氧化锆增韧纳米复合陶瓷粉体粒度与基体强度的关系

目的　探讨氧化锆 (ZrO2 )粉体微观粒度、级配与材料增韧补强效果之间的关系。方法以采用包裹共沉淀法与湿法球磨方法合成的Al2 O3 nZrO2 纳米复合陶瓷粉体为研究对象 ,改变所添加ZrO2 粉体的粒度 ,对粉体形貌进行扫描电镜观察与粉体粒径的测定分析 ;以注浆法将粉体制成样本生坯 ,经 1 4 50℃烧结后 ,测定样本的抗弯强度与断裂韧性。结果　①添加等量、不同粒度ZrO2 的Al2 O3 nZrO2 纳米复合渗透陶瓷材料 ,其基体抗弯强度与断裂韧性差异有显著性 (P <0 0 5) ;②添加粒度分布范围在 0 0 2～ 3 5μm ,包含粒径小于 0 5μm超细颗粒的ZrO2 组 ,增韧增强效果最显著 ,抗弯强度与断裂韧性分别达 (1 1 5 434± 5 31 9)MPa和 (2 0 4± 0 1 0 )MPam1 /2 。结论　添加ZrO2 的粉体粒度与级配是影响Al2 O3 nZrO2 纳米复合渗透陶瓷材料基体强度的重要因素     

氧化锆增韧的纳米复合陶瓷（Al2O3—nZrO2）基体热膨胀性能及孔隙分布的研究

目的考察Al2O3/nZrO2纳米复合陶瓷基体的热膨胀性能及孔隙分布情况.方法包裹共沉淀法与湿法球磨相结合的方法合成Al2O3/nZrO2纳米复合陶瓷粉体,采用粉浆涂塑方法制备测试所需试件,在TMA2940型热机械分析仪上绘制样本从室温到1 000℃的热膨胀曲线;用Autopore Ⅱ 9220型压汞仪(美国MicromeritiecS公司)测定基体试件内的气孔分布.结果1.测得A12O3/nZrO2纳米复合陶瓷基体的热膨胀系数为7.185(25-500℃)～9.267(500～1000℃)(μm/m/℃)略高于渗透玻璃2.W材料基体内气孔呈狭窄的单峰分布,孔径集中于 200A～0.426μm区间,其中孔径小于 1000A的毛细孔占孔隙总体积的35%以上.结论所合成A12O3-nZrO2复合材料的热膨胀性能及孔隙分布利于熔融玻璃的渗透过程.     

Mechanical Properties of a new Dental all-ceramic Material-zirconia Toughened Nanometer-ceramic Composite

目的口腔全瓷修复体以其独特优越性受到医患青睐,但脆性问题一直限制其应用范围及使用可靠性.本研究旨在研制用于玻璃渗透全瓷修复的纳米氧化锆增韧陶瓷并全面检测评价其力学性能.方法采用化学共沉淀与球磨相结合的方法合成纳米氧化锆增韧陶瓷(α-Al2O3/nZrO2 ceramics powder ,W),扫描电镜评价陶瓷材料的粉体形态特征及粒度分布.预制氧化锆含量不同的陶瓷粉体(5wt%,10wt%,15wt% and 20wt%),采用粉浆涂塑技术将材料制成标准试件,并在不同温度下(1 200～1 600 ℃)烧结成型,用三点弯曲法及单边刀口梁法检测材料试件的抗弯强度和断裂韧性.结果1)α-Al2O3/nZrO2材料粉体粒度分布范围大致为0.02～3.0 μm,其中超细粉体(低于0.1 μm)占20%; 2)不同烧结温度组试件的力学强度有显著差异(P＜0.05),1 450 ℃和1 600 ℃组高于1 200 ℃组;3)相同烧结温度下不同氧化锆含量组材料强度有显著差异,一定范围内氧化锆含量增高有助于材料的增韧增强.结论本研究所研制的纳米氧化锆增韧陶瓷材料组分配比及微观特征能增韧增强材料,有望提高玻璃渗透后材料的综合力学性能.     

