Preparation and characterization of collagen-hydroxyapatite composite used for bone tissue engineering scaffold

In this study, highly porous collagen-HA scaffolds were prepared by solid-liquid phase separation method. Microstructure of the composites was characterized by SEM, TEM and XRD. The results show that collagen-HA scaffolds are porous with three-dimension interconnected fiber microstructure, pore sizes are 50-150 microm, and HA particles are dispersed evenly among collagen fiber. Compared with pure collagen, the mechanical property of collagen-HA composite improves significantly. To gain further insight into cell growth throughout 3D scaffolds, the cell proliferation and attachment on the scaffold in vitro was investigated. The collagen-HA composite has good biocompatibility, and adding HA does not affect the histocompatibility of the scaffold materials. The porous collagen-HA composite is suitable as scaffold used for bone tissue engineering.     

Characteristics of calcium sulfate/gelatin composite biomaterials for bone repair

A novel hybrid biomaterial composed of calcium sulfate (CS) and gelatin (GEL) was prepared with the potential of being used as bone filler or scaffold owing to its osteoconduction. Such composite biomaterial, cross-linked or un-cross-linked, could provide a suitable absorbing rate and prevent the CS crystals migrating from the implant for tissue engineering. The structure of the composite was analyzed with infrared (IR) spectroscopy, X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results indicated that the crystal pattern of CS was affected by the addition of GEL. The GEL part affected the development of the CS dihydrate (CSD) crystal by slowing the conversion from CS hemihydrate (CSH) to CSD; thus, the composite actually contained CSD, CSH and GEL. The compressive strength of the CS/CLGEL composite was also investigated. The compressive strength was correlated to the weight proportions of CS in the CS/cross-linked GEL (CS/CLGEL) composite, and the highest compressive strength of 82 MPa was obtained for the composite containing 40 wt% CS. The in vitro absorption test and the SEM results showed that a porous scaffold was formed in situ with the absorption of CS in the CS/CLGEL composite in a certain time. Therefore, the CS/CLGEL composite material can be used as an in situ porous scaffold with a high initial mechanical strength, and the remaining porous GEL scaffold will enable further in-growth of cells. Human osteoblasts were cultured in contact with the CS/CLGEL composite and the primary results suggested that human osteoblasts could attach and spread on the surface of CS/CLGEL films. The preliminary animal model experiment was operated for assessing the potential of the CS/CLGEL composite as a biodegradable bone substitute. The primary results showed that the CS/CLGEL composite filler could promote new bone in-growth, which will stimulate further study.     

Preparation and characterization of nano-hydroxyapatite/chitosan composite scaffolds

A novel nano-hydroxyapatite (HA)/chitosan composite scaffold with high porosity was developed. The nano-HA particles were made in situ through a chemical method and dispersed well on the porous scaffold. They bound to the chitosan scaffolds very well. This method prevents the migration of nano-HA particles into surrounding tissues to a certain extent. The morphologies, components, and biocompatibility of the composite scaffolds were investigated. Scanning electron microscopy, porosity measurement, thermogravimetric analysis, X-ray diffraction, X-ray photoelectron spectroscopy, and Fourier transformed infrared spectroscopy were used to analyze the physical and chemical properties of the composite scaffolds. The biocompatibility was assessed by examining the proliferation and morphology of MC 3T3-E1 cells seeded on the scaffolds. The composite scaffolds showed better biocompatibility than pure chitosan scaffolds. The results suggest that the newly developed nano-HA/chitosan composite scaffolds may serve as a good three-dimensional substrate for cell attachment and migration in bone tissue engineering.     

