表面不同形貌对钛耐腐蚀性能影响的实验研究

目的：评价不同方法表面处理后纯钛表面粗糙程度对其耐腐蚀性能的影响。方法：制备33个纯钛试件并随机分为3组,分别进行喷砂、阳极氧化和机械抛光处理,应用扫描电镜观察不同处理后钛件表面微形貌,在酸性含氟人工唾液中测试开路电位和阳极极化曲线。结果：扫描电镜结果显示喷砂后钛表面有大量的弹坑和划痕,深度较深,且形状不规则,大小不一,边缘锐利,为微米级粗糙表面形态;而阳极氧化表面为大小均一的直径80Jim的纳米管状结构,为纳米级粗糙表面形态;机械抛光表面划痕明显,深度较浅,为微米级粗糙表面形态。在酸性含氟人工唾液中,3组之间自腐蚀电位值的比较为：阳极氧化组〉机械抛光组〉喷砂组;腐蚀电流密度值的比较为：喷砂组〉机械抛光组〉阳极氧化组,具有显著性差异（P〈0．05）。结论：不同的表面处理技术改变了钛材料表面的微形貌并影响了钛的耐腐蚀性能,经阳极氧化处理后的纳米级表面具有更好的耐腐蚀性能,喷砂会使钛的耐腐蚀性降低。     

自制美学镍钛涂层弓丝的耐腐蚀性研究

目的：研究美学镍钛涂层弓丝的耐腐蚀性能。方法：将美学涂层镍钛弓丝与未涂层镍钛弓丝浸泡于人工唾液中,37℃恒温,采用恒电位法测定阳极极化曲线,浸泡实验测定析出镍、铬离子浓度。结果：涂层弓丝的腐蚀电流显著降低,涂层弓丝析出相对低水平的金属离子。结论：美学涂层可降低弓丝合金的腐蚀倾向,提高其耐腐蚀性能。     

氟离子对纯钛表面微弧氧化膜耐腐蚀性能的影响

目的:研究在含氟模拟体液中纯钛表面微弧氧化膜的耐腐蚀性能。方法:制备纯钛试件,利用电化学方法测量纯钛表面微弧氧化处理后的极化曲线和交流阻抗。电化学实验溶液体系分为2组(n=4),分别为不含氟模拟体液组(A组)和加NaF模拟体液组(B组)。结果:和不含氟模拟体液组比较,含氟组中微弧氧化处理后试样的自腐蚀电位、自腐蚀电流密度增大和交流阻抗减少,差异均有显著性(P<0.01)。结论:氟离子可以降低纯钛微弧氧化后的耐腐蚀性能。     

含氟环境对烤瓷金属耐腐蚀性能的影响

目的：研究分析氟离子环境对经烤瓷工序处理后金属耐腐蚀性能的影响。方法：制作金（Au）合金、纯钛（Ti）、钴铬（CoCr）合金、镍铬（NiCr）合金试件各6件,模拟临床烤瓷处理后分别置于人工唾液（A组）,含有0.2% NaF的人工唾液中（B组）,绘制极化曲线,获得并分析材料的自腐蚀电位和腐蚀电流密度。结果：B组与A组比较,镍铬合金、钴铬合金、纯钛自腐蚀电位负值增大,差异有统计学意义（P〈0.05）,金合金无差异。同种金属B组与A组相比腐蚀电流密度增加,差异有统计学意义（P〈0.05）。结论：氟离子环境能使得烤瓷处理过金属的耐腐蚀性能下降,腐蚀速度加快。金合金与纯钛耐腐蚀性能较强,其次是CoCr合金,NiCr合金最差。     

表面等离子渗氮处理钛的生物相容性评价：3．耐腐蚀性能评价

通过进行自然腐蚀实验、阳极极化加速腐蚀实验、四点弱极化实验、失重实验等腐蚀测量实验和原子吸收光谱实验对不同温度和不同时间等离子氪化的金属纯钛和未氮化的纯钛进行对比性研究，发现钛经过表面等离子氮化后耐腐蚀性能有显著提高，离子释放速率有显著下降，而且随氮化温度及时间增加，总体上耐腐蚀性能呈现提高的趋势。     