烧结温度对氧化锆增韧纳米复合陶瓷基体性能的影响

目的　研究不同烧结温度对于Al2 O3 /nZrO2 纳米复合陶瓷基体主要性能的影响。方法　采用包裹共沉淀法与湿法球磨相结合的方法所合成的Al2 O3 /nZrO2 纳米复合渗透陶瓷粉体 ,用粉浆涂塑法制备成测试所需试件样本后 ,分别在 12 0 0℃及 145 0℃两种烧结温度下进行预烧处理 ,测定预烧后陶瓷基体的尺寸稳定性、堆积密度、三点弯曲强度等主要性能参数。结果　 1.12 0 0℃及 145 0℃两种烧结温度预烧处理后Al2 O3 /nZrO2 纳米复合陶瓷基体的线收缩率差异无统计学意义 ;2 .Al2 O3 /nZrO2 纳米复合陶瓷基体 12 0 0℃及145 0℃两种烧结温度预烧处理后堆积密度的差异均有统计学意义 ,145 0℃烧结组试件的堆积密度 (78.1±2 .2 5 %)高于 12 0 0℃组 (72 .7± 2 .91%) ;3.Al2 O3 /nZrO2 纳米复合陶瓷基体 12 0 0℃及 145 0℃两种烧结温度预烧处理后抗弯强度的差异均有统计学意义 ,145 0℃烧结组试件的抗弯强度 (115 .42 4± 5 .319MPa)显著高于12 0 0℃组 (2 2 .2 42± 1.5 73MPa)。结论　不同烧结温度对于Al2 O3 /nZrO2 材料 (W )的力学性能有显著影响 :145 0℃组的堆积密度及抗弯强度均比 12 0 0℃组有所提高 ,但线收缩率仍在允许范围内。     

氧化锆增韧的纳米复合渗透陶瓷(Al2O3-nZrO2)粉体合成的研究

目的　研究Al2 O3 -nZrO2 纳米复合陶瓷粉体的合成。方法　采用包裹共沉淀与湿法球磨相结合的方法合成Al2 O3 -nZrO2 纳米复合陶瓷粉体。结果　①采用观察沉降情况与沉降物体积的方法来评价分散效果 ,粉体分散系沉降过程极慢 ,观察 2 4h后悬浮液的颗粒仍由上而下呈逐渐增浓的弥散分布 ,最后即使经高速离心所得到的沉积物体积亦较小。②SEM观察粉体颗粒分散较好 ,超细颗粒粒径为纳米级。③衍射图剖析结果经稳定剂处理后 ,粉体晶相由单斜相和四方相共同构成 ,即成为有增韧作用的部分稳定ZrO2 粉体。结论　所合成Al2 O3 -nZrO2 粉体的分散效果、粉浆流动性良好且适于操作     

烧结温度与氧化锆含量对氧化锆增韧纳米复合陶瓷基体强度影响的比较研究

目的 氧化锆含量以及陶瓷烧结温度均是决定陶瓷强度的重要因素，本研究旨在比较研究以上两因素与氧化锆增韧的纳米复合陶瓷材料基体强度的关系及影响程度。方法 以采用包裹共沉淀法与湿法球磨相结合的方法合成Al2O3/nZrO2她纳米复合陶瓷粉体(W)为研究对象，GⅠ-Ⅱ型Al2O3粉体(A)及In—Ceram Zirconia粉体(V)作为对照。制备氧化锆含量分别为5wt％、10wt％、15wt％及20wt％的复合粉体(W)，注浆法制成陶瓷基体生坯，分别烧结至1200℃、1450℃及1600℃后，测定陶瓷基体样本的线收缩率及三点抗弯强度。结果 ①1450℃及1600℃组样本的三点抗弯强度均显著高于1200℃组，但1450℃与1600℃组同样本的三点抗弯强度划无统计学差异；②相同烧结温度下除1200℃外，ZrO2含量高的实验组样本强度均明显高于含量低的实验组。结论 提高陶瓷烧结温度在一定范围内可增高陶瓷强度，但二者并非始终成此正相关关系；本课题研制的Al2O3／nZrO2纳米复合陶瓷粉体中氧化锆的添加含量对复合体基体的力学性能有显著增强作用。     

