载辛伐他汀磷酸钙骨水泥/聚乳酸-聚羟基乙酸新型材料对拔牙创骨改建影响的实验研究

选用50只Wistar雄性大鼠,随机均分为实验组和对照组,拔除右下颌中切牙后,实验组即刻植入载辛伐他汀/CPC/PLGA支架材料,对照组植入CPC/PLGA空白支架材料。术后1、2、4、8、12周分别处死实验组和对照组大鼠各5只,采用大体观察、软X线、组织学等方法定性、定量进行骨改建效果评价。结果:术后2、4、8、12周,剩余牙槽嵴相对长度实验组与对照组相比明显升高,差异有统计学意义(P<0.05)。剩余牙槽嵴相对宽度实验组与对照组相比明显升     

局部注射葛根素对鼠拔牙后剩余牙槽嵴吸收影响的实验研究

目的观察中药葛根素对鼠拔牙后剩余牙槽嵴吸收的影响作用。方法制作大鼠下颌中切牙缺失模型,于剩余牙槽嵴的粘膜下注射葛根素,用X线片测量大鼠相对剩余牙槽嵴高度和骨密度值,HE染色观察不同时期剩余牙槽嵴的组织学形态改变。结果实验组剩余牙槽嵴相对高度均大于对照组（P〈0.05）;除一周组外,其余各实验组剩余牙槽嵴光密度测量值均大于对照组（P〈0.01）;组织学观察可见实验组大鼠剩余牙槽嵴表面的成骨质量较对照组高,骨吸收程度较对照组少。结论将葛根素注射于拔牙窝周围能够抑制剩余牙槽嵴的吸收并保存牙槽嵴的高度。     

载辛伐他汀PLGA/CPC复合材料的制备及表征

目的：制备具有药物缓释功能的聚乳酸聚羟基乙酸/磷酸钙骨水泥（PLGA/CPC）组织工程支架材料,评价其物理性能和药物释放性能。方法：通过调整高分子量、低分子量PLGA以及CPC这3种组分的比例将实验分为3组,采用冷冻干燥溶剂挥发技术合成复合材料,通过扫描电镜观察、模拟体液中pH值变化的结果筛选优化配比方案,最后将辛伐他汀载入制备载药复合支架材料,并用分光光度仪测定药物释放情况。结果：按质量比PLGA/CPC（2∶1）的配比所制备的复合支架材料平均孔径大小约120μm,且各孔之间有微孔相互贯通,8周时的pH值可稳定在6.5左右,同时该载药支架材料的缓释效果明显,体外药物释放达48d以上。结论：本实验所制备的载辛伐他汀PLGA/CPC复合材料,能满足骨组织工程支架材料的要求,可应用于剩余牙槽嵴骨吸收修复的研究。     

复合氰基丙烯酸酯一骨形态发生蛋白生物胶预防大鼠牙槽嵴萎缩的实验研究

目的制备复合氰基丙烯酸酯一骨形态发生蛋白(BMP)生物胶,并植入大鼠拔牙窝观察其预防牙槽嵴萎缩的效果。方法选用Wistar大鼠54只,随机分为3组：实验组(复合氰基丙烯酸酯一BMP生物胶组)、对照组(壳聚糖温敏性胶体组)、空白对照组。拔除大鼠下颌切牙后,实验组和对照组在牙槽窝内即刻植入复合氰基丙烯酸酯一BMP生物胶、单纯壳聚糖温敏性胶体,空白对照组则不植入任何材料。39t动物在植入后3、6、9周处死,分离切取下颌骨,用高频钼靶扫描仪获得图像信息,使用Image-Pro Plus软件处理图像,得到剩余牙槽嵴相对高度和牙槽窝相对光密度,组织学观察牙槽窝内的成骨情况。结果术后3、6、9周,实验组的剩余牙槽嵴相对高度和牙槽窝相对光密度均高于对照组和空白对照组(P<0．05);组织学观察显示实验组牙槽窝成骨多于对照组和空白对照组。结论复合氰基丙烯酸酯一BMP生物胶可以用于预防拔牙术后剩余牙槽嵴萎缩,其临床应用前景广阔。     

