Bonding characteristics of newly developed all-in-one adhesives

This study evaluated the microtensile bond strength and the interfacial morphology of newer adhesives. The occlusal surfaces of extracted teeth were ground flat for random allocation to four equal groups. Resin composite was bonded to each surface using either Clearfil SE Bond [SEB], Clearfil Protect Bond [PB], G-Bond [GB], or an experimental adhesive, SSB-200 [SSB]. After storage for 24 h in water at 37 degrees C, they were sectioned into beams (cross-sectional area 1 mm(2)) for microtensile bond strength testing (muTBS) at a crosshead speed of 1 mm/min. The load at failure of each was recorded; the data were analyzed by one-way ANOVA and Games Howell tests. The surfaces of the fractured specimens were observed using SEM. For the ultra-morphology of the interface, the occlusal surfaces of four more teeth were prepared as before and a thin layer of flowable resin composite was bonded to each surface using one of the four adhesives.The mean muTBS ranged from 39.68 MPa (GB) to 64.97 MPa (SEB). There were no statistical differences between SEB and SSB, or between PB and GB (p > 0.05). The muTBS of SEB and SSB were significantly greater than that of PB and GB (p < 0.05). SEMs of the fractured surfaces revealed a mixed (cohesive/interfacial) failure. TEM examination highlighted differences in the hybrid layer; SEB had a thicker layer than the others. In conclusion, the newer all-in-one adhesives produced a thin hybrid layer but varied in their bond strengths. The 2-step self-etching adhesives do not necessarily produce higher bond strengths than that of the all-in-one systems.     

Differential effect of in vitro degradation on resin-dentin bonds produced by self-etch versus total-etch adhesives

OBJECTIVE: To evaluate the effect of an in vitro challenge (NaOCl immersion) on microtensile bond strength (MTBS) of five adhesive systems to dentin. METHODS: Flat dentin surfaces from 40 molars were bonded with three total-etch adhesives (Single Bond, Prime&Bond NT and the experimental Prime&Bond XP), and two self-etching agents (Clearfil SE Bond and Etch&Prime 3.0). Composite build-ups were constructed with Tetric Ceram. Teeth were then sectioned into beams of 1.0 mm2 cross-sectional area. Half of the beams were immersed in 10% NaOCl aqueous solution for 5 h. Each beam was tested in tension in an Instron machine at 0.5 mm/min. Data were analyzed by 2-way ANOVA and multiple comparisons tests (p < 0.05). RESULTS: Clearfil SE Bond and Single Bond attained higher MTBS than the other three adhesives. Prime&Bond NT and Prime&Bond XP performed equally, and Etch&Prime resulted in the lowest MTBS. After NaOCl immersion, MTBS decreased in all groups. The highest MTBS values were obtained for Clearfil SE Bond and Prime&Bond XP. Scaning electron microscopy observation of debonded sticks evidenced dissolution and microstructural alterations of intertubular dentin, except when Clearfil SE Bond was used. CONCLUSIONS: Resin-dentin bonds are prone to chemical degradation. The extent of the resin degradation is adhesive system specific. Chemical degradation of the nonresin infiltrated collagen fibers does also exist in total-etch adhesives. Both processes may reduce long-term resin-dentin bond strength.     

Adhesive performance of dentin bonding agents applied in vivo and in vitro. Effect of intrapulpal pressure and dentin depth

The purpose of this study was to evaluate the influence of intrapulpal pressure and dentin depth on bond strengths of an etch-and-rinse and a self-etching bonding agent to dentin in vitro and in vivo. Twenty-four pairs of premolars were randomly divided into four groups (n = 6) according to the dentin bonding agent, Single Bond and Clearfil SE Bond, and intrapulpal pressure, null or positive. Each tooth of the pair was further designated to be treated in vivo or in vitro. The intrapulpal pressure was controlled in vivo by the delivery of local anesthetics containing or not a vasoconstrictor, while in vitro, it was achieved by keeping the teeth under hydrostatic pressure. Class I cavities were prepared and the dentin bonding agents were applied followed by incremental resin restoration. For the teeth treated in vitro, the same restorative procedures were performed after a 6 month-storage period. Beams with 1 mm(2) cross-sectional area were prepared and microtensile tested. Clearfil SE Bond was not influenced by any of the variables of the study, while bond strengths produced in vitro were significantly higher for Single Bond. Overall, lower bond strengths were produced in deep dentin, which reached statistical significance when Single Bond was applied under physiological or simulated intrapulpal pressure. In conclusion, in vitro bonding may overestimate the immediate adhesive performance of more technique-sensitive dentin bonding systems. The impact of intrapulpal pressure on bond strength seems to be more adhesive dependent than dentin morphological characteristics related to depth.     

