人工全髋聚乙烯假体磨损及其生物学效应

目的 探讨人工关节聚乙烯磨损与假体松动的关系。方法 采用光镜与电镜对15例人工髋关节翻修病例的聚乙烯假体臼杯内表面及假体周围软组织作形态学观察。进而在动物实验中观察微小聚乙烯磨损颗粒促使骨吸收性细胞因子增加，植入物周围骨溶解以及植入物-骨整合强度下降的生物效应。结果 聚乙烯假体在人工关节松动形成时均明显磨损，聚乙烯磨损颗粒诱发机体单核-巨噬细胞增殖并分泌骨吸收性细胞因子。结论 聚乙烯磨损与假体松动密度相关。其中生物因素是引起假体松动的主要途径。     

H/G非骨水泥人工全髋关节置换术后聚乙烯内杯磨损临床研究

目的 对H/G非骨水泥人工全髋关节置换术后聚乙烯内杯的磨损及髋臼周围骨溶解的情况进行总结.方法 我院1991至1995年共进行58例(65髋)H/G非骨水泥人工全髋关节置换,其中35例(40髋)获得10年以上随访.对这35例(40髋)患者获得随访的病例,采用计算机数字化方法测量髋臼聚乙烯内杯的二维线性磨损.结果 35例40髋均有不同程度的磨损,磨损范围2～8 mm,平均磨损为(0.32±0.31)mm/年.10髋聚乙烯磨损超过6 mm,髋臼假体周围的骨溶解严重,并伴有金属假体的移位,其中5髋聚乙烯内杯完伞磨透,金属股骨头与金属髋臼相接触;5髋聚乙烯内杯磨损严重伴明显骨溶解,内杯松动.2髋聚乙烯内杯脱位.共实施翻修手术12例,包括更换聚乙烯内杯和金属股骨头2例、金属闩杯翻修2例、全髋翻修8例.28髋在髋臼侧发现骨溶解,其中14髋股骨侧亦有骨溶解发生.结论 本组病例所观测到的H/G髋臼聚乙烯内杯的磨损程度超过文献所报道,而且由于磨损产生的大量磨屑,导致假体周围出现明显骨溶解,直接影响到假体的稳定.关节置换术后应定期随访,避免出现严重骨溶解后增加翻修手术的困难.     

全髋置换术中聚乙烯内衬的安装

自1963年Ｃｈａｒｎｌｅｙ首先报道全髋关节置换术治疗类风湿性髋关节炎以来,该手术取得了长足的发展。不仅假体设计、制作工艺不断得到改进,而且手术技术也日臻完善。超高分子量聚乙烯髋臼假体与金属股骨头所组合的人工关节被认为是最佳的优化组合,目前在临床上广泛应用。其中大多数非骨水泥固定的人工髋臼是金属外壳与可拆卸的超高分子量聚乙烯所组成。一般聚乙烯内衬与金属壳非常密贴,镶嵌牢靠,有锁定结构,安装时应该很容易〔1〕。临床上有时遇到内衬安装非常困难的情况,而在国内的工具书和文献上却少有报道。笔者曾经遇到4例,现报道如下…     

松动人工髋关节周围组织中聚乙烯磨损颗粒观察

为探讨聚乙烯磨损及其与人工髋关节松动的关系,作者对６例因人工髋关节臼侧假体松动而行翻修术病例的假体周围软组织、软组织中聚乙烯碎屑及臼杯内表面进行了肉眼、偏光交易及扫描电镜观察,分析了聚乙烯内杯员颗粒的产生机制及其在假体周围纤维膜形成、假体松动发生过程中的意义。研究结果显示,假体松动时,在聚乙烯内杯磨损式中,夹有第三体粒（如骨块、骨水泥或金属碎屑）的二个负重面磨擦（三体磨损）占有主要地位。表现为表面     

全髋置换术后聚乙烯内衬与金属壳分离

近半个世纪以来 ,人工髋关节以其良好的疗效得到了认可 ,然而其带来越来越多的并发症 ,也引起了人们的注意。高分子量聚乙烯髋臼假体与金属股骨头的组合 ,即所谓组合型假体(Ｍｏｄｕｌａｒｐｒｏｓｔｈｅｓｉｓ)目前十分流行 ,其中大多数非骨水泥固定的人工髋臼是由金属外壳和可拆卸的高分子量聚乙烯内衬所组成。由于这类假体的广泛应用 ,聚乙烯内衬与金属壳分离 (Ｄｉｓｓｏ ｃｉａｔｉｏｎｏｆｔｈｅ ｐｏｌｙｅｔｈｙｌｅｎｅｌｉｎｅｒｆｒｏｍｍｅｔａｌｓｈｅｌｌ ,ＤＰＬＭＳ)这一并发症逐渐增多。国外文献已有 10余例报道 ,而国内工…     

