反复熔铸对烤瓷合金热膨胀系数的影响

目的 研究反复熔铸对口腔常用烤瓷合金热膨胀系数的影响。方法 运用离心铸造方法,将常用的贵金属、钴铬、镍铬烤瓷合金分别经过1次、2次、3次熔铸后,将合金制成金属棒试件测试热膨胀系数。对测试结果进行统计学分析。结果 每种烤瓷合金经过1~3次熔铸后,每代之间的热膨胀系数值无统计学差异。结论 3种常用烤瓷合金在空气环境下经过1~3次熔铸后热膨胀系数值仍符合临床要求。     

反复熔铸对镍铬烤瓷合金电化学腐蚀性能影响的研究

目的探讨反复熔铸对镍铬烤瓷合金在人工唾液中电化学腐蚀行为的影响。方法试样由镍铬烤瓷合金分别经过1、2、3、4及5次熔铸（即Ⅰ、Ⅱ、Ⅲ、Ⅳ、Ⅴ代试样）后,再经铜导线焊接、聚甲基丙烯酸甲酯包埋、测试面氧化铝砂纸磨光和布轮抛光而成。试样浸泡于人工唾液中[温度为（37．0±1．0）℃,pH为7．4±0．1]24h后,参考ISO10271（2001）标准,采用动电位极化曲线法测试其抗腐蚀性能,并用扫描电镜观察合金腐蚀前后表面形貌的变化。结果各代试样间Ecorr、Ep、Rp、Icorr等电化学参数间差异无统计学意义（P〉0．05）;两两比较表明,Ⅱ代Ep大于Ⅰ代（P=0．023）,余差异无统计学意义;扫描电镜观察,极化扫描后试样表面产生腐蚀．但各代之间没有明显区别。结论镍铬烤瓷合金经反复熔铸5次后电化学腐蚀没有明显改变。     

反复熔铸对非贵金属烤瓷合金弯曲性能的影响

目的:探讨反复熔铸对非贵金属烤瓷合金弯曲性能的影响。方法:弯曲试件由非贵金属烤瓷合金分别经过1次、2次、3次、4次以及5次熔铸后,再经万能工具磨床研磨而成。根据ISO7438标准,对所有试件进行三点弯曲加载直至试件断裂,测试所有非贵金属烤瓷合金试件的弯曲强度及弯曲模量。结果:经过不同铸造次数的非贵金属烤瓷合金,在弯曲强度和弯曲模量上有显著差异(P<0.05)。经过2次、4次铸造的合金与经过1次铸造的合金之间的弯曲强度无显著差异,而经过3次、5次铸造的合金在弯曲强度上显著高于经过1次铸造的合金(P<0.05);经过2次、5次铸造的合金与经过1次铸造的合金之间的弯曲模量无显著差异,而经过3次、4次铸造的合金在弯曲模量上则显著高于经过1次铸造的合金(P<0.05)。结论:非贵金属烤瓷合金至少可以重复铸造5次而不引起弯曲性能的下降。     

反复熔铸对镍铬烤瓷合金表面性能影响的研究

目的研究反复熔铸对镍铬烤瓷合金表面粗糙度、表面自由能等表面性能的影响。方法在真空加压氩气保护条件下,将镍铬烤瓷合金分别经过1~5次熔铸制成方形试件,一面暴露作为测试面,其余表面用树脂包埋,测试面抛光成镜面,测量各试件的表面粗糙度和表面自由能,并确保各试件表面粗糙度无明显区别。然后浸泡于pH 6.8人工唾液中37℃保存3个月,浸泡后再测量各试件表面粗糙度及表面自由能。结果Ⅰ~Ⅴ代镍铬烤瓷合金表面粗糙度没有显著差异;Ⅰ、Ⅱ代镍铬烤瓷合金表面能没有显著差异,Ⅲ~Ⅴ代较Ⅰ代表面能增大并有显著意义。结论在氩气保护真空加压铸造环境中,在不添加新合金情况下,镍铬烤瓷合金经过2~5次熔铸后,表面粗糙度无明显增加,经2次熔铸合金表面自由能无明显差异,经过3~5次熔铸合金表面自由能显著增加。     