聚乳酸-羟基乙酸-辛伐他汀对拔牙术后剩余牙槽嵴吸收影响的实验研究

目的探讨聚乳酸-羟基乙酸(PLGA)复合辛伐他汀对剩余牙槽嵴吸收的预防作用。方法选用60只Wistar雄性大鼠,随机分为实验组和对照组各30只,拔除右下中切牙后,实验组即刻植入PLGA-辛伐他汀支架材料,对照组植入PLGA支架材料。术后7、14、28、56、84d分别处死实验组和对照组大鼠各6只,用软X线、骨密度、测量组织学等方法进行药效评价。结果剩余牙槽嵴相对长度:术后14、28、56、84d对照组比实验组[(0·997±0·007)、(0·965±0·139)、(0·996±0·021)、(0·960±0·026)]明显降低,差异有统计学意义(P<0·05)。牙槽骨骨密度:术后28、56、84d实验组[(7·101±0·025)、(7·178±0·039)、(7·162±0·052)g/cm2]与对照组[(7·074±0·014)、(7·117±0·012)、(7·059±0·037)g/cm2]相比明显升高,差异有统计学意义(P<0·05)。组织学观察显示实验组成骨速度和质量优于对照组。结论以PLGA为载体局部应用辛伐他汀可诱导拔牙窝内骨形成,保存了剩余牙槽嵴的长度和骨量。     

局部应用辛伐他汀对拔牙窝内VEGFmRNA表达的影响及意义

目的：探讨局部应用辛伐他汀促进拔牙术后牙槽骨修复机制。方法：选用健康雄性Wistar大鼠56只,随机分为实验组28只和对照组28只,拔除右下颌中切牙后,实验组即刻植入载辛伐他汀PLGA支架材料,对照组植入单纯PLGA作为对照,于术后5d、1周、2周和4周分别处死大鼠,设计针对VEGFmRNA的寡核苷酸探针,采用原位杂交技术检测拔牙窝VEGFmRNA的表达。结果：术后1周和2周实验组VEGF阳性细胞数和染色强度均高于对照组,且差异有统计学意义,而术后4周,实验组和对照组阳性细胞数无统计学差异,且阳性表达细胞少于术后2周。结论：局部应用辛伐他汀通过增加VEGFmRNA的表达促进拔牙窝骨损伤的愈合。     

拔牙后应用脱细胞真皮基质对保存牙槽嵴的影响

目的：观察脱细胞真皮基质植入拔牙创后牙槽嵴的吸收情况,评价脱细胞真皮基质对于保存牙槽嵴的影响。方法：选用本地产健康成年杂种犬16只,拔除双侧下颌第一前磨牙,左侧拔牙创植入脱细胞真皮基质作为实验组,右侧拔牙创作为空白对照。16只犬随机分为两组,分别于第4、12周处死1组动物。测量第4周、第12周拔牙处的牙槽嵴高度;拔牙创组织制作HE染色切片行组织学观察。结果：第4、12周实验组牙槽嵴高度均明显高于对照组（P〈0.01）;第4周实验组较对照组在组织学上更为成熟。结论：脱细胞真皮基质可以促进拔牙创的早期愈合,保存牙槽嵴高度。     