不同氧化锆含量对氧化锆增韧的纳米复合陶瓷(Al2O3-nZrO2)基体性能影响的研究

目的：研究氧化锆的添加量对Al2O3-nZrO2纳米复合陶瓷基体物理及力学性能的影响。方法：采用包裹共沉淀法与湿法球磨相结合的方法合成Al2O3-nZrO2纳米复合陶瓷粉体，制备氧化锆质量百分数分别为5％、10％、15％及20％的复合粉体（W），以及氧化锆质量百分数分别为12．5％、25％的In-Ceram Zirconia粉体（V）作为对照。采用粉浆涂塑法制作力学性能测试所需的试件样本进行线收缩率、堆积密度、三点抗弯强度及断裂韧性的测试。结果：①氧化锆添加量对于W基体的线收缩率、堆积密度无显著影响（P＞0．05）；②W基体的三点抗弯强度及断裂韧性随氧化锆添加量的增多而显著增强（P＜0．05）；③微观结构观察发现W基体断口起伏不平，细小颗粒密密麻布满稍大颗粒的间隙及表面，彼此熔接成片。结论：氧化锆添加含量对复合体基体的力学性能有显著影响，独特的微观结构是力学性能提高的物质基础。     

氧化锆增韧的纳米复合渗透陶瓷（AlO3—nZrO2）粉体合成的研究

目的 研究AlO3-nZrO2纳米复合陶瓷粉体的合成。方法 采用包裹共沉淀与湿法球磨相结合的方法合成AlO3-nZrO2纳米复合陶瓷粉体。结果 （1）采用观察沉降情况与沉降物体积的方法来评价分散效果，粉体分散系沉降过程极慢，观察24h后悬浮液的颗粒仍由上而下呈逐渐增浓的弥散分布，最后即使经高速离心所得到的沉积物体积亦较小。（2）SEM观察粉体颗粒分散较好，超细颗粒粒径为纳米级。（3）衍射图剖析结果经稳定剂处理后，粉体晶相由单斜盯和四方相共同构成，即成为有增韧作用的部分稳定ZrO2粉体。结论 所合成AlO3-nZrO2粉体的分散效果，粉浆流动性良好且适于操作。     

不同Al2O3纳米粉含量对牙科nAl2O3/ZrO2（3Y）纳米复合陶瓷力学性能的影响

目的 研究不同ɑ-Al2O3纳米粉含量对氧化锆纳米复合陶瓷力学性能的影响.方法 将纳米级ɑ-Al2O3 粉体以不同体积百分比加入ZrO2(3Y)造粒粉中,成型、烧结并测试不同纳米粉含量对试样力学性能的影响.结果 添加5vol% ɑ-Al2O3 纳米粉的试样力学性能最佳,其弯曲强度和断裂韧性分别达到659.17±46.54Mpa和8.55±0.89Mpa·m1/2.结论 纳米ɑ-Al2O3粉的添加有一最适比例,5vol% ɑ-Al2O3 纳米粉的nAl2O3/ZrO2(3Y)纳米复合陶瓷力学性能较好.     