镍铬钛烤瓷金瓷剪切结合强度的测试

目的通过对自制镍铬钛（Ni-Cr-Ti）烤瓷合金与Vita常用瓷的剪切结合强度的测试,探讨镍铬烤瓷合金添加钛、混合稀土金属以及不含铍（Be）对金瓷结合性能的影响。方法使用中国科学院金属研究所研制的镍铬钛烤瓷合金,共分3个试验组,各组成分略有差异,以HI BOND非贵金属烤瓷合金为对照组,所有试件在万能试验机上采用剪切力试验测试金瓷分离时的载荷。结果3个实验组剪切强度值依次为R1组（28.1864±2.80702）MPa,R2组（26.1585±3.38148）MPa,R3组（25.1663±3.12508）MPa,对照组为（29.1436±3.28302）MPa。通过单向方差分析和SNK检验,各组之间差异均无显著性意义（P〉0.05）。结论自制镍铬钛烤瓷合金的金瓷结合良好,剪切结合强度可以达到临床应用的要求。     

���ȶ������ȫ�ɹ����������ɹڿ���ǿ�ȶ����о�

目的 研究氧化锆全瓷冠与贵金属烤瓷冠抗折强度的差异。方法 在精密车床上模拟磨牙牙体预备制作金属基牙代型15个,分为3组。根据代型分别铸造金钯合金和金合金基底冠各5个,氧化锆全瓷冠5个。全部试件均黏固于代型上。采用电子万能测力仪测试试件抗折强度,即用直径5 mm的圆形加载头,以0.5 mm/min速度垂直加载于烤瓷冠牙合面中央至瓷层碎裂,记录瓷裂时强度值。采用单因素方差分析（One-way ANOVA）对各组数据进行分析。结果 金钯合金抗折强度为（3.932 ± 0.27）kN,金合金为（2.280 ± 0.20）kN,氧化锆为（2.08 ± 0.18）kN,金钯合金组抗折强度明显高于其他两组,差异有统计学意义（P 〈 0.05）;金合金组和氧化锆组抗折强度值相近,差异无统计学意义（P 〉 0.05）。结论 研究条件下,金钯合金烤瓷冠抗折强度明显大于金合金烤瓷冠和氧化锆全瓷冠,而金合金烤瓷冠与氧化锆全瓷冠抗折强度则无明显差异。     

不同齿科铸造合金电化学腐蚀的观测研究

目的：研究不同牙科铸造合金或合金的不同处理形式对合金耐腐蚀性能的影响，为临床烤瓷合金的选择提供依据。方法：（1）采用铸造方法分别制作普通镍铬合金、镍铬合金镀金及金合金试样各8个，在人工唾液中测定各试样的极化曲线。（2）对临床采用上述3种合金烤瓷冠修复的735例病例，在修复1年后，分组对临床观察效果进行统计分析。结果：（1）镍铬合金试件和镀金试件，两次的阳极极化曲线皆有明显差异，贵金属试件，极化曲线的斜率和低腐蚀区宽度均无明显变化。（2）修复体戴用1年后，镍铬合金与镍铬合金镀金烤瓷的牙龈指数差异有显著性（P〈0．05），而镀金与贵金属烤瓷修复体的牙龈指数差异无显著性（P〈0．05）;3组病例的菌斑指数在1年内差异均无显著性（p〈0．05），镍铬合金烤瓷修复体牙龈退缩的比率明显高于其他2组（P〈0．05），而镀金与贵金属烤瓷修复体牙龈退缩的比率无明显差别（P〈0．05）。结论；应用极化曲线可以分析金属的表面状态，从而确定金属在何种情况下耐腐蚀性更好。就耐腐蚀性而言，贵金属合金最优，镀金次之，普通烤瓷合金最差。镀金试件镀层不全可造成合金更易受腐蚀，但随着时间的延长，其耐腐蚀能力增强。     

3种不同金属烤瓷冠适合性的对照研究

目的对镍铬合金烤瓷冠、贵金属合金烤瓷冠和金沉积烤瓷冠的边缘适合性进行研究,为临床应用提供一定的理论依据和指导。方法分别制作镍铬合金烤瓷冠、贵金属合金烤瓷冠和金沉积烤瓷冠各8个,将3种烤瓷冠在无水酒精中超声清洁5 min,用聚羧酸锌黏固剂按编号将全冠黏固于各自的塑料代型上,指压就位维持10 min。将黏有冠的塑料代型用自凝塑料包埋制成小方块,用金刚砂片切机沿代型底座唇舌向直径纵剖,抛光后备测。在扫描电镜下,放大120～200倍观察冠组织面与代型粘接面间的黏固剂厚度。结果金沉积烤瓷冠与贵金属合金烤瓷冠的整体黏固剂厚度无统计学差异（P>0.05）,但二者均与镍铬合金烤瓷冠的整体黏固剂厚度有统计学差异（P<0.05）。结论金沉积烤瓷冠与贵金属合金烤瓷冠的边缘适合性优于镍铬合金烤瓷冠。     