Bonding performance of different adhesive systems to deproteinized dentin: microtensile bond strength and scanning electron microscopy

Deproteinization has been shown to optimize dentin bonding, but differences in adhesive composition should be considered. The objective of this study was to evaluate the effect of dentin deproteinization on microtensile bond strength (microTBS) of four total-etch adhesive systems (Single Bond/SB, Prime & Bond NT/PB, One Coat Bond/OC, and PQ1/PQ). The ultrastructure of the resin-dentin interfaces was also examined using scanning electron microscopy. Tukey's multiple-comparison tests indicated that PB and PQ produced significantly higher microTBS (p<0.05) after dentin deproteinization (PB=61.53 MPa, PQ=58.18 MPa). This treatment provided statistically lower results for SB (39.08 MPa), but the microTBS of OC to dentin was unaffected by dentin deproteinization. The bonding performance on deproteinized dentin surfaces depended on the characteristics of each adhesive system, as well as the adhesive dentin specificity to the oxidant effect of sodium hypochlorite. Incorporation of fillers in the adhesive, a possible self-etching action, and the presence of a volatile solvent (acetone) were the main factors for a better union between the adhesive system and deproteinized substrate.     

The effect of six years of water storage on resin composite bonding to human dentin

The aim of this in vitro study was to evaluate dentin bond strength and marginal adaptation of direct resin composite fillings after different storage times. Three hundred sixty cavities were prepared in discs of freshly extracted human third molars and filled with resin composites. Multistep self-etching adhesives (Syntac Classic, A.R.T. Bond, both with and without total etching), three-step etch-and-rinse adhesives (Scotchbond Multi-Purpose Plus, EBS), and two-step etch-and-rinse adhesives (Prime and Bond 2.0, Syntac Single-Component) were used for bonding. After 1, 90, and 2190 days of water storage and 24 h thermocycling (1150 cycles), push-out testing was performed. From the 6-year group, replicas were made after 1 day, 90 days, and 1, 2, 3, 4, 5, and 6 years, and examined regarding marginal adaptation under an SEM (x 200 magnification). In all groups under investigation, push-out bond strengths remained stable after 90 days; however, the strengths significantly decreased after 6 years of water storage. The two-step systems exhibited lower bond strengths than three-step systems after 6 years. Marginal analysis revealed a significant loss regarding the percentage of perfect margins having been stable after 2 years for the three-step etch-and-rinse systems. Overall, the older three-step systems proved to be more effective than the simplified adhesives Syntac Single-Component and Prime and Bond 2.0 with regard to bond strength and marginal adaptation.     

Effect of acid etching on dentin wettability and roughness: self-etching primers versus phosphoric acid

OBJECTIVE: To compare the effect of self-etching primers and phosphoric acid on the wettability and roughness of smear layer-covered and smear layer-free dentin. MATERIALS AND METHOD: Three self-etching primers (Clearfil SE Bond, AdheSE, and Xeno III) and 10% (w/w) phosphoric acid (H(3)PO(4)) solution were evaluated. The substrates were midcoronal dentin with and without smear layer. For each liquid, pH, density, and surface tension were determined. Water wettability of dentin and roughness were measured before and after each etching. Wettability of self-etching primers and phosphoric acid was measured on untreated dentin. RESULTS: Water wettability increased after acid conditioning similarly for all the liquids used. On smear layer-covered surfaces, self-etching primers achieved a comparable wetting but with greater contact angles than phosphoric acid. However, on smear layer-free surfaces, the increasing sequence of contact angle was Clearfil SE < AdheSE < Xeno III < Phosphoric acid. The treatment with phosphoric acid (lowest pH) produced the highest roughness increase on both dentin substrates. The roughening effect of the self-etching adhesives was more evident for AdheSE and Xeno III. CONCLUSIONS: Self-etching primers and phosphoric acid promote similar water wettability increase. However, self-etching primers provided lower dentin roughness increase than pretreatment with phosphoric acid. The presence of smear layer did not affect the results of self-etching and phosphoric acid treatments.     