2种纳米粉体对牙科ZrO2陶瓷掺杂增强效果的比较

目的观察不同纳米粉体填充到微米尺度的ZrO2造粒粉中对陶瓷ZrO2纳米复合材料性能的影响。方法利用超声波．共沉淀法制备纳米α-Al2O3粉体;利用反向沉淀法制备氧化钇稳定的纳米锆粉体;作为第二相,以不同的量（体积百分比,vol％）填充到基质微米ZrO2造粒粉中,高温煅烧后,测试了纳米粉体掺杂ZrO2陶瓷复合材料的弯曲强度、断裂韧性和维氏硬度等力学性能。结果纳米α—Al2O3的最佳填充量为5vol％,此时ZrO2复相陶瓷的弯曲强度和断裂韧性分别为（659．17±46．54）MPa和（8．55±0．89）MPam^1/2;纳米ZrO2的最佳填充量为10vol％,此时ZrO2复相陶瓷的弯曲强度和断裂韧性分别为（673．17±47．19）MPa和（9．01±0．82）MPam^1/2。结论当填充纳米ZrO2和纳米α-Al2O3的量〉5vol％（如10vol％）时．前者增强效果优于后者;但当填充量≤5vol％时,后者的增强效果优于前者。     

Occlusion (Part 2 of 2)

In the previous Journal of Esthetic and Restorative Dentistry's Talking with Patients, we defined occlusion and malocclusion and discussed when and why malocclusion is a concern. In this issue we will discuss the diagnosis and treatment of malocclusions.     

Characterisation of a Bioactive SiO2-CaO-CaF2-Na2O Glass Used in Composites

ObjectivesTo characterise the ion release, pH changes and apatite formation of a phosphate free bioactive glass.MethodsA SiO₂-CaO-CaF₂-Na₂O glass was synthesized by a melt route with a composition close to the reactive glass in the commercial Cention N® composite. The glass was characterized after immersion in three media: Artificial Saliva pH4 (AS4) Artificial Saliva pH7 (AS7) and in a high phosphate artificial saliva at pH6.5 (AS6.5). The pH and fluoride release were measured using a pH meter and an ion selective electrode. The concentration of Ca, P, Na and Si were measured by ICP-OES. The glass powders after immersion were characterized by FTIR, X-ray powder diffraction and ¹⁹F MAS-NMR.ResultsThe glass increased the pH in all three media. Fluoride was detected in all three media but was much higher in AS 6.5. Calcium fluoride formed in AS4 with a small amount of fluorapatite at long immersion times. Fluorapatite and calcium fluoride formed in AS7, whilst in AS6.5 fluorapatite formed.The ion concentrations in solution after immersion reflected the glass composition and the immersion media with fluorapatite being favoured by higher pHs and phosphate contents in the media.SignificanceThe results demonstrated the ability of the glass to increase the pH and to form fluorapatite in phosphate containing media. This may explain the low incidence of secondary caries found in the commercial composite. Unlike the commercial composite evidence was found for the precipitation of fluorite, which will act to reduce the release of fluoride for preventing secondary caries.     

2-Hydroxyethyl methacrylate as an inhibitor of matrix metalloproteinase-2

This study evaluated the effect of different concentrations of 2-hydroxyethyl methacrylate (HEMA) on the inhibition of matrix metalloproteinase-2 (MMP-2) in vitro . Mouse gingival explants were cultured overnight in Dulbecco's modified Eagle's minimal essential medium, following which the expression of secreted enzymes was analyzed by gelatin zymography and the effects of different amounts of HEMA on enzyme activity were investigated. The gelatinolytic proteinases present in the conditioned media were characterized as being matrix metalloproteinases (MMPs) by means of specific chemical inhibition. The MMPs present in the conditioned media were identified, using immunoprecipitation, as MMP-2. Three major bands were detected in the zymographic assays and were characterized, according to their respective molecular weights, into the following forms of MMP-2: zymogene (72 kDa), intermediate (66 kDa), and active (62 kDa). All forms of MMP-2 were inhibited by HEMA in a dose-dependent manner, implying that MMP-2 may be inhibited by HEMA in vivo .     

