Long-term wear of ceramic matrix composite materials for hip prostheses under severe swing phase microseparation

The purpose of this study was to evaluate the long-term wear performance of alumina matrix composite (AMC) heads against alumina matrix composite inserts and alumina matrix composite heads against alumina (Al) inserts with the use of a hip-joint simulator incorporating severe swing phase joint microseparation. The wear of AMC on Al produced an average wear rate of 0.61 mm3/million cycles over the 5-million-cycle test duration. The wear of AMC on AMC produced an average wear rate of 0.16 mm3/million cycles over the 5-million-cycle test duration. Both the AMC on alumina and AMC on AMC produced significantly lower wear than previously tested HIPed alumina, where an average wear rate of 1.84 mm3/million cycles was reported over 5 million cycles. The wear mechanisms and wear debris of AMC on AMC and AMC on Al were similar to those observed in previous alumina retrieval studies with stripe wear caused by intragranular fracture and wear debris consisting of predominantly uniform 10-20-nm-sized particles and a few irregular particles up to 3 microm in size.     

Quantitative analysis of wear and wear debris from metal-on-metal hip prostheses tested in a physiological hip joint simulator

Osteolysis and loosening of artificial joints caused by UHMWPE wear debris has prompted renewed interest in metal-on-metal (MOM) hip prostheses. This study investigated the wear and wear debris morphology generated by MOM prostheses in a physiological anatomical hip simulator for different carbon content cobalt chrome alloys. The low carbon pairings demonstrated significantly higher "bedding in" and steady state wear rates than the mixed and high carbon pairings. The in vitro wear rates reported here were up to one or two orders of magnitude lower than the clinical wear rates for first-generation MOM hip prostheses. Two methods for characterising the metal wear debris were developed, involving digestion, scanning electron microscopy and transmission electron microscopy. The metal wear particles characterised by the two methods were similar in size, 25-36 nm, and comparable to particles isolated from periprosthetic tissues from first and second-generation MOM hip prostheses. Due to the small size of the metal particles, the number of particles generated per year for MOM prostheses in vitro was estimated to be up to 100 times higher than the number of polyethylene particles generated per year in vivo. The volumetric wear rates were affected by the carbon content of the cobalt chrome alloy and the material combinations used. However, particle size and morphology was not affected by method of particle characterisation, the carbon content of the alloy or material combination.     

Relative carriage rates of nuclear dehydrogenating clostridia in two populations of different colorectal cancer risk

Carriage of nuclear dehydrogenating clostridia has been associated with colon cancer and implicated in its aetiology. This study has compared the carriage of these organisms in a British population at high risk for the development of colon cancer with a low risk Nigerian population. Clostridia were found in all of the stools from both populations. Nuclear dehydrogenating clostridia were only found in the stools of the British subjects (32%). These results support the suggestion that the carriage rate of nuclear dehydrogenating clostridia in a population is related to the risk of colon cancer.     

Preparation of Cell Wall Antigens of Staphylococcus aureus

Cell walls were prepared from Staphylococcus aureus strains Copenhagen and 263 by high-speed mixing in the presence of glass beads followed by differential centrifugation. Insoluble peptidoglycan complexes were derived from cell walls by extraction of teichoic acid with 10% trichloroacetic acid. Intact teichoic acid was prepared from each strain by digestion of cell walls with lysostaphin and isolated by column chromatography. Soluble glycopeptide (peptidoglycan in which only the glycan has been fragmented) and the stable complex of teichoic acid with glycopeptide were prepared by digestion of cell walls with Chalaropsis B endo-N-acetylmuramidase and were separated by column chromatography. Amino acid and amino sugar contents of walls and subunits of walls were comparable to those reported by others.     

