3种金属底板托槽喷砂处理前后粘结强度的比较及其意义

目的：探讨在人工唾液条件下临床正畸常用的3种金属底板托槽及脱落后经喷砂处理3种托槽的粘结强度,评价其粘结性能。方法：收集60颗因正畸需要拔除的上颌前磨牙,随机分为国产直丝弓新亚托槽（新亚）组、进口直丝弓MBT超薄托槽（MBT）组和日本直丝弓TOMY自锁托槽（TOMY）组,每组20颗。托槽脱落后将牙齿随机分为6组,分别粘结新的和脱落后经喷砂处理的3种托槽,每组10个。采用万能电子力学实验机测定每组的抗剪切强度,放大镜观察每组牙釉质表面粘结剂残留指数（ARI）,扫描电镜观察不同底板托槽及脱落后经喷砂处理后的托槽底板形貌。结果：在人工唾液条件下,TOMY组初次粘结新托槽和再次粘结新托槽的抗剪切强度高于新亚组和MBT组（P<0.05）,而新亚组的抗剪切强度与MBT组比较差异无统计学意义（P>0.05）;再次粘结脱落后经喷砂处理的3组托槽中,TOMY组抗剪切强度大于新亚组和MBT组（P<0.05）,而新亚组的抗剪切强度与MBT组比较差异无统计学意义（P>0.05）;TOMY组和MBT组脱落后经喷砂处理的托槽抗剪切强度较原托槽均增大（P<0.05）。各组的ARI比较差异无统计学意义（P>0.05）。扫描电镜观察,3种托槽底板均为纵横相间的网格,TOMY组更为致密,喷砂后砂粒嵌入网格中,TOMY组和MBT组砂粒更多嵌入倒凹处;再次喷砂后,砂粒嵌入范围增加,并且新亚组网底的网格结构出现破坏,其他2组未见明显异常。结论：3种底板托槽的粘结强度均能满足临床需要,其中TOMY组托槽的粘结强度优于其他2组。喷砂法处理脱落的TOMY和MBT托槽后可以提高托槽的粘结强度。     

不同粘接剂对托槽脱落牙面再粘接强度的影响

目的研究不同粘接剂对托槽脱落牙面再粘接新托槽的剪切强度的影响。方法正畸拔除人离体前磨牙60颗,随机分为A、B、C组,每组20颗。使用京津釉质粘合剂粘接前磨牙托槽,浸泡于生理盐水37℃恒温水浴24 h后加载剪切力使托槽脱落,再分别使用京津釉质粘合剂、GC Fuji ORTHO LC粘接剂、Transbond XT粘接剂粘接新托槽,生理盐水37℃恒温水浴24 h后加载剪切力使托槽脱落,记录托槽抗剪切强度,并记录托槽脱落后粘接剂残留指数。结果 3组间的抗剪切强度差异有显著性（P〈0.05）;3组间ARI指数差异有显著性（P〈0.05）。结论对于初次使用京津釉质粘合树脂粘接的托槽脱落,使用Transbond XT粘接剂再次粘接新托槽粘接强度最大。     

两种底板托槽抗剪切强度的对比研究

①目的　对目前最常用的燕尾底板托槽和网状底板托槽的粘结强度进行对比研究。②方法　选择因正畸需要而拔除的双尖牙为实验样本 ,将离体牙随机分为两组 ,每组 10颗。在第 1组牙面上粘结燕尾底板托槽 ,在第 2组牙面上粘结网状底板托槽。以材料力学实验机分别对两组进行抗剪切强度的测定 ,并对每一牙面上的粘结剂残留量进行粘结剂残留指数 (ARI)计分统计。③结果　两种底板托槽之间的抗剪切强度比较 ,差异无显著性(t=1.5 4 2 ,P >0 .0 5 ) ,其ARI计分比较 ,差异亦无显著性 (Hc =0 .0 0 0 ,P >0 .0 5 )。④结论　体外研究结果提示这两种托槽在粘结强度上差别不大。     