In vitro cell performance on hydroxyapatite particles/poly(L-lactic acid) nanofibrous scaffolds with an excellent particle along nanofiber orientation

Highly porous hydroxyapatite (HA)/poly(L-lactide) (PLLA) nanofibrous scaffolds were prepared by incorporating needle-shaped nano- or micro-sized HA particles into PLLA nanofibers using electrospinning. The scaffolds had random or aligned fibrous assemblies and both types of HA particles were perfectly oriented along the fiber long axes. The biocompatibility and cell signaling properties of these scaffolds were evaluated by in vitro culture of rat osteosarcoma ROS17/2.8 cells on the scaffold surface. Cell morphology, viability and alkaline phosphatase (ALP) activity on each scaffold were examined at different time points. The HA/PLLA scaffolds exhibited higher cell viability and ALP activity than a pure PLLA scaffold. In addition, micro-sized HA particles supported cell proliferation and differentiation better than nano-sized ones in random scaffolds through a 10 day culture period and in aligned scaffolds at an early culture stage. The fibrous assembly of the scaffold had a pronounced impact on the morphology of the cells in direct contact with the scaffold surface, but not on cell proliferation and differentiation. Thus, HA/PLLA nanofibrous scaffolds could be good candidates for bone tissue engineering.     

Performance of hydroxyapatite bone repair scaffolds created via three-dimensional fabrication techniques

The current study analyzes the in vivo performance of porous sintered hydroxyapatite (HA) bone repair scaffolds fabricated using the TheriForm solid freeform fabrication process. Porous HA scaffolds with engineered macroscopic channels had a significantly higher percentage of new bone area compared with porous HA scaffolds without channels in a rabbit calvarial defect model at an 8-week time point. An unexpected finding was the unusually large amount of new bone within the base material structure, which contained pores less than 20 microm in size. Compared with composite scaffolds of 80% polylactic-co-glycolic acid and 20% beta-tricalcium phosphate with the same macroscopic architecture as evaluated in a previous study, the porous HA scaffolds with channels had a significantly higher percentage of new bone area. Therefore, the current study indicates that scaffold geometry, as determined by the fabrication process, can enhance the ability of a ceramic material to accelerate healing of calvarial defects.     

Three-dimensional macroporous calcium phosphate bioceramics with nested chitosan sponges for load-bearing bone implants

Three-dimensional macroporous calcium phosphate bioceramics embedded with porous chitosan sponges were synthesized to produce composite scaffolds with high mechanical strength and a large surface/volume ratio for load-bearing bone repairing and substitutes. The macroporous calcium phosphate bioceramics with pore diameters of 300 microm to 600 microm were developed using a porogen burnout technique, and the chitosan sponges were formed inside the pores of the bioceramics by first introducing chiosan solution into the pores followed by a freeze-drying process. Our scanning electron microscopy results showed that the pore size of chitosan sponges formed inside the macroporous structure of bioceramics was approximately 100 microm, a structure favorable for bone tissue in-growth. The compressive modulus and yield stress of the composite scaffolds were both greatly improved in comparison with that of HA/beta-TCP scaffolds. The simulated body fluid (SBF) and cell culture experiments were conducted to assess the bioactivity and biocompatibility of the scaffolds. In the SBF tests, a layer of randomly oriented needle-like apatite crystals formed on the scaffold surface after sample immersion in SBF, which suggested that the composite material has good bioactivity. The cell culture experiments showed that MG63 osteoblast cells attached to the composite scaffolds, proliferated on the scaffold surface, and migrated onto the pore walls, indicating good cell biocompatibility of the scaffold. The cell differentiation on the composite scaffolds was evaluated by alkaline phosphatase (ALP) assay. Compared with the control in tissue culture dishes, the cells had almost the same ALP activity on the composite scaffolds during the first 11 days of culture.     

Characteristics of calcium sulfate/gelatin composite biomaterials for bone repair

