牙科纳米氧化锆陶瓷粉体的制备

目的 :探讨用于增韧牙科氧化铝陶瓷的纳米氧化锆陶瓷粉体的制备方法。方法 :应用沉淀法 ,比较不同前驱物浓度和 pH值等条件下 ,所制备氧化锆粉体的物理性能。 结果 :ZrOCl2 ·8H2 O浓度为 0 .3～ 0 .5mol/L、pH 8.5时 ,经 70 0℃煅烧 2h后 ,可获得性能优良、粒径约为 10 0nm的氧化锆陶瓷粉体。 结论 :选择适当的条件 ,该方法可制得粒径小、团聚少的纳米氧化锆陶瓷粉体。     

牙科着色氧化钇稳定四方多晶氧化锆陶瓷的制备及颜色性能

目的添加不同着色剂组合配制着色的牙科氧化钇稳定四方多晶氧化锆（3Y-TZP）陶瓷,并测定其颜色性能。方法将TZ-3Y-S粉体与一定组分的着色剂球磨混合后,在200 MPa压力下等静压成型,在1 500 ℃烧结2 h,烧制5种具有一定颜色的氧化锆材料,每个颜色组分别制备10 mm×10 mm×0.5 mm和10 mm×10 mm×1 mm着色氧化锆陶瓷片,在黑色背景下用柯尼卡美能达CM-2600d分光光度计进行颜色测定,并与VITA In-Ceram YZ染色液比色板颜色作比较。结果通过对粉体进行着色,配制出具有一定颜色的本体着色氧化锆陶瓷材料,颜色明度逐级降低,饱和度逐渐增大,2种厚度3Y-TZP陶瓷的颜色片色差较小,颜色空间范围是L*：67.76～77.78;a*：-2.19～3.80;b*：12.13～25.01。与VITA In-Ceram YZ染色液比色板相比,颜色空间近似,但明度的最低值仍较高。结论着色氧化锆陶瓷材料适宜用于临床上与饰面瓷颜色匹配,有必要再进一步研究低明度的着色氧化锆色片。     

牙科用Ce-Y-Mg复合稳定氧化锆增韧陶瓷的基本性能

目的 :探讨牙科用Ce -Y -Mg复合稳定氧化锆增韧陶瓷 (zirconiatoughenedceramic,ZTC)的基本性能。方法 :化学共沉淀法制备的三元复合稳定 (Ce-Y -Mg)氧化锆粉体造粒后 ,经双相干压成型 ,13 5 0℃烧结 ,磨光并抛光后测试其物理和力学性能。结果 :三元复合稳定 (Ce -Y -Mg)氧化锆增韧陶瓷烧结后密度为 6.0 1g/cm3,是理论密度的 98.5 2 % ,三点弯曲强度为 70 9Mpa ,断裂韧性为 11.6MPam1/2 。结论 :Ce -Y -Mg复合稳定剂可以对氧化锆陶瓷起到很好的增韧效果 ;Ce -Y -Mg复合稳定氧化锆增韧陶瓷强度高、韧性好 ,力学性能能够满足牙科桩钉标准。     

牙科用氧化锆陶瓷的低温时效及其影响因素

牙科用氧化锆陶瓷由于其良好的力学性能、高温稳定性、生物安全性和低热传导率,现已广泛应用于临床,特别是后牙全冠及固定桥修复。然而,在相对较低的温度及潮湿的环境下,氧化锆发生由部分稳定的四方晶相向单斜晶向的改变,即低温时效现象,影响其力学性能。本文探讨了牙科用氧化锆的低温时效及其影响因素,并讨论了改善其抗低温时效性的途径。     

反向沉淀法制备牙科纳米氧化锆粉体

目的 制备分散性好，粒度分布均匀的纳米级zrO2粉体。方法 以乙醇为溶剂，应用反向沉淀法，制备纳米级zrO2粉体并测试其性能。结果 前驱体粉体经600℃煅烧后，得到晶粒平均粒径为D101=15．39nm的以四方相为主的纳米级ZrO2粉体，经800℃、1000℃煅烧后，分别得到晶粒平均粒径为D111=27．29nm和D111=28．86nm的单斜相zrO2粉体。结论 以乙醇为溶剂，应用反向沉淀法可制备出分散性好、粒度均匀的纳米级zrO2粉体，低表面张力的乙醇为溶剂可以产生良好的“反团聚”效果。     

不同Al2O3纳米粉含量对牙科nAl2O3/ZrO2（3Y）纳米复合陶瓷力学性能的影响

目的 研究不同ɑ-Al2O3纳米粉含量对氧化锆纳米复合陶瓷力学性能的影响.方法 将纳米级ɑ-Al2O3 粉体以不同体积百分比加入ZrO2(3Y)造粒粉中,成型、烧结并测试不同纳米粉含量对试样力学性能的影响.结果 添加5vol% ɑ-Al2O3 纳米粉的试样力学性能最佳,其弯曲强度和断裂韧性分别达到659.17±46.54Mpa和8.55±0.89Mpa·m1/2.结论 纳米ɑ-Al2O3粉的添加有一最适比例,5vol% ɑ-Al2O3 纳米粉的nAl2O3/ZrO2(3Y)纳米复合陶瓷力学性能较好.     