树脂托槽与瓷修复材料粘接抗剪切强度的实验研究

目的研究不同瓷表面处理方法对树脂托槽与瓷修复体粘接抗剪切强度的影响,找到适合瓷面与树脂托槽粘接的粘接剂和瓷表面处理方法。方法90颗制作好瓷贴面的离体牙随机均分为A、B、C三组:A组使用京津釉质粘合剂,B组使用光固化复合树脂,C组使用BISCO正畸单组分粘接剂粘接树脂托槽。每组再按照瓷表面处理方法的不同分为三组,在粘接前分别用酒精擦拭、打磨去釉氢氟酸酸蚀和打磨去釉氢氟酸酸蚀后涂硅烷偶联剂处理瓷贴面表面。所有样本在37℃恒温水浴中储存24小时后测定抗剪切粘接强度并记录去粘接后瓷贴面的破裂情况。结果BISCO正畸单组分粘接剂组的粘接强度明显高于京津釉质粘合剂组和光固化复合树脂粘接剂组(P<0.05),瓷贴面经打磨去釉氢氟酸酸蚀或再涂硅烷偶联剂处理后使用BISCO正畸单组分粘接剂粘接取得了正畸临床有效的粘接强度。各组去粘接后瓷破裂率没有显著性差异(P>0.05)。结论京津釉质粘合剂和光固化复合树脂粘接剂不适于正畸树脂托槽的粘接,BISCO正畸单组分粘接剂经打磨去釉、氢氟酸酸蚀后才能取得正畸临床有效的粘接强度,瓷面涂布硅烷偶联剂可增加其粘接强度且对去粘接后的瓷面破裂率无影响。     

底板形态和粘结时间对托槽粘结强度的影响

目的 对目前正畸临床上最常用的金属网底托槽和微蚀刻底托槽的粘结强度进行对比分析,并确定力加载的适宜时间。方法 选取正畸临床上减数拔除的上颌第一前磨牙120颗,随机分为2组,第1组粘结金属网底托槽,第2组粘结金属微蚀刻底托槽。每组分别在粘结后5min、10min、15min、30min、60min、24h测定抗剪切强度(SBS),并统计粘结剂残留指数(ARI),电镜扫描托槽粘结前、脱落后底板形貌。结果 金属网底托槽组和微蚀刻底托槽组SBS均随粘固时间的延长而增大,24h时粘结强度最大,且与其他时间点有统计学差异(P<0.05)。结论 两种金属托槽的粘结强度均能满足临床需要,可在托槽粘结后5min进行正畸力的加载。     

表面处理及粘结剂对氧化锆与牙釉质间剪切粘结强度的影响

目的研究表面喷砂处理及不同正畸粘结剂对氧化锆陶瓷与牙釉质间剪切粘结强度的影响。方法40颗离体上颌第一前
磨牙,应用计算机辅助设计与计算机辅助制作系统设计和制作粘结面与牙面紧密贴合的个性化氧化锆陶瓷试件。将试件随机
分为4组,分别选择粘结面喷砂处理和粘结面无处理,选择京津釉质粘结剂和3M Transbond XT光固化粘结剂。按要求粘结24 h
后,万能材料试验机测定剪切粘结强度,并进行统计学分析。结果喷砂组剪切粘结强度显著高于未喷砂组（P<0.05）,两种粘结
剂的剪切粘结强度无显著差异（P>0.05）。结论表面喷砂处理后,无论使用京津釉质粘结剂或是3M Transbond XT光固化粘结
剂,氧化锆陶瓷与牙釉质间均可获得足够的剪切粘结强度。
     

喷砂、激光蚀刻和酸蚀法对正畸托槽黏接强度的影响

目的:确定喷砂法和激光蚀刻法是否可以成为黏接正畸托槽的牙釉质的处理方法。方法:选择70颗因正畸原因拔除的前磨牙,均分为7组:喷砂组、激光蚀刻组(0.5、0.75、1、1.5、2 W)和传统酸蚀法组,黏接正畸托槽后,进行抗剪切黏接强度测试,同时观察剩余黏接剂指数。对实验结果分别进行统计学分析。结果:传统酸蚀法和三组高能量激光蚀刻法(1、1.5、2 W)的抗剪切黏接强度均可满足临床要求,而剩余两组低能量激光蚀刻法(0.5、0.75 W)和喷砂法的抗剪切黏接强度值均较低。低能量激光蚀刻组的牙釉质表面剩余有较少的黏接剂。结论:黏接正畸托槽不适宜使用喷砂法和低能量激光蚀刻法,而高能量激光蚀刻可满足正畸临床黏接托槽的要求。     

