牙科树脂材料抗菌性能的研究进展

牙科树脂材料广泛应用于牙体缺损治疗,但树脂材料的聚合收缩易造成微渗漏,并积聚细菌菌斑,导致牙体组织出现继发龋.赋予牙科树脂材料抗菌性能是解决这一问题的重要途径之一,在牙科树脂材料中添加抗菌剂是赋予其抗菌性能的主要方法.抗菌剂主要分为释放型、非释放型及混合型三大类.抗菌效果方面,抗菌剂的选择及添加量会影响牙科树脂材料的抗...     

树脂基托抗菌性的研究进展

牙列缺损（失）是口腔的常见病和多发病,可摘局部义齿及全口义齿是其修复的常用方法。但义齿使用后,基托表面常有细菌粘附,菌斑沉积,造成基牙龋病和牙周病,甚至产生义齿性口炎。聚甲基丙烯酸甲酯（polymethylmethyacrylate, PMMA）作为义齿基托的主要材料,无法满足口腔复杂的环境要求,因此,提高义齿基托的抗菌性一直是各国学者关注的焦点。本文对近年来义齿基托抗菌性能方面的研究现状做一综述。     

锶强化生物活性玻璃牙釉质粘合树脂的抗菌性能与机械性能测试

目的通过向正畸牙釉质粘合树脂中添加锶强化生物活性玻璃,并对其抗菌性能及机械性能进行测试,寻求合适的添加比例,为正畸临床应用提供理论依据。方法分别将质量分数为1%、2%、3%、4%、5%的锶强化生物活性玻璃掺入到牙釉质粘合树脂中作为实验组,分别为1、2、3、4及5组,未掺入锶强化生物活性玻璃的牙釉质粘合树脂作为对照组,即0组。采用抑菌环法和贴膜法对以上各组进行抑菌活性测试;应用万能试验机对以上各组的剪切强度进行测试,观察并记录托槽脱落后牙面牙釉质粘合树脂残留指数(adhesive resin residual,ARI)。结果各实验组及对照组均未出现抑菌环,实验组4和5组的抗菌率达到99.9%,具有强抗细菌作用。实验各组的剪切强度与对照组相比,均有显著性差异(P<0.05)。实验各组之间比较,随掺入比例增加,剪切强度呈现降低趋势,但无统计学差异(P>0.05)。实验各组剪切强度均在临床可接受的剪切强度范围内,能够满足正畸临床要求。实验各组及对照组牙面均有牙釉质粘合树脂残留,ARI计分均在2~4分之间,各组间ARI计分比较无统计学差异(P>0.05)。结论掺入4%质量分数的锶强化生物活性玻璃的正畸牙釉质粘合树脂既表现出强抗菌作用,剪切强度又能够达到正畸临床需要,并对釉质表面粘合树脂的残留量无影响。     

牙科树脂中添加无机抗菌剂的研究进展

牙科树脂材料,包括义齿基托树脂和复合树脂等,广泛地应用于口腔修复科和口腔内科治疗。由于口腔是个有菌环境,树脂上容易黏附和聚集细菌,形成菌斑,导致黏膜炎或龋病等疾病。添加无机抗菌剂赋予树脂抗菌性能,可以减少细菌在其上的黏附、聚集和繁殖。本文就研究较多的纳米载银、纳米二氧化钛、氧化锌这三类无机抗菌剂在牙科树脂中的进展作一综述。     

纳米载体在抗菌牙科树脂中的应用进展

抗菌牙科树脂因具有良好的抗菌防龋性能而得到广泛应用，但随着研究的深入，一些不足仍需改进。纳米载体因其纳米尺寸、高比表面积等优势，一直是药物载体的研究热点。纳米载体负载抗菌剂共同构成抗菌纳米载药体系，将其加入到树脂基质中，可以合成抗菌牙科树脂，实现抗菌药物的缓释，提高抗龋效果，呈现出了巨大的发展前景。文章对应用于抗菌牙科树脂中的纳米载体进行综述，总结了纳米载体对抗菌牙科树脂的改进作用，希望为抗菌牙科树脂的进一步优化研发提供借鉴。     