全髋关节置换术后股骨偏距减小与聚乙烯内衬磨损的关系

 目的 探讨全髋关节置换术后股骨偏距减小与聚乙烯内衬磨损的关系。方法　选择90例单侧全髋关节置换术后即刻拍摄双髋正位X线片的病例。利用Coreldraw 12.0等比例重建术后即刻双髋正位X线片,依据股骨偏距减小值(F)分为五组：F＜2 mm组、2≤F≤4 mm组、4＜F≤6 mm组、6＜F≤8 mm组、8＜F≤10 mm组,每组18例;等比例重建终末随访(4～7年,平均5.6年)双髋正位X线片,测量聚乙烯内衬线性磨损量、速度和角度。结果　(1)五组聚乙烯内衬线性磨损量分别为(0.72±0.13) mm、(0.78±0.11) mm、(0.87±0.09) mm、(0.99±0.09) mm、(1.17±0.15) mm,除第1组与第2组外其余组间差异有统计学意义。(2)聚乙烯内衬线性磨损速度分别为(0.132±0.025) mm/年、(0.139±0.019) mm/年、(0.159±0.029) mm/年、(0.183±0.032) mm/年、(0.213±0.023) mm/年,除第1组与第2组外其余组间差异有统计学意义。(3)聚乙烯内衬线性磨损角度分别为5.0°±3.5°、3.2°±3.8°、-4.3°±4.9°、-8.7°±4.1°、-13.0°±4.7°,除第1组与第2组外其余组间差异有统计学意义。结论 全髋关节置换术中股骨偏距的重建应尽量达到正常解剖水平,股骨头中心向外上方迁移可能会造成应力分布不均和假体磨损增加。     

金属对聚乙烯假体全髋关节置换术后磨损的中期随访研究

【摘要】〓目的〓对金属-聚乙烯(MOP)全髋关节置换术(THA)后患者的界面磨损进行回顾性研究,探讨不同年龄段患者金属-聚乙烯全髋关节置换术的临床疗效。 方法〓收集2003年5月到2008年11月期间于常熟市第一人民医院行THA患者资料研究,共获得完整病例资料84例(88髋),按年龄及活动量分为两组:年龄<50岁和活动量大病例组(A组)和年龄≥50岁和活动量小病例组(B组)。全髋假体为钻铬钼合金-高分子聚乙烯全髋假体,临床疗效应用Harris评分标准进行临床随访和对比研究,影像学进行内衬磨损率及骨溶解测量分析。 结果〓所有病例均取的至少5年的完整随访资料,其中A组有3例3髋(7.7%)因假体松动而最终行翻修手术,而B组资料中无任何翻修病例。所有病例均未发生骨折、感染、深静脉血栓(DVT)等常见并发症。A组Harris评分由术前34.13±6.28改善至手术后91.35±2.68,B组35.51±5.32改善至90.05±2.47;影像学观察,A组内衬磨损率为每年0.19±0.24 mm,B组为每年0.09±0.13 mm,两组中MOP内衬磨损差异具有统计学意义(P<0.05);A组MOP全部发生不同程度的骨溶解,B组MOP骨溶解的发生率为63.16%,两组比较,P<0.05)。结论〓对于小于50岁和活动量大的患者,MOP假体的内衬磨损、骨溶解及影像学松动率均明显高于年龄≥50岁和活动量小的病例组,因此,对于年轻患者使用MOP假体应慎重,而对于老年病人和低活动需求的病人行THA时中期疗效较好。     

股骨颈骨折人工股骨头置换术后髋臼磨损的测量及其临床意义

目的 以计算机数字化方法测量人工股骨头假体置换术后髋臼的磨损,并探讨磨损程度与临床症状的相关性.方法 对84例人工股骨头置换术后的病例进行随访.利用计算机测量股骨头中心相对于髋臼中心的矢量位移,进行临床检查、磨损计量和放射学检查.结果 本组随访1～6年,平均3.8年.最常见的问题是髋臼臼底机械磨损引起的疼痛.根据Merled'Aubigé评分法,优或良21例,中25例,差58例.平均线性磨损为4.03 mm,磨损率为1.06 mm/年.结论 在进行临床随访、放射学观察的同时,磨损情况也是全面评价人工股骨头置换临床结果的一个重要指标,对股骨颈骨折患者的关节置换以选择全髋关节置换为宜.     