脉冲钕钇铝石榴石激光对氟斑牙托槽抗剪切强度的影响

目的将不同能量脉冲钕钇铝石榴石(Nd:YAG)激光对离体氟斑牙表面釉质进行照射,并与酸蚀技术联合应用,探索提高氟斑牙托槽粘结强度的方法。方法将正常牙5颗和中度氟斑牙50颗,其中正常牙酸蚀1 min作为正常组;氟斑牙被随机分成10组,每组5颗,其中一组酸蚀1 min作为对照组,剩下9组按以下方式处理:经50 mJ照射、50 mJ照射+酸蚀1 min、50 mJ照射+酸蚀2 min、100 mJ照射、100 mJ照射+酸蚀1 min、100 mJ+酸蚀2 min、180 mJ照射、180 mJ照射+酸蚀1 min、180 mJ照射+酸蚀2 min。其中激光照射频率均为20 Hz,照射时间为20 s,酸蚀剂均为37%磷酸。在处理过的牙面粘结不锈钢方丝弓托槽,测试其抗剪切强度。结果单独激光处理组抗剪切强度高度显著低于正常组(P<0.01),显著低于对照组(P<0.05)。激光技术和酸蚀技术联合使用组抗剪切强度较激光单独使用组升高,其中100 mJ照射+酸蚀1 min,抗剪切强度最高,显著高于对照组(P<0.01)。结论在酸蚀条件和时间相同的情况下,激光预处理能协同增强酸蚀作用,提高氟斑牙托槽粘结力,100 mJ激光照射+酸蚀1 min,抗剪切强度最高,随着激光能量的增加和酸蚀时间的延长,粘结强度并不增加。     

瓷面处理技术与陶瓷托槽的抗剪切力强度

目的在不同瓷面处理技术单独或联合使用,并用发光二极管进行光照的条件下,对陶瓷托槽的抗剪切强度进行比较。方法将30个表面光滑的瓷面随机分为3组,每组10个。每组瓷面处理如下:第1组:9.6%氢氟酸酸蚀2 m in,涂布硅烷偶联剂;第2组:氧化铝颗粒喷砂,9.6%氢氟酸酸蚀2 m in,涂布硅烷偶联剂;第3组:氧化铝颗粒喷砂,涂布硅烷偶联剂,用光固化树脂粘接剂将陶瓷托槽粘接于瓷面上,分别测量抗剪切强度。结果方差分析表明组间存在显著差异(P<0.001)。第3组的抗剪切强度最低(5.35±1.28,P<0.001)。第1组(11.10±1.45)和第2组(10.38±1.09;P>0.05)之间没有明显差别。结论应用氢氟酸和硅烷偶联剂处理瓷表面可获得最大的抗剪切强度。在应用氢氟酸和硅烷偶联剂之前喷砂没有增加粘接强度。     

三种不同托槽粘结强度的体外实验研究

目的：评价国产陶瓷托槽的粘结性能,为临床提供参考。方法：将60颗上颌前磨牙包埋后随机分成6组,分别用光固化复合树脂粘结剂、化学固化复合树脂粘结剂粘结国产陶瓷托槽、进口陶瓷托槽、国产金属托槽,用Instron万能材料力学实验机测试其抗剪切强度,同时计算牙面粘结剂的残留指数（ Adhesive Remnant Index, ARI）,进行统计处理。结果：国产陶瓷托槽与进口陶瓷托槽、国产金属托槽之间有统计学差异（ P﹤0.05）;统计结果显示2种粘结剂之间差异无统计学意义（P＞0.05）;各组ARI指数无显著性差异（P＞0.05）。结论：国产陶瓷托槽的抗剪切强度明显低于进口陶瓷托槽和国产金属托槽;国产陶瓷托槽无论与光固化复合树脂粘结剂还是化学固化复合树脂粘结剂联合使用,都能满足临床需要;所有组别中,粘结破坏多位于托槽与粘结剂界面。     