Degradation patterns of different adhesives and bonding procedures

Various types of resin adhesives and procedures are available in the clinical field, so comprehensive understanding of degradation is required for each material and bonding procedure. The objective of this study was to investigate the bond durability for different adhesives and bonding procedures. Resin-dentin bonded beams were prepared with the use of two adhesives (One-Up Bond F/self-etching primer system and One Bond/total-etch adhesive) and two experimental groups for the bonding procedure (wet and dry bonding of the total-etch adhesive). Those samples were soaked in water for 24 h(control), 6 and 12 months. After the water immersion, the bond strengths were measured by the microtensile bond test, and subsequently fractography was performed with the use of SEM. Statistically significant reduction of the bond strength (p < 0.05) was apparent after 12 months of water exposure in the range 22-48% of the control. The bonding resin was eluted from the hybrid layer of the self-etching and the total-etch adhesives for the wet bonding. Micromorphological alterations were found due to the hydrolysis of collagen fibrils with the total-etch adhesive for the dry bonding mode. These pathologic alterations were in accord with the bond strength.     

Characterisation of resin-dentine interfaces by compressive cyclic loading

The aims of this in vitro study were to evaluate the ultra-morphological changes in resin-dentine interfaces after different amounts of thermomechanical load (TML), and to determine the corresponding microtensile bond strengths (microTBS). Enamel/dentine discs with a thickness of 2 mm were cut from 24 human third molars and bonded with four adhesives involving different adhesion approaches: Syntac (Ivoclar Vivadent; used as multi-step etch-and-rinse adhesive), Clearfil SE Bond (Kuraray; two-step self-etch adhesive), Xeno III (Dentsply DeTrey; mixed all-in-one self-etch primer adhesive system), and iBond (Heraeus Kulzer; non-mixed all-in-one self-etch adhesive). The resin-dentine discs were cut into beams (width 2 mm; 2 mm dentine, 2 mm resin composite) and subsequently subjected to cyclic TML using ascending amounts of mechanical/thermal cycles (20 N at 0.5 Hz of mechanical load and 5-55 degrees C of thermal cycles: for 0/0, 100/3, 1,000/25, 10,000/250, 100,000/2,500 cycles). Loaded specimens were either cut perpendicularly in order to measure microTBS (n=20; crosshead speed: 1 mm/min) or were immersed in an aqueous tracer solution consisting of 50 wt% ammoniacal silver nitrate and processed for ultra-morphological nanoleakage examination using transmission electron microscopy (TEM). microTBS were significantly decreased by increasing amounts of TML for all adhesives (p<0.05). Bond strengths after 0 vs. 100,000 thermomechanical cycles were: Syntac: 41.3/30.1 MPa; Clearfil SE Bond 44.8/32.5 MPa; Xeno III 27.5/13.7 MPa; iBond 27.0/6.2 MPa. Relatively early, a certain amount of nanoleakage was observed in all groups by TEM, which was more pronounced for Xeno III and iBond. The incidence of nanoleakage remained stable or was even reduced with increasing load cycles for all adhesives except iBond, where exact failure origins were detected within the adhesive and at the top of the hybrid layer.     

Ultramorphological analysis of resin-dentin interfaces produced with water-based single-step and two-step adhesives: nanoleakage expression

This study evaluated the nanoleakage patterns in bonded interfaces using two single-step, self-etching adhesives (Adper Prompt-AD, and One-up Bond F-OB), two two-step, self-etching primers (Clearfil SE Bond-CF, and Unifil Bond-UB), and one two-step, total-etch adhesive (Single Bond-SB). Dentin surfaces were bonded with the adhesive systems and stored in water at 37 degrees C for 1 week and 6 months. After storage periods, teeth were sectioned into 0.8 mm-thick slabs, coated with nail varnish except for the bonded interfaces, and immersed in ammoniacal AgNO(3) for 24 h. After immersion in photodeveloping solution, bonded sections were prepared and observed under a SEM using the backscattered electron mode. Undemineralized, unstained, epoxy resin-embedded sections were prepared for TEM. Nanoleakage patterns were qualitatively compared between periods. Nanoleakage was observed in all bonded specimens at both periods. CF and UB presented silver deposits predominantly restricted to the thin (0.5 microm) hybrid layer (HL) at both periods. Although no evident differences were observed in the nanoleakage pattern of UB at 7 days and 6 months, CF presented enlarged areas of silver impregnation after 6 months. SB presented accumulation of silver particles mostly within the HL at 7 days, which was intensified after 6 months. AD and OB presented massive silver accumulation within the HL and the overlying adhesive layer. No evident differences were noticed between storage periods. Silver impregnation increased for all adhesive systems from 7 days to 6 months, except for UB.     

