羟基磷灰石/磷酸三钙作为细胞载体的体外实验

目的：探讨羟基磷灰石/磷酸三钙（HA/TCP）复合材料作为组织工程载体的可能;为基质材料表面改性提供实验基础。方法：应用人骨髓基质细胞（hBMSCs）和脐静脉内皮细胞(UVECs)和HA/TCP进行混合培养,应用光学显微镜、荧光显微镜及扫描电子显微镜对其进行观察。结果：人骨髓基质细胞和脐静脉内皮细胞在HA/TCP表面均生长良好,并可观察到细胞长入基质材料微孔内的改变。结论：羟基磷灰石/磷酸三钙（HA/TCP）复合材料可作为细胞移植的载体。     

纳米羟基磷灰石与聚己内酯复合电纺纤维膜

用水热法合成的棒状纳米羟基磷灰石（nHA）,引发ε-己内酯（ε-CL）开环聚合得到nHAPCL复合材料。用静电纺丝法分别制备了聚己内酯（PCL）、nHA/PCL共混材料和nHAPCL复合材料的3种电纺纤维膜。通过FT-IR、DSC、SEM、TGA和拉伸试验机表征了样品的结构、热性能和力学性能。结果表明：nHA-PCL电纺膜的结晶性能优于nHA/PCL材料,且热稳定性和力学性能都优于其他两种膜,nHA-PCL电纺膜的完全分解温度为420 °C,拉伸强度和断裂伸长率分别达到28.2 MPa和55.6%。3种膜的纤维直径均小于500 nm,nHA-PCL电纺膜的纤维表面比较粗糙。在人体仿生液中诱导矿化4 d后,nHAPCL电纺膜纤维表面出现磷灰石沉积,而纯PCL和共混nHA/PCL电纺膜的纤维表面沉积的磷灰石很少,nHA-PCL复合电纺膜具有较好的诱导成骨性能。     

羟基磷灰石/丝蛋白复合骨材料的生物相容性

以共沉淀法制备了羟基磷灰石/丝蛋白(HA/SF)复合骨修复材料,并对材料进行了XRD、TEM、SEM、孔径分布和孔隙率等相关的测试和表征。结果表明:该复合材料的无机组分为20~30 nm长、5 nm宽的棒状羟基磷灰石(HA)结晶,这些晶粒沿c轴自组装团聚成簇分散在丝蛋白基质中形成三维多孔结构,其孔径分布在0.3~115μm之间,开口孔隙率达66%。该材料植入动物体内,未出现明显的排异反应,在植入部位有连续的骨性连接和新生骨形成,说明HA/SF复合材料具有良好的生物相容性和骨诱导活性。     

天然型复合网孔状羟基磷灰石修复牙周骨缺损

目的评价天然型复合网孔状羟基磷灰石(IHA/BMP)修复牙槽骨缺损的临床效果。方法随机抽取52名牙周病患者的60颗患牙,随机分3组:天然型复合网孔状羟基磷灰石(IHA/BMP)组、天然型网孔状羟基磷灰石(IHA)、羟基磷灰石(HA)(对照组)。患者经牙周基础治疗后,分别植入IHA/BMP、IHA、HA 3种生物活性材料。于术前、术后3、6、12个月,分别对患牙牙周附着丧失水平(CAL)和牙齿松动度两个临床指标进行分析。结果 IHA/BMP组疗效优于IHA组和HA组。IHA/BMP组牙周附着丧失水平(CAL)及牙齿松动度术后3、6、12个月逐渐减小。IHA组、HA组牙周附着丧失水平(CAL)及牙齿松动度术后6～12个月无明显减少。结论 IHA/BMP可以促进牙周病患牙牙槽骨修复,有可能成为临床治疗骨缺损的一种理性修复材料。     

PHBV/HA骨修复材料的研究

利用硝酸钙与磷酸钠的水溶液制备羟基磷灰石(HA)，同时在HA生成过程中与聚羟基丁酸一戊酸酯(PHBV)复合，探索了HA增强PHBV使之适于作为骨修复材料的一种新途径。结果表明，HA的均匀分散增进了复合材料中两相问的相互结合，能明显地提高复合材料的力学性能。     