人工髋关节置换术后脱位及内衬分离的原因和防治

目的探讨人工髋关节置换术后脱位及内衬分离的原因和防治。方法行人工全髋关节置换术40例,2例术后发生脱位,1例内衬脱落。对其临床表现、诊断、治疗和结果进行了临床分析。结果2例股骨头脱位手法复位,1例行内衬翻新手术,术后随访Harris评分84.3分。结论术中假体位置不当、髋部软组织松弛为术后脱位及内衬分离的主要原因;另外,手术入路、假体选择、髋臼缘骨赘和骨水泥均可导致术后脱位。术后肌肉和关节囊重新恢复张力之前,使用牵引或外展架是正确选择。反复脱位和内衬分离须翻新手术。     

人工髋关节置换术失败原因分析

目的 对人工髋关节置换术后失败的病例进行分析。总结经验，提高人工髋关节置换术的长期疗效。方法 １９９６年１１月～１９９９年４月共进行人工髋关节翻修手术３５例（３６髋），根据前次手术失败的原因进行分组并分析。结果 根据病例统计，在同一失败病例中，失败的原因往往不止一个，最常见的原因是假体松动、假体周围骨溶解，共２４例次，其次为人工股骨头引起髋臼磨损７例次，假体置入位置不良６例次，人工髋关节脱位３例次，术后感染３例次，假体股骨西柄断裂２例次。结论 人工髋关节置换术作为髋关节重建的一种有效的治疗方法而得到广泛的应用。其长期可靠的疗效与严格掌握手术指征，假体的适当选择和手术中正确操作有关。     

Excessive polyethylene wear and acetabular bone defects from standard use of a hooded acetabular insert in total hip arthroplasty

Purpose

In total hip arthroplasty (THA) the use of a polyethylene (PE) insert with a hooded rim can be considered to reduce dislocation risks. This benefit has to be balanced against the potential introduction of impingement of the femoral component on this rim. We present a case series of early acetabular revisions for excessive PE wear and acetabular bone defects from overuse of such a hooded rim insert.

Material and methods

Twenty-eight patients with 34 consecutive early acetabular revisions were evaluated on failure mechanism. One type of implant was used in all cases. Standard pelvic radiographs and pre-operative CT scans were used to quantify PE wear, implant positioning and acetabular bone defects.

Results

An acetabular revision with impaction grafting was performed in all cases with a mean cup survival of ten years (range 1.3–19.3). No concurrent stem revisions were necessary. Overall implant positioning was adequate with a mean cup inclination of 45° (range 39–57) and anteversion of 25° (range eight to 45). The mean PE wear was 0.24 mm/year (range 0.00–1.17). The mean acetabular bone defect on pelvic CT scans was calculated as 352 mm² (range zero to 1107) and 369 mm² (range zero to 1300) in the coronal and transversal planes, respectively. A hooded acetabular insert was retrieved in all cases and profound PE wear, typically from the posterior hooded rim, was encountered.

Conclusion

The use of hooded acetabular inserts may be considered to improve implant stability intra-operatively. This case series clearly presents that together with these devices, component impingement with concordant complications such as accelerated PE wear may be introduced. Standard use of these stabilizing inserts should thus be avoided.     

从骨溶解的X线特征探讨磨损颗粒与人工髋关节无菌性松动的关系

目的 探讨自人工关节关节面首产生的磨损颗凿的迁移途径及其易素积部位与骨溶解之间的。方法 观察因无菌性松动行翻修术的３９个国产人工髋关节的术前Ｘ线片,按关节类型分组统计假体周围不同区域补性和膨胀发现有溶解的发生经,并测算溶骨带宽度或溶骨面积。结果 髋臼衬性骨溶解的发和率各区差异无显著性意义（Ｐ〉０．０５）,宽度以三区（Ｄｅｌｅｃ分区法）最大（Ｐ〈０．０５）;膨胀发现有溶解在人工股骨头和全髋关节中髋臼     