A novel hybrid biomaterial composed of calcium sulfate (CS) and gelatin (GEL) was prepared with the potential of being used as bone filler or scaffold owing to its osteoconduction. Such composite biomaterial, cross-linked or un-cross-linked, could provide a suitable absorbing rate and prevent the CS crystals migrating from the implant for tissue engineering. The structure of the composite was analyzed with infrared (IR) spectroscopy, X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results indicated that the crystal pattern of CS was affected by the addition of GEL. The GEL part affected the development of the CS dihydrate (CSD) crystal by slowing the conversion from CS hemihydrate (CSH) to CSD; thus, the composite actually contained CSD, CSH and GEL. The compressive strength of the CS/CLGEL composite was also investigated. The compressive strength was correlated to the weight proportions of CS in the CS/cross-linked GEL (CS/CLGEL) composite, and the highest compressive strength of 82 MPa was obtained for the composite containing 40 wt% CS. The in vitro absorption test and the SEM results showed that a porous scaffold was formed in situ with the absorption of CS in the CS/CLGEL composite in a certain time. Therefore, the CS/CLGEL composite material can be used as an in situ porous scaffold with a high initial mechanical strength, and the remaining porous GEL scaffold will enable further in-growth of cells. Human osteoblasts were cultured in contact with the CS/CLGEL composite and the primary results suggested that human osteoblasts could attach and spread on the surface of CS/CLGEL films. The preliminary animal model experiment was operated for assessing the potential of the CS/CLGEL composite as a biodegradable bone substitute. The primary results showed that the CS/CLGEL composite filler could promote new bone in-growth, which will stimulate further study.     

多孔HA/PU复合支架材料生物相容性的评估

进行了三维多孔立体结构的纳米羟基磷灰石/聚氨酯(HA/PU)复合支架材料体外细胞培养和体内肌肉埋植实验研究,评估材料的生物相容性。实验选用SD大鼠的骨髓基质干细胞(BMSCs)和健康的SD雌性大鼠,进行细胞相容性、形态学观察和组织学切片分析。HA/PU支架材料的多孔性为细胞的生长提供了良好的微环境,细胞在内部贴壁爬行、增殖并分化,细胞毒性为零级,材料与周围组织有良好的结合,降解的空间有结缔组织纤维长入。实验表明,HA/PU复合支架材料具有良好的细胞亲和性和组织学相容性,可作为一类新型组织工程支架材料。     

Preparation,in vitro degradability,cytotoxicity, and in vivo biocompatibility of porous hydroxyapatite whisker-reinforced poly(L-lactide) biocomposite scaffolds

Biodegradable and bioactive scaffolds with interconnected macroporous structures, suitable biodegradability, adequate mechanical property, and excellent biocompatibility have drawn increasing attention in bone tissue engineering. Hence, in this work, porous hydroxyapatite whisker-reinforced poly(L-lactide) (HA-w/PLLA) composite scaffolds with different ratios of HA and PLLA were successfully developed through compression molding and particle leaching. The microstructure, in vitro mineralization, cytocompatibility, hemocompatibility, and in vivo biocompatibility of the porous HA-w/PLLA were investigated for the first time. The SEM results revealed that these HA-w/PLLA scaffolds possessed interconnected pore structures. Compared with porous HA powder-reinforced PLLA (HA-p/PLLA) scaffolds, HA-w/PLLA scaffolds exhibited better mechanical property and in vitro bioactivity, as more formation of bone-like apatite layers were induced on these scaffolds after mineralization in SBF. Importantly, in vitro cytotoxicity displayed that porous HA-w/PLLA scaffold with HA/PLLA ratio of 1:1 (HA-w₁/PLLA₁) produced no deleterious effect on human mesenchymal stem cells (hMSCs), and cells performed elevated cell proliferation, indicating a good cytocompatibility. Simultaneously, well-behaved hemocompatibility and favorable in vivo biocompatibility determined from acute toxicity test and histological evaluation were also found in the porous HA-w₁/PLLA₁ scaffold. These findings may provide new prospects for utilizing the porous HA whisker-based biodegradable scaffolds in bone repair, replacement, and augmentation applications.     

Solvent-free polymer/bioceramic scaffolds for bone tissue engineering: fabrication,analysis, and cell growth

