Effect of silane activation on shear bond strength of fiber-reinforced composite post to resin cement

PURPOSE

Among the surface treatment methods suggested to enhance the adhesion of resin cement to fiber-reinforced composite posts, conflicting results have been obtained with silanization. In this study, the effects of silanization, heat activation after silanization, on the bond strength between fiber-reinforced composite post and resin cement were determined.

MATERIALS AND METHODS

Six groups (n=7) were established to evaluate two types of fiber post (FRC Postec Plus, D.T. Light Post) and three surface treatments (no treatment; air drying; drying at 38℃). Every specimen were bonded with dual-curing resin cement (Variolink N) and stored in distilled water for 24 hours at 37℃. Shear-bond strength (MPa) between the fiber post and the resin cement were measured using universal testing device. The data were analyzed with 1-way ANOVA and by multiple comparisons according to Tukey''s HSD (α=0.05). The effect of surface treatment, fiber post type, and the interactions between these two factors were analyzed using 2-way ANOVA and independent sample T-tests.

RESULTS

Silanization of the FRC Postec Plus significantly increased bond strength compared with the respective non-treated control, whereas no effect was determined for the D.T. Light Post. Heat drying the silane coupling agent on to the fiber-reinforced post did not significantly improve bond strength compared to air-syringe drying.

CONCLUSION

The bond strength between the fiber-reinforced post and the resin cement was significantly increased with silanization in regards to the FRC Postec Plus post. Bond strength was not significantly improved by heat activation of the silane coupling agent.     

Effects of post surface conditioning before silanization on bond strength between fiber post and resin cement

PURPOSE

Post surface conditioning is necessary to expose the glass fibers to enable bonding between fiber post and resin cement. The purpose of the present study was to evaluate the effect of different surface conditioning on tensile bond strength (TBS) of a glass fiber reinforced post to resin cement.

MATERIALS AND METHODS

In this in vitro study, 40 extracted single canal central incisors were endodontically treated and post spaces were prepared. The teeth were divided into four groups according to the methods of post surface treatment (n=10): 1) Silanization after etching with 20% H₂O₂, 2) Silanization after airborne-particle abrasion, 3) Silanization, and 4) No conditioning (Control). Adhesive resin cement (Panavia F 2.0) was used for cementation of the fiber posts to the root canal dentin. Three slices of 3 mm thick were obtained from each root. A universal testing machine was used with a cross-head speed of 1 mm/minute for performing the push-out tests. Two-way ANOVA and Tukey post hoc tests were used for analyzing data (α=0.05).

RESULTS

It is revealed that different surface treatments and root dentin regions had significant effects on TBS, but the interaction between surface treatments and root canal regions had no significant effect on TBS. There was significant difference among H₂O₂ + Silane Group and other three groups.

CONCLUSION

There were significant differences among the mean TBS values of different surface treatments. Application of hydrogen peroxide before silanization increased the bond strength between resin cements and fiber posts. The mean TBS mean values was significantly greater in the coronal region of root canal than the middle and apical thirds.     

Effects of silica coating and silane surface conditioning on the bond strength of rebonded metal and ceramic brackets

Objective

The aim of this study was to evaluate the effects of tribochemical silica coating and silane surface conditioning on the bond strength of rebonded metal and ceramic brackets.

Material and Methods

Twenty debonded metal and 20 debonded ceramic brackets were randomly assigned to receive one of the following surface treatments (n=10 for each group): (1) sandblasting (control); (2) tribochemical silica coating combined with silane. Brackets were rebonded to the enamel surface on the labial and lingual sides of premolars with a light-polymerized resin composite. All specimens were stored in distilled water for 1 week and then thermocycled (5,000 cycles) between 5-55°C. Shear bond strength values were measured using a universal testing machine. Student''s t-test was used to compare the data (α=0.05). Failure mode was assessed using a stereomicroscope, and the treated and non-treated bracket surfaces were observed by scanning electron microscopy.

Results

Rebonded ceramic brackets treated with silica coating followed by silanization had significantly greater bond strength values (17.7±4.4 MPa) than the sandblasting group (2.4±0.8 MPa, P<0.001). No significant difference was observed between the rebonded metal brackets treated with silica coating with silanization (15±3.9 MPa) and the sandblasted brackets (13.6±3.9 MPa). Treated rebonded ceramic specimens primarily exhibited cohesive failure in resin and adhesive failure at the enamel-adhesive interface.

