Human tooth germ stem cell response to calcium-silicate based endodontic cements

Objective

The aim of this study was to compare the cytotoxic effects of endodontic cements on human tooth germ stem cells (hTGSCs). MTA Fillapex, a mineral trioxide aggregate (MTA)-based, salicylate resin containing root canal sealer, was compared with iRoot SP, a bioceramic sealer, and AH Plus Jet, an epoxy resin-based root canal sealer.

Material and Methods

To evaluate cytotoxicity, all materials were packed into Teflon rings (4 mmµ3 mm) and co-cultured with hTGSCs with the aid of 24-well Transwell permeable supports, which had a pore size of 0.4 µm. Coverslips were coated with MTA Fillapex, iRoot SP and AH Plus Jet and each coverslip was placed onto the bottom of one well of a six-well plate for scanning electron microscopy (SEM) analysis. Before the cytotoxicity and SEM analysis, all samples were stored at 37ºC and at 95% humidity and 5% CO₂ for 24 hours to set. The cellular viability was analyzed using MTS test (3-(4,5-dimethyl-thiazol-2-yl)-5-(3-carboxy-methoxy-phenyl)-2-(4-sulfo-phenyl)-2H-tetrazolium). The cytotoxic effects and SEM visualization of the tested materials were analyzed at 24-hour, 72-hour, one-week and two-week periods.

Results

On the 1^st day, only MTA Fillapex caused cytotoxicity compared to negative control (NC) group (p<0.008). No significant difference was observed between the other tested materials at this period (p>0.05). After 14 days of incubation with the test materials, MTA Fillapex exhibited significantly higher cytotoxicity compared with iRoot SP, AH Plus Jet and the NC group (P<0.008). In the SEM analysis, the highest levels of cell attachment were observed for iRoot SP and the control group. After 24 hours, MTA Fillapex reduced the number of cells attached to the surface.

Conclusions

Within the limitations of this study, sealers exerted different cytotoxic effects on hTGSCs. Although all materials have exerted cellular toxicity, iRoot SP and AH Plus Jet may promote better attachment to hTGSCs.     

Effects of calcium hydroxide addition on the physical and chemical properties of a calcium silicate-based sealer

Recently, various calcium silicate-based sealers have been introduced for use in root canal filling. The MTA Fillapex is one of these sealers, but some of its physicochemical properties are not in accordance with the ISO requirements.

Objective

The aim of this study was to evaluate the flowability, pH level and calcium release of pure MTA Fillapex (MTAF) or containing 5% (MTAF5) or 10% (MTAF10) calcium hydroxide (CH), in weight, in comparison with AH Plus sealer.

Material and Methods

The flowability test was performed according to the ISO 6876:2001 requirements. For the pH level and calcium ion release analyses, the sealers were placed individually (n=10) in plastic tubes and immersed in deionized water. After 24 hours, 7 and 14 days, the water in which each specimen had been immersed was evaluated to determine the pH level changes and calcium released. Flowability, pH level and calcium release data were analyzed statistically by the ANOVA test (α=5%).

Results

In relation to flowability: MTAF>AH Plus>MTAF5>MTAF10. In relation to the pH level, for 24 h: MTAF5=MTAF10=MTAF>AH Plus; for 7 and 14 days: MTAF5=MTAF10>MTAF>AH Plus. For the calcium release, for all periods: MTAF>MTAF5=MTAF10>AH Plus.

Conclusions

The addition of 5% CH to the MTA Fillapex (in weight) is an alternative to reduce the high flowability presented by the sealer, without interfering in its alkalization potential.     

Long-term cytotoxic effects of contemporary root canal sealers

Objectives:

The aim of the present study was to investigate the effects of root canal sealers on the cytotoxicity of 3T3 fibroblasts during a period of 5 weeks.

Material and Methods:

Fibroblasts (3T3, 1x10⁵ cells per well) were incubated with elutes of fresh specimens from eight root canal sealers (AH Plus, Epiphany, Endomethasone N, EndoReZ, MTA Fillapex, Pulp Canal Sealer EWT, RoekoSeal and Sealapex) and with elutes of the same specimens for 5 succeeding weeks after immersing in simulated body fluid. The cytotoxicity of all root canal sealers was determined using the MTT assay. Data were analyzed using ANOVA and Tukey''s test.

