目的探讨镍铬合金烤瓷修复体是否会对人体尿液中的镍、铬含量造成影响。方法选择要求拆除原镍铬烤瓷修复体的患者86例,于修复体拆前、拆后1个月,分别检测患者尿镍、铬含量,并按年龄、性别、修复体数目、修复体戴入时间以及修复体有无金属暴露等进行分组分析。结果 86例患者在镍铬烤瓷修复体拆除前后的尿镍含量分别为(3.52±3.05)μg/L、(3.31±3.28)μg/L,差异无统计学意义(P>0.05);拆除前后的尿铬含量分别为(0.81±0.54)μg/L、(1.34±1.15)μg/L,差异亦无统计学意义(P>0.05)。患者的尿镍、铬含量与年龄、性别、修复体的数量、修复时间以及有无金属暴露等均无明显的相关性(P>0.05)。结论镍铬合金烤瓷修复体所释放的镍、铬离子量微小,短期内不足以对人体尿液中的镍、铬含量造成影响。     

戴用镍铬合金烤瓷冠对免疫功能影响的横断面研究

目的 探讨口内戴用镍铬合金烤瓷冠是否导致机体免疫功能学指标改变.方法 对镍铬合金烤瓷冠戴用者795例和对照组198人进行问卷调查、测定尿镍铬和血免疫功能指标,并分析镍铬烤瓷冠戴用时间、尿镍铬与免疫功能指标间的关系.结果 将镍铬合金烤瓷冠戴用者和对照组的所有样本合并,根据尿镍和尿铬水平分为尿镍低水平组(＜ 37.28 μg/mol肌酐)、中水平组(37.28～ 115.73 μg/mol肌酐)和高水平组(＞115.73 μg/mol肌酐);尿铬低水平组(＜34.72 μg/mol肌酐)、中水平组(34.72 ～79.81 μg/mol肌酐)和高水平组(＞79.81 μg/mol肌酐).结果 仅发现尿镍高水平组的血清白细胞介素( interleukin,IL)1β水平[(1.50±0.84) μg/L]显著低于尿镍低水平组[(1.63±0.82)μg/L](P＜0.05),未发现尿镍中水平组与低水平组间、尿铬各水平组间在血清肿瘤坏死因子α(tumor necrosis factor-alpha,TNF-α)、IL-1β和IL-6间的差异有统计学意义.单因素方差分析和各影响因素的线性回归分析仅发现年龄与TNF-α的升高有关,未发现戴用时间、数量和金属裸露水平,以及尿镍和尿铬对TNF-α、IL-1β和IL-6等免疫学指标的显著影响.结论 本研究未观察 到戴用镍铬合金烤瓷冠与机体免疫功能指标TNF-α、IL-1β和IL-6的升高具有相关关系.     

镍铬合金烤瓷冠修复患者头发中镍铬元素的含量

目的:观察镍铬合金烤瓷冠修复后患者头发中镍铬元素含量的变化,探讨镍铬合金长期存在于口腔中的安全性。方法:选取60名经体检合格的健康人作为正常对照组;60名上、下颌前牙有任意3颗行镍铬合金烤瓷冠修复的患者作为实验组。实验组修复后半年及1年和对照组均采用火焰原子吸收光谱法测定头发镍铬元素含量。结果:头发镍含量:实验组半年与对照组比较无显著性差异(P>0.05);实验组1年与对照组相比较有显著性差异(P<0.05);实验组1年与半年比较无显著性差异(P>0.05)。头发铬含量:各组之间比较均无显著性差异(P>0.05)。结论:镍铬合金烤瓷冠修复后会在口腔环境中释放一定的镍、铬,且释放的量与时间有关,但量很微小。     

镍铬合金烤瓷冠冠组织面离子析出的研究

目的研究含铬质量分数不同的两种镍铬合金烤瓷冠在人工唾液中镍、铬离子的析出量。方法用含铬质量分数为26.0%和12.6%的镍铬烤瓷合金,烧结成各12颗烤瓷冠,分别放于人工唾液中,于1、2、4、8、16、32周末用石墨炉原子吸收分光光度计测量各样本在人工唾液中的镍、铬离子浓度。结果1)低铬和高铬合金冠组样本中铬离子析出量从1~4周逐渐增加,然后逐渐下降;高铬合金冠组镍离子析出于第4周达到高峰,而低铬合金冠组镍离子的析出呈持续缓慢地上升;2)实验前后低铬合金冠组烤瓷冠的质量差别大于高铬合金冠组,其差异有统计学意义(P<0.01)。结论1)低铬和高铬合金冠组铬离子的析出量均于第4周达高峰;2)低铬合金冠组镍离子的析出明显高于高铬合金冠组;3)实验前后低铬合金冠组样本的质量损失明显大于高铬合金冠组。     

