纳米SiO2溶胶对氧化锆基底与饰面瓷结合强度的影响

目的:探讨采用溶胶-凝胶技术在氧化锆表面制备薄纳米SiO2涂层对氧化锆基底与饰面瓷结合强度的影响,指导氧化锆全瓷冠的制作.方法:将软质氧化锆试件切割成15 mm×10 mm×2.5 mm大小的长方形瓷块40片,分为4组,每组10件,分别采用4种处理方式.A组-仅经1450℃结晶处理;B组-先经30％纳米SiO2溶胶渗透后,再经1450℃结晶处理;C组-先经1450℃结晶,然后用30％纳米SiO2溶胶渗透,再经1450℃热处理;D组-表面涂布纳米SiO2溶胶后,1450℃结晶处理;E组-镍铬合金烤瓷组,使用失蜡铸造法制作12 mm×8 mm×2 mm长方形镍铬合金条块10件.5组试件在其表面堆塑直径为5 mm、高4 mm的饰面瓷圆柱,然后进行剪切强度测试.采用SPSS 19.0软件包对数据进行统计学分析.结果:5组试件的剪切强度分别为A组(28.12±2.95) MPa、B组(31.09±3.94) MPa、C组(25.60±2.45) MPa、D组(31.75±4.90) MPa、E组(28.67±3.95) MPa.单因素方差分析显示5组间具有显著差异(P＜0.05),其中,C组与B组和D组均具有显著差异.结论:①溶胶-凝胶技术在结晶致密前氧化锆基底表面制备纳米SiO2涂层,能提高氧化锆基底与饰面瓷的结合强度;②在结晶致密的氧化锆基底表面制备纳米SiO2涂层,能降低氧化锆基底与饰面瓷的结合强度;③氧化锆与氧化锆专用饰面瓷的结合强度与常用金属与饰面瓷的结合强度一致;④通过溶胶-凝胶技术在结晶致密前的氧化锆基底表面导入SiO2溶胶,提高氧化锆与饰面瓷结合强度的技术路线切实可行.     

TiN镀膜提高纯钛与聚合瓷结合强度的研究

目的:研究纯钛铸件镀制TiN薄膜对提高钛与聚合瓷结合强度的可行性.方法:铸造纯钛试件12片,随机分为2组,一组表面常规处理,另一组表面镀制TiN薄膜,分别与Ceramage聚合瓷粘接.运用平行界面剪切法测试钛-聚合瓷的结合强度.并在扫描电镜下观察钛-聚合瓷结合界面的形貌.采用SPSS11.0软件包进行两样本t检验.结果:TIN镀膜组结合强度为(29.78±0.78)MPa,高于常规处理组结合强度(25.73±0.37)MPa,有显著性差异(P＜0.01),两者均大于IS09693:1999标准所要求的基本值25MPa(P＜0.01).结论:TIN镀膜可以有效提高钛-聚合瓷的结合强度.     

喷砂粒度对激光快速成形纯钛与瓷结合强度的影响

目的 探讨不同喷砂粒度对激光快速成形(laser rapid forming,LRF)纯钛与瓷结合强度的影响,以期为LRF纯钛的临床应用提供参考.方法 利用LRF技术加工纯钛,测量LRF纯钛、铸钛和牙本质瓷试件的热膨胀系数(n=3).分别以0.5 MPa压力,50、120、250 μm的Al_2O_3对LRF纯钛表面进行喷砂处理(LRF纯钛-50μm组、LRF纯钛-120 μm组、LRF纯钛-250μm组),以0.5 MPa压力、50μm Al_2O_3喷砂处理铸钛试件作为对照(铸钛-50 μm组),测量4组钛试件的表面粗糙度(n=10)、表面接触角(n=10)并观察试件表面形貌,4组钛试件烤瓷后(n=5)测量钛-瓷结合强度.结果 LRF纯钛与铸钛的热膨胀系数[分别为(9.79±0.31)×10~(-6)和(9.84±0.42)× 10~(-6)/℃]与牙本质瓷[(8.93±0.36)×10~(-6)/℃]匹配.随着喷砂粒度的增大,LRF纯钛表面粗糙度增加,表面接触角增大.铸钛-50 μm组的钛-瓷结合强度[(26.42±1.65)MPa]略大于LRF纯钛-50μm组[(25.91±1.02)MPa],两组差异无统计学意义(P＞0.05);LRF纯钛-120 μm组钛-瓷结合强度[(21.86±1.64)MPa]与LRF纯钛-250μm组[(19.96 ±1.03)MPa]的差异无统计学意义(P＞0.05);其余各组间钛-瓷结合强度的差异均有统计学意义(P＜0.05).结论 经0.5 MPa、50 μm Al2O3喷砂处理后,LRF纯钛与瓷的结合强度可达到ISO 9693所要求的基本值(25 MPa).     

