0.82; p < 0.05 for static modulus and r = 0.90; p < 0.05 for the dynamic modulus) both at 24h. Water storage significantly affected both static and dynamic moduli of elasticity (ANOVA two factors; p < 0.05). SIGNIFICANCE: The low moduli of the flowable composites do not allow their use in posterior cavities under high stress. However, this does not exclude their use for minimally-invasive Class I cavities when the opposing tooth is stabilized to a large amount on the natural enamel.The Grindosonic method is very useful and simple for determining the dynamic moduli although it gives higher values than the static one. The elastic modulus evolution of resin-based materials after water storage is unpredictable since different patterns were observed as a function of time.     

Human eosinophils express and release IL-13 following CD28-dependent activation

Human eosinophils produce a large number of cytokines, including immunoregulatory cytokines. Given that eosinophils store and release interleukin (IL)-4, a key cytokine in the pathogenesis of allergic inflammation, and that IL-4 and IL-13 share common biological functions, we investigated the possibility that IL-13 may be synthesized by these cells. Using flow cytometry and immunocytochemistry, we show that eosinophils synthesize and store IL-13. Granule localization was demonstrated after subcellular fractionation, and IL-13 immunoreactivity was localized to crystalloid, granule-enriched fractions. Furthermore, electron microscopic analyses specifically localized IL-13 to the dense cores of bicompartmental secondary granules. Upon CD28 ligation, IL-13 was released by eosinophils, whereas a combination of CD28 and immunoglobulin A complexes resulted in decreased IL-13 secretion. Furthermore, eosinophil-derived IL-13 exerts a biological effect, inducing CD23 expression on B cells. By having the capacity to synthesize and release IL-13, eosinophils may participate in the development and maintenance of the T helper cell type 2 response, a prominent feature of allergic diseases.     

Reduced polymerization stress of MAPO-containing resin composites with increased curing speed,degree of conversion and mechanical properties

Objectives

The degree and rate of photopolymerization in resin-based dental composites will significantly affect polymer network formation and resultant material properties that may determine their clinical success. This study investigates the mechanical properties, the generation of stress from polymerization, tooth cusp deflection and marginal integrity of experimental resin composites that contain different photoinitiators.

Methods

Experimental light-activated resin composites (60 vol% particulate filled in 50/50 mass% bis-GMA/TEGDMA) were formulated using a monoacylphosphine oxide (MAPO) photoinitiator and compared with a conventional camphoroquinone (CQ)-based system. Similar radiant exposure was used (18 J cm⁻²) for polymerization of each material although the curing protocol was varied (400 mW cm⁻² for 45 s, 1500 mW cm⁻² for 12 s and 3000 mW cm⁻² for 6 s). Degree and rate of polymerization was calculated in real-time by near infrared spectroscopy and the generation of stress throughout polymerization measured using a cantilever beam method. Flexural strength and modulus were acquired by three-point bend tests. Standardized cavities in extract pre-molar teeth were restored with each material, the total cuspal deflection measured and post-placement marginal integrity between the tooth and restoration recorded.

Results

Generally, MAPO- exhibited a significantly higher degree of conversion (72 ± 0.8 to 82 ± 0.5%) compared with CQ-based materials (39 ± 0.7 to 65 ± 1.6%) regardless of curing protocol (p < 0.05) and MAPO-based materials exhibited less difference in conversion between curing protocols. CQ-based materials exhibited between ∼85 and 95% of the maximum rate of polymerization at <15% conversion, whereas MAPO-based RBCs did not approach the maximum rate until >50% conversion. Higher irradiance polymerization had a significant deleterious effect on the mechanical properties of CQ-based materials (p < 0.05) whereas MAPO-based materials exhibited increased strength and modulus and were less affected by the curing method. Total cuspal deflection in restored extracted teeth was higher for CQ- compared with MAPO-based materials cured at the lowest irradiance curing protocol (12.9 ± 4.0 and 8.3 ± 1.5 μm) and similar at 3000 mW cm⁻¹ for 6 s (10.1 ± 3.5 and 9.0 ± 1.5 μm). A significant decrease in marginal integrity was observed for CQ-based RBCs cured at high irradiance for short exposure time compared with that of the MAPO-based RBC cured using a similar protocol (p = 0.037).

Significance

Polymer network formation dictates the final properties of the set composite and the use MAPO photoinitiators may provide an effective restorative material that exhibits higher curing speeds, increased degree of conversion, strength and modulus without compromise in terms of polymerization stress and marginal integrity between tooth and restoration.     

Treatment with removable partial dentures: a longitudinal study. Part I

The aim of this study was to evaluate the effectiveness of an oral rehabilitation by removable partial denture (RPD). Between 1983 and 1994, 629 patients were provided with an RPD at the Dental School of the Université catholique de Louvain. All the RPDs were constructed with a cobalt-chromium framework. All the treatments were provided by dental students under the supervision of clinical instructors. At recall time (1998-2000), 269 patients could not be reached neither by telephone nor by mail and 27 had died. Consequently, 333 patients were called for clinical examination and 254 of these (76.3%) actually attended. For a total of 292 RPDs fitted for these 254 patients, 218 (74.7%) were still being worn at the time of the check-up. Seventy-four dentures were considered to be 'failures', either because they were replaced by another RPD or by a complete denture, or because they had actually never been worn. The statistical analysis (Mantel-Haenszel and Kaplan-Meier) shows that the number of failures is significantly higher at the lower jaw compared with the upper jaw. Most of the failures are attributable to RPDs with free-end saddles and, in particular, to class I mandibular dentures. The patients are wearing their denture(s) mostly continuously (63.6%) and award a high degree of satisfaction to their denture. In general, the results recorded may be considered as very satisfactory, all the more so as we have no regular recall procedures established at our school and as check-up asked for spontaneously by the patients in the course of the period of observation are most of the time occasional or non-existent.