Results:

RoekoSeal was the only sealer that did not show any cytotoxic effects (p<0.05). All the other tested sealers exhibited severe toxicity initially (week 0). MTA Fillapex remained moderately cytotoxic after the end of experimental period. Toxicity of the other tested sealers decreased gradually over time. The evaluated root canal sealers presented varying degrees of cytotoxicity, mainly in fresh mode.

Conclusions:

RoekoSeal had no cytotoxic effect both freshly mixed and in the other tested time points. MTA Fillapex was associated with significantly less cell viability when compared to the other tested root canal sealers.     

Biocompatibility and bioactivity of calcium silicate-based endodontic sealers in human dental pulp cells

Mineral Trioxide Aggregate (MTA) is a calcium silicate-based material. New sealers have been developed based on calcium silicate as MTA Fillapex and MTA Plus.

Objective

The aim of this study was to evaluate biocompatibility and bioactivity of these two calcium silicate-based sealers in culture of human dental pulp cells (hDPCs).

Material and Methods

The cells were isolated from third molars extracted from a 16-year-old patient. Pulp tissue was sectioned into fragments with approximately 1 mm³ and kept in supplemented medium to obtain hDPCs adherent cultures. Cell characterization assays were performed to prove the osteogenic potential. The evaluated materials were: MTA Plus (MTAP); MTA Fillapex (MTAF) and FillCanal (FC). Biocompatibility was evaluated with MTT and Neutral Red (NR) assays, after hDPCs exposure for 24 h to different dilutions of each sealer extract (1:2, 1:3 and 1:4). Unexposed cells were the positive control (CT). Bioactivity was assessed by alkaline phosphatase (ALP) enzymatic assay in cells exposed for one and three days to sealer extracts (1:4 dilution). All data were analyzed by ANOVA and Tukey post-test (p≤0.05%).

Results

MTT and NR results showed suitable cell viability rates for MTAP at all dilutions (90-135%). Cells exposed to MTAF and FC (1:2 and 1:4 dilutions) showed significant low viability rate when compared to CT in MTT. The NR results demonstrated cell viability for all materials tested. In MTAP group, the cells ALP activity was similar to CT in one and three days of exposure to the material. MTAF and FC groups demonstrated a decrease in ALP activity when compared to CT at both periods of cell exposure.

Conclusions

The hDPCs were suitable for the evaluation of new endodontic materials in vitro. MTAP may be considered a promising material for endodontic treatments.     

Physical Properties of 5 Root Canal Sealers

Introduction

The aim of this study was to evaluate the pH change, viscosity and other physical properties of 2 novel root canal sealers (MTA Fillapex and Endosequence BC) in comparison with 2 epoxy resin-based sealers (AH Plus and ThermaSeal), a silicone-based sealer (GuttaFlow), and a zinc oxide-eugenol–based sealer (Pulp Canal Sealer).

Methods

ISO 6876/2001 specifications were followed. The pH change of freshly mixed and set sealers was evaluated during periods of 1 day and 5 weeks, respectively. The viscosity was investigated at different injection rates (72, 10, and 5 mm/min) at room temperature by using a syringe-based system that was based on the Instron 3360 series universal testing system.

Results

The flow, dimensional change, solubility, and film thickness of all the tested sealers were in agreement with ISO 6876/2001 recommendations. The MTA Fillapex sealer exhibited a higher flow than the Endosequence BC sealer (P < .05). The MTA Fillapex and Endosequence BC sealers showed the highest film thicknesses among the tested samples. The Endosequence BC sealer exhibited the highest value of solubility, which was in accordance with 3% mass fraction recommended by the ISO 6876/2001, and showed an acceptable dimensional change. The MTA Fillapex and Endosequence BC sealers presented an alkaline pH at all times. The pH of fresh samples of the AH Plus and ThermaSeal sealers was alkaline at first but decreased significantly after 24 hours. The viscosity of the tested sealers increased with the decreased injection rates.

Conclusions

The tested sealers were pseudoplastic according to their viscosities as determined in this study. The MTA Fillapex and Endosequence BC sealers each possessed comparable flow and dimensional stability but higher film thickness and solubility than the other sealers tested.     

Sealer Penetration into Dentinal Tubules in the Presence or Absence of Smear Layer: A Confocal Laser Scanning Microscopic Study

Introduction

The aim of this study was to test the dentinal tubule penetration of AH26 (Dentsply DeTrey, Konstanz, Germany) and MTA Fillapex (Angelus, Londrina, PR, Brazil) in instrumented root canals obturated by using cold lateral compaction or warm vertical compaction techniques in either the presence or absence of the smear layer.