This study examines the potential use of porous polycaprolactone (PCL) and polycaprolocatone/hydroxyapatite (PCL/HA) scaffolds fabricated through melt molding and porogen leaching for bone tissue engineering. While eliminating organic solvents is desirable, the process steps proposed in this study for uniformly dispersing HA particles (~5?μm in size) within the scaffold can also contribute to homogeneous properties for these porous composites. Poly(ethylene oxide) (PEO) was chosen as a porogen due to its similar density and melting point as PCL. Pore size of the scaffold was controlled by limiting the size of PCL and PEO particles used in fabrication. The percent of HA in the fabricated scaffolds was quantified by thermogravimetric analysis (TGA). Mechanical testing was used to compare the modulus of the scaffolds to that of bone, and the pore size distribution was examined with microcomputed tomography (μCT). Scanning electron microscopy (SEM) was used to examine the effect on scaffold morphology caused by the addition of HA particles. Both μCT and SEM results showed that HA could be incorporated into PCL scaffolds without negatively affecting scaffold morphology or pore formation. Energy-dispersive X-ray spectroscopy (EDS) and elemental mapping demonstrated a uniform distribution of HA within PCL/HA scaffolds. Murine calvaria-derived MC3T3-E1 cells were used to determine whether cells could attach on scaffolds and grow for up to 21 days. SEM images revealed an increase in cell attachment with the incorporation of HA into the scaffolds. Similarly, DNA content analysis showed a higher cell adhesion to PCL/HA scaffolds.     

Poly(lactide-co-glycolide)/hydroxyapatite composite scaffolds for bone tissue engineering

Biodegradable polymer/bioceramic composite scaffolds can overcome the limitations of conventional ceramic bone substitutes such as brittleness and difficulty in shaping. However, conventional methods for fabricating polymer/bioceramic composite scaffolds often use organic solvents (e.g., the solvent casting and particulate leaching (SC/PL) method), which might be harmful to cells or tissues. Furthermore, the polymer solutions may coat the ceramics and hinder their exposure to the scaffold surface, which may decrease the likelihood that the seeded osteogenic cells will make contact with the bioactive ceramics. In this study, a novel method for fabricating a polymer/nano-bioceramic composite scaffold with high exposure of the bioceramics to the scaffold surface was developed for efficient bone tissue engineering. Poly(D,L-lactic-co-glycolic acid)/nano-hydroxyapatite (PLGA/HA) composite scaffolds were fabricated by the gas forming and particulate leaching (GF/PL) method without the use of organic solvents. The GF/PL method exposed HA nanoparticles at the scaffold surface significantly more than the conventional SC/PL method does. The GF/PL scaffolds showed interconnected porous structures without a skin layer and exhibited superior enhanced mechanical properties to those of scaffolds fabricated by the SC/PL method. Both types of scaffolds were seeded with rat calvarial osteoblasts and cultured in vitro or were subcutaneously implanted into athymic mice for eight weeks. The GF/PL scaffolds exhibited significantly higher cell growth, alkaline phosphatase activity, and mineralization compared to the SC/PL scaffolds in vitro. Histological analyses and calcium content quantification of the regenerated tissues five and eight weeks after implantation showed that bone formation was more extensive on the GF/PL scaffolds than on the SC/PL scaffolds. Compared to the SC/PL scaffolds, the enhanced bone formation on the GF/PL scaffolds may have resulted from the higher exposure of HA nanoparticles at the scaffold surface, which allowed for direct contact with the transplanted cells and stimulated the cell proliferation and osteogenic differentiation. These results show that the biodegradable polymer/bioceramic composite scaffolds fabricated by the novel GF/PL method enhance bone regeneration compared with those fabricated by the conventional SC/PL method.     

Biocompatibility and osteogenesis of biomimetic Bioglass-Collagen-Phosphatidylserine composite scaffolds for bone tissue engineering