Conclusions

In comparison to sandblasting, silica coating with aluminum trioxide particles followed by silanization resulted in higher bond strengths of rebonded ceramic brackets.     

EFFECT OF RELINING ON FIBER POST RETENTION TO ROOT CANAL

One of the clinically relevant problems dentists face when restoring endodontically treated teeth is the mismatch between fiber post and post space diameters, which results in an excessively thick resin cement layer. Fiber post relining appears as a solution for this problem.

Objectives:

The aim of this study was to evaluate the effect of fiber post relining with composite resin on push-out bond strength.

Material and Methods:

Twenty bovine incisors were selected to assess post retention. The crowns were removed below the cementoenamel junction and the root canals were treated endodontically and flared with diamond burs. The roots were allocated into two groups (n=10): G1: fiber posts without relining and G2: fiber posts relined with composite resin. The posts were cemented with a dual-cured resin cement and the specimens were sectioned transversally. Three 1.5-mm thick slabs were obtained per root and identified as cervical, medium and apical thirds. The push-out test was performed at a crosshead speed of 0.5 mm/min until post dislodgement occurred. The failure mode of fractured specimens was analyzed under scanning electron microscopy. Data were analyzed by split-plot ANOVA and post-hoc Tukey''s test at a pre-set alpha of 0.05.

Results:

Relined fiber posts presented higher retention values than non-relined post in all thirds. No statistically significant differences (p>0.05) were found among thirds for relined posts. All failures occurred at the interface between resin cement and root dentin.

Conclusions:

Relining with composite resin seems to be an effective method to improve the retention of fiber posts to flared root canals.     

Resistance to compression of weakened roots subjected to different root reconstruction protocols

Objective

This study evaluated, in vitro, the fracture resistance of human non-vital teeth restored with different reconstruction protocols.

Material and methods

Forty human anterior roots of similar shape and dimensions were assigned to four groups (n=10), according to the root reconstruction protocol: Group I (control): non-weakened roots with glass fiber post; Group II: roots with composite resin by incremental technique and glass fiber post; Group III: roots with accessory glass fiber posts and glass fiber post; and Group IV: roots with anatomic glass fiber post technique. Following post cementation and core reconstruction, the roots were embedded in chemically activated acrylic resin and submitted to fracture resistance testing, with a compressive load at an angle of 45º in relation to the long axis of the root at a speed of 0.5 mm/min until fracture. All data were statistically analyzed with bilateral Dunnett''s test (α=0.05).

Results

Group I presented higher mean values of fracture resistance when compared with the three experimental groups, which, in turn, presented similar resistance to fracture among each other. None of the techniques of root reconstruction with intraradicular posts improved root strength, and the incremental technique was suggested as being the most recommendable, since the type of fracture that occurred allowed the remaining dental structure to be repaired.

Conclusion

The results of this in vitro study suggest that the healthy remaining radicular dentin is more important to increase fracture resistance than the root reconstruction protocol.     

Effect of ascorbic acid,ethanol and acetone on adhesion between the treated fiber posts and composite resin cores

PURPOSE

The aim of the present study was to assess the effect of ascorbic acid, ethanol and acetone on microtensile bond strength between fiber posts pre-treated with hydrogen peroxide and composite resin cores.

MATERIALS AND METHODS

Twenty four fiber posts were pre-treated with 24% hydrogen peroxide and divided into 4 groups as follows: G1: no treatment, as control group; G2: treatment with 10% ascorbic acid solution for 5 minutes; G3: treatment with 70% ethanol solution for 5 minutes; and G4: treatment with 70% acetone solution for 5 minutes. Each fiber post was surrounded by a cylinder-shaped polyglass matrix which was subsequently filled with composite resin. Two sections from each sample were selected for microtensile test at a crosshead with speed of 0.5 mm/min. Statistical analyses were performed using one-way ANOVA and a post hoc Tukey HSD test. Fractured surfaces were observed under a stereomicroscope at ×20 magnification. The fractured surfaces of the specimens were observed and evaluated under a SEM.

RESULTS

Means of microtensile bond strength values (MPa) and standard deviations in the groups were as follows: G1: 9.70±0.81; G2: 12.62±1.80; G3: 16.60±1.93; and G4: 21.24±1.95. G4 and G1 had the highest and the lowest bond strength values, respectively. A greater bond strength value was seen in G3 compared to G2. There were significant differences between all the groups (P<.001). All the failures were of the adhesive mode.