载辛伐他汀PLGA/CPC支架材料复合BMSCs修复大鼠颅骨缺损的实验研究

目的:探讨载辛伐他汀PLGA/CPC支架材料复合骨髓间充质干细胞(BMSCs)构建组织工程骨,修复大鼠颅骨临界尺寸骨缺损的可行性以及效果。方法:24只雄性大鼠随机均分为3组;在大鼠颅骨人字缝两侧各做一直径5 mm的骨缺损。每组16个骨缺损再随机分为:载辛伐他汀PLGA/CPC/BMSCs(Brdu标记的BMSCs)组(n=4);载辛伐他汀PLGA/CPC组(n=4);单纯PLGA/CPC组(n=4)以及空白对照组(n=4)。术后4、8、12周取标本分别进行大体观察,HE染色及免疫组织化学染色来评价骨再生情况。结果:术后4、8、12周组织学观察表明载辛伐他汀PLGA/CPC/BMSCs组的成骨质量和速度明显优于其他3组,免疫组化结果显示载辛伐他汀PLGA/CPC/BMSCs组骨钙素(OC)阳性表达IOD值明显高于其他3组。结论:载辛伐他汀PLGA/CPC支架材料复合BMSCs可以诱导大鼠颅骨临界尺寸骨缺损内的新骨形成,成骨质量优于其他3组,而且可以明显缩短骨愈合时间。     

牙周膜干细胞用于犬牙槽嵴组织工程化增高的实验研究

目的：探讨牙周膜干细胞复合生物支架材料增高重建牙槽嵴效果,为缺牙后牙槽嵴重度萎缩的种植义齿修复奠定基础.方法：分离培养牙周膜干细胞（PDLSCs）,将其分别与骨组织工程支架材料羟基磷灰石-磷酸三钙（HA/TCP）及附着龈组织工程材料脱细胞真皮基质（ADM）复合诱导后,植入犬双尖牙缺失致牙槽嵴缺损部位,PDLSCs-HA/TCP植入骨缺损区,PDLSCs-ADM植入粘骨膜缺损区.植入32周,大体测量植入前后增高牙槽嵴高度;X-线片显示牙槽嵴高度与密度变化;组织学观察边界区新生牙槽骨结构,未植入做对照.结果：细胞-材料复合体植入后牙槽嵴高度显著增高,由移植前4.15＆#177;0.20,增加到移植后9.30＆#177;0.15（P＜0.05）.X-线显示邻牙标记部位冠方有类骨密度硬组织形成,牙槽嵴明显增高.组织学显示：与对照组比较,细胞材料移植组可见缺损区有新生骨样组织形成,可见骨陷窝和骨细胞样结构.结论：PDLSCs分别与骨及粘骨膜组织工程支架材料HA/TCP、ADM复合后体内移植,可显著增高牙槽嵴高度,是牙槽嵴增高重建、实现无牙合种植修复的有效途径.     

复方骨形成蛋白生物膜植入牙槽窝的实验研究

目的:以骨形成蛋白、固定化凝血酶、头孢哌酮钠为主药,水溶性壳聚糖为主要膜材,制备复方骨形成蛋白牙槽生物黏附膜,植入大鼠牙槽窝观察其对拔牙后牙槽骨的影响。方法:选用大鼠54只,随机分为3组(实验组、单纯壳聚糖组、对照组),在拔除大鼠下颌切牙后牙槽窝内即刻植入复方骨形成蛋白生物膜、单纯壳聚糖及空白对照。3组动物于植入后3、6、9周时处死,切取下颌骨,用软X线机检查剩余牙槽嵴相对剩余高度、双能X线骨密度分析仪测定骨密度值、常规病理切片观察牙槽窝成骨情况。结果:植入后3、6、9周时实验组剩余牙槽嵴相对剩余高度和骨密度值均高于单纯壳聚糖组及对照组,差异有统计学意义(P<0.05);病理切片显示实验组牙槽窝成骨情况优于单纯壳聚糖组及对照组。结论:复方骨形成蛋白生物膜处方组成合理,是预防剩余牙槽骨吸收的有效方法之一,有一定的临床意义。     