小切口人工全髋关节置换术

目的 :初步探讨小切口人工全髋关节置换术的优越性。方法 :比较了 9例小切口人工全髋关节置换术与传统人工全髋关节置换术在切口长度、术中出血量、术后引流、手术时间、术后疼痛、住院天数、住院费用、早期活动、并发症、Harri评分方面的不同。结果 :发现在相同条件下 ,小切口手术明显减少了术中出血、术后疼痛、住院天数、住院费用 ,促进了早期活动 ,并且对手术的效果无影响。结论 :小切口在人工全髋关节置换术中是可行的     

人工髋关节翻修术72例探讨

目的探讨人工髋关节置换术后失败的原因,骨缺损的处理、假体的选择及根据,观察翻修的术后疗效。方法2000年1月～2008年6月,本组共对72例患者进行了人工髋关节翻修术。翻修术所置换的假体包括,普通金属杯加内衬45例,大头臼杯15例,Cage加聚乙烯臼杯9例,聚乙烯臼杯3例;普通柄43例(其中12例应用骨水泥固定),加长柄29例(其中5例应用骨水泥固定,7例为组合型柄)。39例假体柄取出容易,20例假体柄取出困难。13例假体臼、17例假体柄使用骨水泥固定,其中10例臼及柄均使用骨水泥固定;55例假体臼、32例假体柄植骨,其中28例假体臼及柄均植骨。结果平均随访31.7个月。Harris评分:术前平均39.4(9～58)分,术后平均92.0(65～99)分。无感染或脱位患者。结论(1)无菌性松动、关节感染和医源性错误是人工髋关节翻修的主要原因;(2)股骨假体柄取出困难和严重骨质缺损是髋关节翻修术中常见的难题;(3)应用松质骨骨块、颗粒骨和骨屑混合打压植骨,尽量多用自体骨填补缺损,而少用异体骨、人工骨或骨水泥;(4)假体的选择主要依据是骨质缺损的程度。     

中青年患者采用陶对陶与金属对聚乙烯全髋置换术的中远期疗效比较研究

目的分析比较陶瓷对陶瓷(CoC)与金属对聚乙烯(MoP)在中青年患者行初次全髋关节置换术(THA)的中远期疗效。方法回顾性分析自2000-03—2009-05采用第3代CoC行THA 68例(CoC组)和采用MoP行THA 43例(MoP组)的临床资料。采用Harris评分及UCLA评分评估患者髋关节功能和活动水平,采用Kaplan-Meier生存分析评估假体生存情况,采用影像学征象评估骨溶解、假体松动等并发症,并记录陶瓷假体碎裂、吱吱音等陶瓷假体特异性并发症。结果CoC组获得平均9.7(5~13)年随访,MoP组获平均10.5(5~15)年随访。MoP组均发生不同程度骨溶解,CoC组未见骨溶解;MoP组11例髋臼侧松动,5例股骨柄假体松动,下沉2 mm,而CoC组未见假体松动;MoP组聚乙烯平均线性磨损是0.25 mm/年,CoC组陶瓷内衬几乎无磨损,无法精准测得。MoP组以翻修手术作为终点的假体5年及10年的生存率分别为95.7%和80.4%,而CoC组为98.6%和97.3%,其中,MoP组的翻修都与假体松动有关,而CoC组是因3例三明治陶瓷内衬碎裂引起。结论第3代CoC与MoP假体比较,更能满足活动量大、使用寿命长的中青年患者行THA的需要,中远期疗效满意。     

Risk factors for heterotopic ossification in total hip arthroplasty

This study prospectively evaluated 928 patients with 1318 primary total hip replacements for heterotopic ossification (HO). The mean clinical and radiological follow-up was 2.5 years (range 1.5–3.6 years). HO was noted in 44.6% of all total hips replaced. It was graded as mild (Brooker 1) in 29.2%, moderate (Brooker 2) in 10.5%, and severe (Brooker 3 and 4) in 4.2%. The following factors showed a significantly increased risk of HO: hypertrophic osteoarthritis, HO after contralateral total hip replacement, trochanteric osteotomy, lateral or anterolateral approach, previous hip surgery, subtrochanteric femoral osteotomy, and male gender (p < 0.05 in chi-square analysis of independence and multivariable analysis). Patients with rheumatoid arthritis showed less HO. A combination of any of these factors resulted in a significant increase in the risk of developing HO. Received: 7 November 2000