聚乳酸/羟基磷灰石复合材料的机械性能及其细胞毒性

目的：制备不同质量配比聚乳酸/羟基磷灰石(PLLA/HA)复合材料,对其机械性能和细胞毒性进行研究,得出两者的最佳质量配比,并探讨其作为乳前牙根管桩材料的可行性。方法：以NH4H2PO4、Ca(CH3COO)2?H2O　和CH3COONH4为原料制备微球型HA。采用溶液共混法和热压成型法制备PLLA/HA复合材料,按复合材料中HA质量分数不同分为PLLA、PLLA-3%HA、PLLA-5%HA、PLLA-7%HA和PLLA-9%HA组。采用扫描电子显微镜(SEM)观察HA形貌和尺寸;X射线晶体衍射(XRD)法进行物相分析;傅立叶变换红外光谱(FT-IR)法分析产物成分;万能材料试验机测试复合材料的弯曲强度和弹性模量;MTT法检测PLLA/HA复合物对L929细胞相对增殖率(RGR)的影响。结果：扫描电镜,所制备的HA为片层状晶体所构成的微球形,直径约1 μm,大小均匀,形态一致。XRD图谱,观测到HA的特征峰,无明显杂峰。FT-IR谱图中可见PO43－基团在565、606和1 042 cm－1处的强吸收峰。与PLLA组比较,含有HA的各组PLLA-HA复合材料的弯曲强度和弹性模量明显增高（P<0.01）,PLLA-5%HA组材料的弯曲强度和弹性模量最大（138 MPa、4.6 GPa）。MTT法,PLLA、PLLA-3%HA、PLLA-5%HA、PLLA-7%HA和PLLA-9%HA各组复合材料RGR均在93%以上,细胞毒性级别均为0～1级。结论：PLLA/HA复合材料具有一定的力学性能,无细胞毒性,有望成为理想的乳前牙根管桩材料。     

羟基磷灰石膜复合材料与人血管内皮细胞的相容性

目的利用脉冲激光沉积方法在人工心脏机械瓣膜上沉积纳米相羟基磷灰石(HA)薄膜,探讨其组织相容性。方法将人血管内皮细胞与纳米相HA薄膜复合材料体外复合培养,进行形态学和功能测定,同时分别测定在HA材料组和空白对照组中血管内皮细胞分泌一氧化氮(NO)、前列环素(PGI2)水平。结果人血管内皮细胞能在纳米相HA薄膜复合材料上良好地黏附、增殖、生长。人脐静脉血管内皮细胞分泌NO和PGI2在HA材料和空白对照组差异无显著性(P>0.05)。结论纳米相HA薄膜复合材料具有良好的细胞相容性,可作为组织工程化机械瓣膜材料。     

C/C-HA涂层复合材料体内体外骨组织响应行为

采用声电沉积法,在CVIC/C表面制备了羟基磷灰石涂层。通过成骨细胞培养以及犬股骨植入实验,借助SEM,酶联免疫检测仪,荧光学显微镜等测试手段,考察了CVI碳/碳复合材料及声电沉积在其表面的HA涂层的体内体外骨组织响应行为。结果表明,在体外HA涂层有利于成骨细胞粘附、增殖、分化;在体内,种植初期,HA涂层有利于缓解碳/碳复合材料表面碳颗粒释放,促进碳/碳羟基磷灰石涂层复合植入体与骨形成骨性结合。     

牙源性多孔双相生物陶瓷的制备和性能研究

收集临床上离体牙,经高温煅烧去除有机成分,将其与( NH4)2 HPO4溶液混合后再次煅烧,制得以羟基磷灰石( HA)和β-磷酸三钙(β-TCP)为主要成分的双相陶瓷,磨碎过200目筛,用有机泡沫浸渍法制备多孔生物陶瓷,对材料进行物相分析、扫描电镜、孔隙率、元素分析和抗压强度检测。牙源性多孔陶瓷材料呈白色,主要物相为 HA 和β-TCP,为大孔/微孔多孔网状结构,孔隙率为74.85%,Ca/P为1.62,抗压强度应为(3.483±0.321)MPa。     