Local application of simvastatin to rat incisor sockets augments bone

Decrease of the alveolar ridge after tooth extraction causes difficulties in prosthodontic treatment, especially in implant supported prostheses. Statins, which are inhibitors of cholesterol synthesis and therapeutic drugs for hypercholestemia, stimulate BMP-2 expression in osteoblasts. The purpose of the present study was to examine how local application of simvastatin, one of the statins, to the tooth socket after tooth extraction affects alveolar bone. A mixture of lactic acid/glycolic acid copolymer (PLGA), alpha-tricalcium phosphate (alpha-TCP), calcium carbonate was prepared as a carrier for simvastatin. Ninety-six male Wistar rats, 10 weeks old, were used. After right mandibular incisor extraction, they were divided into eight groups and tooth sockets were treated differently: no treatment (control), PLGA carrier only, or PLGA containing 0.1, 0.25, 0.5, 1.0, 2.0, and 4.0 mg simvastatin, respectively. They were sacrificed at 4 and 8 weeks. Bone mineral content (BMC) of the alveolar ridge was measured with dual-energy X-ray absorptiometry and histological analyses were performed. All groups treated with simvastatin showed higher BMC compared to the control group and PLGA carrier group at 4 and 8 weeks. Histological analyses revealed that the thickness of cortical bone of the statin group increased compared to the control group at 4 and 8 weeks; however, newly-formed bone in the tooth socket of the statin group was less than in those of the control group and PLGA carrier group. The results of this study show that local application of simvastatin may enhance bone formation and preserve the alveolar ridge after tooth extraction.     

辛伐他汀对大鼠正畸牙保持阶段牙周组织中BMP-2表达的影响

目的：在大鼠处于正畸牙保持期时,以全身施药辛伐他汀的方法,来研究其对牙周组织中骨形成蛋白2（bonemorphogenetieprotein2,BMP-2）表达的影响。方法：选用78只8周龄雄性Wistar大鼠,随机分成3组。1）空白对照组：将大鼠的前牙实施连轧,将其作为支抗,向近中的方向牵移上颌两侧的第-磨牙,持续进行21d之后将其处死。2）构建牙移动模型的对照组,21d之后,在左侧的上颌安装相应的保持装置,各保持1、3、7、14、21、28d,在保持期内,给予注射腹腔生理盐水。3）实验组：改组的保持及加力措施与对照组相同,在保持期期间,给予注射腹腔辛伐他汀。在保持期结束之后,采用免疫组化染色法,并结合定量分析法,对移动牙的牙周组织内的BMP-2水平进行检测和观察。结果：在整个保持期,对照组的BMP-2量逐渐减少,实验组呈逐渐增加的趋势。相同时间的实验用药组与实验对照组比较,实验组的BMP-2量较于对照组普遍要高。除了对照组中的第28天组之外,其余各小组BMP-2的表达强度均强于空白对照组（P〈0．01）。结论：腹腔注射辛伐他汀能够增加大鼠实验性牙移动后保持阶段牙周组织中BMP-2的表达,从而促进骨细胞的生成、骨质矿化。     

辛伐他汀对大鼠胫骨骨缺损修复作用的实验研究

目的：研究辛伐他汀作为激活物对骨生成的促进作用。方法：通过制备大鼠胫骨骨缺损模型填入Bio-oss骨粉,同时给予口服辛伐他汀（实验组）,并设立空白组、对照组（骨缺损单纯填入Bio-oss骨粉）,于术后4、8、12周分别处死大鼠,进行定性、定量分析,观测骨增量变化。结果：空白组无法形成正常骨愈合;实验组在骨量形成和新骨改建速度方面明显优于对照组。结论：辛伐他汀有促进新骨生成作用。     