Methods

Forty-five extracted single-rooted human mandibular premolar teeth were used. The crowns were removed, and the root canals were instrumented by using the Self-Adjusting File (ReDent-Nova, Ra'anana, Israel) with continuous sodium hypochlorite (2.6%) irrigation. Final irrigation was either with 5% EDTA or with sodium hypochlorite. The canals were dried and obturated by using rhodamine B–labeled AH26 or MTA Fillapex in combination with the cold lateral compaction or the warm vertical compaction technique. After setting, the roots were sectioned horizontally at 4-, 8-, and 12-mm distances from the apical tip. On each section, sealer penetration in the dentinal tubules was measured by using confocal laser scanning microscopy.

Results

Regardless of the usage of EDTA, MTA Fillapex, compared with AH26, was associated with greater sealer penetration when used with the cold lateral compaction technique, and, conversely, AH26, compared with MTA Fillapex, was associated with greater sealer penetration when used with the warm vertical compaction technique (P < .05). Removal of the smear layer increased the penetration depth of MTA Fillapex used with the cold lateral compaction technique (P < .05); however, it had no significant effect on the penetration depth of AH26.

Conclusions

Greater sealer penetration could be achieved with either the MTA Fillapex–cold lateral compaction combination or with the AH26–warm vertical compaction combination. Smear layer removal was critical for the penetration of MTA Fillapex; however, the same did not hold for AH26.     

Regaining Apical Patency after Obturation with Gutta-percha and a Sealer Containing Mineral Trioxide Aggregate

Introduction

MTA Fillapex (Angelus Solucoes Odontologicas, Londrina PR, Brazil) was introduced as a mineral trioxide aggregate (MTA)-based sealer used for endodontic obturation. There is a lack of research that evaluates the ability of different solvents to soften MTA-based sealers during retreatment. This study tested the ability of 4 commonly used endodontic solvents to soften gutta-percha and MTA Fillapex to allow for the re-establishment of apical patency.

Methods

Eighty-six extracted maxillary anterior teeth were instrumented to the working length to a size 45 (.04 taper size). Teeth were divided into 2 groups (n = 43 for each group). MTA Fillapex was placed into all canals. Group 1 was obturated with gutta-percha to the working length, and group 2 was obturated 2 mm short of the working length to ensure the apical 2 mm was filled with sealer only. Both groups were divided into 4 subgroups (n = 10). The remaining teeth served as the control group. Each subgroup was exposed to 1 of the following solvents: chloroform, Endosolv R (Septodont, Saint-Maur, France), Endosolv E (Septodont), or eucalyptol.

Results

Patency was re-established in 100% of the teeth in groups 1 and 2 when tested with chloroform or Endosolv E, 80% of the teeth in group 1 and 90% in group 2 when tested with eucalyptol, and 10% of the teeth in group 1 and 50% in group 2 tested when with Endosolv R. The chi-square test indicated there was a statistical difference between Endosolv R and the other tested solvents for both groups.

Conclusions

Chloroform, Endosolv E, and Eucalyptol soften GP and MTA Fillapex sufficiently to aid in re-establishing apical patency during endodontic retreatment.     

Comparative evaluation of the calcium release from mineral trioxide aggregate and its mixture with glass ionomer cement in different proportions and time intervals – An in vitro study

Background

Addition of glass ionomer cement (GIC) has been suggested to improve the setting time and handling characteristics of mineral trioxide aggregate (MTA). This study evaluated the effect of adding GIC to MTA in terms of calcium release, an issue that has not been previously studied.

Materials and methods

The study comprised four groups with five samples each: a control group of MTA alone and experimental groups I (1MTA:1GIC), II (2MTA:1GIC), and III (1MTA:2GIC) based on the mixture of MTA and GIC powders in the respective proportions by volume. Calcium release from the samples was measured by atomic absorption spectrophotometry at 15 min, 6 h, 24 h, and 1 week after setting. The level of statistical significance was set at p < 0.05.

Results

Groups I (1MTA:1GIC) and III (1MTA:2GIC) released significantly less calcium than the control group at all time periods, except at 15 min for group I. Group II (2MTA:1GIC) showed no significant difference in calcium release compared to the control at any time period. Group II exhibited greater calcium release than group I or III at all time periods, with significant differences between groups I and II at 1 week and between groups I and III at 24 h and 1 week. There were no statistical differences in calcium release between groups I and III.