羟基磷灰石在牙种植外科植骨中的应用

羟基磷灰石(HA)由于具有良好的生物相容性和骨传导作用,目前被广泛应用于骨缺损的植骨。本文综合了近些年来国内外相关文献,就羟基磷灰石的性能特点及其新兴复合材料的研制和在牙种植外科植骨中的应用作一综述。     

BIOACTIVITY OF BIORESORBABLE OSTEOSYNTHETICDEVICES MADE OF HYDROXYAPATITE／ POLY-DL- LAC- TIDE COMPOSITES： AN EXPERIMENTAL STUDY

Aim. To investigate the bioactivity of the serf-designed biodegradable osteosynthetic devices made of resorbable hydroxyapatite microparticles/ poly-DL-lactide (HA/PDLLA) composites. Method. Forty-three rabbits with a transverse transcondylar osteotomy of the distal femur were fLxed intramedullary by a HA/PDLLA rod, the duration of follow-up were 3,6,12, 24 and 36 weeks. Histological, scanning electron microscopic (SEM), energy dispersive X-ray (EDX) and biomechanical analyses were done. Resudts. Active new bone formation and direct bone-bonding were seen at the bone-implant interface. Generous apatite crystals deposited and grew on the surface of the composites at 3 - 6 weeks postoperation. The interracial shear strength increased significantly. Conclusion. Through the incorporating of resorbable HA microparticles, specific bone-bonding and active osteogenic capacity is introduced. This kind of bioactivity, together with other properties such as sufficient mechanical strength, enhanced biocompatibi]ity and mdiopacity, which are intrinsically unobtainable in totally resorbable polymer/polymer systems, make the HA/PDLLA composites become a desirable material for the internal fixation of cancellous bone.     

羟基磷灰石涂层加速种植体－骨界面骨融合的形成

以成年杂种犬为实验对象，以未涂层纯钛种植体为对照，用定量组织学方法研究两种羟基磷灰石（ＨＡ１和ＨＡ２）涂层种植体穿骨皮质种植１、３、６个月后，种植体－骨组织界面骨融合形成的情况。结果表明：两种羟基磷灰石涂层种植体均能在种植早期加速界面骨融合的形成，其中ＨＡ２涂层种植体的骨融合指数在各种植程期均高于ＨＡ１涂层和未涂层纯钛种植体，显示出良好的生物活性。     

4种生物材料大鼠体内生物相容性的对比实验研究

目的：探讨羟基磷灰石（HA）、高密度多孔聚乙烯（Medpor）、聚己内酯（PLA）、硅橡胶在大鼠体内的生物相容性,为骨组织修复材料的选择和临床修复骨缺损提供参考依据.方法：Wistar大鼠28只随机分为对照组、实验1组和实验2组,实验1组分别将HA、Medpor植入大鼠背部左、右侧肌肉内,实验2组分别将PLA、硅橡胶植入大鼠背部左、右侧肌肉内,对照组不植入任何材料.分别于术后2、4、8、12周处死大鼠,进行大体标本、光镜和电镜下观察.结果：所有动物没有出现感染死亡.实验1组HA界面的炎性反应较重,Medpor界面无明显炎性反应,Medpor与周围组织紧密结合,组织可长入材料的微孔内.实验2组PLA界面无明显炎性反应,并可在体内缓慢降解,硅橡胶界面的炎性反应较重.结论：Medpor和PLA具有良好的生物相容性,无毒性及免疫原性,是较好的生物材料.     

钛表面羟基磷灰石涂层含镧量对附着细胞生物学性能的影响

目的 研究钛表面羟基磷灰石涂层含镧量对附着细胞生物学性能的影响.方法 接种牛血清白蛋白于含不同浓度镧(0、0.3、0.8 g/L)电解液微弧氧化法HA涂层的纯钛试件表面,比较蛋白在各组试件表面初期黏附情况;培养成骨细胞,接种于上述试件表面,在不同时点进行MTT、碱性磷酸酶活性定量测定和扫描电镜观察.结果 蛋白表面初期黏...     

