牙科氧化锆陶瓷的低温时效性能研究

目的 研究时效对5种牙科氧化锆陶瓷结构稳定性的影响.方法 5种氧化锆预烧结块(A组:TZ-3YS;B组:Vita In-Ceram YZ;C组:Ivoclar;D组:Cercon Smart;E组:Kavo)各切取15 mm×15 mm×1.5 mm氧化锆试件18片,常压致密烧结.时效处理如下:置于高温高压消毒炉中进行循环热处理,条件是134℃,0.2 MPa压力,维持时间为0h、1h、2h、3h、4 h、5h.X射线衍射分析(X-ray diffraction,XRD)试件的晶相结构,计算试件表面单斜相(m相)的相对含量.原子力显微镜观察A组和D组时效1、4 h的抛光试件.A组氧化锆再制备25 mm×4 mm×1.2 mm的试件30根,均分为未退火组(时效前)、退火组(时效前)和时效组(时效后),测试试件的三点弯曲强度.结果 除D组试件外,A、B、C、E组试件的m相含量均随时效时间的延长而增加,A组试件的m相含量最高,E组次之,B组和C组相近.XRD未检测到D组试件表面有m相,但使用原子力显微镜可观察到D组试件有m相晶核的成核和生长.时效前后A组试件的三点弯曲强度未衰减,未退火组试件三点弯曲强度[(1301±169)MPa]显著高于退火组[(1120±185)MPa]和时效组[(1158±111)MPa],差异有统计学意义(P＜0.05);而退火组与时效组间差异无统计学意义(P＞0.05).结论 牙科氧化锆陶瓷的低温时效效应具有时间依赖性,但时效效应并未使TZ-3YS的三点弯曲强度降低.     

Biaxial flexural strength of Turkom-Cera core compared to two other all-ceramic systems

Advances in all-ceramic systems have established predictable means of providing metal-free aesthetic and biocompatible materials. These materials must have sufficient strength to be a practical treatment alternative for the fabrication of crowns and fixed partial dentures.

Objectives

The aim of this study was to compare the biaxial flexural strength of three core ceramic materials.

Material and methods

Three groups of 10 disc-shaped specimens (16 mm diameter x 1.2 mm thickness - in accordance with ISO-6872, 1995) were made from the following ceramic materials: Turkom-Cera Fused Alumina [(Turkom-Ceramic (M) Sdn Bhd, Puchong, Selangor, Malaysia)], In-Ceram (Vita Zahnfabrik, Bad Säckingen, Baden-Württemberg, Germany) and Vitadur-N (Vita Zahnfabrik, Bad Säckingen, Baden-Württemberg, Germany), which were sintered according to the manufacturer''s recommendations. The specimens were subjected to biaxial flexural strength test in a universal testing machine at a crosshead speed of 0.5 mm/min. The definitive fracture load was recorded for each specimen and the biaxial flexural strength was calculated from an equation in accordance with ISO-6872.

Results

The mean biaxial flexural strength values were: Turkom-Cera: 506.8±87.01 MPa, In-Ceram: 347.4±28.83 MPa and Vitadur-N: 128.7±12.72 MPa. The results were analyzed by the Levene''s test and Dunnett''s T3 post-hoc test (SPSS software V11.5.0 for Windows, SPSS, Chicago, IL, USA ) at a preset significance level of 5% because of unequal group variances (P<0.001). There was statistically significant difference between the three core ceramics (P<0.05). Turkom-Cera showed the highest biaxial flexural strength, followed by In-Ceram and Vitadur-N.

Conclusions

Turkom-Cera core had significantly higher flexural strength than In-Ceram and Vitadur-N ceramic core materials.     

Comparison of the translucency of shaded zirconia all-ceramic systems

PURPOSE

The purpose of this study was to evaluate and compare the translucency of shaded zirconia all-ceramic systems.