镍铬合金烤瓷冠配戴者尿镍、铬水平和肾功能的关系分析

目的:探讨镍铬合金烤瓷冠配戴者中的尿镍和尿铬水平是否与机体的肾功能损伤有关。方法:对795例镍铬合金烤瓷冠配戴者进行烤瓷冠修复的问卷调查,尿镍、铬测定和血、尿肾功能生化指标测定,采用SPSS12.0软件包进行t检验、单因素方差分析和Logistic回归分析,探讨尿镍、铬水平与肾功能指标间的关系。结果:根据尿镍水平,将研究对象均分为3组(<38、38～90和≥90μg/mol肌酐)后,尿镍水平为38～90μg/mol肌酐剂量组,血肌酐明显升高,但肾小球滤过率的估计值(eGFR)明显下降,各组间不存在线性趋势,未观察到血和尿中其他各肾功能生化指标在不同尿镍剂量组间的差异。不同尿铬剂量组间(<38、38~88和≥88μg/mol肌酐),血生化指标无显著改变,但尿N-乙酰-β-D-氨基葡糖苷酶(UNAG)和尿视黄醇结合蛋白(URBP)随剂量上升呈现下降趋势。各尿镍和尿铬剂量组间eGFR的异常率和各尿肾功能指标的异常率均无显著改变。结论:镍铬合金烤瓷冠配戴者尿中镍和铬的排泄水平与机体肾损伤无关。     

金铂合金与镍铬合金烤瓷颜色和金瓷结合强度的比较研究

目的 探讨金铂合金烤瓷与镍铬合金烤瓷颜色和金瓷结合强度的差别,为临床选择修复材料 提供理论依据。方法 ①制作不同体瓷厚度的金铂、镍铬合金烤瓷圆盘试件各15件,用美能达CR-100色 度计测量试件上遮色瓷、体瓷后的L、a、b值,计算两种金属烤瓷颜色(A2)间的色差△E。②制作金铂、镍铬 合金烤瓷棒盘试件各5件,通过剪切实验测量金瓷结合强度。结果 ①金铂合金烤瓷颜色比镍铬合金烤瓷颜 色要偏黄、偏红,明度小,两种金属烤瓷颜色(A2)的色差△E在遮色瓷时最大,随体瓷增厚而减小。②金铂合 金烤瓷金瓷结合强度85.08±15.16MPa,镍铬合金烤瓷金瓷结合强度54.76±8.74MPa,统计学分析P<0.05。结论 金铂合金烤瓷不仅金瓷结合强度高,不易崩瓷,而且颜色更接近天然牙。     

烤瓷用镍-铬合金金属氧化膜的研究

目的 分析国产Ｎｉ－Ｃｒ合金在烤瓷烧结条件下所生成的金属氧化膜的性能,探讨颈部灰线的成因。方法 应用Ｘ线衍射法与电子扫描法对国产Ｎｉ－Ｃｒ合金铸年经烤瓷烧结后,表现氧化膜的物相以及氧化膜与基体合金的成分进行分析;同时,应用俄歇电子能谱对经烤瓷烧结后与未经烤瓷烧结的铸件表现氧化膜的厚度、各元素变化趋势进行了分析研究。结果经烧结后的铸件表现氧化膜中主要有Ｃｒ２Ｏ３、ＮｉＣｒ２Ｏ４、ＳｉＯ２等氧化物及合     

金沉积烤瓷全冠的临床研究

目的评价金沉积烤瓷冠的临床应用性能.方法将96例患者分为两组,试验组46例患者制作沉积金烤瓷冠76件;对照组50例患者制作镍铬合金烤瓷冠88件.修复完成时和完成后1月、18月随访,检查修复体颜色、颈缘适合性、颈缘变色、牙龈出血指数4项指标和瓷损坏.结果两组修复体颜色、颈缘变色、牙龈出血指数3项检查指标的比较有统计学差异(P＜0.05).两组颈缘适合性无统计学差异.结论沉积金烤瓷冠临床效果优于镍铬合金烤瓷冠.     