自制镍铬烤瓷合金剪切结合强度的比较研究

目的探讨镍铬烤瓷合金中添加钛（Ti）、稀土金属以及不含铍（Be）对金瓷结合性能的影响。方法选用中国科学院金属研究所研制的镍铬烤瓷合金,按照是否含铍和稀土金属分为3个实验组（R1、R2、R3组）;以HI BONDNi-Cr烤瓷合金作为对照组（R4组）。对金瓷结合试件行剪切结合强度测试和金瓷界面的扫描电镜观察与能谱分析。结果R1、R2、R3、R4组剪切结合强度间差异无统计学意义（P＞0.05）。扫描电镜观察金瓷界面形貌可见,合金与瓷紧密接触,无裂缝。各组界面元素种类接近。结论自制镍铬烤瓷合金的金瓷结合良好,剪切结合强度可以达到临床应用的要求。在镍铬烤瓷合金中加入Ti和稀土金属且不含Be可作为临床使用的更好推荐。     

金沉积基底烤瓷冠用于前牙修复的疗效研究

目的：探讨金沉积基底烤瓷冠应用于前牙的临床修复效果。方法：制作金沉积基底烤瓷冠、铸造金铂合金基底烤瓷冠与铸造镍铬合金基底烤瓷冠各50件,并观察三者戴入时及戴入烤瓷冠36个月后的冠边缘的密合度、冠的折裂、折断情况、颜色及牙龈边缘染色等。结果：金沉积基底烤瓷冠与铸造金铂合金基底烤瓷的边缘密合度无差异,均明显优于铸造镍铬合金基底烤瓷冠（P〈0.001）;三者在强度方面无显著性差异;金沉积基底烤瓷冠与铸造金铂合金基底烤瓷冠的颜色基本相似,均较镍铬合金烤瓷冠更接近于天然牙（P〈0.005）;而金沉积基底烤瓷冠和铸造金铂合金基底烤瓷冠均未出现如铸造镍铬合金基底烤瓷冠的牙龈边缘染色现象。结论：金沉积基底烤瓷冠有良好的边缘密合度、抗折强度以及良好的颜色表现力,且无牙龈边缘染色现象,具有良好的临床疗效。     

反复熔铸对牙科烤瓷合金显微结构的影响

目的: 探讨反复熔铸对钴铬、纯钛、钯铜镓、金铂烤瓷合金显微结构的影响。方法: 在真空加氩气保护环境下,将4种烤瓷合金单纯反复熔铸1~3次。每次再熔铸前,烤瓷合金均经过课题组前期研究所得“烤瓷合金再熔铸前最佳处理方法”处理,根据金属显微组织检验方法（GB/T13298-2015）,分别对熔铸前、熔铸1~3次后的烤瓷合金进行研磨、抛光、浸蚀,采用金相显微镜或扫描电镜检测金相显微结构。结果: 随着熔铸次数增加,钴铬烤瓷合金晶粒粗化、晶粒间基质和晶界间化合物增多。纯钛烤瓷合金随熔铸次数增加,晶粒粗化明显。2次熔铸后,晶粒有等轴化倾向,3次熔铸则出现针刺状β相。钯铜镓烤瓷合金在2、3次熔铸后,晶粒结构略有长大。金铂烤瓷合金晶粒结构未随熔铸次数发生明显改变。结论: 反复熔铸显著改变钴铬、纯钛、钯铜镓烤瓷合金的显微结构,建议由厂家回收再利用烤瓷合金废旧料。     

Development of Ag-Pd-Au-Cu alloy for multiple dental applications. Part 1. Effects of Pd and Cu contents, and addition of Ga or Sn on physical properties and bond with ultra-low fusing ceramic