MATERIALS AND METHODS

Translucency of 3 different zirconia all-ceramic systems colored by different techniques was compared with a lithium disilicate glass-ceramic (IPS e.max Press). Square-shaped specimens with 0.5 mm thickness were fabricated from In-Ceram YZ, ICE Zirkon and Katana systems in A1, A2 and A3.5 shades according to Vitapan Classical shade tab (n=11). Specimens were then veneered and glazed with corresponding veneer ceramic recommended by each zirconia system manufacturer and the total thickness was set to 1.5 mm. Translucency measurements were performed with VITA Easyshade Compact spectrophotometer after each stage and translucency parameter was calculated. Data were statistically analyzed with repeated measures ANOVA and Tukey multiple comparison test.

RESULTS

The control group was significantly more translucent than the zirconia systems (P<.05). ICE Zirkon cores showed the least translucency; neither In-Ceram YZ nor Katana systems were superior to each other in terms of translucency. Translucency of all specimens was decreased after veneering, and the translucency rankings were changed.

CONCLUSION

Coloring technique did not have a significant effect on translucency of zirconia cores. Although zirconia systems were less translucent than lithium disilicate glass ceramic, they had partial translucency and there were translucency differences among the zirconia systems. Chroma affected the translucency of precolored zirconia cores.     

Influence of the preparation design and artificial aging on the fracture resistance of monolithic zirconia crowns

PURPOSE

The aim of this study was to evaluate the fracture resistance and fracture behavior of monolithic zirconia crowns in accordance with the preparation design and aging simulation method.

MATERIALS AND METHODS

An upper first molar was prepared sequentially with three different preparation designs: shoulderless preparation, 0.4 mm chamfer and 0.8 mm chamfer preparation. For each preparation design, 30 monolithic zirconia crowns were fabricated. After cementation on Cr-Co alloy dies, the following artificial aging procedures were performed: (1) thermal cycling and mechanical loading (TCML): 5000 cycles of thermal cycling 5℃–55℃ and chewing simulation (1,200,000 cycles, 50 N); (2) Low Temperature Degradation simulation (LTD): autoclave treatment at 137℃, 2 bar for 3 hours and chewing simulation; and (3) no pre-treatment (control group). After artificial aging, the crowns were loaded until fracture.

RESULTS

The mean values of fracture resistance varied between 3414 N (LTD; 0.8 mm chamfer preparation) and 5712 N (control group; shoulderless preparation). Two-way ANOVA analysis showed a significantly higher fracture loads for the shoulderless preparation, whereas no difference was found between the chamfer preparations. In contrast to TCML, after LTD simulation the fracture strength of monolithic zirconia crowns decreased significantly.

CONCLUSION

The monolithic crowns tested in this study showed generally high fracture load values. Preparation design and LTD simulation had a significant influence on the fracture strength of monolithic zirconia crowns.     

Four-point flexural strength and microtensile bond strength of digitally and conventionally veneered zirconia

This study intended to evaluate the effect of digital veneering on four-point flexural strength (FS) and microtensile bond strength (μTBS) of veneered zirconia. Two different zirconia blocks, a lithium disilicate and a feldspathic ceramic block, and two different layering ceramics were used. IPS e.max Zir CAD (ZC) and Vita In-Ceram YZ (YZ) with yttria stabilized tetragonal zirconia polycrystals (3Y-TZP) were used as substructures. IPS e.max CAD (LD), Vita Mark II (VMII), IPS e.max Ceram (EC) and Vita VM9 (VM9) were used for veneering. Resin cement and fusion ceramic were placed between veneer and zirconia substructure for digital veneering. A total of one hundred and fifty specimens in five groups (n = 30) were prepared for FS and tested in universal machine at 1.0 mm/min. One hundred specimens in five groups (n = 20) were obtained for the μTBS and tested at 1.0 mm/min. Statistical analysis was made by one way ANOVA and Tukey HSD. Conventional veneering showed statistically significant FS. ZC veneered with EC had the highest mean FS and the lowest was obtained in groups veneered through resin cement. YZ layered with VM9 had the highest mean μTBS. ZC veneered through fusion ceramic and YZ veneered through resin cement showed significantly lower and similar μTBS.     