CAI烤瓷用镍铬合金临床应用108例分析

对108例使用CAI烤瓷用镍铬合金和Vita瓷粉制成180个金属烤瓷修复体.追踪观察6年半发现该种合金与Vita瓷粉结合牢固符合临床要求,失败率仅为8.33％:金属表面仍保持光泽,未见到腐蚀现象,说明该种材料耐腐蚀性能良好。并分析了失败原因,提出了临床需要注意的问题和预防措施。     

镍铬烤瓷冠修复患者尿镍铬水平调查研究

目的探讨佩戴镍铬烤瓷冠材料对患者尿镍铬水平的影响。方法对浙江某县45例烤瓷冠修复患者进行问卷调查,其中接触组（镍铬烤瓷冠）37例、对照组（含钛烤瓷冠）8例．对其收集尿样并测定尿中镍、铬的水平。结果两样本t检验结果显示．镍铬烤瓷冠修复患者尿镍水平（平均1．47μg／g肌酐）与对照组（平均1．55μg／g肌酐）相比差别很小,接触组尿铬水平（平均2．06μg／g肌酐）高于对照组（平均1．17μg／g肌酐）,但差异均没有统计学意义。线性回归分析结果显示,在控制性别、年龄、体质指数、吸烟和饮酒等因素的影响后．所有研究对象尿镍和尿铬水平均不受佩戴烤瓷冠的类型、时间和数量的影响（P〉0．1）。结论本研究结果显示．目前尚不能认为镍铬烤瓷冠材料促进镍铬经尿排泄．需进一步加大样本量进行研究．     

三种烤瓷桥临床修复六年的回顾分析

目的 追踪观察金沉积基底冠熔结镍铬桥体烤瓷桥、金合金烤瓷桥和镍铬合金烤瓷桥的临床效果,为评价不同烤瓷桥临床修复的远期效果提供参考.方法 制作金沉积基底冠熔结镍铬桥体烤瓷桥(A组)35件,同期分别制作金合金烤瓷桥(B组)和镍铬合金烤瓷桥(c组)各35件,临床检查105件修复体的边缘密合性,随访复查修复体的基牙继发龋和修复体折裂、折断、脱落情况.结果 105件修复体平均随访6年.A组边缘密合性好(100%),明显好于B组(91%)与C组(77%)(P<0.01).6年内A组基牙继发龋率为0%(0/35),B组基牙继发龋率为6%(2/35),c组基牙继发龋率为14%(5/35).A组中有1例在修复2年后饰面瓷崩瓷,占3%;随访期内B组无崩瓷现象;C组1例在修复4年后饰面瓷崩瓷,占3%,3种修复体崩瓷率差异无统计学意义(P>0.05).其余修复体均无桥架松动、折断以及修复体脱落.结论 金沉积基底冠熔结镍铬桥体烤瓷桥有良好的边缘密合度,强度可满足临床要求,有临床应用价值.但其与常规铸造合金烤瓷桥一样,需谨慎使用,提倡用于无髓基牙烤瓷桥修复.     

低温瓷熔附于Ti-75合金的实验研究

目的　探讨Ti 75合金表面烤瓷的可行性。方法　采用电子探针界面分析及剪切强度测试的方法 ,考察金瓷界面的结合状态及结合强度。结果　Ti 75合金与低温瓷 (Ti Bond)的剪切强度为 (47 38± 7 95 )MPa ,与传统金瓷修复体 (NC VMK6 8)的剪切强度 (48 5 0± 7 6 0 )MPa相比 ,差异无显著性 (P >0 0 5 )。电子探针界面分析显示 ,Ti 75合金与低温瓷结合紧密 ,无裂隙 ,低温瓷对Ti 75有良好的浸润作用。同时 ,亦可见到Ti元素从Ti 75基体向瓷内扩散 ,Si、Sn等元素从瓷中向Ti 75扩散。结论　Ti 75合金可以作为口腔用烤瓷合金。     

Annealing of Co-Cr dental alloy: effects on nanostructure and Rockwell hardness

PURPOSE

The aim of the study was to evaluate the effect of annealing on the nanostructure and hardness of Co-Cr metal ceramic samples that were fabricated with a direct metal laser sintering (DMLS) technique.