Effect of saliva contamination of shear bond strength of orthodontic brackets when using a self-etch primer

Summary The effect of saliva contamination on the shear bond strength of orthodontic brackets, at various stages of the bonding procedure using a new self-etch primer was studied. The samples were divided into 4 groups according to 4 different enamel surface conditions: Group A: dry; Group B: saliva contamination before priming; Group C: saliva contamination after priming, and Group D: saliva contamination before and after priming. Stainless steel brackets were bonded in each test group with a light-cured composite resin (TransbondXT 3M). The shear bond strength was determined in the first 30 min after bonding. The analysis of variance indicated that the shear bond strengths of the 4 groups were significantly different (F=11. 89,P<0.05). Tukey HSD tests indicated that contamination both before and after the application of the acid-etch primer resulted in a significantly lower (=4.6±1.7 MPa) shear bond strength than either the control group (=8.8±1.9MPa) or the groups where contamination occurred either before (=7.9±2.0 MPa) or after (=6.9±1.5 MPa) the application of the primer. It was concluded that the new acid-etch primer could maintain adequate shear bond strength if contamination occurred either before or after the application of the primer. On the other hand, contamination both before and after the application of the primer could significantly reduce the shear bond strength of orthodontic brackets. MAO Jing, female, born in 1962, Professor     

牙釉质表面不同状态对自酸蚀体系剪切强度的影响

目的:研究牙釉质表面不同状态对自酸蚀体系剪切强度的影响. 方法:选择新鲜拔除无龋坏,无缺损的牛切牙32个,流水冲洗下.低速金刚砂片平行于牙长轴切取厚约2.0 mm,约3.5～4.0 mm2的牙釉质片,金钢砂车针表面磨切呈平面,依次以200目、400目、600目砂纸打磨牙釉质,形成标准粘结面,超声波清洁, 将标准粘结面常规处理.加压充填树脂,分层固化.同时以全酸蚀粘结系统作对照组. 所得的试件分为4组:即刻测试组(自酸蚀和全酸蚀)和24 h后测试组(自酸蚀和全酸蚀),每组8个试件.即刻测试:将粘结处理完成后的试件直接放置在万能试验机上测试其剪切强度,剪切头速度为0.5 mm/min. 24 h后将粘结处理完成后的试件放置在人工唾液中24 h,在万能试验机上测试其剪切强度,剪切头速度为0.5 mm/min.结果:经One-Way ANOVA统计分析,可知三种不同状态在自酸蚀粘结系统下即可和24 h测试组比较组内及组间均存在显著差异(P<0.01),与对照组比较,自酸蚀即刻测试组存在显著差异(P<0.01),自酸蚀24 h测试组的剪切强度值存在显著差异(P<0.01). 结论:牙釉质表面在半干燥条件下的即刻和24 h测试组的剪切强度值最大.     

3种正畸秞质粘接剂在不同粘接条件下的抗剪切强度比较

[目的]比较3种正畸秞质粘接剂在干性（无唾液污染）和湿性（有唾液污染）两种不同粘接条件下的抗剪切强度以及托槽去除后牙面粘接剂的残留指数,寻求一种具有最佳临床效果的秞质粘接剂。[方法]收集60颗新鲜人类前磨牙随机分为6组,分别采用京津秞质粘接剂,单组份化学固化粘接剂以及树脂改良型玻璃离子,在干性和湿性（放置于37℃、人工唾液环境）两种条件下粘接正畸托槽,24 h后检测3种材料的抗剪切强度,统计牙面上粘接材料的残留指数。[结果]在干性条件下三种材料的抗剪切强度差异无显著性意义。在湿性条件下,前两种材料的抗剪切强度明显下降,与干性条件下三组差异 有显著性意义。树脂改良型玻璃离子的抗剪切强度虽然有所下降,但与干性条件下三组差异无显 著性意义。通过牙面残留指数统计发现,前两种粘接剂 在干性条件下,粘接剂的断裂部位多发生在粘接剂-托槽之间;在湿性条件下多发生在牙秞质及 粘接剂之间,而树脂改良型玻璃离子在干湿性条件下多发 生在粘接剂之间。[结论]树脂改良型玻璃离子在干性和湿性条件下粘接托槽产生的抗剪切强度能够满足正畸临床的粘接强度需要,避免了去除托槽时对牙釉质产生的撕裂,是一种较为理想的正畸粘接剂。     