Conclusions

Adding GIC to improve the setting time and handling properties of the MTA powder can be detrimental to the calcium-releasing ability of the resultant mixture, depending on the proportion of GIC added. Adding MTA and GIC at a proportion of 2:1 by volume did not impact calcium release from the mixture. These findings should be verified through further clinical studies.     

Effect of MTA-based sealer on the healing of periapical lesions

Some manufacturers have recently added specific components to improve the ease of handling and insertion material properties of MTA in order to create MTA-based sealers.

Objective:

The aim of this study was to evaluate the healing of periapical lesions in canine teeth after a single session of endodontic treatment with MTA Fillapex^® compared with Sealapex or Endo-CPM-Sealer^®.

Material and Methods:

Sixty-two root canals were performed on two 1-year-old male dogs. After coronal access and pulp extirpation, the canals were exposed to the oral cavity for 6 months in order to induce periapical lesions. The root canals were prepared, irrigated with a solution of 2.5% sodium hypochlorite and filled with gutta-percha and different sealers, according to the following groups: 1) Sealapex; 2) Endo-CPM-Sealer^®; and 3) MTA Fillapex. Some teeth with periapical lesions were left untreated for use as positive controls. Healthy teeth were used as negative controls. After 6 months, the animals were sacrificed and serial sections from the roots were prepared for histomorphologic analysis and stained with hematoxylin and eosin and the Brown and Brenn technique. The lesions were scored according to pre-established histomorphologic parameters and the scores statistically analyzed using the Kruskal-Wallis test.

Results:

All 3 materials produced similar patterns of healing (p>0.05); in particular, persistent inflammation and absence of complete periapical tissue healing were consistently noted.

Conclusions:

Preparation of the infected root canals followed by filling with the materials studied was insufficient to provide complete healing of the periapical tissues.     

Perceived color shift of ceramics according to the change of illuminating light with spectroradiometer

PURPOSE

Perceived color of ceramics changes by the spectral power distribution of ambient light. This study aimed to quantify the amount of shifts in color and color coordinates of clinically simulated seven all-ceramics due to the switch of three ambient light sources using a human vision simulating spectroradiometer.

MATERIALS AND METHODS

CIE color coordinates, such as L*, a* and b*,of ceramic specimens were measured under three light sources, which simulate the CIE standard illuminant D65 (daylight), A (incandescent lamp), and F9 (fluorescent lamp). Shifts in color and color coordinate by the switch of lights were determined. Influence of the switched light (D65 to A, or D65 to F9), shade of veneer ceramics (A2 or A3), and brand of ceramics on the shifts was analyzed by a three-way ANOVA.

RESULTS

Shifts in color and color coordinates were influenced by three factors (P<.05). Color shifts by the switch to A were in the range of 5.9 to 7.7 ΔE*_abunits, and those by the switch to F9 were 7.7 to 10.2; all of which were unacceptable (ΔE*_ab > 5.5). When switched to A, CIE a* increased (Δa*: 5.6 to 7.6), however, CIE b* increased (Δb*: 4.9 to 7.8) when switched to F9.

CONCLUSION

Clinically simulated ceramics demonstrated clinically unacceptable color shifts according to the switches in ambient lights based on spectroradiometric readings. Therefore, shade matching and compatibility evaluation should be performed considering ambient lighting conditions and should be done under most relevant lighting condition.     

Evaluation of crown discoloration induced by endodontic sealers and colour change ratio determination after bleaching

The aim of this study was to evaluate tooth discoloration after the use of root canal sealers and the effect of internal bleaching on sealer discoloration. The crowns of 56 incisors were cut and randomly filled with four sealers (n = 14): Pulpispad, AH26, MTA Fillapex, EndoREZ. The colour measurement was taken with a spectrophotometer prior and after placement of sealers. Colour changes (ΔE) were recorded after 4 weeks then sealers were removed and an internal bleaching treatment was performed. After bleaching treatment colour changes (ΔE) were measured. Data were analysed using ANOVA and Tukey’s test (α = 0.05). All tested sealers induced varying chromatic alterations. Pulpispad showed statistically more discoloration than other sealers (P < 0.05). After bleaching, EndoREZ showed statistically more bleaching ratio than MTA Fillapex and AH26 (P < 0.05). Internal bleaching was efficient in discoloured teeth induced by root canal sealers.     