Ag-Pd-Au-Cu quaternary alloys consisting of 30-50% Ag, 20-40% Pd, 10-20% Cu and 20% Au (mother alloys) were prepared. Then 5% Sn or 5% Ga was added to the mother alloy compositions, and another two alloy systems (Sn-added alloys and Ga-added alloys) were also prepared. The bond between the prepared alloys and an ultra-low fusing ceramic as well as their physical properties such as the solidus point, liquidus point and the coefficient of thermal expansion were evaluated. The solidus point and liquidus point of the prepared alloys ranged from 802 degrees C to 1142 degrees C and from 931 degrees C to 1223 degrees C, respectively. The coefficient of thermal expansion ranged from 14.6 to 17.1 x 10(-6)/degrees C for the Sn- and Ga-added alloys. In most cases, the Pd and Cu contents significantly influenced the solidus point, liquidus point and coefficient of thermal expansion. All Sn- and Ga-added alloys showed high area fractions of retained ceramic (92.1-100%), while the mother alloy showed relatively low area fractions (82.3%) with a high standard deviation (20.5%). Based on the evaluated properties, six Sn-added alloys and four Ga-added alloys among the prepared alloys were suitable for the application of the tested ultra-low fusing ceramic.     

牙用烤瓷支架钴铬钼合金反复烧结对金瓷结合的影响

目的研究反复烧结对牙用烤瓷支架Co-Cr-No合金（DA9-4合金）金瓷结合的影响。方法用DA9-4合金制作30根直径2.2mm、长50.0mm的圆棒,上瓷制成瓷盘高1.5mm、厚1.1mm的金瓷棒盘试件;另制30个25.0mm×3.0mm×0.5mm金属片,上瓷为瓷厚1.1mm的三点弯曲试件。试件分别随机分成常规烤瓷程序烧结一次组（对照组）、常规烤瓷程序烧结二次组、常规烤瓷程序烧结三次组,每组10个试件。在WD-10A型万能测试机上测试三点弯曲结合强度,棒盘金瓷最大剪切破坏载荷及剥瓷百分率。结果3次烧结金瓷结合情况相似,各次烧结弯曲结合强度、棒盘金瓷最大剪切破坏载荷及剥瓷百分率差异均无统计学意义（P〉0.05）。结论反复烧结不大于3次对DA9-4合金的金瓷结合无明显影响。     

真空充氩反复熔铸对烤瓷合金化学成分的影响

目的 研究真空加氩气环境中反复熔铸对4种常用非镍基烤瓷合金（钴铬、纯钛、钯基和金铂烤瓷合金）化学成分的影响。方法 真空加氩气保护环境下反复熔铸钴铬、纯钛、钯基和金铂烤瓷合金1~3次,每次再熔铸前对废旧合金均经过相应的再熔铸前处理,打磨抛光后,采用能谱仪检测4种烤瓷合金1~3次熔铸后的化学成分。结果 4种合金反复熔铸1~3次的化学成分含量变化均无统计学差异（P>0.05）。结论 真空加氩气环境中反复熔铸对钴铬、纯钛、钯基和金铂烤瓷合金的化学成分无明显影响。     

Investigation of Pd-Ag alloy for porcelain fusing. (Part 2) Thermal expansion (author's transl)]

Thermal expansion coefficient and thermal expansion hysteresis (residual expansion after thermal cycles) were measured using nine Pd-Ag alloys (In and/or Sn added) prepared in Part 1. The following results were obtained. (1) The thermal expansion coefficients were ranged 13 approximately 15 x 10(-6)/ degrees C in the temperature range of 400 to 200 degrees C. (2) The effects of the addition of indium and tin to the thermal expansion coefficient depended on the concentration of palladium and silver. (3) The thermal expansion hysteresis was ranged from 0.21 to -0.02% third thermal cycle. It was very small in comparison with that of precious alloys. (4) The thermal expansion hysteresis decreased with increase of addition of indium and tin. (5) The thermal expansion coefficient had no correlation with the bonding strength.     