CONCLUSION

Application of antioxidant agents may increase microtensile bond strength between fiber posts treated with hydrogen peroxide and composite cores. Acetone increased bond strength more than ascorbic acid and ethanol.     

Evaluation of the resin cement thicknesses and push-out bond strengths of circular and oval fiber posts in oval-shapes canals

PURPOSE

The aim of this study was to evaluate whether the push-out bond strength varies between oval and circular fiber posts, and to examine the effect on the resin cement thicknesses around the posts.

MATERIALS AND METHODS

Eighteen mandibular premolar roots were separated into two groups for oval and circular fiber posts systems. Post spaces were prepared and fiber posts were luted to the post spaces. Roots were cut horizontally to produce 1-mm-thick specimens. Resin cement thicknesses were determined with a metallographic optical microscope and push-out tests were done.

RESULTS

No significant differences were observed in terms of push-out bond strength between the oval and circular fiber posts (P>.05) The resin cement thicknesses of the oval posts were greater than those of the circular posts group in the coronal, middle and apical specimens (P<.05).

CONCLUSION

In the light of these results, it can be stated that resin cement thickness does not affect the push-out bond strength.     

A comparative evaluation of fracture resistance of endodontically treated teeth restored with different post core systems - an in-vitro study

PURPOSE

To compare the fracture resistance and the mode of failure of endodontically treated teeth restored with different post-core systems.

MATERIALS AND METHODS

Root canal treatment was performed on 40 maxillary incisors and the samples were divided into four groups of 10 each. For three experimental groups post space preparation was done and teeth were restored with cast post-core (Group B), stainless steel post with composite core (Group C) and glass fiber post with composite core using adhesive resin cement (Group D). Control group (A) samples were selected with intact coronal structure. All the samples were prepared for ideal abutment preparation. All the samples were subjected to a load of 0.5 mm/min at 130° until fracture occurred using the universal testing machine. The fracture resistance was measured and the data were analyzed statistically. The fracture above the embedded resin was considered to be favorable and the fracture below the level was considered as unfavorable. The statistical analysis of fracture resistance between different groups was carried out with t-test. For the mode of failure the statistical analysis was carried out by Kruskal-Wallis test and Chi-Square test.

RESULTS

For experimental group Vs control group the fracture resistance values showed significant differences (P<.05). For the mode of failure the chi-square value is 16.1610, which means highly significant (P=.0009) statistically.

CONCLUSION

Endodontically treated teeth without post core system showed the least fracture resistance demonstrating the need to reinforce the tooth. Stainless steel post with composite core showed the highest fracture resistance among all the experimental groups. Teeth restored with the Glass fiber post showed the most favorable fractures making them more amenable to the re-treatment.     

Shear bond strength of composite resin to titanium according to various surface treatments

STATEMENT OF PROBLEM

When veneering composite resin-metal restoration is prepared, the fact that bond strength between Ti and composite resin is relatively weak should be considered.

PURPOSE

The purpose of this study is to evaluate the shear bond strength between the veneering composite resin and commercial pure (CP) Ti / Ti-6Al-4V alloy according to the method of surface treatment.

MATERIAL AND METHODS

The disks were cast by two types of metal. Their surfaces were treated by sandblasting, metal conditioner, TiN coating and silicoating respectively. After surface treatment, the disks were veneered by composite resin (Tescera™, Bisco, USA) which is 5 mm in diameter and 3 mm in thickness. The specimens were stored in water at 25℃ for 24 hours, and then evaluated for their shear bond strength by universal testing machine (STM-5®, United Calibration, USA). These values were statistically analyzed.

RESULTS

1. All methods of surface treatment were used in this study satisfied the requirements of ISO 10477 which is the standard of polymer-based crown and bridge materials. 2. The metal conditioner treated group showed the highest value in shear bond strength of CP Ti, silicoated group, TiN coated group, sandblasted group, in following order. 3. The silicoated group showed the highest value in shear bond strength of Ti-6Al-4V alloy, metal conditioner treated group, sandblasted group, TiN coated group, in following order.

CONCLUSION

Within the limitations of this study, all methods of surface treatment used in this study are clinically available.     

Polymerization behavior and thermal characteristics of two new composites at five temperatures: refrigeration to preheating

PURPOSE

Heat of composite polymerization (HP) indicates setting efficacy and temperature increase of composite in clinical procedures. The purpose of this in vitro experimental study was to evaluate the effects of 5 temperatures on HP of two new composites.