生物活性玻璃的抗菌机制及其影响因素

生物活性玻璃(bioactive glasses, BGs)是一种以SiO₂-Na₂O-CaO-P₂O₅氧化物体系为基础的生物活性材料,具有良好的成骨活性、抗菌性和生物相容性。BGs对临床上常见的多种口腔细菌都具有显著的抗菌作用,且不会产生耐药性,有作为口腔抑菌剂的潜在应用前景。然而对于它的抑菌机制尚未见总结性研究,该文回顾了BGs对口腔常见致病菌的抗菌作用及机制,并对其影响因素进行总结。     

促牙本质再矿化的生物活性树脂研究进展

诱导混合层裸露胶原再矿化是提高树脂牙本质粘接耐久性的重要方法.然而粘接界面有限的矿化离子源限制了牙本质再矿化的临床应用.采用无机材料对粘接树脂改性,可制备出具有生物活性的树脂修复材料,这些树脂在溶液中可缓慢释放矿化离子(如Ca2+、pO43-、OH-等),具有促进脱矿牙体组织再矿化的潜能.用于树脂改性的无机材料包括硅酸盐、磷酸钙盐、生物活性玻璃等.研究证实生物活性树脂修复材料具有促进脱矿牙本质再矿化、抑制胶原纤维降解的能力,但在树脂中添加无机材料会影响树脂的力学性能,制备具有良好力学性能的生物活性树脂是研究的重点和难点.本文将分类阐述不同生物活性树脂修复材料在牙本质再矿化中的作用.     

树脂基窝沟封闭剂材料的研究进展

龋病是一种在儿童和青少年中普遍存在的口腔疾病。窝沟封闭剂广泛用于预防龋齿，其中树脂基封闭剂因其操作方便和高保留率而备受欢迎，但仍存在微渗漏、生物安全性等问题。本文对树脂基窝沟封闭剂材料的组成成分与分类、生物安全性、抗菌性能和再矿化技术等方面的研究现状，存在的问题和未来发展方向进行综述。     

牙科复合树脂基质的研究新进展

复合树脂在口腔临床的应用越来越广泛,树脂基质作为复合树脂的主体成分,对树脂性能影响很大.目前,一些新型的树脂基质相继开发出来.本文对近年来在这方面的研究作一综述.     

复合树脂纳米抗菌成分的研究进展

复合树脂被应用广泛于牙体的充填修复治疗,继发龋和充填修复体折裂仍然是复合树脂充填修复失败的主要原因。近年来,加入纳米抗菌成分的复合树脂具有了一定的抗菌性和良好的机械性,正逐渐成为研究的热点,本文就复合树脂中的纳米抗菌成分的研究进展作一综述。     

Surface antibacterial properties of resin and resin-modified dental cements.

OBJECTIVE: Cements possessing antibacterial properties may reduce bacteria-induced fixed partial denture complications. The purpose of this study was to evaluate the antibacterial properties of 4 dental cements using the direct contact test (DCT) and the agar diffusion test (ADT). METHOD AND MATERIALS: The ADT was performed using mitis salivarius agar plates. Each plate was evenly inoculated with freshly grown mutans streptococci. Two samples of each test material-RelyX ARC, Variolink II, GC FujiCEM, and Principle-were placed, and the inhibition halo obtained was measured after 48 hours. For the DCT, 8 samples were placed on the sidewalls of wells in a 96-well microtiter plate. After polymerization, freshly grown Streptococcus mutans cells (1 X 10(6)) were placed on the surface of each sample for 1 hour at 37 degrees C. Fresh medium was then added to each well, and bacterial growth was followed for 16 hours in a temperature-controlled spectrophotometer. Similarly prepared samples were aged in phosphate-buffered saline for 1 or 7 days and the DCT was repeated. Analysis of variance (ANOVA) and Tukey multiple comparisons were applied to the data. RESULTS: In the ADT, GC FujiCEM showed an inhibition zone of 2.0 +/- 0.3 mm, and Principle showed an inhibition zone of 1.2 +/- 0.2 mm. In the DCT, freshly polymerized samples of GC FujiCEM and Principle exhibited potent antibacterial properties, while samples of Variolink II and RelyX ARC showed moderate antibacterial properties. Principle showed some antibacterial properties even after 1 day (P < .001). CONCLUSION: None of the tested cements in this study possesses long-term antibacterial properties.     