Evaluation of shear bond strength of two resin-based composites and glass ionomer cement to pure tricalcium silicate-based cement (Biodentine?)

Objectives

Tricalcium silicate is the major constituent phase in mineral trioxide aggregate (MTA). It is thus postulated that pure tricalcium silicate can replace the Portland cement component of MTA. The aim of this study was to evaluate bond strength of methacrylate-based (MB) composites, silorane-based (SB) composites, and glass ionomer cement (GIC) to Biodentine^® and mineral trioxide aggregate (MTA).

Material and Methods

Acrylic blocks (n=90, 2 mm high, 5 mm diameter central hole) were prepared. In 45 of the samples, the holes were fully filled with Biodentine^® and in the other 45 samples, the holes were fully filled with MTA. The Biodentine^® and the MTA samples were randomly divided into 3 subgroups of 15 specimens each: Group-1: MB composite; Group-2: SB composite; and Group-3: GIC. For the shear bond strength (SBS) test, each block was secured in a universal testing machine.

Results

The highest (17.7±6.2 MPa) and the lowest (5.8±3.2 MPa) bond strength values were recorded for the MB composite-Biodentine^® and the GIC-MTA, respectively. Although the MB composite showed significantly higher bond strength to Biodentine (17.7±6.2) than it did to MTA (8.9±5.7) (p<0.001), the SB composite (SB and MTA=7.4±3.3; SB and Biodentine^®=8.0±3,6) and GIC (GIC and MTA=5.8±3.2; GIC and Biodentine=6.7±2.6) showed similar bond strength performance with MTA compared with Biodentine (p=0.73 and p=0.38, respectively).

Conclusions

The new pure tricalcium-based pulp capping, repair, and endodontic material showed higher shear bond scores compared to MTA when used with the MB composite.     

EFFECT OF EUGENOL-BASED ENDODONTIC SEALER ON THE ADHESION OF INTRARADICULAR POSTS CEMENTED AFTER DIFFERENT PERIODS

Objective:

This study evaluated in vitro the influence of an eugenol-based sealer (EndoFill) on the retention of stainless steel prefabricated posts cemented with zinc phosphate and resin-based (Panavia F) cements after different periods of root canal obturation, using the pull-out test.

Material and methods:

Sixty upper canines were decoronated and the roots were embedded in resin blocks. The specimens were distributed into 3 groups, according to the period elapsed between canal obturation and post cementation: Group I - immediately; Group II - 72 h and Group III - 4 months. The groups were subdivided according to the type of cement used for post cementation: A - zinc phosphate and B - Panavia F. Following the experimental periods, specimens were subjected to pull- out test in an Instron machine with application of tensile force at a crosshead speed of 0.5 mm/min until post dislodgement. The maximum forces required for post removal were recorded (kN) and means were subjected to statistical analysis by 2-way ANOVA and Tukey-Kramer test (α=0.001)

Results:

There were statistically significant differences (p<0.01) between the posts cemented with zinc phosphate cement (0.2112 kN) and Panavia F (0.0501 kN). However, no statistically significant differences (p>0.05) were found between the three post cementation periods, regardless of the cement.

Conclusions:

It was concluded that the eugenol-based sealer influenced the tensile strength of the posts cemented with the resin cement, but had no influence on the time waited between root canal obturation and post space preparation/post cementation.     

High-efficiency tooth bleaching using non-thermal atmospheric pressure plasma with low concentration of hydrogen peroxide

Light-activated tooth bleaching with a high hydrogen peroxide (HP; H₂O₂) concentration has risks and the actual role of the light source is doubtful. The use of conventional light might result in an increase in the temperature and cause thermal damage to the health of the tooth tissue.

Objective:

This study investigated the efficacy of tooth bleaching using non-thermal atmospheric pressure plasma (NAPP) with 15% carbamide peroxide (CP; CH₆N₂O₃) including 5.4% HP, as compared with conventional light sources.

Material and Methods:

Forty human teeth were randomly divided into four groups: Group I (CP+NAPP), Group II (CP+plasma arc lamp; PAC), Group III (CP+diode laser), and Group IV (CP alone). Color changes (ΔE ) of the tooth and tooth surface temperatures were measured. Data were evaluated by one-way analysis of variance (ANOVA) and post-hoc Tukey''s tests.