MATERIALS AND METHODS

From each material (Core Max II [CM] and King Dental [KD]), 5 groups of 5 specimens each were prepared and their total HPs (J/gr) were measured and recorded, at one of the constant temperatures 0℃, 15℃, 23℃, 37℃ and 60℃ (2 × 5 × 5 specimens) using a differential scanning calorimetry (DSC) analyzer. The data were analyzed using a two-way ANOVA, a Tukey''s test, an independent-samples t-test, and a linear regression analysis (α=0.05).

RESULTS

No polymerization reactions occurred at 0℃; then this temperature was excluded from statistical analyses. The mean HP of the remaining 20 KD specimens was 20.5 ± 14.9 J/gr, while it was 40.7 ± 12.9 J/gr for CM. The independent-samples t-test showed that there were significant differences between the HP of the two materials at the temperatures 15℃ (P=.0001), 23℃ (P=.0163), 37℃ (P=.0039), and 60℃ (P=.0106). Linear regression analysis showed statistically significant correlations between environment temperatures and HP of CM (R²=0.777).

CONCLUSION

Using CM is advantageous over conventional composite because of its better polymerization capacity. However due to its high HP, further studies should assess its temperature increase in vivo. Preheating KD is recommended. Refrigerating composites can negatively affect their polymerization potential.     

Adhesion between fiber posts and resin luting agents: a microtensile bond strength test and an SEM investigation following different treatments of the post surface

PURPOSE: (1) To evaluate the interfacial strength between FRC Postec posts and three luting agents (Multilink, Variolink II, and MultiCore Flow) following different surface treatments, and (2) to observe the effect of sandblasting (Rocatec Pre) on the surface morphology of methacrylate-based fiber posts. MATERIALS AND METHODS: The posts received one of the following surface treatments: (1) sandblasting, (2) sandblasting + silanization, (3) silanization or (4) no treatment. The three luting agents were bonded to the post and the post-cement bond strength was evaluated with the microtensile test. SEM observation of sandblasted and nontreated posts was performed. Post-cement interfaces were also evaluated. Data were statistically analyzed with two-Way ANOVA with post treatment and luting agent as factors. Tukey's test was applied for post-hoc comparisons. RESULTS: Post treatment and the interaction between type of luting agent and type of post treatment were significant factors for bond strength (p < 0.001). The type of luting agent did not significantly influence bond strength (p = 0.07). Sandblasting + silanization performed better than sandblasting or no treatment (p < 0.001). Silanization resulted in significantly higher bond strengths than no treatment (p = 0.045). No differences were detected between sandblasting + silanization and silanization. SEM observation revealed an increased surface roughness and exposure of fibers in sandblasted posts. CONCLUSION: Silanization was confirmed to be a reliable method for improving the bond strength of resin luting agents to fiber posts. Bond strength of resin luting agents to fiber posts was not influenced by the type of luting agent. The sandblasting procedure modified the methacrylate-based post surface texture.     

The effect of denture base surface pretreatments on bond strengths of two long term resilient liners

PURPOSE

Purpose of this study was to evaluate effect of two surface treatments, sandblasting and monomer treatment, on tensile bond strength between two long term resilient liners and poly (methyl methacrylate) denture base resin.

MATERIALS AND METHODS

Two resilient liners Super-Soft and Molloplast-B were selected.Sixty acrylic resin (Trevalon) specimens with cross sectional area of 10×10 mm were prepared and divided into two groups of 30 specimens each. Each group was surface treated (n = 10) by sandblasting (250 µ alumina particles), monomer treatment (for 180 sec) and control (no surface treatment). Resilient liners were processed between 2 poly(methyl methacrylate) surfaces, in the dimensions of 10×10×3 mm. Tensile strength was determined with Instron Universal testing machine, at a crosshead speed of 5 mm/min; and the modes of failure (adhesive, cohesive or mixed) were recorded. The data were analyzed using one-way ANOVA, followed by Tukey HSD test (α = 0.05).

RESULTS

Monomer pretreatment of acrylic resin produced significantly higher bond strengths when compared to sandblasting and control for both resilient liners (P < .001). Sandblasting significantly decreased the bond strength for both the liners when compared to monomer pretreatment and control (P < .001). Mean bond strength of Super-Soft lined specimens was significantly higher than Molloplast-B in various surface treatment groups (P < .05).