口腔种植体体内生物学评价方法的研究进展

口腔种植体的体内生物学评价主要是通过动物实验获得种植体的生物安全性、骨结合效能及稳定性等相关生物学指标,为种植体表面处理改进、结构设计优化、缩短负重时机等提供科学依据。目前,鲜有报道,本文对有关口腔种植体的体内生物学评价方法进行综述。     

纳米载银无机抗菌剂在树脂基托中应用的研究进展

近年来,载银纳米无机抗菌剂在医学生物领域得到了广泛应用,本文介绍载银纳米无机抗菌剂在树脂基托中应用的研究进展,分析其在树脂基托中的抗菌作用、生物安全性及对基托性能、颜色的影响。     

Fracture toughness of modified dental resin systems

This study compared the relative fracture toughness of a Bis-GMA//TEGDMA (50:50 wt%)-based resin system modified by 5, 10, and 15 wt% of a methacrylate-terminated poly(butadiene-acrylonitrile-acrylic acid) terpolymer toughening agent. After storage in distilled water at 37 +/- 2 degrees C for 7 days, plane strain fracture toughness (KIC) was determined on an Instron testing machine at a 0.5-mm min-1 displacement rate. The glass transition temperature (Tg) in degrees C was determined after 7 days (dry and wet) storage by thermomechanical analysis. The results of this study showed significantly improved fracture toughness and lowered water sorption with the modified resin systems which was indicated by higher wet glass transition temperatures.     

牙科抗菌磷酸锌黏固剂的制备及其抗菌性能的检测

目的 探讨抗菌磷酸锌黏固剂的加工工艺及其抗菌性能.方法 采用研磨法将载银无机抗菌剂添加在磷酸锌黏固剂粉体中合成载银抗菌磷酸锌黏固剂.以普通磷酸锌黏固剂作为对照,进行大体观察和扫描电镜观察.然后通过细菌(变异链球菌、白假丝酵母菌、牙龈卟啉单胞菌)接种于抗菌磷酸锌黏固剂上,计算出样品的抗细菌率.结果 大体观察显示,抗菌磷酸锌黏固剂与普通磷酸锌黏固剂无明显差异.扫描电镜观察显示,抗菌磷酸锌黏固剂表面均匀散布Conval PAg-40颗粒.抗菌磷酸锌黏固剂对变异链球菌、白假丝酵母菌、牙龈卟啉单胞菌均有抗菌效果,且抗菌能力区别明显.结论 添加载银抗菌剂对磷酸锌黏固剂的表面结构无明显影响且具有一定的抗菌性.     

水中浸泡对自修复抗菌复合树脂性能影响的实验研究

目的 合成新型牙科自修复抗菌复合树脂,并探讨水中浸泡对其相关性能的影响。方法 在前期研究的基础上,制备含牙科自修复单体三乙二醇二甲基丙烯酸酯的微胶囊,以7.5%的质量百分比添加到含长链烷基季铵盐修饰的纳米抗菌二氧化硅填料的复合树脂中,生成自修复抗菌复合树脂,并以商品化的Tetric N-Ceram纳米瓷化复合树脂作为对照。复合树脂试件在37 ℃蒸馏水中浸泡处理不同时间,用三点弯曲试验来检测其力学性能;用单刃V形切口梁法来测试其断裂韧性及自修复效率;建立人牙菌斑生物膜体外模型,通过菌落计数、乳酸代谢分析等手段来评价其抗菌性能。结果 浸泡30 d后,对照组和实验组所有复合树脂力学性能及断裂韧性下降明显（P<0.05）,而后随着浸泡时间的延长,下降不明显（P>0.05）;水浸泡处理对自修复效率没有明显影响（P>0.05）,浸泡270 d后仍然可以获得64%的自修复效率;随着浸泡时间的延长,与对照组相比,实验组复合树脂对人牙菌斑生物膜的代谢仍然可以产生明显的抑制作用（P<0.05）,而实验组各时间段之间菌落计数及乳酸产生量则没有明显差异（P>0.05）,显示出良好的抗菌性能。结论 水中浸泡可以明显影响自修复抗菌复合树脂的力学性能,而自修复特性及抗菌性能则没有明显的变化。