Chemical solubility and flexural strength of zirconia-based ceramics

PURPOSE: This study was undertaken to investigate the chemical solubility and flexural strengths of 3 zirconia-based dental ceramics: In-Ceram Zirconia (IZ), In-Ceram 2000 YZ CUBES (YZ Zirconia) (Vita Zahnfabrik), and Cercon (Dentsply). A pressable lithium disilicate-reinforced glass ceramic (IPS Empress 2, Ivoclar Vivadent) was used as a control. MATERIALS AND METHODS: Ten block specimens (12 x 6 x 4 mm) of each ceramic material were prepared for chemical solubility testing. Each specimen was refluxed in 4% acetic acid solution for 16 hours. The percentage loss of mass and the loss of mass per unit of surface area for each specimen were calculated. Ten bar-shaped (21 x 5 x 2 mm) and 10 disk-shaped (16 mm diameter, 1.2 mm thickness) specimens of each ceramic material were prepared and tested for uniaxial flexural strength (UFS) and biaxial flexural strength (BFS). X-ray diffraction analyses were conducted to determine the relative amount of the monoclinic phase of the as-sintered and fractured surfaces of the zirconia ceramics. RESULTS: There were no significant differences among the ceramics in chemical solubility by percentage mass or mass/surface area. For UFS, YZ Zirconia (899 +/- 109 MPa) > Cercon (458 +/- 95 MPa) IZ (409 +/- 60 MPa) > Empress 2 (252 +/- 36 MPa). For BFS, YZ Zirconia (1,107 +/- 116 MPa) > Cercon (927 +/- 146 MPa) > IZ (523 +/- 51 MPa) > Empress 2 (359 +/- 43 MPa). The fractured YZ Zirconia surface contained approximately 5 times as much monoclinic phase compared to that of its intact surface. The fractured IZ and Cercon surfaces contained approximately twice as much monoclinic phase compared to those of intact surfaces. CONCLUSION: The ceramics tested all satisfied the chemical solubility allowance required of core ceramic material (type I, Class 1 or type II, Class 1) according to the International Organization for Standardization 6872:1995(E) specifications on dental ceramic. The zirconia-based ceramics possessed significantly higher flexural strengths than the control lithium disilicate ceramic. Their clinical application appears sufficiently promising for long-term clinical studies to be undertaken.     

Pressed ceramics onto zirconia. Part 1: Comparison of crystalline phases present, adhesion to a zirconia system and flexural strength

Objectives

To compare the crystalline phases present, quantify the adhesion to zirconia and measure the mechanical properties of four commercially available pressed ceramics suitable for zirconia substructures.Materials and methods This study compares the X-ray diffraction response and the mechanical properties of four different pressed ceramics (Noritake CZR Press, Vita PM9, Wieland PressXzr and IPS e.max ZirPress) to Vita In-Ceram YZ zirconia substrate. The adhesion was determined using the interfacial strain energy release rate fracture mechanics approach; in addition biaxial flexural strength values of each material was determined.

Results

X-ray diffraction analysis revealed that Noritake CZR Press and Vita PM9 contain leucite whereas IPS e.max ZirPress and Wieland PressXzr are non-leucite amorphous materials.The strain energy release rate results revealed that the pressed ceramics with leucite have better adhesion than non-leucite ceramics to zirconia. Differences were observed between biaxial strength results for the pressed ceramics from bilayer compared with monolayer specimens.

Conclusions

Pressed ceramics compatible with zirconia tested in this study were of two types; leucite containing and non-leucite containing essentially glass ceramics. Leucite containing pressable ceramics appears to have better adhesion to zirconia.     

Mechanical properties of zirconia after different surface treatments and repeated firings

PURPOSE

This study investigated the influence of surface conditioning procedures and repeated firings on monoclinic content and strength of zirconia before cementation.