反复熔铸对钴铬烤瓷合金细胞相容性的影响

目的:探讨反复熔铸对钴铬烤瓷合金生物相容性的影响.方法:将钴铬烤瓷合金分别经过1～3次熔铸,使用DMEM细胞培养液进行浸提并采用电感耦合等离子体原子发射光谱仪(ICP-AES),检测浸提液中金属离子的种类和水平,使用合金浸提液培养小鼠肺结缔组织成纤维细胞(L-929),采用流式细胞仪检测L-929细胞周期的改变,Annexin-V-FITC/PI法检测L-929细胞凋亡与死亡情况.采用SPSS 13.0软件包对数据进行统计学分析.结果:经过反复熔铸后,第3代合金与第1、第2代相比,除镓(Ga)的析出量增高外(P＜0.05),其他金属离子的析出量及金属离子析出的总量均无显著变化(P＞0.05);第1～3代合金对L-929细胞周期的影响无显著差异,早期凋亡率、晚期凋亡与坏死率差异均无显著性(P＞0.05).结论:经1～3次熔铸的钴铬烤瓷合金生物相容性未发生明显改变.     

含氟环境对烤瓷金属耐腐蚀性能的影响

目的：研究分析氟离子环境对经烤瓷工序处理后金属耐腐蚀性能的影响。方法：制作金（Au）合金、纯钛（Ti）、钴铬（CoCr）合金、镍铬（NiCr）合金试件各6件,模拟临床烤瓷处理后分别置于人工唾液（A组）,含有0.2% NaF的人工唾液中（B组）,绘制极化曲线,获得并分析材料的自腐蚀电位和腐蚀电流密度。结果：B组与A组比较,镍铬合金、钴铬合金、纯钛自腐蚀电位负值增大,差异有统计学意义（P〈0.05）,金合金无差异。同种金属B组与A组相比腐蚀电流密度增加,差异有统计学意义（P〈0.05）。结论：氟离子环境能使得烤瓷处理过金属的耐腐蚀性能下降,腐蚀速度加快。金合金与纯钛耐腐蚀性能较强,其次是CoCr合金,NiCr合金最差。     

反复熔铸对Ni-Cr烤瓷合金机械性能的影响

目的 :比较反复熔铸对Ni Cr烤瓷合金机械性能的影响。方法 :Ni Cr烤瓷合金经过熔铸 4次后 ,用拉伸实验对各代铸件的抗拉强度、屈服强度、延伸率等机械性能指标进行比较 ,并作金相和断口电镜观察。结果 :Ni Cr烤瓷合金反复熔铸 4次的抗拉强度、0 .2 %屈服强度无显著性差异 (P >0 .0 5 ) ,延伸率之间有显著性差异(P <0 .0 5 ) ;结构观察显示 ,随着熔铸次数的增加 ,铸件的树枝状晶粒明显减小 ,缩孔缩松数分布增多增广 ,有夹杂物产生 ,并且出现一些杂质富积区。结论 :Ni Cr烤瓷合金反复熔铸 4次后 ,在其机械性能方面能够满足烤瓷合金的基本要求     

K2O-Al2O3-SiO2系统牙科玻璃陶瓷与牙本质粘结强度的实验研究

目的：研究K2O-Al2O3-SiO2系统牙科陶瓷材料在使用Variolink Ⅱ树脂粘结剂时与牙本质的粘结强度。方法：依据”白榴石微晶化”热处理温度制备K2O-Al2O3-SiO2系统牙科玻璃陶瓷瓷锭;在已拔除的前磨牙中选择24个无龋坏、无裂纹者即刻完成根管充填;在每个离体牙的近中邻殆面制备Ⅱ类洞型,洞型的颊舌径3mrn、近远中径4mm、洞型顶部到洞底的轴壁长2mm、近中邻轴壁宽1mm;随机将离体牙分成两组制作嵌体蜡型,第1组离体牙使用K2O-Al2O3-SiO2系统牙科玻璃陶瓷材料制作嵌体,第2组离体牙使用IPS—Empress牙科陶瓷材料制作嵌体,两组嵌体均使用Variolink Ⅱ树脂粘结材料进行粘结,粘结后的所有样本均承受300次5℃～55℃的热循环;将样品修整成1．5mm×1．5min×3．0mm的立方体,其中陶瓷与牙体各占1／2,用微拉伸方法进行粘结强度测试。结果：K2O-Al2O3-SiO2系统牙科玻璃陶瓷和IPS—Empress牙科陶瓷与牙本质的粘结强度分别为（11．28±5．36）MPa和（12．61±1．74）MPa。结论：在使用Variolink Ⅱ粘结材料的情况下,K2O-Al2O3-SiO2系统牙科玻璃陶瓷和IPS—Empress牙科陶瓷与牙本质的粘结强度没有显著性差别。