MATERIALS AND METHODS

Five groups of Co-Cr dental alloy samples were manufactured in a rectangular form measuring 4 × 2 × 2 mm. Samples fabricated by a conventional casting technique (Group I) and prefabricated milling blanks (Group II) were examined as conventional technique groups. The DMLS samples were randomly divided into three groups as not annealed (Group III), annealed in argon atmosphere (Group IV), or annealed in oxygen atmosphere (Group V). The nanostructure was examined with the small-angle X-ray scattering method. The Rockwell hardness test was used to measure the hardness changes in each group, and the means and standard deviations were statistically analyzed by one-way ANOVA for comparison of continuous variables and Tukey''s HSD test was used for post hoc analysis. P values of <.05 were accepted as statistically significant.

RESULTS

The general nanostructures of the samples were composed of small spherical entities stacked atop one another in dendritic form. All groups also displayed different hardness values depending on the manufacturing technique. The annealing procedure and environment directly affected both the nanostructure and hardness of the Co-Cr alloy. Group III exhibited a non-homogeneous structure and increased hardness (48.16 ± 3.02 HRC) because the annealing process was incomplete and the inner stress was not relieved. Annealing in argon atmosphere of Group IV not only relieved the inner stresses but also decreased the hardness (27.40 ± 3.98 HRC). The results of fitting function presented that Group IV was the most homogeneous product as the minimum bilayer thickness was measured (7.11 Å).

CONCLUSION

After the manufacturing with DMLS technique, annealing in argon atmosphere is an essential process for Co-Cr metal ceramic substructures. The dentists should be familiar with the materials that are used in clinic for prosthodontics treatments.     

镍铬合金在人工唾液中的电化学腐蚀行为

目的 本项研究旨在探讨镍铬合金在体外的电化学腐蚀行为。方法 实验应用极化曲线方法，将镍铬合金浸泡在人工唾液中，温度为36．5℃，pH值为7．0，测量试样的腐蚀电位和自腐蚀电流密度。应用X射线光电子能谱(X-ray photoelectron spectroscopy，XPS)，分析试样表面的元素成分变化。结果 实验结果表明，镍铬合金的点蚀电位为-390mV，钝化电位为-160mV，活性溶解区从-160mV到-270mV。它的自腐蚀电流密度为0．262μAcm^-2。极化曲线试验后，对试片表面进行XPS能谱分析，所得原子峰高图发现，随着氩离子刻蚀的由浅入深，金属元素镍(Ni)、铬(Cr)、钼(Mo)、铁(Fe)的含量逐渐增加，而非金属元素氧(O)、碳(C)的含量则逐渐减少。由于钙(Ca)为介质中的元素，其含量也呈逐渐减少。结论 镍铬合金在人工唾液中，经过电化学极化曲线试验，会发生腐蚀反应，生成腐蚀产物附着于试样表面。     

齿科钴铬-镍铬合金激光焊接后耐腐蚀性评价

目的:研究激光焊接钴铬-镍铬合金的体外电化学行为及离子释出情况。方法:在体外模拟口腔环境中,测出激光焊接钴铬-镍铬合金阳极极化曲线及特征指数;检测激光焊接镍铬-钴铬合金在不同时间的离子释出情况,以钴铬合金、镍铬合金为对照。结果:钴铬合金自腐蚀电位低于镍铬合金,激光焊接钴铬-镍铬合金的自腐蚀电位、维钝电流密度、破裂电位介于前两者之间;激光焊接镍铬-钴铬合金,镍离子释出量7日后少于镍铬合金,钴离子释出量始终高于镍铬合金。结论:激光焊接钴铬-镍铬合金后,钴铬合金的阳极保护作用可减少镍铬合金镍离子释出,有助于改善镍铬合金生物相容性;激光焊接钴铬-镍铬合金,对其整体耐腐蚀性未有较大影响。     

反复熔铸对Ni-Cr烤瓷合金机械性能的影响

目的 :比较反复熔铸对Ni Cr烤瓷合金机械性能的影响。方法 :Ni Cr烤瓷合金经过熔铸 4次后 ,用拉伸实验对各代铸件的抗拉强度、屈服强度、延伸率等机械性能指标进行比较 ,并作金相和断口电镜观察。结果 :Ni Cr烤瓷合金反复熔铸 4次的抗拉强度、0 .2 %屈服强度无显著性差异 (P >0 .0 5 ) ,延伸率之间有显著性差异(P <0 .0 5 ) ;结构观察显示 ,随着熔铸次数的增加 ,铸件的树枝状晶粒明显减小 ,缩孔缩松数分布增多增广 ,有夹杂物产生 ,并且出现一些杂质富积区。结论 :Ni Cr烤瓷合金反复熔铸 4次后 ,在其机械性能方面能够满足烤瓷合金的基本要求     