MATERIALS AND METHODS

Sintered bar-shaped zirconia specimens were subjected to no surface treatment (control), air abrasion, or grinding (n=21). Their roughness was evaluated using a profilometer, and microscope analysis was performed on one specimen of each group. Then, 2 or 10 repeated firings (n=10) were executed, the monoclinic content of specimens was analyzed by X-ray diffraction, and a three-point flexural strength test was performed. Surface roughness values were compared using one-way analysis of variance (ANOVA) and Tukey honestly significant difference (HSD) tests, the monoclinic content values were tested using Kruskal-Wallis and Mann-Whitney U tests, and the flexural strength values were tested using two-way ANOVA and Tukey HSD tests (P=.05). Spearman''s correlation test was performed to define relationships among measured parameters.

RESULTS

Surface-treated specimens were rougher than untreated specimens and had a higher monoclinic content (P<.005), and the relationship between roughness and monoclinic content was significant (P<.000). Neither surface treatment nor firing significantly affected the flexural strength, but Weibull analysis showed that for the air-abraded samples the characteristic strength was significantly lower after the 10^th firing than after the 2^nd firing.

CONCLUSION

After firing, a negligible amount of monoclinic content remained on the zirconia surfaces, and rougher surfaces had higher monoclinic contents than untreated surfaces. Multiple firings could be performed if necessary, but the fracture probability could increase after multiple firings for rougher surfaces.     

Flexural strengths of implant-supported zirconia based bridges in posterior regions

PURPOSE

Impact forces in implant supported FDP (fixed dental prosthesis) are higher than that of tooth supported FDPs and the compositions used in frameworks also has a paramount role for biomechanical reasons. The aim of this study was to evaluate the flexural strength of two different zirconia frameworks.

MATERIALS AND METHODS

Two implant abutments with 3.8 mm and 4.5 mm platform were used as premolar and molar. They were mounted vertically in an acrylic resin block. A model with steel retainers and removable abutments was fabricated by milling machine; and 10 FDP frameworks were fabricated for each Biodenta and Cercon systems. All samples were thermo-cycled for 2000 times in 5-55℃ temperature and embedded in 37℃ artificial saliva for one week. The flexural test was done by a rod with 2 mm ending diameter which was applied to the multi-electromechanical machine. The force was inserted until observing fracture. The collected data were analyzed with SPSS software ver.15, using Weibull modulus and independent t-test with the level of significance at α=.05.

RESULTS

The mean load bearing capacity values were higher in Biodenta but with no significant differences (P>.05). The Biodenta frameworks showed higher load bearing capacity (F₀=1700) than Cercon frameworks (F₀=1520) but the reliability (m) was higher in Cercon (m=7.5).

CONCLUSION

There was no significant difference between flexural strengths of both zirconia based framework systems; and both Biodenta and Cercon systems are capable to withstand biting force (even parafunctions) in posterior implant-supported bridges with no significant differences.     

Mechanical behavior and microstructural characterization of different zirconia polycrystals in different thicknesses

PURPOSETo characterize the microstructure of three yttria partially stabilized zirconia ceramics and to compare their hardness, indentation fracture resistance (IFR), biaxial flexural strength (BFS), and fatigue flexural strength.MATERIALS AND METHODSDisc-shaped specimens were obtained from 3Y-TZP (Vita YZ HT), 4Y-PSZ (Vita YZ ST) and 5Y-PSZ (Vita YZ XT), following the ISO 6872/2015 guidelines for BFS testing (final dimensions of 12 mm in diameter, 0.7 and 1.2 ± 0.1 mm in thicknesses). Energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD) and scanning electron microscopy (SEM) analyses were performed, and mechanical properties were assessed by Vickers hardness, IFR, quasi-static BFS and fatigue tests.RESULTSAll ceramics showed similar chemical compositions, but mainly differed in the amount of yttria, which was higher as the amount of cubic phase in the diffractogram (5Y-PSZ > 4Y-PSZ > 3Y-TZP). The 4Y- and 5Y-PSZ specimens showed surface defects under SEM, while 3Y-TZP exhibited greater grain uniformity on the surface. 5Y-PSZ and 3Y-TZP presented the highest hardness values, while 3Y-TZP was higher than 4Y- and 5Y-PSZ with regard to the IFR. The 5Y-PSZ specimen (0.7 and 1.2 mm) showed the worst mechanical performance (fatigue BFS and cycles until failure), while 3Y-TZP and 4Y-PSZ presented statistically similar values, higher than 5Y-PSZ for both thicknesses (0.7 and 1.2 mm). Moreover, 3Y-TZP showed the highest (1.2 mm group) and the lowest (0.7 mm group) degradation percentage, and 5Y-PSZ had higher strength degradation than 4Y-PSZ group.CONCLUSIONDespite the microstructural differences, 4Y-PSZ and 3Y-TZP had similar fatigue behavior regardless of thickness. 5Y-PSZ had the lowest mechanical performance.     