Effect of load cycling and in vitro degradation on resin-dentin bonds using a self-etching primer

The objective of this study was to evaluate the effect of in vitro degradation and mechanical loading on microtensile bond strength (MTBS) and microleakage (ML) of a resin composite to dentin using a self-etching primer adhesive [Clearfil SE Bond (SEB)] under two hydration statuses. Twenty-four flat dentin surfaces were divided in groups: 1) blot-dried, 2) air-dried. SEB was applied and resin buildups were performed with Tetric Ceram. Specimens were divided in four subgroups: a) sectioned into beams, b) load cycled, c) beams were immersed in NaOCl for 5 h, d) load cycled and immersed in NaOCl. Beams were tested in tension. For ML testing, 80 Class V cavities were prepared and molars divided in subgroups as described above (in group c and d, specimens were kept in distilled water for 1 year, instead of the 5-h NaOCl immersion). ML was assessed by dye penetration. Analysis of variance and multiple comparisons tests were used for MTBS. For ML, Mann-Whitney U and Wilcoxon matched pairs signed ranked were used (p<0.05). SEB applied to completely dehydrated dentin produced the highest MTBS, at 24-h evaluation. In vitro degradation always decreased MTBS, and fatigue loading only diminished MTBS on dehydrated dentin. Load cycling increased dye penetration on dentin margins. Degradation always increased ML in both enamel and dentin margins.     

Light-curing efficiency of dental adhesives by gallium nitride violet-laser diode determined in terms of ultimate micro-tensile strength

The purpose of this study was to evaluate whether violet-laser diode (VLD) can be used as light-curing source. The ultimate (micro-)tensile strength (μTS) of three adhesives was determined when cured by VLD in comparison with curing by two different types of commercial LED light-curing units. One VLD (VLM 500) and two LED units (Curenos and G-Light Prima) were used to cure the adhesive resin of the two-step self-etch adhesives Clearfil SE Bond, Tokuso Mac Bond II, and FL-Bond II. A 0.6-mm thick acrylic mould was filled with adhesive resin and cured for 60 s. After 24-h water storage, specimens were trimmed into an hourglass shape with a width of 1.2 mm at the narrowest part, after which the μTS was determined (n=10). In addition, the light transmittance of each adhesive was characterized using a UV-vis-NIR spectrometer. No significant difference in curing efficiency between VLD and LED were observed for both Tokuso Mac Bond II and FL-Bond II (p>0.05). For Clearfil SE Bond, the μTS of VLD-cured specimens was higher than that of the specimens cured by the LED Curenos unit (p<0.05). Spectrometry revealed that this marked difference must be attributed to a different light transmittance of Clearfil SE Bond for visible blue light versus for the lower area of UV and visible violet light. In conclusion, A GaN-based violet laser diode can be used as light-curing source to initiate polymerization of dental resins.     

An innovative quaternary ammonium methacrylate polymer can provide improved antimicrobial properties for a dental adhesive system

A quaternary ammonium methacrylate polymer (QAMP) with antimicrobial potential was synthesized. The resulting product (QAMP) was characterized by FTIR spectroscopy, NMR spectroscopy, visible spectrophotometry, XRPD and TGA. The in vitro susceptibility tests against Streptococcus mutans of QAMP were investigated prior and after incorporation into a commercial adhesive system (Clearfil? SE Bond). The release of quaternary ammonium compounds from the experimental adhesive system (Clearfil? SE Bond?+?5% QAMP) was performed during 1, 7, 14, 21 and 30 days. Spectroscopic data confirmed that QAMP was successfully obtained. Thermogravimetric analysis indicated that QAMP was heat stable. Prior incorporation into the adhesive system, QAMP revealed an inhibition halo of 18.33?±?0.6?mm. By agar disk diffusion test, Clearfil? SE Bond containing 5% QAMP presented an inhibition halo (16.67?±?1.5?mm) similar to Clearfil? Protect Bond (positive control, 17.00?±?1.7, p?=?0.815) and significantly higher than Clearfil? SE Bond (negative control, 11.00?±?1.0, p?=?0.006). The minimum inhibitory/bactericidal concentrations for Clearfil? SE Bond containing 5% QAMP were 20?μL?mL^?1. The release of quaternary ammonium compounds from the experimental adhesive containing QAMP was very low (5.1%) when compared to Clearfil? Protect Bond that released 47.2% of its quaternary ammonium monomer (MDPB) after 30 days. The QAMP can offer enhanced antimicrobial properties for self-etching adhesive systems.     