不同粗糙表面的纯钛种植体的耐腐蚀性评价

目的：本文通过对不同粗糙度表面纯钛种植体（光滑、机械表面、大粗糙表面、2种不同的微粗糙表面以及各表面的不同氧化状态）的耐腐蚀性的评价,寻找具有较好的耐腐蚀的表面状态。方法：对5种不同粗糙度及相应的2种氧化表面的种植体进行电化学实验,进行自然腐蚀电位及剩余电位的测定、自然腐蚀电位随时间波动检测、腐蚀速度测定、阳极极化曲线测定。结果：400℃、45min表面氧化的微粗糙表面的钛种植体的耐腐蚀性最好。结论：对微粗糙表面进行适当的氧化处理使种植体表面的保护层增厚,同时使保护层更均匀、一致和致密,从而使种植体的耐腐蚀性能更好,种植体更稳定。     

医用钛及钛合金种植体材料的研究进展

从钛及其合金的成分,组织与性能,钛表面的腐蚀与离子释放,钛及其合金的组织反应和钛的表面活性化处理等四个方面综述了近几年有关钛及春合金种植体材料的研究进展,提出具有合适粗糙度,表面离子释放少的活性表面设计和制作将是今后的重要研究方向之一。     

含银羟基磷灰石种植体的细胞毒性研究

目的：在钛种植体表面构筑羟基磷灰石钠米银涂层并进行生物学评价。方法：采用恒电位电化学法在纯钛表面构建纳米级羟基磷灰石／纳米银（HAp／Nanosilver）涂层。采用扫描电镜（SEM），检测手段对涂层进行理化性能的表征。考察了涂层的结构组分和表面的微观形貌，而后将人牙周膜成纤维样细胞培养于涂层表面，采用细胞毒性评价及其形态观察，分析比较不同表面涂层对牙周膜成纤维样细胞粘附率及增殖率的影响。结果：羟基磷灰石纳米银涂层体外细胞培养显示其具有良好的生物活性。结论：本实验构筑的涂层具有良好的生物相容性和细胞粘附性，应用前景广阔。     

等离子渗氮对纯钛耐腐蚀性能影响的研究

目的：模拟口腔环境,研究在不同pH值（pH=6.8,pH=5.5）的人工唾液中,等离子渗氮对纯钛的电化学腐蚀行为的影响。方法：用Tafel曲线法,在不同pH值人工唾液中测定等离子渗氮对纯钛的自腐蚀电阻、自腐蚀电流密度、自腐蚀电位,并与对照组未等离子渗氮的纯钛进行比较分析。应用扫描电子显微镜（SEM）观察试件表面形貌变化。结果：在同一pH值的人工唾液中,等离子渗氮后纯钛的自腐蚀电阻、自腐蚀电流密度和自腐蚀电位与对照组比较均有显著性差异（P〈0.05）,pH值降低,纯钛自腐蚀电流密度增大,自腐蚀电阻、自腐蚀电位降低。SEM观察表明,pH=5.5时纯钛表面腐蚀现象更严重。结论：等离子渗氮后纯钛的耐腐蚀性能得到提高,pH值下降,耐腐蚀性能降低。     

等离子渗氮和镀膜复合处理对氟环境中纯钛耐腐蚀性能的影响

目的：观察等离子渗氮和磁控溅射镀膜复合处理对氟环境中纯钛铸件耐腐蚀性能的影响。方法：用动电位极化技术测试对照组和复合处理组纯钛铸件在氟质量浓度为1000mg/L的人工唾液中的自腐蚀电流密度和自腐蚀电位,扫描电镜观察试件表面形貌,能谱分析腐蚀面的微量元素,对结果进行分析比较。结果：对照组和复合处理组纯钛铸件在氟离子1000mg/L的人工唾液中的自腐蚀电流密度分别为（3101.58±245.07）nA和（8.60±0.45）nA,自腐蚀电位分别为（-0.50±0.11）V和（-0.20±0.02）V。复合表面处理后纯钛铸件的自腐蚀电流密度明显减小（P〈0.01）,自腐蚀电位明显大（P〈0.01）。扫描电镜显示,复合处理后纯钛铸件较对照组纯钛铸件的表面腐蚀形貌明显减轻,对照组纯钛铸件腐蚀面发现氟元素而复合处理组未发现氟元素。结论：等离子渗氮和磁控溅射镀膜复合处理能明显提高纯钛铸件的耐腐蚀性。     