Biaxial flexural strength and phase transformation of Ce-TZP/Al2O3 and Y-TZP core materials after thermocycling and mechanical loading

PURPOSE

The purpose of the present study was to evaluate the effect of thermocycling and mechanical loading on the biaxial flexural strength and the phase transformation of one Ce-TZP/Al₂O₃ and two Y-TZP core materials.

MATERIALS AND METHODS

Thirty disc-shaped specimens were obtained from each material. The specimens were randomly divided into three groups (control, thermocycled, and mechanically loaded). Thermocycling was subjected in distilled water for 10000 cycles. Mechanical loading was subjected with 200 N loads at a frequency of 2 Hz for 100000 times. The mean biaxial flexural strength and phase transformation of the specimens were tested. The Weibull modulus, characteristic strength, 10%, 5% and 1% probabilities of failure were calculated using the biaxial flexural strength data.

RESULTS

The characteristic strengths of Ce-TZP/Al₂O₃ specimens were significantly higher in all groups compared with the other tested materials (P<.001). Statistical results of X-ray diffraction showed that thermocycling and mechanical loading did not affect the monoclinic phase content of the materials. According to Raman spectroscopy results, at the same point and the same material, mechanical loading significantly affected the phase fraction of all materials (P<.05).

CONCLUSION

It was concluded that thermocycling and mechanical loading did not show negative effect on the mean biaxial strength of the tested materials.     

Influence of aging on flexural strength of translucent zirconia for monolithic restorations

Statement of problem

Concern has been raised with regard to the low-temperature degradation (LTD) of translucent yttria-stabilized tetragonal zirconia polycrystalline (Y-TZP) for monolithic zirconia restorations.

In vitro evaluation of low-temperature aging effects and finishing procedures on the flexural strength and structural stability of Y-TZP dental ceramics