Development of hatching blastocysts from immature human oocytes following in-vitro maturation and fertilization using a co-culture system

Recently, in-vitro maturation (IVM) of immature human oocytes recovered from non-stimulated follicles has been applied in the treatment of infertility. However, in previous reports, very few embryos cultured in conventional medium have reached the expanded blastocyst stage following in-vitro maturation and fertilization (IVM/IVF). The objective of this study was to investigate whether the developmental competence of human embryos following IVM/IVF could be enhanced by the use of a human ampullary cell co-culture system. Immature human oocytes were aspirated from small follicles at Caesarean section and then cultured in medium containing human menopausal gonadotrophin for 36 to 48 h, followed by insemination. Zygotes were randomly cultured either in conventional culture medium alone or in the co-culture system. Of 48 embryos cultured in conventional medium alone, all arrested at the 2-16- cell stage on day 3 after insemination. Of 46 embryos cultured in the co-culture system, 26 embryos (56.5%) arrested at the 2-16-cell stage. Six embryos (13%) developed to the morula stage. Fourteen embryos (30.4%) developed to expanded blastocysts and two blastocysts were hatching on day 7 after insemination. We conclude that co-culture significantly enhances the development of blastocysts in embryos resulting from IVM/IVF.      

Detection of chromosomes and estimation of aneuploidy in human spermatozoa using fluorescence in-situ hybridization

The development and application of fluorescence in-situ hybridization (FISH) has opened the way for comprehensive studies on numerical chromosome abnormalities in human spermatozoa. FISH can be rapidly applied to large numbers of spermatozoa and thus overcomes the major limitation of karyotyping spermatozoa after penetration of zona-free hamster oocytes. The simultaneous hybridization of two or more chromosome-specific probes to spermatozoa and subsequent detection of the bound probes using different fluorescent detection systems enables two or more chromosomes to be localized simultaneously in the same spermatozoon and provides a technique for undertaking reasonable estimates of aneuploidy. The most commonly used probes are those which bind to the centromeric region of specific chromosomes. Most studies to date have concentrated on estimating aneuploidy in spermatozoa from normospermic men, although reports are beginning to appear on aneuploidy in spermatozoa from subfertile and infertile men. Multi- probe FISH studies have generally reported disomy (hyperhaploidy) estimates of 0.05-0.2% per chromosome. There is preliminary evidence that some chromosomes such as X, Y and 21 are predisposed towards higher rates of non-disjunction during spermatogenesis. There are also suggestions of inter-donor variability in aneuploidy frequencies for specific chromosomes, although this requires confirmation in larger studies. While FISH is clearly a powerful technique that has many applications in reproductive medicine, it must also be realized that it does have limitations and the technology itself is still evolving and has yet to be fully validated on spermatozoa.      

Preliminary observations on polar body extrusion and pronuclear formation in human oocytes using time-lapse video cinematography

In this study, we have used time-lapse video cinematography to study fertilization in 50 human oocytes that had undergone intracytoplasmic sperm injection (ICSI). Time-lapse recording commenced shortly after ICSI and proceeded for 17-20 h. Oocytes were cultured in an environmental chamber which was maintained under standard culture conditions. Overall, 38 oocytes (76%) were fertilized normally, and the fertilization rate and embryo quality were not significantly different from 487 sibling oocytes cultured in a conventional incubator. Normal fertilization followed a defined course of events, although the timing of these events varied markedly between oocytes. In 35 of the 38 fertilized oocytes (92%), there were circular waves of granulation within the ooplasm which had a periodicity of 20-53 min. The sperm head decondensed during this granulation phase. The second polar body was then extruded, and this was followed by the central formation of the male pronucleus. The female pronucleus formed in the cytoplasm adjacent to the second polar body at the same time as, or slightly after, the male pronucleus, and was subsequently drawn towards the male pronucleus until the two abutted. Both pronuclei then increased in size, the nucleoli moved around within the pronuclei and some nucleoli coalesced. During pronuclear growth, the organelles contracted from the cortex towards the centre of the oocyte, leaving a clear cortical zone. The oocyte decreased in diameter from 112 to 106 microm (P < 0.0001) during the course of the observation period. The female pronucleus was significantly smaller in diameter than the male pronucleus (24.1 and 22.4 microm respectively, P = 0.008) and contained fewer nucleoli (4.2 and 7.0 respectively, P < 0.0001). After time-lapse recording, oocytes were cultured for 48 h prior to embryo transfer or cryopreservation. Embryo quality was related to fertilization events and periodicity of the cytoplasmic wave, and it was found that good quality embryos arose from oocytes that had more uniform timing from injection to pronuclear abuttal and tended to have a longer cytoplasmic wave. In conclusion, we have shown that time-lapse video cinematography is an excellent tool for studying fertilization and early embryo development, and have demonstrated that human fertilization comprises numerous complex dynamic events.