柠檬精油对牙周致病菌抑制作用及其安全性初步研究

目的:探讨柠檬精油对牙周致病菌的体外抗菌活性及对细胞增殖的影响。方法:采用微量液体稀释法测定柠檬精油对Pg、Fn、Aa、Pi的最小抑菌浓度(minimal inhibitory concentration,MIC)及最小杀菌浓度(minimum bactericidal concentration,MBC);以较低浓度的MIC为标准稀释LEO作为实验组,采用MTT法测定柠檬精油对HUVECs的毒性作用,明确抑菌浓度下LEO的安全性。结果:柠檬精油对牙周主要致病菌均有抑菌作用,Pg、Fn、Aa、Pi的MIC分别是9.0 g/L、4.5 g/L、4.5 g/L、9.0 g/L,Aa、Fn的 MBC是9.0 g/L,Pg、Pi的MBC未测得。1/2MIC、1/20MIC浓度的LEO能够抑制人脐静脉内皮细胞的生长,而低于1/200MIC浓度的LEO则对人脐静脉内皮细胞的生长没有影响,其中1/200MIC浓度的LEO作用明显优于0.02%的CHX。结论:体外环境中,柠檬精油对牙周致病菌Pg、Fn、Aa、Pi具有抗菌活性,低浓度应用对机体相对安全。     

Oral cancer: molecular technologies for risk assessment and diagnosis

Purpose: The effective biomarkers related to diagnosis, metastasis, drug resistance and irradiation sensitivity of oral cancers will help the pathologist and oncologist to determine the molecular taxonomy diagnosis and design the individualization treatment for the patients with oral cancers.     

Computer-assisted planning for maxillofacial prosthodontic rehabilitation

Computerized tomography (CT) planning and the use of CT derived surgical templates for implant placement have shown promise for restoring function within months after surgical reconstruction of acquired post-oncologic defects.     

Stimulated whole saliva components in children with Down syndrome

The authors report on the components of stimulated whole saliva from children with Down syndrome—including pH, flow rate, sialic acid and protein concentrations, and amylase and peroxidase activity. Saliva samples were collected from 35 children aged 6–10 years. Of the participants, 17 had Down syndrome and 18 did not. To stimulate saliva production, the children chewed a piece of parafilm for 10 minutes before the sample was collected. Soon after collecting the saliva sample, the authors measured pH using a portable pH-meter. Sialic acid levels were determined with a thiobarbituric acid assay. Protein content was determined with Folin's phenol reagent. Amylase was assayed and the authors measured the maltose produced by the breakdown of starch and peroxidase using ortho-dianisidine.
No statistically significant difference was observed in levels of sialic acid (free and total) between the two groups. Protein concentration was about 36% higher in the group with Down syndrome. However, the salivary flow rate, pH, and amylase and peroxidase activities were lower among the children with Down syndrome.     

Effect of Pingyangmycin on human venous malformation endothelial cells

Purpose: Venous malformations are common vascular anomalies with a propensity of the head and neck. Intralesional injection of Pingyangmycin (PYM, bleomycin A5 hydrochloride) is a widely used sclerotherapy method for the treatment of venous malformation.     

牙髓再生的研究现状

目前,根管治疗术在临床上已得到了广泛的应用并成功的保存了患牙,但其仍有许多术后并发症。随着组织工程技术在口腔领域的应用,构建一种组织工程化牙髓进行牙髓-牙本质复合体的再生治疗成为可能。近年来国内外已有很多关于牙髓再生的研究,并且已经取得了一定成果。本文将对目前国内外牙髓再生的研究进展现状作一综述。     