STATEMENT OF PROBLEM: Yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) ceramic material has been reported to possess exceptionally high flexural strength; however, the strength of Y-TZP ceramics can be affected by surface treatments performed by dental laboratory technicians and by intraoral conditions. PURPOSE: This study investigated the influence of low-temperature-degradation (LTD) treatment, airborne-particle abrasion, and polishing on the flexural strength and structural stability of a Y-TZP ceramic material. MATERIAL AND METHODS: By sectioning zirconia ceramic blocks (Vita In-Ceram YZ blocks) into 25 x 4 x 2-mm bars, 310 specimens were fabricated and divided into 9 groups: Group C, as-sintered (control); group B24h, boiled in water for 24 hours; group B7d, boiled in water for 7 days; group H6h, stored in humidified air at 250 degrees C for 6 hours; group H24h, stored in humidified air at 250 degrees C for 24 hours; group H7d, stored in humidified air at 250 degrees C for 7 days; group P, polished; group A, airborne-particle abraded; and group AB, airborne-particle abraded and boiled for 7 days. The flexural strengths (MPa) of all specimens were determined by using a 3-point bending test. The variability was analyzed by using Weibull statistics. Pairwise differences among the 9 groups were evaluated by using confidence intervals (95%) for scale and shape parameters. From every block used, 8 specimens were obtained and every specimen was marked according to the location of its origin from the original block. Surfaces of the specimens were evaluated by using scanning electron microscopy (SEM) at various magnifications. X-ray diffraction analysis was performed to identify possible tetragonal-to-monoclinic phase transformations. Energy dispersive spectroscopy (EDS) was used to obtain information on the chemical composition. RESULTS: Aging or "finishing" treatments had no significant negative effects on flexural strengths. Mean flexural strengths ranged from 796.7 to 950.2 MPa. Group A exhibited the highest mean flexural strength (950.2 MPa). Weibull modulus values ranged between 5.6 and 9.3. Tetragonal-to-monoclinic phase transformation was detected for a specimen boiled for 24 hours. More tetragonal-to-monoclinic phase transformation was detected for specimens boiled for 7 days and stored in humidified air at 250 degrees C for 7 days. The SEM examination of fractured surfaces revealed sintering defects, and EDS analysis showed less yttria concentration on Y-TZP specimens that were boiled for 7 days. CONCLUSION: Within the limitations of this study, the results suggested that the LTD procedures and the polishing treatment used did not reduce the flexural strengths of zirconia bars. Airborne-particle abrasion increased the flexural strength of specimens. CLINICAL IMPLICATIONS: Although polishing, airborne-particle abrasion, and various low-temperature degradation (LTD) treatments did not significantly degrade the strength of the Y-TZP ceramic material, LTD resulted in loss of yttria. Over time, gradual dissolution of yttria could decrease the tetragonal-phase stability and long-term clinical serviceability of this dental ceramic material.     

Effect of solution temperature on the mechanical properties of dual-cure resin cements

PURPOSE

This study was to evaluate the effect of the solution temperature on the mechanical properties of dualcure resin cements.

MATERIALS AND METHODS

For the study, five dual-cure resin cements were chosen and light cured. To evaluate the effect of temperature on the specimens, the light-cured specimens were immersed in deionized water at three different temperatures (4, 37 and 60℃) for 7 days. The control specimens were aged in a 37℃ dry and dark chamber for 24 hours. The mechanical properties of the light-cured specimens were evaluated using the Vickers hardness test, three-point bending test, and compression test, respectively. Both flexural and compressive properties were evaluated using a universal testing machine. The data were analyzed using a two way ANOVA with Tukey test to perform multiple comparisons (α=0.05).

RESULTS

After immersion, the specimens showed significantly different microhardness, flexural, and compressive properties compared to the control case regardless of solution temperatures. Depending on the resin brand, the microhardness difference between the top and bottom surfaces ranged approximately 3.3-12.2%. Among the specimens, BisCem and Calibra showed the highest and lowest decrease of flexural strength, respectively. Also, Calibra and Multilink Automix showed the highest and lowest decrease of compressive strength, respectively compared to the control case.

CONCLUSION

The examined dual-cure resin cements had compatible flexural and compressive properties with most methacrylate-based composite resins and the underlying dentin regardless of solution temperature. However, the effect of the solution temperature on the mechanical properties was not consistent and depended more on the resin brand.     

Internal fit of two all-ceramic systems and metal-ceramic crowns

Objectives

The aim of this study was to investigate the internal fit (IF) of glass-infiltrated alumina (ICA - In-Ceram Alumina), yttria-stabilized tetragonal zirconia polycrystals (Y-TZP - IPS e.max ZirCAD), and metal-ceramic (MC - Ni-Cr alloy) crowns.

Material and Methods

Sixty standardized resin-tooth replicas of a maxillary first molar were produced for crown placement and divided into 3 groups (n=20 each) according to the core material used (metal, ICA or Y-TZP). The IF of the crowns was measured using the replica technique, which employs a light body polyvinyl siloxane impression material to simulate the cement layer thickness. The data were analyzed according to the surfaces obtained for the occlusal space (OS), axial space (AS) and total mean (TM) using two-way ANOVA with Tukey''s multiple comparison test (p<0.05).