Nanoleakage within the hybrid layer: a correlative FEISEM/TEM investigation

The aim of this study was to compare the nanoleakage patterns of the resin-dentin interfaces of three dentin bonding systems at both TEM and field emission in lens SEM (FEI-SEM) levels. A standardized smear layer was created with 180-grit silicon carbide paper (SiC) on dentin disks obtained from 18 noncarious human third molars. Specimens were randomly divided into three groups and bonded with a two-step total etching adhesive (Single Bond, SB), a two-step, self-etching adhesive (Clearfil SE BOND, SEB), and a one-step, self-etching adhesive (XENO III, XEIII). Nanoleakage was evaluated by using an ammoniacal silver-nitrate solution. Specimens were processed for TEM and FEI-SEM observation. The TEM of SB revealed silver deposits in adhesive and hybrid layers (HL). High-magnification FEI-SEM micrographs clearly identified these deposits as spherical clusters mainly associated with nonembedded collagen fibrils. TEM and FEI-SEM examination of SEB revealed some clusters of silver deposits within porosities and small channels of the HL. Additional silver deposits were observed between the peritubular dentin walls and the resin tags. XEIII revealed very fine and diffuse silver grains throughout the entire HL. SEM visualization of nanoleakage at a high level of resolution has not been previously described. FEI-SEM technology supported the TEM visualization with three-dimensional morphological data of the relations between the HL constituents and nanoleakage. The results of the present study confirm the hypothesis that both total- and self-etch adhesives are not able to fully infiltrate the dentin substrate.     

Elemental distributions and microtensile bond strength of the adhesive interface to normal and caries-affected dentin

The aim of this study was to evaluate the microtensile bond strength (microTBS) and the elemental contents of the adhesive interface created to normal versus caries-affected dentin. Extracted human molars with coronal carious lesions were used in this study. A self-etching primer/adhesive system (Clearfil Protect Bond) was applied to flat dentin surfaces with normal and caries-affected dentin according to the manufacturer's instructions. After 24 h water storage, the bonded specimens were cross-sectioned and subjected to a microTBS test and electron probe microanalysis for the elemental distributions [calcium (Ca), phosphorus (P), magnesium (Mg), and nitrogen (N)] of the resin-dentin interface after gold sputter-coating. The microTBS to caries-affected dentin was lower than that of normal dentin. The demineralized zone of the caries-affected dentin-resin interface was thicker than that of normal dentin (approximately 3 microm thick in normal dentin; 8 microm thick in caries-affected dentin), and Ca and P in both types of dentin gradually increased from the interface to the underlying dentin. The caries-affected dentin had lost most of its Mg content. The distributions of the minerals, Ca, P, and Mg, at the adhesive interface to caries-affected dentin were different from normal dentin. Moreover, a N peak, which was considered to be the collagen-rich zone resulting from incomplete resin infiltration of exposed collagen, was observed to be thicker within the demineralized zone of caries-affected dentin compared with normal dentin.     

A challenge to the conventional wisdom that simultaneous etching and resin infiltration always occurs in self-etch adhesives