CONCLUSION

Surface pretreatment of the acrylic resin with monomer prior to resilient liner application is an effective method to increase bond strength between the base and soft liner. Sandblasting, on the contrary, is not recommended as it weakens the bond between the two.     

EFFECT OF CYCLIC LOADING ON FRACTURE STRENGTH OF ENDODONTICALLY TREATED TEETH RESTORED WITH CONVENTIONAL AND ESTHETIC POSTS

Introduction:

Esthetic post and core systems were recently introduced. There are few reports regarding their behavior under cyclic loading.

Objectives:

This study compared the effect of cyclic loading on survival rate, residual strength and mode of fracture of endodontically treated teeth restored with esthetic and direct metallic post systems subjected to mechanical cyclic loading.

Materials and Methods:

Thirty canines were endodontically treated, decoronated and prepared for metal free ceramic crowns, leaving 1.5 mm of dentin for ferrule effect. They were distributed in 3 groups and restored as follows: group 1 with zirconia posts (Cosmopost) and glass-ceramic cores (IPS Empress Cosmopost); group 2 with fiber reinforced composite posts (FibreKor) and group 3 with titanium posts (AZthec Anchor). Direct resin composite (Build It FR Resin Composite) was used as core in groups 2 and 3. All specimens were restored with all ceramic crowns (IPS Empress 2). A resin cement/adhesive system (Cement It/Bond It Primer A+B) was used to lute the posts to root canals and metal free porcelain crowns to the teeth preparation. Specimens were subjected to mechanical load of 250 N for 500,000x at a frequency of 1.7 Hz and then to static load until failure in a universal testing machine. Data were analyzed using One-way ANOVA and Fischer Exact tests α=0.05.

Results:

All groups had 100% survival rate after cyclic loading; fracture strength values (SD) in N were: group 1 = 886.5(170.6), group 2 = 762.2(113.6) and group 3 = 768.9(72.9); there was no difference among groups (p=0.08); the percentage of mode of favorable fracture found was: group 1 = 60%, group 2 = 90% and group 3 = 50%; there was no correlation between the mode of failure and post and core system used (P=0.142).

Conclusions:

Esthetic post and core systems showed statistically equivalent fracture strength values, mode of failure and survival rate compared to conventional direct metallic post and resin composite core system after cyclic loading.     

Bond strength of three luting agents to zirconia ceramic - influence of surface treatment and thermocycling

Objective

This in vitro study aimed to evaluate the influence of different surface treatments, 3 luting agents and thermocycling on microtensile bond strength (µTBS) to zirconia ceramic.

Material and Methods

A total of 18 blocks (5x5x4 mm) were fabricated from zirconia ceramic (ICE Zirkonia) and duplicated into composite blocks (Alphadent). Ceramic blocks were divided into 3 groups (n=6) according to the following surface treatments: airborne-particle abrasion (AA), silica-coating, (SC) (CoJet) and silica coating followed by silane application (SCSI) (ESPE Sil). Each group was divided into 3 subgroups (n=2) according to the 3 luting agents used. Resin-modified glass-ionomer cement (RMGIC, Ketac Cem Plus), self-adhesive resin cement (UN, RelyX Unicem) and adhesive resin cement (ML, MultiLink Automix) were used for bonding composite and zirconia blocks. Each bonding assembly was cut into microbars (10 mm long and 1±0.1 mm²). Seven specimens of each subgroup were stored in water bath at 37ºC for 1 week. The o ther 7 specimens were stored in water bath at 37ºC for 30 days then thermocycled (TC) for 7,500 cycles. µTBS values were recorded for each specimen using a universal testing machine. Statistical analyses were performed using a 3-way ANOVA model followed by serial 1-way ANOVAs. Comparison of means was performed with Tukey''s HSD test at (α=0.05).

Results

µTBS ranged from 16.8 to 31.8 MPa after 1 week and from 7.3 to 16.4 MPa after 30 days of storage in water and thermocycling. Artificial aging significantly decreased µTBS (p<0.05). Considering surface treatment, SCSI significantly increased µTBS (p<0.05) compared to SC and AA. Resin cements (UN and ML) demonstrated significantly higher µTBS (p<0.05) compared to RMGIC cement.

Conclusions

Silica coating followed by silane application together with adhesive resin cements significantly increased µTBS, while thermocycling significantly decreased µTBS.     