Results

No differences among the different areas were detected in the MC group. For the Y-TZP and ICA groups, AS was statistically lower than both OS and TM. No differences in AS were observed among the groups. However, OS and TM showed significantly higher values for ICA and Y-TZP groups than MC group. Comparisons of ICA and Y-TZP revealed that OS was significantly lower for Y-TZP group, whereas no differences were observed for TM.

Conclusions

The total mean achieved by all groups was within the range of clinical acceptability. However, the metal-ceramic group demonstrated significantly lower values than the all-ceramic groups, especially in OS.     

Polymerization behavior and thermal characteristics of two new composites at five temperatures: refrigeration to preheating

PURPOSE

Heat of composite polymerization (HP) indicates setting efficacy and temperature increase of composite in clinical procedures. The purpose of this in vitro experimental study was to evaluate the effects of 5 temperatures on HP of two new composites.

MATERIALS AND METHODS

From each material (Core Max II [CM] and King Dental [KD]), 5 groups of 5 specimens each were prepared and their total HPs (J/gr) were measured and recorded, at one of the constant temperatures 0℃, 15℃, 23℃, 37℃ and 60℃ (2 × 5 × 5 specimens) using a differential scanning calorimetry (DSC) analyzer. The data were analyzed using a two-way ANOVA, a Tukey''s test, an independent-samples t-test, and a linear regression analysis (α=0.05).

RESULTS

No polymerization reactions occurred at 0℃; then this temperature was excluded from statistical analyses. The mean HP of the remaining 20 KD specimens was 20.5 ± 14.9 J/gr, while it was 40.7 ± 12.9 J/gr for CM. The independent-samples t-test showed that there were significant differences between the HP of the two materials at the temperatures 15℃ (P=.0001), 23℃ (P=.0163), 37℃ (P=.0039), and 60℃ (P=.0106). Linear regression analysis showed statistically significant correlations between environment temperatures and HP of CM (R²=0.777).

CONCLUSION

Using CM is advantageous over conventional composite because of its better polymerization capacity. However due to its high HP, further studies should assess its temperature increase in vivo. Preheating KD is recommended. Refrigerating composites can negatively affect their polymerization potential.     

Influence of shading on zirconia's phase transformation and flexural strength after artificial aging

ObjectivesThe aim of this study was to determine the phase transformation and the influence of aging on the flexural strength of different colored zirconia. The effect of hydrothermal aging in an autoclave was compared with the effect of mechanical stress by simulating chewing.MethodsHigh-strength zirconia (3Y-TZP) was investigated in three different colors: uncolored, A3, and D3. Disc-shaped specimens (N = 3) were analyzed by X-ray diffraction (XRD), and flexural strength was determined on bar-shaped specimens (N = 15) in a 4-point bending test before and after performing two different aging protocols: aging in an autoclave (134 °C, 70 h) and aging in a chewing simulator (5 kg load, 1.2 million cycles). During autoclave aging, the fraction of monoclinic phase on the surface was determined every 5 h. Once this exceeded 25 vol%, aging of the bar specimens was stopped.ResultsWhile in the unstained group the mean value of the proportion of monoclinic phase already exceeded 25 vol% after 30 h in the autoclave, this was the case in both stained groups only after 70 h. No measurable phase transformation could be detected after chewing simulation. Only color A3 showed a statistically significant (p ≤ 0.05) decrease in flexural strength after aging in the chewing simulator.SignificanceThe colored zirconia showed a higher resistance to phase transformation through hydrothermal aging. The metal oxides in the staining solutions are assumed to hinder the phase transformation in the zirconia. Therefore, the significant reduction in the stained zirconia after chewing simulation is particularly interesting     

Effect of the infrastructure material on the failure behavior of prosthetic crowns

Objectives

To evaluate the effect of infrastructure (IS) material on the fracture behavior of prosthetic crowns.