牙科着色氧化锆陶瓷饰瓷前后的力学性能及断裂模式分析

目的:本研究对牙科氧化锆陶瓷着色及构筑饰面瓷前后的力学性能及断裂模式进行分析.方法:球磨混合一定组分的着色剂(氧化铁及氧化铈)和3Y-TZP(钇稳定氧化锆)粉体制备着色氧化锆陶瓷.根据ISO6872牙科陶瓷标准,制备着色和未着色氧化锆陶瓷的三点弯曲强度样品和构筑饰面瓷后的双层瓷样品,核心瓷与饰面瓷的厚度比为1:1.对所获得样品进行三点弯曲强度、断裂韧性和维氏硬度测试.采用X射线衍射(XRD)分析物相结构,扫描电镜(SEM)观察样品的断裂模式.结果:白色氧化锆陶瓷与着色氧化锆陶瓷的三点弯曲强度分别为1301 MPa和1203:MPa,统计学结果显示二者间没有明显差异,构筑饰面瓷后的三点弯曲强度分别为817 MPa和803 MPa,统计学结果显示二者间没有明显差异,但构筑饰面瓷后比单一材料样品强度降低,二者间有显著差异.在所有的双层瓷样品中,断裂模式的应力位移曲线显示为单峰断裂模式,断裂起始于核心瓷的张应力面中心区域同时发生饰面瓷的破碎和瓷层剥脱.结论:对氧化锆粉体的适当着色并没有明显影响材料的机械性能,着色和未着色氧化锆材料与饰面瓷具有良好的物理匹配性.     

制备高性能氧化锆陶瓷牙科修复体的初步研究

目的 :本文对以氧化钇稳定四方相氧化锆 (Y -TZP)纳米微粉为原料 ,经部分烧结 -牙科计算机辅助设计/计算机辅助制造系统 (CAD/CAM)加工 -完全烧结三步法制备高性能的牙科修复体的工艺路线进行了初步探索。方法 :先经模压成型 ,低温烧结 ,制作了可供CAD/CAM加工的部分烧结Y -TZP陶瓷块 ;然后经牙科CAD/CAM机加工 ,得到初步的牙科修复体 ;最后对此修复体进行完全烧结 ,得到高性能的氧化锆牙科修复体。结果 :部分烧结的陶瓷块的切削性能优良 ,与CAD/CAM预期时间吻合。完全烧结的陶瓷材料机械性能优良 ,弯曲强度达到710MPa,断裂韧性达到 4 .77MPa·m1/ 2 。在完全烧结过程中 ,各个方向收缩均匀一致。得到的牙冠形态逼真 ,无裂纹。结论 :部分烧结 -CAD/CAM加工 -完全烧结三步法制备高性能的牙科修复体的工艺路线为一条切实可行的路线     

烧结温度对牙科氧化锆增韧陶瓷性能的影响

目的 研究烧结温度对牙科氧化锆增韧陶瓷(zirconia toughened ceramic，ZTC)物理性能和弯曲强度的影响。方法 3％摩尔比的三氧化二钇(3mol％ Y2O3)稳定氧化锆粉体干压成型后，分别在1490℃、1530℃、1570℃、1610℃烧结，然后测试其密度、表面气孔率、线收缩率和弯曲强度。结果 从本项实验所得数据中可以看出，随着烧结温度的升高，氧化锆增韧陶瓷的密度和线收缩率呈上升趋势，表面气孔率呈下降趋势，弯曲强度呈现先上升后下降趋势。结论 在所设定的温度范围内，从烧结温度低和强度高的要求进行选择，3mol％ Y2O3稳定氧化锆增韧陶瓷的最佳烧结温度在1570℃左右。     

烧结温度与氧化锆含量对氧化锆增韧纳米复合陶瓷基体强度影响的比较研究

目的 氧化锆含量以及陶瓷烧结温度均是决定陶瓷强度的重要因素，本研究旨在比较研究以上两因素与氧化锆增韧的纳米复合陶瓷材料基体强度的关系及影响程度。方法 以采用包裹共沉淀法与湿法球磨相结合的方法合成Al2O3/nZrO2她纳米复合陶瓷粉体(W)为研究对象，GⅠ-Ⅱ型Al2O3粉体(A)及In—Ceram Zirconia粉体(V)作为对照。制备氧化锆含量分别为5wt％、10wt％、15wt％及20wt％的复合粉体(W)，注浆法制成陶瓷基体生坯，分别烧结至1200℃、1450℃及1600℃后，测定陶瓷基体样本的线收缩率及三点抗弯强度。结果 ①1450℃及1600℃组样本的三点抗弯强度均显著高于1200℃组，但1450℃与1600℃组同样本的三点抗弯强度划无统计学差异；②相同烧结温度下除1200℃外，ZrO2含量高的实验组样本强度均明显高于含量低的实验组。结论 提高陶瓷烧结温度在一定范围内可增高陶瓷强度，但二者并非始终成此正相关关系；本课题研制的Al2O3／nZrO2纳米复合陶瓷粉体中氧化锆的添加含量对复合体基体的力学性能有显著增强作用。     