Influence of modification in core building procedure on fracture strength and failure patterns of premolars restored with fiber post and composite core

PURPOSE

The influence of the modified process in the fiber-reinforced post and resin core foundation treatment on the fracture resistance and failure pattern of premolar was tested in this study.

MATERIALS AND METHODS

Thirty-six human mandibular premolars were divided into 4 groups (n = 9). In group DCT, the quartz fibre post (D.T. Light-post) was cemented with resin cement (DUO-LINK) and a core foundation was formed with composite resin (LIGHT-CORE). In group DMO and DMT, resin cement (DUO-LINK) was used for post (D.T. Light-post) cementation and core foundation; in group DMO, these procedures were performed simultaneously in one step, while DMT group was accomplished in separated two steps. In group LCT, the glass fiber post (LuxaPost) cementation and core foundation was accomplished with composite resin (LuxaCore-Dual) in separated procedures. Tooth were prepared with 2 mm ferrule and restored with nickel-chromium crowns. A static loading test was carried out and loads were applied to the buccal surface of the buccal cusp at a 45 degree inclination to the long axis of the tooth until failure occurred. The data were analyzed with MANOVA (α = .05). The failure pattern was observed and classified as either favorable (allowing repair) or unfavorable (not allowing repair).

RESULTS

The mean fracture strength was highest in group DCT followed in descending order by groups DMO, DMT, and LCT. However, there were no significant differences in fracture strength between the groups. A higher prevalence of favorable fractures was detected in group DMT but there were no significant differences between the groups.

CONCLUSION

The change of post or core foundation method does not appear to influence the fracture strength and failure patterns.     

COMPARISON OF THE FRACTURE RESISTANCE OF ENDODONTICALLY TREATED TEETH RESTORED WITH PREFABRICATED POSTS AND COMPOSITE RESIN CORES WITH DIFFERENT POST LENGTHS

Objective:

This study evaluated the fracture strengths of endodontically treated teeth restored with prefabricated posts with different post lengths.

Material and methods:

Thirty freshly extracted canines were endodontically treated. They were randomly divided into groups of 10 teeth and prepared according to 3 experimental protocols, as follows; Group 1/3 PP: teeth restored with prefabricated post and composite resin core (Z250) with post length of 5.0mm; Group 1/2 PP and Group 2/3 PP: teeth restored with prefabricated post and composite resin core (Z250) with different combinations of post length of 7.5mm and 10mm, respectively. All teeth were restored with full metal crowns. The fracture resistance (N) was measured in a universal testing machine (crosshead speed 0.5mm/min) at 45 degrees to the tooth long axis until failure. Data were analyzed by one-way analysis of variance (α=.05).

Results:

The one-way analysis of variance demonstrated no significant difference among the different post lengths (P>.05) (Groups 1/3 PP = 405.4 N, 1/2 PP = 395.6 N, 2/3 PP = 393.8 N). Failures occurred mainly due to core fracture.

Conclusion:

The results of this study showed that an increased post length in teeth restored with prefabricated posts did not significantly increase the fracture resistance of endodontically treated teeth.     

Influence of cement thickness on resin-zirconia microtensile bond strength

PURPOSE

The aim of this study was to evaluate the influence of resin cement thickness on the microtensile bond strength between zirconium-oxide ceramic and resin cement.

MATERIALS AND METHODS

Thirty-two freshly extracted molars were transversely sectioned at the deep dentin level and bonded to air-abraded zirconium oxide ceramic disks. The specimens were divided into 8 groups based on the experimental conditions (cement type: Rely X UniCem or Panavia F 2.0, cement thickness: 40 or 160 µm, storage: thermocycled or not). They were cut into microbeams and stored in 37℃ distilled water for 24 h. Microbeams of non-thermocycled specimens were submitted to a microtensile test, whereas those of thermocycled groups were thermally cycled for 18,000 times immediately before the microtensile test. Three-way ANOVA and Sheffe''s post hoc tests were used for statistical analysis (α=95%).

RESULTS

All failures occurred at the resin-zirconia interface. Thermocycled groups showed lower microtensile bond strength than non-thermocycled groups (P<.001). Differences in cement thickness did not influence the resin-zirconia microtensile bond strength given the same resin cement or storage conditions (P>.05). The number of adhesive failures increased after thermocycling in all experimental conditions. No cohesive failure was observed in any experimental group.