Methods

Restorations were fabricated using a metal die simulating a prepared tooth. Four groups were evaluated: YZ-C, Y-TZP (In-Ceram YZ, Vita) IS produced by CAD-CAM; IZ-C, In-Ceram Zirconia (Vita) IS produced by CAD-CAM; IZ-S, In-Ceram Zirconia (Vita) IS produced by slip-cast; MC, metal IS (control). The IS were veneered with porcelain and resin cemented to fiber-reinforced composite dies. Specimens were loaded in compression to failure using a universal testing machine. The 30° angle load was applied by a spherical piston, in 37 °C distilled water. Fractography was performed using stereomicroscope and SEM. Data were statistically analyzed with Anova and Student–Newman–Keuls tests (α = 0.05).

Results

Significant differences were found between groups (p = 0.022). MC showed the highest mean failure load, statistically similar to YZ-C. There was no statistical difference between YZ-C, IZ-C and IZ-S. MC and YZ-C showed no catastrophic failure. IZ-C and IZ-S showed chipping and catastrophic failures. The fracture behavior is similar to reported clinical failures.

Significance

Considering the ceramic systems evaluated, YZ-C and MC crowns present greater fracture load and a more favorable failure mode than In-Ceram Zirconia crowns, regardless of the fabrication type (CAD-CAM or slip-cast).     

Influence of cement thickness on resin-zirconia microtensile bond strength

PURPOSE

The aim of this study was to evaluate the influence of resin cement thickness on the microtensile bond strength between zirconium-oxide ceramic and resin cement.

MATERIALS AND METHODS

Thirty-two freshly extracted molars were transversely sectioned at the deep dentin level and bonded to air-abraded zirconium oxide ceramic disks. The specimens were divided into 8 groups based on the experimental conditions (cement type: Rely X UniCem or Panavia F 2.0, cement thickness: 40 or 160 µm, storage: thermocycled or not). They were cut into microbeams and stored in 37℃ distilled water for 24 h. Microbeams of non-thermocycled specimens were submitted to a microtensile test, whereas those of thermocycled groups were thermally cycled for 18,000 times immediately before the microtensile test. Three-way ANOVA and Sheffe''s post hoc tests were used for statistical analysis (α=95%).

RESULTS

All failures occurred at the resin-zirconia interface. Thermocycled groups showed lower microtensile bond strength than non-thermocycled groups (P<.001). Differences in cement thickness did not influence the resin-zirconia microtensile bond strength given the same resin cement or storage conditions (P>.05). The number of adhesive failures increased after thermocycling in all experimental conditions. No cohesive failure was observed in any experimental group.

CONCLUSION

When resin cements of adhesive monomers are applied over air-abraded zirconia restorations, the degree of fit does not influence the resin-zirconia microtensile bond strength.     

Evaluation of the bond strength between aged composite cores and luting agent

PURPOSE

The aim of this study was to evaluate effect of different surface treatment methods on the bond strength between aged composite-resin core and luting agent.

MATERIALS AND METHODS

Seventy-five resin composites and also seventy-five zirconia ceramic discs were prepared. 60 composite samples were exposed to thermal aging (10,000 cycles, 5 to 55℃) and different surface treatment. All specimens were separated into 5 groups (n=15): 1) Intact specimens 2) Thermal aging-air polishing 3) Thermal aging- Er:YAG laser irradiation 4) Thermal aging- acid etching 5) Thermal-aging. All specimens were bonded to the zirconia discs with resin cement and fixed to universal testing machine and bond strength testing loaded to failure with a crosshead speed of 0.5 mm/min. The fractured surface was classified as adhesive failure, cohesive failure and adhesive-cohesive failure. The bond strength data was statistically compared by the Kruskal-Wallis method complemented by the Bonferroni correction Mann-Whitney U test. The probability level for statistical significance was set at α=.05.

RESULTS

Thermal aging and different surface treatment methods have significant effect on the bond strength between composite-resin cores and luting-agent (P<.05). The mean baseline bond strength values ranged between 7.07 ± 2.11 and 26.05 ± 6.53 N. The highest bond strength of 26.05 ± 6.53 N was obtained with Group 3. Group 5 showed the lowest value of bond strength.

CONCLUSION

Appropriate surface treatment method should be applied to aged composite resin cores or aged-composites restorations should be replaced for the optimal bond strength and the clinical success.