This study provided morphological evidence that discrepancies between the depth of demineralisation and the depth of resin infiltration can occur in some mild self-etch adhesives. Sound dentine specimens derived from extracted human third molars were bonded with 5 one-step and 5 two-step self-etch adhesives. One millimeter thick slabs containing the resin-dentine interfaces were immersed in 50 wt% aqueous ammoniacal silver nitrate and processed for TEM examination. A zone of partially etched but uninfiltrated dentine was identified beneath the hybrid layers in the milder versions of both one-step and two-step self-etch adhesives. This zone was characterised by the occurrence of silver deposits along the interfibrillar spaces of mineralised collagen fibrils. The silver infiltrated interfibrillar spaces were clearly identified from the one-step self-etch adhesives Xeno III, iBond, Brush&Bond and the experimental adhesive, and were thinner and only occasionally observed in the two-step self-etch adhesives Clearfil SE Bond and Clearfil Protect Bond. The more aggressive one-step and two-step adhesives that exhibit more abrupt transitions from completely demineralised to mineralised dentin were devoid of these silver-infiltrated interfibrillar spaces beneath the hybrid layers. Incomplete resin infiltration observed in some self-etch adhesives may be caused by the reduced etching potential of the acidic monomers toward the base of hybrid layers, or the presence of acidic but non-polymerisable hydrolytic adhesive components, creating potential sites for the degradation of the bonded created by these self-etch adhesives.     

Effect of cyclic loading on bonding of fiber posts to root canal dentin

This study evaluated the effect of mechanical loading on microtensile bond strength (MTBS) when luting fiber posts to root canal dentin. Forty maxillary premolars were endodontically treated, and the roots were prepared for post cementation using the FRC Postec system. A light-cured composite (Clearfil Photo Core, Kuraray) was used in combination with four adhesive systems: Single Bond (3M ESPE), Multilink Primer (Vivadent), Clearfil Photo Bond (Kuraray), and Clearfil New Bond (Kuraray). A composite build-up was performed around the root to provide adequate gripping during testing. For each experimental group, half of the specimens were load cycled under 90 N (5000 cycles, 3 cycles/s). Specimens were cut to obtain beams with the post in the center and with the radicular dentin overlaid by the composite build-up on each side. Microtensile testing was performed with a universal testing machine at a cross-head speed of 0.5 mm/min. The failure mode was classified under a stereomicroscope. ANOVA and Student-Newman-Keuls multiple comparison tests were performed. After 24 h, all adhesives performed similarly. When specimens were subjected to mechanical loading, decreases in MTBS were observed for Clearfil New Bond and Multilink Primer.     

Nanoleakage and microshear bond strength in deproteinized human dentin

This study evaluated the influence of dentin deproteinization with NaOCl on the microshear bond strength (microSBS) and the nanoleakage patterns of three dentin bonding systems (DBS). Occlusal dentin surfaces, obtained from extracted noncarious human molars, were divided into two experimental groups, according to dentin surface treatment: Group I-37% H(3)PO(4)/15s and Group II-37% H(3)PO(4)/15s + 10% NaOCl/1 min. The dentin surfaces were bonded with one of the following DBS: Scotchbond Multipurpose-SBMP, Prime & Bond NT-PB and Clearfil SE Bond-SE. After 1 week storage in water at 37 degrees C, the specimens were subjected to the microSBS test. The data were analyzed by two-way ANOVA and Student-Newman-Keuls' test (p = 0.05). The nanoleakage was evaluated using scanning electron microscopy (SEM) in backscattered electron imaging regime. No significant difference in microSBS between dentin treatments was found for SBMP. For PB, microSBS increased after NaOCl dentin treatment. SE showed a reduction in microSBS in deproteinized specimens. SEM analysis showed different nanoleakage patterns for each DBS. Irrespective of dentin treatments, all SBMP specimens showed nanoleakage. SE did not show nanoleakage with the two dentin treatments. PB showed nanoleakage within the hybrid layer only in acid-etched specimens. The influence of dentin deproteinization was dependent on the dentin bonding system formulation.     

Micro-tensile bond strength of sound and caries-affected primary tooth dentin measured with original designed jig

To measure the micro-tensile bond strength (MTBS) on sound and caries-affected primary tooth dentin using an original designed jig that was developed for making symmetric and uniformly-sized specimens for the micro-tensile strength testing. The MTBS of dumbbell-shaped specimens and matchstick-shaped specimens were measured. Dumbbell-shaped specimens: The occlusal surfaces of 15 sound primary molars were ground with a water-cooled air turbine using a diamond bur. The adhesive systems and resin-based composites were Clearfil SE Bond and Clearfil AP-X (SE group) and Single Bond and Z250 (SB group). Matchstick-shaped specimens: Sixteen primary molars (5 sound and 11 carious) were used. The occlusal surfaces of sound teeth were ground with a water-cooled air turbine using a diamond bur. Infected dentin was determined by a caries detecting dye solution and removed with a round-shaped steel bur under water-cooling and with a hand instrument. SE was applied. Data was statistically analyzed using ANOVA and Fisher's PLSD at p < 0.05. The MTBSs (MPa) for the dumbbell-shaped specimens were 8.9 +/- 7.0 in the SE group and 10.3 +/- 5.8 in the SB group and that for the matchstick-shaped specimens were 9.0 +/- 6.3 in the sound-SE group and 9.2 +/- 5.8 in the carious-SE group. No significant difference was observed among them.     