磁控溅射氮化锆涂层对钛-低熔瓷结合强度的影响

目的 探讨磁控溅射氮化锆涂层(ZrN)对钛-低熔瓷结合强度的影响,以期为钛-瓷修复体的临床应用提供参考.方法 根据随机数字表将16根纯钛试件随机分为涂层组和对照组,每组8根.涂层组纯钛试件表面磁控溅射ZrN涂层,对照组不进行表面处理.两组试件均按厂家规定烧结程序烧结粘接瓷、遮色瓷和牙本质瓷.X射线衍射(x-ray diffraction,XRD)分析涂层结构,万能实验机对两组试件进行三点弯曲实验,以计算钛-瓷结合强度并进行t检验.对钛-瓷结合界面进行扫描电镜(SEM)观察和能谱分析,对钛-瓷分离界面进行SEM观察.结果 XRD观察到涂层组试件ZrN新相.涂层组试件钛-瓷结合强度[(45.991±0.648)MPa]高于对照组[(29.483±1.007)MPa],差异有统计学意义(P=0.000).SEM显示涂层组钛-瓷分离界面瓷剩余数量较多,分布散在,而对照组钛-瓷分离界面未见明显瓷剩余.结论 磁控溅射ZrN涂层可显著提高钛-瓷结合强度.     

表面处理对两种钛瓷粉的钛瓷结合力的影响

目的:研究不同表面处理方法及不同钛瓷粉对钛瓷结合力的影响,以寻找合理有效的钛表面处理方法及适合临床应用的钛瓷粉,为临床钛烤瓷修复体的制作和应用提供理论依据。方法:本实验根据ISO9693标准中三点弯曲法制作试件,试件随机分3组,每组14个,分别采用600目砂纸打磨、打磨 喷砂及打磨 喷砂 酸洗的表面处理方法后,在试件中部烤瓷,测试结合强度并对钛瓷结合界面进行扫描电镜观察,将结果与Ni-Cr合金组进行比较。结果:经过喷砂和喷砂酸洗后,Ti22瓷粉与钛的结合强度为(28.58±1.25)MPa和(31.39±5.87)MPa,Vita Titankeramik瓷粉与钛的结合强度为(26.57±4.04)MPa和(29.66±1.12)MPa,显著高于打磨组的(19.55±0.37)MPa和(20.94±1.10)MPa(P<0.05),喷砂与喷砂酸洗组之间无统计学差异。两种瓷粉间无统计学差异(P>0.05)。经过喷砂及喷砂处理的各组结合强度均达到ISO9693临床标准(>25MPa)。但与普通烤瓷对照组比较,钛瓷结合力显著小于普通烤瓷结合力。结论:喷砂及喷砂酸洗能有效增强钛瓷结合力,满足临床应用要求。     

粘接瓷对纯钛与低熔瓷粉结合强度的影响

目的 通过研究粘接瓷对纯钛与低熔瓷粉结合强度的影响,探讨粘接瓷影响钛-瓷结合的作用机制.方法 根据ISO 9693中三点弯曲法制作钛试件40个,分为4组,每组10个;分别进行砂纸打磨(B组)、打磨+喷砂(S组)、打磨+表而烧结GC Initial Ti粘接瓷(BG组)和打磨+喷砂+表面烧结粘接瓷(SG组)处理;于4组试件中部烧结低熔瓷粉(Vita Titankeramik).测试钛-瓷结合强度,体视显微镜观察钛-瓷断裂模式,并对钛试件剥脱面进行扫描电镜观察.结果 表面烧结粘接瓷的BG组和SG组的钛-瓷结合强度分别为(32.72±4.46)和(34.25±6.52)MPa,均达到ISO9693的临床标准(＞25 MPa),并显著高于不应用粘接瓷的B组和S组[分别为(20.70±3.15)和(23.92±5.02)MPa,P＜0.05].结论 粘接瓷能有效提高钛-瓷结合强度.     