四种烤瓷基底冠金属对人牙龈成纤维细胞分泌前列腺素E2和环加氧酶2的影响

目的 观察4种烤瓷基底冠金属浸提液对人牙龈成纤维细胞分泌前列腺素E2和环加氧酶2的影响.方法 制备镍铬合金、钴铬合金、纯钛、金钯合金金属浸提液,以无金属浸泡的达尔伯克改良伊格尔培养基培养液作为空白对照,培养人牙龈成纤维细胞,分别培养1、6、12、24h,收集上清液,酶联免疫吸附测定法测定前列腺素E2的表达水平;制作细胞爬片,用免疫荧光法观察各组环加氧酶2的表达.结果 镍铬合金、钴铬合金组6、12、24h前列腺素E2表达水平(镍铬:45.568±0.926、60.538±0.988、73.754±0.507;钴铬:40.496±0.693、53.216±0.327、65.470±1.086)高于相应空白对照组(31.122±0.642、31.230±0.634、30.980±0.746),差异均有统计学意义(P＜0.05);纯钛、金钯合金组前列腺素E2表达水平(钛:31.564±0.719、31.998±0.856、32.066±0.513;金钯:31.540±0.821、31.136±0.518、31.340±0.443)与相应空白对照组差异均无统计学意义(P＞0.05).镍铬合金、钴铬合金组环加氧酶2的染色深而均匀;纯钛、金钯合金组与空白对照组染色浅且不均匀.结论 镍铬合金、钴铬合金使人牙龈成纤维细胞分泌前列腺素E2和环加氧酶2增加,而纯钛、金钯合金不影响前列腺素E2和环加氧酶2的分泌.     

镍铬合金烤瓷修复体拆除前后患者尿和血清中镍铬含量的评估

目的 通过测定镍铬合金烤瓷修复体拆除前后患者尿和血清中的镍铬含量,对镍铬合金的临床应用安全性进行科学评估.方法 选择因怀疑镍铬合金烤瓷修复体的镍、铬元素对全身有影响,主动要求拆除修复体的患者86例,于修复体拆前、拆后1个月采用石墨炉原子吸收光谱法检测患者尿镍、铬含量(86例)和血清镍、铬含量(69例).结果 镍铬烤瓷修复体拆除前后86例患者尿镍含量分别为(3.52±3.05)和(3.31 ±3.28) μg/L,尿铬含量分别为(0.81±0.54)和(1.34±1.15) μg/L;修复体拆除前后69例患者血清镍含量分别为(2.04±1.06)和(2.67±2.32) μg/L,血清铬含量分别为(1.07±0.88)和(1.02±0.86) μg/L;拆除前后差异均无统计学意义(P＞0.05).结论 本项研究条件下镍铬合会烤瓷修复体释放的镍、铬离子量微小,不足以对人体尿液及血液中的镍、铬含量造成影响.     

A comparative study on the bond strength of porcelain to the millingable Pd-Ag alloy

PURPOSE

The porcelain fused to gold has been widely used as a restoration both with the natural esthetics of the porcelain and durability and marginal fit of metal casting. However, recently, due to the continuous rise in the price of gold, an interest towards materials to replace gold alloy is getting higher. This study compared the bond strength of porcelain to millingable palladium-silver (Pd-Ag) alloy, with that of 3 conventionally used metal-ceramic alloys.

MATERIALS AND METHODS

Four types of metal-ceramic alloys, castable nonprecious nickel-chrome alloy, castable precious metal alloys containing 83% and 32% of gold, and millingable Pd-Ag alloy were used to make metal specimens (n=40). And porcelain was applied on the center area of metal specimen. Three-point bending test was performed with universal testing machine. The bond strength data were analyzed with a one-way ANOVA and post hoc Scheffe''s tests (α=.05).

RESULTS

The 3-point bending test showed the strongest (40.42 ± 5.72 MPa) metal-ceramic bond in the nonprecious Ni-Cr alloy, followed by millingable Pd-Ag alloy (37.71 ± 2.46 MPa), precious metal alloy containing 83% of gold (35.89 ± 1.93 MPa), and precious metal alloy containing 32% of gold (34.59 ± 2.63 MPa). Nonprecious Ni-Cr alloy and precious metal alloy containing 32% of gold showed significant difference (P<.05).

CONCLUSION

The type of metal-ceramic alloys affects the bond strength of porcelain. Every metal-ceramic alloy used in this study showed clinically applicable bond strength with porcelain (25 MPa).