羟基磷灰石义眼台植入术20例临床分析

目的：探讨羟基磷灰石义眼台植入术的临床应用及其疗效。方法：观察20例20眼巩膜壳后肌锥间隙内羟基磷灰石义眼台植入术患者,Ⅰ期植入者9例,Ⅱ期植入者11例。结果：随访时间2～37个月,平均17个月,均获得较满意的效果。结论：巩膜壳后羟基磷灰石义眼台植入术,义眼台固定于肌锥间隙内,并保留了眼外肌与巩膜原有的解剖关系,损伤小,术后反应轻,并发症少。     

羟基磷灰石义眼座Ⅰ期植入改良术

目的介绍一种羟基磷灰石义眼座Ⅰ期植入方法，减少术后结膜裂开、义眼座暴露等并发症。方法对13例（13眼）患者采用羟基磷灰石义眼座Ⅰ期植入改良术——自体后部巩膜移植术法：眼球内容剜后，剪取后部巩膜瓣，植入义眼座，将自体后巩膜移植至眼球前部修补缺损的角膜区。结果13例病人，除2例发生球结膜小范围轻微裂开、1例义眼座表面不规整致使眼片安装不稳定外，所有病人无义眼座暴露、义眼外突或下陷、上睑退缩等并发症。结论羟基磷灰石义眼座Ⅰ期植入时，用自体后巩膜移植遮盖义眼座,可以有效地减少术后结膜裂开、义眼座暴露等并发症，是临床医生值得选择的手术方法之一。     

医用羟基磷灰石纳米粒的制备和特性:电子显微镜、傅里叶变换红外光谱、核磁共振、X射线对羟基磷灰石纳米粒的观测

目的制备医用羟基磷灰石（HA）纳米粒并观测其特性；方法采用常态表面活性剂（水包油）制备HA纳米粒，用电子显微镜、傅里叶变换红外光谱、核磁共振、X射线等对HA纳米粒进行观测。结果HA纳米粒的平均尺寸为：长10-30nm，宽5-10nm；电子衍射图像显示纳米粒为多晶质，且存在晶格缺损。结论成功制备了一种适合医用的新型羟基磷灰石纳米粒。     

羟基磷灰石薄膜对人血浆纤维蛋白原的吸附性能

目的：探讨羟基磷灰石(HA)薄膜的制备方法及其对人血浆纤维蛋白原(Fib)的吸附性能。方法：用电子束蒸发和射频磁控溅射两种技术制备了天然HA薄膜。用原子力显微镜(AFM)观察了HA薄膜的表面形貌，并用光反射干涉仪(RIfS)测试和比较了两种不同技术制备的HA薄膜对Fib的吸附性能。结果：用电子束蒸发和射频磁控溅射制备的HA薄膜，对Fib的吸附厚度分别为7．01nm和0．75nm。结论：用电子束蒸发技术制备的HA薄膜对Fib的吸附能力和吸附牢固度均高于采用射频磁控溅射技术制备的HA薄膜。     

纳米羟基磷灰石/胶原骨修复材料

目的：制备纳米相羟基磷灰石／胶原（nano-HAp/Collagen,NHAC)复合材料,并检测骨修复性能。方法：采用仿生方法制备NHAC复合材料。结果：NHAC复合材料成分与微结构具有同天然骨类似的某些特征。复合材料的矿物含量约为50％,矿物相为含有碳酸根的羟基磷灰石,结晶度低,晶粒尺寸为纳米量级,矿物相均匀沉积在I型胶原蛋白基质上,NHAC复合材料的力学性能表现为各向同性,其显微硬度可以达到骨皮质显微硬度的下限,用颗粒型NHAC材料压制成的致密种植体植入骨髓腔后,界面层可发生溶解－再沉积的动态快速更新过程,巨噬细胞可在种植体表面或深入种植体内部通过吞噬和胞外降解方式吸收种植体材料,种植体表面及内部被吸收后,伴随有新骨的沉积,这一现象类似骨组织的重塑过程,可使NHAC种植体整合入活体骨的新陈代谢中并最终为自体现有组织所取代。结论：NHAC是生物活性材料,种植体与最组织可形成界面化学键合。