磁控溅射氮化铌对钛-瓷结合强度的影响

目的 探讨磁控溅射氮化铌(niobium nitride,NbN)对钛-瓷(Vita钛瓷粉系统)结合强度的影响,以期为钛-瓷修复体的临床应用提供参考.方法 根据随机数字表将60个钛试件随机分为T1、T2、T3和T4四个实验组.T1和T2组试件表面均先行120μm Al2O3喷砂,T2组试件表面再行磁控溅射氮化铌涂层.T3和T4组试件表面均先行磁控溅射氮化铌涂层,T4组试件表面再行120μmAl2O3喷砂.X射线衍射分析仪(X-ray diffraction,XRD)分析各组涂层物相.试件烤瓷后用万能实验机测试钛-瓷结合强度.扫描电子显微镜-X射线能谱仪(scanning electron microscopy with energy depressive spectrum,SEM-EDS)观察和分析钛-瓷结合界面.结果 XRD观察到T2、T3和T4组均存在立方晶型的氮化铌新相.三点弯曲实验测得T1-T4组试件的钛-瓷结合强度分别为(27.2±0.8)、(43.1±0.6)、(31.4±1.0)和(44.9±0.6)Mpa,4组间差异有统计学意义(P<0.05).两两比较显示,任意两组间差异均有统计学意义(P<0.05).SEM观察T1和T3组钛-瓷结合界面可见明显孔隙和裂纹,T2和T4组钛-瓷结合较好,EDS线扫描显示,T1组钛基底氧化明显,T2组和T3组界面处存在钛氧化行为,T4组界面处钛基底的氧化得到抑制.结论 磁控溅射氮化铌可抑制烤瓷侧钛基底的氧化,提高钛-瓷结合强度,同时表明Al2O3喷砂处理也能提高钛-瓷结合强度.     

不同厚度溶胶-凝胶法二氧化硅薄膜对钛瓷结合强度的影响

目的：探讨溶胶-凝胶法在纯钛表面制备不同厚度的二氧化硅薄膜对钛瓷结合强度的影响。方法：将纯钛试件随机分成四组。一次组、二次组和四次组钛试件分别经过一个、两个和四个（硅溶胶甩膜＋热处理）周期处理,对照组未经过以上处理。在各组试件中份熔附Ti-22钛专用瓷,用三点弯曲法测试钛瓷分离时的载荷。结果：一次组、二次组、四次组和对照组的钛瓷的分离载荷分别为：6.040±0.798N、5.604±0.742N、6.081±0.947N和8.816±0.923N,实验组的钛瓷结合强度明显小于对照组（P〈0.05）。结论：不同厚度的二氧化硅薄膜均不能提高钛瓷结合强度。     

钛的氧化行为对钛瓷结合力的影响

目的:观察钛的氧化行为对钛瓷结合力的影响。方法:铸造28mm×3mm×0.5mm的纯钛试件24个,喷砂、清洗后分为4组,每组6个,第1组不进行预氧化处理,第2、3、4组分别在750、800、900℃温度下,在烤瓷炉内进行预氧化处理5min。于每个金属试件中份8mm×3mm处,依次熔附Noritake TI-22瓷系统的黏结剂、遮色瓷、牙本质瓷,瓷层总厚度1mm。在拉伸试验机上采用三点弯曲法测试金瓷分离时的加载值。使用薄层X线衍射仪观察4组试件未附瓷的钛表面氧化膜中氧化物的种类。结果:不预氧化、750、800、900℃预氧化试件的金瓷分别加载(N)测试结果为10.33、9.98、5.53、3.37。不预氧化试件表面氧化膜中的氧化物全部是Ti6O;750、800、900℃试件的氧化膜中的氧化物为Ti6O和TiO2,900℃试件氧化膜中的TiO2的量明显增加。结论:随着氧化温度的升高,氧化膜中TiO2含量明显增加,钛瓷结合力显著下降,说明钛的高温氧化行为对钛瓷结合力有不利的影响。     