新型多孔磷酸钙支架对骨髓间充质干细胞生物学行为的影响

目的评价新型多孔磷酸钙（CPC）作为骨组织工程支架对Beagle犬骨髓间充质干细胞（BMSCs）黏附、增殖及成骨分化等生物学行为的影响。方法将Beagle犬BMSCs接种于新型多孔CPC三维支架表面,以磷酸三钙（TCP）和聚乳酸-聚羟基乙酸共聚物（PLGA）为对照组,通过观察细胞形态、绘制细胞生长曲线、测定碱性磷酸酶（ALP）活性、进行茜素红染色并半定量测定骨钙素等方法,检测BMSCs在支架材料上的黏附、增殖及成骨分化情况。结果细胞形态和生长曲线结果显示BMSCs在新型多孔CPC三维支架材料表面分布均匀,生长及增殖活跃。ALP活性半定量结果表明,CPC、TCP组ALP表达强度明显高于PLGA组（P＜0.05）,CPC组与TCP组间的差异无统计学意义（P＞0.05）。骨钙素染色与半定量检测结果均显示：各观察点PLGA组钙盐沉积量明显少于CPC和TCP组（P＜0.05）,而TCP和CPC组间的差异无统计学意义（P＞0.05）。结论本实验所用多孔CPC材料具有与TCP类似但优于PLGA的良好生物相容性,利于BMSCs的黏附、增殖及成骨分化,可作为支架材料与BMSCs共同培养,构建具有成骨能力的组织工程化骨。     

中老年鼠与青少年鼠牙正畸移动的比较研究

目的：比较中老年鼠与青少年鼠牙对正畸力的反应。为中老年人正畸提供实验依据。方法：选用12月龄SD大鼠20只（A组）,7周龄SD大鼠20只（B组）,以上颌中切牙做支抗,牵引第一磨牙近中移动,分别于加力后3 d、1周、2周、3周随机处死其中的5只大鼠,测量左右侧牙齿移动距离;拍摄X线片;组织学观察,测量压力侧牙周膜的宽度变化;统计压力侧和张力侧成骨细胞、破骨细胞数。比较中老年鼠（A组）与青少年鼠（B组）之间的差别。结果：①牙齿移动距离：加力3 d、1周、2周、3周后,A组牙齿移动距离较B组小（P〈0.05）。②牙周韧带宽度：A组在每个时间段均窄于B组,差异均具有显著性（P〈0.05）。③成骨细胞及破骨细胞数：两组大鼠均呈现明显的压力区和张力区。加力1周时,A组压力侧破骨细胞明显少于B组,差异有高度显著性（P〈0.01）;3周时,A组压力侧及张力侧成骨细胞均少于B组,差异有显著性（P〈0.05）。结论：正畸力均可使中老年鼠和青少年鼠牙产生移动,但无论是移动速度还是牙周韧带、成骨细胞及破骨细胞的反应,中老年鼠均低于青少年鼠;提示在临床上对中老年病例的正畸过程中要注意力的控制,并关注牙周组织的反应。     

辛伐他汀与骨粉复合物填充大鼠胫骨骨缺损修复作用的实验研究

目的研究辛伐他汀作为激活物对大鼠胫骨骨缺损修复的促进作用。方法实验组用辛伐他汀与Bio-Oss骨粉复合物填入大鼠胫骨骨缺损模型,对照组骨缺损单纯填入Bio-Oss骨粉,空白组骨缺损部位不放入骨粉。术后4、8、12周分别处死大鼠,定性、定量分析,观测骨增量变化和骨缺损修复进程。结果空白组无法正常愈合;实验组在新骨生成和改建速度上明显好于对照组。结论辛伐他汀有促进新骨生成作用,加速了骨缺损修复进程。     

柚皮甙复合自固化磷酸钙支架材料修复骨缺损的实验研究

目的：探讨柚皮甙/自固化磷酸钙材料修复骨缺损的效果。方法：将柚皮甙与自固化磷酸钙复合,植入兔下颌骨的缺损区。分别在术后4、8、12周取材,进行大体观察、X线检测、扫描电镜、组织学观察、以及新骨的形成观察。结果：每时间点大体观察、X线、扫描电镜、组织学观察及新骨的形成,实验组均优于对照组。结论：柚皮甙/自固化磷酸钙材料具有明显加速成骨的作用。