不同瓷表面处理对托槽与瓷面粘结强度的影响

目的:通过观察Nd∶YAG激光与氢氟酸(HF)联合处理的瓷面,探讨不同瓷表面处理方法对瓷面与托槽粘结强度的影响。 方法:将48个金属烤瓷试样根据表面处理方法随机分为空白对照组、HF组、机械打磨组、0.75W激光组、1.05W激光组和1.45W激光组。经温度循环实验后,测定各组试样剪切强度和拉伸强度。 结果:各处理组试样剪切强度和拉伸强度与空白对照组比较差异有统计学意义(P<0.01),1.05W激光组和1.45W激光组试样剪切强度和拉伸强度与HF组比较差异有统计学意义(P<0.05),1.05W激光组试样剪切强度和拉伸强度均高于其他各组(P<0.05)。试样的剪切强度与拉伸强度呈正相关关系(r=0.426,P=0.000)。 结论:能量参数为1.05W的Nd∶YAG激光与HF联合处理即可获得理想的粘结强度,且剪切强度愈大其拉伸强度愈大。     

复合体联合不同粘接剂与乳牙牙本质间剪切强度的研究

目的比较复合体与全酸、自酸蚀粘结剂合用和乳牙牙本质间的剪切强度,为临床选择复合体修复乳牙的粘结系统提供理论依据。方法滞留乳磨牙40颗制成40个牙本质试件,随机分成2组,一组为全酸蚀粘结剂组,另一组为自酸蚀粘结剂组,两组均按操作要求进行复合体粘结修复,然后测定两组剪切强度。结果全酸蚀粘结剂组与自酸蚀粘结剂组的牙本质剪切粘结强度无明显统计学差异（P〉0.05）。结论全酸蚀与自酸蚀粘接剂均可做为复合体与乳牙牙本质间的粘接剂。     

不同表面处理方法对氧化锆与树脂水门汀粘接强度的影响

目的：研究不同表面处理对氧化锆与树脂水门汀粘接强度的影响。方法：将40个氧化锆试件随机分为4组,每组10个：对照组,无处理;喷砂组,用Al2O3 颗粒对氧化锆试件表面均匀喷砂;紫外线（ultraviolet,UV）照射组,将氧化锆试件置于紫外线消毒箱中的紫外灯下方10 mm处照射48 h;低温等离子处理组,将氧化锆试件置于舱式低温等离子体发生器内处理30 s。分组处理后观察氧化锆试件表面形态,测量表面接触角及剪切粘接强度。结果：UV照射及低温等离子处理组氧化锆试件表面形态无明显改变,喷砂组氧化锆试件表面形态明显改变。喷砂组、UV照射组和等离子处理组氧化锆试件表面接触角分别为48.8°±2.6°、27.1°±3.6°和32.0°±3.3°,较对照组接触角(64.1°±2.0°)明显减小。喷砂处理组氧化锆试件剪切粘接强度（14.82±2.01） MPa大于对照组（9.41±1.07） MPa,差异有统计学意义（P<0.05）。UV处理组氧化锆试件剪切粘接强度（10.02±0.64） MPa大于对照组（9.41±1.07） MPa,但差异无统计学意义（P>0.05）。低温等离子处理后其剪切粘接强度（18.34±3.05） MPa大于对照组（9.41±1.07） MPa、喷砂处理组（14.82±2.01） MPa和UV处理组（10.02±0.64） MPa,且差异有统计学意义（P<0.05）。X射线光电子能谱分析(X ray photoelectron spectroscopy, XPS)结果显示UV及低温等离子处理使氧化锆试件表面氧元素含量增加,碳元素含量减少,碳/氧比值减小。结论：UV照射及低温等离子处理均可在不改变氧化锆表面形态的基础上显著改善其表面的亲水性;UV照射后氧化锆与树脂的剪切粘接强度虽无明显提高,但试件断裂模式由粘接断裂向混合断裂转变;低温等离子处理能显著提高氧化锆与树脂水门汀的粘接强度。