CONCLUSION

When resin cements of adhesive monomers are applied over air-abraded zirconia restorations, the degree of fit does not influence the resin-zirconia microtensile bond strength.     

Evaluating resin-enamel bonds by microshear and microtensile bond strength tests: effects of composite resin

Objectives

The aims of this study were to evaluate the effect of resin composite (Filtek Z250 and Filtek Flow Z350) and adhesive system [(Solobond Plus, Futurabond NR (VOCO) and Adper Single Bond (3M ESPE)] on the microtensile (µTBS) and microshear bond strength (µSBS) tests on enamel, and to correlate the bond strength means between them.

Material and methods

Thirty-six extracted human molars were sectioned to obtain two tooth halves: one for µTBS and the other one for µSBS. Adhesive systems and resin composites were applied to the enamel ground surfaces and light-cured. After storage (37ºC/24 h) specimens were stressed (0.5 mm/ min). Fracture modes were analyzed under scanning electron microscopy. The data were analyzed using two-way ANOVA and Tukey''s test (α=0.05).

Results

The correlation between tests was estimated with Pearson''s product-moment correlation statistics (α =0.05). For both tests only the main factor resin composite was statistically significant (p<0.05). The correlation test detected a positive (r=0.91) and significant (p=0.01) correlation between the tests.

Conclusions

The results were more influenced by the resin type than by the adhesives. Both microbond tests seem to be positive and linearly correlated and can therefore lead to similar conclusions.     

A simplified etching technique to improve the adhesion of fiber post

PURPOSE

Numerous methods were used to etch the fiber posts to improve its bonding to root canal dentin. Our aim was to evaluate the efficacy of 37% phosphoric acid in etching fiber posts in comparison with 24% hydrogen peroxide.

MATERIALS AND METHODS

Ninety human maxillary central incisors were taken and post space preparation was done. Ninety fiber posts were taken and divided into three groups (n=30) based on the surface treatment they received (H₃PO₄, H₂O₂, distilled water) and each group was further divided (n=10) based on the time period of application (15 seconds, 30 seconds, 60 seconds). All the posts were luted into canals using Rely X UniCem-2. Each tooth was then sectioned into six slices and subjected to push out test. Data obtained was subjected to statistical analysis at P<.05. The surface topography was evaluated using scanning electron microscopy.

RESULTS

Highest bond strength values were noted in 15 seconds etched phosphoric acid group and 60 seconds etched hydrogen peroxide group with no significant difference between two groups. Surface topography revealed complete epoxy layer removal with no damage to its structural integrity in those groups.

CONCLUSION

H₃PO₄ etching for a period of 15 seconds is an effective alternative in improving the adhesion of fiber post to root dentin.     

Effect of different ferrule designs on the fracture resistance and failure pattern of endodontically treated teeth restored with fiber posts and all-ceramic crowns

Objective

This study investigated the effect of different ferrule heights on endodontically treated premolars.

Materials and Methods

Fifty sound mandibular first premolars were endodontically treated and then restored with 7-mm fiber post (FRC Postec Plus #1 Ivoclar-Vivadent) luted with self-polymerized resin cement (Multilink, Ivoclar Vivadent) while the coronal section was restored with hybrid composite core build-up material (Tetric Ceram, Ivoclar-Vivadent), which received all-ceramic crown. Different ferrule heights were investigated: 1-mm circumferential ferrule without post and core (group 1 used as control), a circumferential 1-mm ferrule (group 2), non-uniform ferrule 2-mm buccally and 1-mm lingually (group 3), non-uniform ferrule 3-mm buccally and 2-mm lingually (group 4), and finally no ferrule preparation (group 5). The fracture load and failure pattern of the tested groups were investigated by applying axial load to the ceramic crowns (n=10). Data were analyzed statistically by one-way ANOVA and Tukey’s post-hoc test was used for pair-wise comparisons (α=0.05).

Results

There were no significant differences among the failure load of all tested groups (P<0.780). The control group had the lowest fracture resistance (891.43±202.22 N) and the highest catastrophic failure rate (P<0.05). Compared to the control group, the use of fiber post reduced the percentage of catastrophic failure while increasing the ferrule height did not influence the fracture resistance of the restored specimens.

Conclusions

Within the limitations of this study, increasing the ferrule length did not influence the fracture resistance of endodontically treated teeth restored with glass ceramic crowns. Insertion of a fiber post could reduce the percentage of catastrophic failure of these restorations under function.