氧化锆陶瓷在口腔医学领域中的应用

氧化锆陶瓷具有的高强度、高韧性、优良的生物相容性和近乎完美的美观性,使其在生物材料应用领域占有重要地位,尤其在口腔医学中的应用更是与日俱增。本文概述了氧化锆作为口腔材料的特点,详述了氧化锆在口腔医学方面运用的研究进展,提出了亟待解决的一些问题。     

Clinical Success of Zirconia in Dental Applications

The application of ceramic materials for the fabrication of dental restorations is a focus of interest in esthetic dentistry. The ceramic materials of choice are glass ceramics, spinel, alumina, and zirconia. Zirconia was introduced into dentistry in the 1990s because of its good mechanical and chemical properties and is currently being used as a material for frameworks, dowels, implants, abutments, and orthodontic brackets. Many in vitro studies about zirconia use have been published, but clinical long-term studies are very important. This article presents data regarding the incidence of clinical success and complications of zirconia in these dental applications. Clinical studies published to date seem to indicate that zirconia is well tolerated and sufficiently resistant.     

Fracture Resistance of Yttria-Stabilized Zirconia Dental Implant Abutments

Purpose: An in vitro study was performed to assess the effect of different degrees of clinical reduction of zirconia abutments on the failure load of clinical assemblies.
Materials and Methods: Zirconia abutments (Y-TZP Ceramic Abutment, Astra Tech) were prepared with 0, 0.5, or 1 mm of external axial reduction starting 1 mm above the height-of-contour. Abutments (n = 10) were attached to implant analogs (25 Ncm torque) embedded in a stainless steel cylinder using Field's metal. Fracture loads (N) were determined when assemblies were loaded at 60° off-axis until failure (Instron, CHS = 0.1 mm/min). Groups were statistically compared using ANOVA ( p < 0.05).
Results: Fracture loads for all assemblies displayed large variations within groups. There were no statistically significant differences ( p > 0.05) among different abutment groups with a mean fracture load of 429 N (±140) for the control group, 576 N (±120) for 0.5-mm margins, and 547 (±139) for 1.0-mm margins. All fractures occurred at the interface where the abutment was connected to the analog.
Conclusion: In this in vitro study of simulated ultimate assembly strength, the preparation of zirconia abutments did not significantly impair the fracture resistance of simulated implant assemblies. All implant abutments fractured at rates higher than the maximum incisal forces (90–370 N) estimated to occur in the anterior region of the mouth.     

Properties of Packable Dental Composites

The introduction of many new packable composites suggests that these products are rapidly gaining popularity. The purpose of this study was to evaluate the in vitro properties of a variety of packable composites and to determine if significant enhancements in physical and mechanical properties have been achieved for these materials compared with two popular nonpackable posterior composites. For the five packable and two regular composites tested (ALERT, Pyramid-Dentin, Pyramid-Enamel, Solitaire, SureFil, Heliomolar, and Z100), the values for fracture toughness, flexure strength, flexure modulus, hardness, and volumetric polymerization shrinkage were determined. In general, although the packable composites were of heavier consistency, they had mechanical properties that were intermediate to (ALERT, Pyramid, and SureFil) or lower than (Solitaire) those of the nonpackable materials. These results could have been predicted based on the similar meth-acrylate resin chemistry and filler volumes of the various composites. No composite had adequate depth-of-cure when tested in increments greater than 2 mm thick. Polymerization contraction of the packable composites was similar to or higher than that of the nonpackable composites. In addition, the radiopacity of at least one material, Solitaire, was not considered to be adequate (less than 2 mm of aluminum). The results of this study suggest that these packable composites are unlikely to offer improved clinical performance over well-placed nonpackable composites.
CLINICAL SIGNIFICANCE
Packable composites have physical and mechanical properties that are similar to those of nonpackable posterior composites and are, therefore, expected to provide equivalent clinical performance.     

氧化锆质量分数对牙科复相铝瓷强度和断裂韧性的影响

目的测定所制备的牙科氧化锆增韧复相铝瓷（ZTCA）的力学性能,探讨氧化锆质量分数变化对ZTCA力学性能的影响及其增韧机制。方法溶胶- 凝胶法制备单相Al2O3粉体,表面诱导沉淀法制备4组不同ZrO2质量分数的ZTCA粉体。将5组粉体干压成型后烧结并加工成标准试件用于力学性能试验,测定三点弯曲强度及断裂韧性;扫描电子显微镜观察基体断口形貌;X射线衍射分析ZTCA基体晶相组成。结果ZTCA抗弯强度随ZrO2的增加先上升而后下降;ZrO2加入量为30%时,抗弯强度最高,为304.5 MPa,对应的断裂韧性为1.85 MPa·m1/2;ZTCA基体晶相包括α- Al2O3、四方相氧化锆以及少量的单斜相氧化锆。结论ZrO2质量分数不同对应ZTCA的强韧化机制不同,ZrO2质量分数为15%～30%时,材料以应力诱导相变增韧为主;ZrO2质量分数大于30%时,还存在微裂纹增韧机制。