Fatigue resistance of yttria‐stabilized tetragonal zirconia polycrystal clasps for removable partial dentures

With the rapid development of computer‐aided design/computer‐aided manufacturing (CAD /CAM ) systems, the application of zirconia in removable partial dentures is expected to expand. Clasps composed of zirconia should improve esthetics without inducing the risk of metal allergy. The aim of this study was to examine the fatigue resistance of yttria‐stabilized tetragonal zirconia polycrystal (Y‐TZP) clasps for removable partial dentures. Yttria‐stabilized tetragonal zirconia polycrystal and cobalt‐chromium (Co‐Cr) alloy were prepared using CAD /CAM systems. Specimens were either of the semicircular type or of the flat type, with cross‐sectional areas of taper ratios of 0.50, 0.75, and 1.00. All specimens were tested using the cantilever test and the constant displacement fatigue test, and data were analyzed using ANOVA . During the cantilever test, the maximum displacement prior to fracture was greater than the required undercut, and the semicircular‐type specimen exhibited a higher fracture load than the flat type. None of the specimens displayed permanent deformation and showed almost the same degree of deformation after fatigue testing. A lower taper ratio was associated with lower average load values and greater displacement. Within the limitations of this study, it was possible to conclude that Y‐TZP provides the required undercut and adequate retentive force for removable partial denture clasps. Additionally, Y‐TZP and Co‐Cr alloy had almost the same degree of deformation even after the simulated lifespan of removable partial dentures.     

Imbalance of coagulation and fibrinolysis can predict vascular access failure in patients on hemodialysis after vascular access intervention

Objective

For patients with end-stage renal disease on hemodialysis, the durability of vascular access (VA) is still far from optimal, and access survival after intervention for access failure is an important aspect. Procoagulant status is a leading cause of access failure. Coagulation-fibrinolysis imbalance can occur in hemodialyzed patients, but the influence of the imbalance has not been fully elucidated.

Prevention of hair graying by factors that promote the growth and differentiation of melanocytes

Epidermal melanocyte precursors migrate into developing hair follicles to form the melanocyte stem cell system required to supply pigmented melanocytes necessary for hair pigmentation in repetitive hair cycles. Hair graying is caused by irreversible defects in the self‐renewal and/or development of follicular melanocyte stem cells in the hair follicles. To investigate the mechanism(s) of hair graying during the normal aging process, we established a hair graying model in mice by repeatedly plucking or shaving trunk hairs. We repeatedly plucked or shaved trunk hairs to induce and accelerate the hair graying and counted the gray hairs. By using this functional model of hair graying in mice, we assessed the effects of genes known to affect melanocyte development, such as Kitl, hepatocyte growth factor (HGF) and endotheline 3 (ET3). After increasing the total numbers of cumulative hair cycles by plucking or shaving, we observed a significant increase in the gray hair of C57BL/6 mice. Kitl expression in the skin was the most effective for preventing hair graying and a significant effect was also confirmed for HGF and ET3 expression. The repeated hair plucking or shaving led to hair graying without any genetic lesion. Kitl is a more effective factor for prevention of hair graying than HGF or ET3. Our simple model of hair graying may provide a basic tool for screening the molecules or reagents preventing the progression of hair graying.