Results:

Group I showed the highest bleaching efficacy, with a ΔE value of 1.92-, 2.61 and 2.97-fold greater than those of Groups II, III and IV, respectively (P<0.05). The tooth surface temperature was maintained around 37ºC in Group I, but it reached 43ºC in Groups II and III.

Conclusions:

The NAPP has a greater capability for effective tooth bleaching than conventional light sources with a low concentration of HP without causing thermal damage. Tooth bleaching using NAPP can become a major technique for in-office bleaching in the near future.     

Effect of polishing and glazing on the color and spectral distribution of monolithic zirconia

PURPOSE

The aim of this study was to evaluate the effect of polishing and glazing on the color and spectral distribution of monolithic zirconia.

MATERIALS AND METHODS

Forty-five monolithic zirconia specimens (16.3 mm × 16.4 mm × 2.0 mm) were fabricated and divided into 5 groups according to the number of A2-coloring liquid applications (Group I to V). Each group was divided into 3 subgroups according to the method of surface treatments (n=3): N: no treatment; P: polishing; G: glazing. Color and spectral distribution of five different areas of each specimen were measured according to CIELAB color space in the reflectance mode relative to the standard illuminant D65 on a reflection spectrophotometer. Data were analyzed using one-way ANOVA followed by Tukey''s HSD test, Pearson correlation and regression analysis (α=.05).

RESULTS

There was a significant difference in CIE L^* between Subgroup N and P, and in CIE b^* between Subgroup P and G in each group. Spectral reflectance generally decreased in Subgroup P and G in comparison with Subgroup N. Color differences between Subgroup P and G were within the perceptibility threshold (ΔE^*_ab< 3.7) in most groups. Highly significant correlation was found between CIE b^*and each subgroups as the number of coloring liquid applications increased (R²>0.88, P<.001).

CONCLUSION

A perceptible color difference can be detected after polishing of monolithic zirconia. Polishing decreases the lightness, and glazing also decreases the lightness, but increases the yellowness of monolithic zirconia.     

The comparison of MTA,Geristore® and Amalgam with or without Bioglass as a matrix in sealing the furcal perforations (in vitro study)

Aim

The objective of this in vitro was to assess the sealing ability of MTA, Geristore®, and amalgam with and without Bioglass as a matrix used to repair furcation perforations in mandibular molars by using dye penetration.

Materials and methods

One hundred mandibular molars were randomly divided into six experimental groups. Five teeth with perforation were used as positive control while five teeth without perforation were used as negative control group. Furcal perforations were made in the teeth. Perforations were repaired with amalgam in group 1, amalgam and Bioglass in group 2, MTA in group 3, MTA and Bioglass in group 4, Geristore® in group 5, and Geristore® and Bioglass in group 6. All repairing materials were allowed to set for 72 h. Leakage at the repaired sites was then evaluated using dye penetration and clearing technique under stereomicroscope.

Results

The perforations repaired with MTA and Geristore® leaked significantly less than amalgam (p = 0.000). Bioglass reduced sealing ability of MTA and Geristore® significantly (p = 0.000, p = 0.019), while reduced the sealing ability of amalgam insignificantly (p = 0.78).

Conclusion

MTA and Geristore® have shown acceptable sealing ability in furcal perforation in comparison to amalgam while Bioglass as a matrix beneath them has reduced their sealing ability.     

EVALUATION OF APICAL MICROLEAKAGE OF TEETH SEALED WITH FOUR DIFFERENT ROOT CANAL SEALERS

Objectives:

to compare the apical sealing ability of four root canal sealers. Materials and methods: forty extracted human maxillary canines were instrumented 1 mm short of the anatomical apex and randomly assigned to four groups (n=10), according to the root canal sealer used for obturation: Endofill, AH Plus, EndoREZ and Epiphany. Root canals were obturated with guttapercha points, except for the Epiphany group, in which resin points (Resilon) were used. The teeth were immersed in India ink for seven days and clarified using methyl salicylate. The extent of apical dye penetration was measured with a measuroscope in all aspects of the canal.

Results:

AH Plus (0.02 mm ± 0.07), Epiphany (0.00 mm ± 0.00) and EndoREZ (0.32 mm ± 0.62) did not differ statistically to each other (p>0.01). EndoFill presented the highest dye penetration mean (0.83 mm ± 0.73) and was statistically different from the other sealers (p<0.01).

Conclusions:

the resin-based root canal sealers presented lesser apical microleakage than the zinc oxide and eugenol based sealer. No statistical differences were observed among resin based sealers.