ESR investigation of ROS generated by H2O2 bleaching with TiO2 coated HAp

It is well known that clinical bleaching can be achieved with a solution of 30% hydrogen peroxide (H2O2) or H2O2/titanium dioxide (TiO2) combination. This study examined the hypothesis that TiO2 coated with hydroxyapatite (HAp-TiO2) can generate reactive oxygen species (ROS). ROS are generated via photocatalysis using electron spin resonance (ESR). The bleaching properties of HAp-TiO2 in the presence of H2O2 can be measured using hematoporphyrin litmus paper and extracted teeth. We demonstrate that superoxides (O2(?-)) and hydroxyl radicals (HO(?)) can be generated through excitation of anatase TiO2, rutile TiO2, anatase HAp-TiO2, and rutile HAp-TiO2 in the presence of H2O2. The combination of R HAp-TiO2 with H2O2 produced the highest level of HO(?) generation and the most marked bleaching effects of all the samples. The superior bleaching effects exhibited by R HAp-TiO2 with H2O2 suggest that this combination may lead to novel methods for the clinical application of bleaching treatments.     

K2O-Na2O-Al2O3-SiO2系统牙科微晶玻璃匹配氧化铝陶瓷的初步研究

目的:研究 K₂O-Na₂O-Al₂O₃-SiO₂系统牙科微晶玻璃匹配氧化铝陶瓷的热处理温度制度。方法:根据氧化铝陶瓷的热膨胀系数调整K₂O-Na₂O-Al₂O₃-SiO₂系统牙科微晶玻璃的原材料配比,利用K₂O-Na₂O-Al₂O₃-SiO₂系统牙科微晶玻璃的热处理温度制度形成微晶玻璃-氧化铝陶瓷复合材料;利用偏振光显微镜和X射线衍射分析仪观察样品的形态及显微结构特性,利用材料试验机测试材料的抗压强度。结果:经过原材料组份的调整,白榴石晶粒约1.0 μm、在玻璃基质中分布均匀;微晶玻璃-氧化铝陶瓷复合材料的抗压强度为500 MPa。结论:K₂O-Na₂O-Al₂O₃-SiO₂系统牙科微晶玻璃的热处理温度制度适合匹配氧化铝陶瓷。     

Smad2基因MH2结构域表达载体的构建和其在大肠杆菌中的表达

目的：构建Ｓｍａｄ２基因ＭＨ２结构域原核融合表达载体,在大肠杆菌中表达ＭＨ２结构域,为制备抗ＭＨ２抗体,研究Ｓｍａｄ２基因和ＭＨ２结构域的功能奠定基础。方法：用ｐＧＥＸ－４Ｔ－２表达载体构建ｐＧＥＸ－４Ｔ－２／Ｓ２ＭＨ２原核融合表达载体,转化大肠杆菌ＤＨ５α,ＩＰＴＧ诱导表达ＧＳＴ－ＭＨ２融合蛋白,１００ｇ／ＬＳＤＳ－ＰＡＧＥ检测表达产物。结果：重组载体转化ＤＨ５α,经ＩＰＴＧ诱导４ｈ后,在１００ｇ／ＬＳＤＳ－ＰＡＧＥ上出现一条新的蛋白条带,相对分子质量（Ｍｒ）约为４９×１０３。结论：构建成功ｐＧＥＸ－４Ｔ－２／Ｓ２ＭＨ２融合表达载体,在大肠杆菌ＤＨ５α内表达获得ＧＳＴ－ＭＨ２融合蛋白。     

真核表达载体pIRES2-EGFP-hBMP2的构建和鉴定

目的:构建并鉴定人hBMP2基因的真核表达载体pIRES2-EGFP-hBMP2。方法:采用RT-PCR方法从人成骨肉瘤细胞中克隆hBMP2基因,连接T载体并测序正确后与真核表达载体pIRES2-EGFP连接,并进行酶切鉴定,最后将pIRES2-EGFP-hBMP2转染入HEK293细胞中,利用荧光显微镜和Western blot进行表达鉴定。结果:成功克隆了人BMP2基因,酶切鉴定和测序均正确,构建的真核表达载体pIRES2-EGFP-hBMP2能够正确表达hBMP2蛋白。结论:构建了hBMP2基因的真核表达载体pIRES2-EGFP-hBMP2,为研究该基因的功能奠定了基础。