In vitro evaluation of caries inhibition promoted by self-etching adhesive systems containing antibacterial agents

This study evaluated the cariostatic effect of antibacterial self-etching adhesive systems, by means of an in vitro bacterial caries model. Seventy-five prepared bovine slabs were randomly divided into groups (n=15): (1) unbonded composite, no carious challenge (UNB-NC); (2) unbonded composite, carious challenge (UNB-C); (3) Clearfil SE Bond, no antibacterial agent (CSE); (4) Protect Bond, containing MDPB and fluoride (PB); and (5) Reactmer Bond, fluoride-releasing (RB). All preparations were restored with Filtek Z-250. Groups (2)-(5) were submitted to a medium containing Streptococcus mutans (ATCC-- 25175) for 5 days, and Group (1) was kept in a noninoculated medium. Insoluble polysaccharides present in tooth biofilms were quantified, Knoop hardness (KHN) was measured on the enamel adjacent to restorations, and standard 35-mm polarized light photomicrographs were taken as illustrations. Polysaccharide and Knoop hardness results were analyzed with the use of ANOVA, with a split-split-plot statistical design for KHN. Except for Group (1), all groups showed similar caries formation. Biofilm over PB restorations showed the smallest amounts of polysaccharides (14.37 microg/mg), and CSE showed the highest amounts (20.87 microg/mg). All self-etching systems tested were unable to inhibit secondary caries in a bacterial model simulating a high caries challenge, even though there was reduced glucan synthesis provided by the adhesive system containing MDPB and fluoride.     

Initial adhesion of glass-fiber-reinforced composite to the surface of porcine calvarial bone

The aim of this preliminary study was to compare the initial bond strength of the glass-fiber-reinforced composite veil to the surface of the porcine calvarial compact bone using different adhesives. Fiber-reinforced composite (FRC) made of E-glass fiber veil with the BisGMA-PMMA resin system was used in the study. For the shear bond strength test, porcine calvarial bone cubes were mounted into resin matrix. FRC-veil discs were bonded to compact bone with different types of adhesives: (A) BisGMA-HEMA based (3M-ESPE Scotchbond Multi-Purpose Adhesive), (B) 4-META/UDMA/BisGMA based (Unifil Bond Bonding Agent) and MDP based (Clearfil Se Bond adhesive), (C) UDMA/BisGMA/PMMA-based experimental adhesive, and (D) silane-based (APS, ICS, MPS) experimental adhesives. The surface of the bone was mechanically roughened and was either used as such, treated with dental primers (Unifil Bond Self-etching Primer, Clearfil Se Bond Primer), or treated with an experimental silane mixture (APS, ICS, MPS), or with a mixture of the experimental silane liquid and Clearfil Se Bond Primer. The 3M-ESPE Scotchbond Multi-Purpose Adhesive and UDMA/BisGMA/PMMA experimental adhesive gave poor results in the shear bond test (0.58 and 0.40 MPa, respectively). Unifil Bond Bonding Agent and Clearfil Se Bond adhesive with respective primers markedly improved the shear bond strength; with Unifil the result was 3.40 MPa, and with Clearfil it was 6.19 MPa. When the bone surface was primed with a mixture of Clearfil Se Bond Primer and Clearfil Porcelain Bond Activator, the Clearfil Se Bond adhesive-impregnated FRC veil gave the best adhesion to the bone surface in this test: 9.50 MPa. The addition of bioactive glass granules between the veil and the bone lowered the shear bond strength in the test system described above to 6.72 MPa. The test systems with the silane mixture were also promising. In the SEM study, it was found that the mechanical treatment reveals the pores of the bone surface. Chemical treatments of the bone surface improved the adhesion of the FRC veil to the bone. The results showed that the adhesion of the FRC to the surface of the bone can be significantly improved with mechanical roughening and with special chemical treatments of the bone surface.