纳米硅涂层对钛瓷结合强度的影响

目的探讨纯钛表面纳米硅涂层改性对钛瓷结合强度的影响。方法将16个纯钛试件（25 mm×3 mm×0.5 mm）平均分为2组,A组用溶胶-凝胶法在表面形成钠米硅涂层,B组不作处理。在试件中份烧结Vita Titankeramik瓷粉,测试钛瓷间的三点弯曲结合强度;对钛瓷结合界面和分离界面进行扫描电子显微镜观察,对钛瓷结合界面进行X射线能谱分析;并用X射线衍射分析仪分析涂层结构。结果A组钛瓷结合界面的硅元素明显增加,钛瓷结合强度为（37.768±0.777）MPa,明显大于B组的结合强度（29.483±1.007）MPa,其差异有统计学意义（P=0.000）。扫描电子显微镜显示A组钛瓷分离界面瓷残留较多。结论纳米硅涂层可明显提高钛瓷结合强度。     

Occlusion (Part 2 of 2)

In the previous Journal of Esthetic and Restorative Dentistry's Talking with Patients, we defined occlusion and malocclusion and discussed when and why malocclusion is a concern. In this issue we will discuss the diagnosis and treatment of malocclusions.     

Characterisation of a Bioactive SiO2-CaO-CaF2-Na2O Glass Used in Composites

ObjectivesTo characterise the ion release, pH changes and apatite formation of a phosphate free bioactive glass.MethodsA SiO₂-CaO-CaF₂-Na₂O glass was synthesized by a melt route with a composition close to the reactive glass in the commercial Cention N® composite. The glass was characterized after immersion in three media: Artificial Saliva pH4 (AS4) Artificial Saliva pH7 (AS7) and in a high phosphate artificial saliva at pH6.5 (AS6.5). The pH and fluoride release were measured using a pH meter and an ion selective electrode. The concentration of Ca, P, Na and Si were measured by ICP-OES. The glass powders after immersion were characterized by FTIR, X-ray powder diffraction and ¹⁹F MAS-NMR.ResultsThe glass increased the pH in all three media. Fluoride was detected in all three media but was much higher in AS 6.5. Calcium fluoride formed in AS4 with a small amount of fluorapatite at long immersion times. Fluorapatite and calcium fluoride formed in AS7, whilst in AS6.5 fluorapatite formed.The ion concentrations in solution after immersion reflected the glass composition and the immersion media with fluorapatite being favoured by higher pHs and phosphate contents in the media.SignificanceThe results demonstrated the ability of the glass to increase the pH and to form fluorapatite in phosphate containing media. This may explain the low incidence of secondary caries found in the commercial composite. Unlike the commercial composite evidence was found for the precipitation of fluorite, which will act to reduce the release of fluoride for preventing secondary caries.     

2-Hydroxyethyl methacrylate as an inhibitor of matrix metalloproteinase-2

This study evaluated the effect of different concentrations of 2-hydroxyethyl methacrylate (HEMA) on the inhibition of matrix metalloproteinase-2 (MMP-2) in vitro . Mouse gingival explants were cultured overnight in Dulbecco's modified Eagle's minimal essential medium, following which the expression of secreted enzymes was analyzed by gelatin zymography and the effects of different amounts of HEMA on enzyme activity were investigated. The gelatinolytic proteinases present in the conditioned media were characterized as being matrix metalloproteinases (MMPs) by means of specific chemical inhibition. The MMPs present in the conditioned media were identified, using immunoprecipitation, as MMP-2. Three major bands were detected in the zymographic assays and were characterized, according to their respective molecular weights, into the following forms of MMP-2: zymogene (72 kDa), intermediate (66 kDa), and active (62 kDa). All forms of MMP-2 were inhibited by HEMA in a dose-dependent manner, implying that MMP-2 may be inhibited by HEMA in vivo .     