Oropharyngeal dysphagia in amyotrophic lateral sclerosis alters quality of life

Dysphagia is one of the most important complications encountered in amyotrophic lateral sclerosis (ALS). Our aim was to determine whether oropharyngeal dysphagia impacted the quality of life (QoL) of patients with ALS. Thirty consecutive patients were recruited (31–82 years, 18 men). Swallowing function was evaluated using a standardised videofluoroscopic barium swallow. All the patients completed a specific questionnaire on quality of life in dysphagia (SWAL‐QoL) immediately after the videofluoroscopy. The results of dysphagia outcome severity scale separated 14 patients with oropharyngeal dysphagia and 16 with normal swallowing function. There was no difference in the average age, weight and body mass index of the two groups (dysphagic patients: 68 ± 11 kg versus non‐dysphagic patients: 69 ± 14 kg). Most of the dysphagic patients had a bulbar affection based on their Norris scores which determine the importance of cranial nerves illness (20 ± 8), significantly lower than those of the non‐dysphagic patients (35 ± 5) (P < 0·0001). There was no difference in the neurological peripheral symptoms evaluated by Amyotrophic Lateral Sclerosis Functional Rating Scale scores (dysphagic patients: 26 ± 7 versus non‐dysphagic patients: 27 ± 8) (ns). The swallowing quality of life questionnaire revealed that the dysphagic patients had significant burden (P < 0·001). They were affected by the necessity to applied a food selection (P < 0·01), by the increase in eating duration (P < 0·05) and described a decrease in eating desire (P < 0·05). They complained of fear regarding the risk of dysphagia (P < 0·05). They also described difficulties with oral communication (P < 0·001). All of those complained about dysphagia which impacted directly mental health (P < 0·05) and social life (P < 0·05). In conclusion, oropharyngeal dysphagia is a common symptom accompanying ALS, which alters the patient's QoL, especially social health.     

拔牙位点保存用复合温敏凝胶的构建及体外表征

目的:制备多壁碳纳米管/羟基磷灰石/壳聚糖复合温敏凝胶,探讨其作为拔牙位点保存材料的理化性能。方法:采用原位沉积方法制备多壁碳纳米管/羟基磷灰石(MWNT/ HA简称HAC)复合无机材料,将其分散至壳聚糖温敏凝胶中,制备壳聚糖/多壁碳纳米管/羟基磷灰石(CS /MWNT/HA简称CS/HAC)复合温敏凝胶,以成胶时间、孔径、孔隙率、机械强度及降解性能为指标优化配方设计,并表征复合温敏凝胶的微观形貌及理化性能。结果:以10 g/L的HAC作为补强成分加入到壳聚糖溶液中,能够在不影响成胶并保证一定孔隙率(84%)的前提下,提高材料的机械性能(抗压强度0.441 MPa),所获复合温敏凝胶具有适宜的临床操作时间(12 min),并具有可控的降解速率。结论:负载HAC的复合温敏凝胶具有良好的成型性,并具有较好的机械性能,在拔牙位点保存领域具有良好的应用前景。     

替牙期骨性Ⅲ类错牙合患者颞下颌关节特征的锥形束CT研究

目的:采用锥形束CT(CBCT)研究替牙期骨性Ⅲ类错牙合患者颞下颌关节的影像学特征,探讨Ⅲ类功能状态下,颞下颌关节的生长、改建机制。方法:从就诊于昆明医科大学附属口腔医院正畸科的患者中选取符合纳入标准的替牙期骨性Ⅲ类错牙合患者及骨性Ⅰ类错牙合患者各20名,使用NNT viewer 5.3图像处理软件进行三维重建及线距和角度的测量,并进行统计学分析。结果:替牙期骨性Ⅲ类错牙合患者组和替牙期骨性Ⅰ类错牙合患者组对比结果为:矢状面双侧关节前间隙偏小、双侧关节上间隙偏小、双侧关节结节斜度偏小;冠状面双侧关节内间隙偏小,双侧关节上间隙偏小,双侧关节外间隙偏小,右侧髁状突角度偏小;横截面右侧髁状突前后径偏小。结论:替牙期骨性Ⅲ类错牙合患者颞下颌关节发育不充分,呈现髁状突,关节窝深度,关节结节斜度;冠状面关节内、外间隙均较小的特征。骨性Ⅲ类错牙合患者髁状突在关节窝中处于前置近关节窝顶位置。骨性Ⅲ类错牙合患者颞下颌关节影像学特征与其功能状态相适应。