ESR investigation of ROS generated by H2O2 bleaching with TiO2 coated HAp

It is well known that clinical bleaching can be achieved with a solution of 30% hydrogen peroxide (H2O2) or H2O2/titanium dioxide (TiO2) combination. This study examined the hypothesis that TiO2 coated with hydroxyapatite (HAp-TiO2) can generate reactive oxygen species (ROS). ROS are generated via photocatalysis using electron spin resonance (ESR). The bleaching properties of HAp-TiO2 in the presence of H2O2 can be measured using hematoporphyrin litmus paper and extracted teeth. We demonstrate that superoxides (O2(?-)) and hydroxyl radicals (HO(?)) can be generated through excitation of anatase TiO2, rutile TiO2, anatase HAp-TiO2, and rutile HAp-TiO2 in the presence of H2O2. The combination of R HAp-TiO2 with H2O2 produced the highest level of HO(?) generation and the most marked bleaching effects of all the samples. The superior bleaching effects exhibited by R HAp-TiO2 with H2O2 suggest that this combination may lead to novel methods for the clinical application of bleaching treatments.     

K2O-Na2O-Al2O3-SiO2系统牙科微晶玻璃匹配氧化铝陶瓷的初步研究

目的:研究 K₂O-Na₂O-Al₂O₃-SiO₂系统牙科微晶玻璃匹配氧化铝陶瓷的热处理温度制度。方法:根据氧化铝陶瓷的热膨胀系数调整K₂O-Na₂O-Al₂O₃-SiO₂系统牙科微晶玻璃的原材料配比,利用K₂O-Na₂O-Al₂O₃-SiO₂系统牙科微晶玻璃的热处理温度制度形成微晶玻璃-氧化铝陶瓷复合材料;利用偏振光显微镜和X射线衍射分析仪观察样品的形态及显微结构特性,利用材料试验机测试材料的抗压强度。结果:经过原材料组份的调整,白榴石晶粒约1.0 μm、在玻璃基质中分布均匀;微晶玻璃-氧化铝陶瓷复合材料的抗压强度为500 MPa。结论:K₂O-Na₂O-Al₂O₃-SiO₂系统牙科微晶玻璃的热处理温度制度适合匹配氧化铝陶瓷。     

Smad2基因MH2结构域表达载体的构建和其在大肠杆菌中的表达

目的：构建Ｓｍａｄ２基因ＭＨ２结构域原核融合表达载体,在大肠杆菌中表达ＭＨ２结构域,为制备抗ＭＨ２抗体,研究Ｓｍａｄ２基因和ＭＨ２结构域的功能奠定基础。方法：用ｐＧＥＸ－４Ｔ－２表达载体构建ｐＧＥＸ－４Ｔ－２／Ｓ２ＭＨ２原核融合表达载体,转化大肠杆菌ＤＨ５α,ＩＰＴＧ诱导表达ＧＳＴ－ＭＨ２融合蛋白,１００ｇ／ＬＳＤＳ－ＰＡＧＥ检测表达产物。结果：重组载体转化ＤＨ５α,经ＩＰＴＧ诱导４ｈ后,在１００ｇ／ＬＳＤＳ－ＰＡＧＥ上出现一条新的蛋白条带,相对分子质量（Ｍｒ）约为４９×１０３。结论：构建成功ｐＧＥＸ－４Ｔ－２／Ｓ２ＭＨ２融合表达载体,在大肠杆菌ＤＨ５α内表达获得ＧＳＴ－ＭＨ２融合蛋白。     

真核表达载体pIRES2-EGFP-hBMP2的构建和鉴定

目的:构建并鉴定人hBMP2基因的真核表达载体pIRES2-EGFP-hBMP2。方法:采用RT-PCR方法从人成骨肉瘤细胞中克隆hBMP2基因,连接T载体并测序正确后与真核表达载体pIRES2-EGFP连接,并进行酶切鉴定,最后将pIRES2-EGFP-hBMP2转染入HEK293细胞中,利用荧光显微镜和Western blot进行表达鉴定。结果:成功克隆了人BMP2基因,酶切鉴定和测序均正确,构建的真核表达载体pIRES2-EGFP-hBMP2能够正确表达hBMP2蛋白。结论:构建了hBMP2基因的真核表达载体pIRES2-EGFP-hBMP2,为研究该基因的功能奠定了基础。