A novel biomimetic composite scaffold Bioglass-Collagen-Phosphatidylserine (BG-COL-PS) was fabricated with a freeze-drying technique. The macrostructure and morphology as well as mechanical strength of the scaffolds were characterized. Scanning electronic microscopy (SEM) showed that the BG-COL-PS scaffolds exhibited interconnected porous structures with pore sizes of several microns up to about 300 μm. The scaffolds have a porosity of 75.40% and the corresponding compressive strength of 1.5469 Mpa. Rat mesenchymal stem cells (rMSCs) were seeded on BG-COL-PS or BG-COL scaffolds and cultured for 21 days in vitro. Based on the results of SEM, dsDNA content, alkaline phosphatase (ALP) activity, osteogenic gene expression analysis and alizarin red staining, the responses of MSCs to the scaffold exhibited a higher degree of attachment, growth as well as osteogenic differentiation than those on BG-COL scaffolds in vitro. To investigate the in vivo biocompatibility and osteogenesis of the composite scaffolds, both pure BG-COL-PS scaffolds and MSC/scaffold constructs were implanted in rat femurs defects for 6 weeks and studied histologically and radiographically. The in vivo results showed that BG-COL-PS composite scaffolds exhibited good biocompatibility and extensive osteoconductivity with host bone. Moreover, the BG-COL-PS/MSC constructs dramatically enhanced the efficiency of new bone formation than pure BG-COL-PS scaffolds or BG-COL/MSC constructs. All these results demonstrate the usefulness of PS composited BG-COL-PS scaffolds for inducing enhanced bone formation. The BG-COL-PS scaffolds fulfill the basic requirements of bone tissue engineering scaffold and have the potential to be applied in orthopedic and reconstructive surgery.     

Evaluation of biomimetic scaffold of gelatin-hydroxyapatite crosslink as a novel scaffold for tissue engineering: biocompatibility evaluation with human PDL fibroblasts, human mesenchymal stromal cells, and primary bone cells

Biomimetic gelatin (gel)-hydroxyapatite (HA) composites have been prepared for studying hard tissue engineering scaffolds. However, the biocompatibility test of this form of material using these three cell types, which are periodontal ligament (PDL) fibroblast cells, human mesenchymal stromal cells (HMSc) and primary cells from human hip bone (HBc) has never been evaluated. The objective of this article is to prepare and evaluate the biocompatibility of gel-HA crosslinked scaffold for tissue engineering. Two different scaffolds were prepared: preparation (1), 2.5% gel/2.5% HA; preparation (2), 2.5% gel/5% HA. Three cell types including PDL, HMSc, and HBc were used. Assessment of biocompatibility and osteoblastic cellular responses was evaluated using a three-dimensional cell culture method and scanning electron microscopy (SEM). From SEM, it was observed that scaffold (1) exhibits stable porous formation with well-blended and dispersed HA powder. All three cell types were able to proliferate in both scaffolds. The HMSc and HBc got attached to the scaffolds to a significantly higher degree and subsequently proliferated more than PDL. The alkaline phosphatase (ALP) activities of HMSc and HBc were stronger when cultured in scaffold (S1) than (S2). It was seen that the two scaffold preparations show good biocompatibility with all three cell types tested. The better cellular responses with scaffold (S1) than (S2) might be due to the different structural and morphological characteristics, that is, scaffold (S1) retained more small-sized apatite crystals and a better developed pore configuration than scaffold (S2). Based on these findings, the biomimetically synthesized composite scaffolds have the potential to be used in hard tissue regeneration and tissue engineering fields.     

Biocompatibility and osteogenesis of biomimetic nano-hydroxyapatite/polyamide composite scaffolds for bone tissue engineering

In this study, we prepared nano-hydroxyapatite/polyamide (n-HA/PA) composite scaffolds utilizing thermally induced phase inversion processing technique. The macrostructure and morphology as well as mechanical strength of the scaffolds were characterized. Mesenchymal stem cells (MSCs) derived from bone marrow of neonatal rabbits were cultured, expanded and seeded on n-HA/PA scaffolds. The MSC/scaffold constructs were cultured for up to 7 days and the adhesion, proliferation and differentiation of MSCs into osteoblastic phenotype were determined using MTT assay, alkaline phosphatase (ALP) activity and collagen type I (COL I) immunohistochemical staining and scanning electronic microscopy (SEM). The results confirm that n-HA/PA scaffolds are biocompatible and have no negative effects on the MSCs in vitro. To investigate the in vivo biocompatibility and osteogenesis of the composite scaffolds, both pure n-HA/PA scaffolds and MSC/scaffold constructs were implanted in rabbit mandibles and studied histologically and microradiographically. The results show that n-HA/PA composite scaffolds exhibit good biocompatibility and extensive osteoconductivity with host bone. Moreover, the introduction of MSCs to the scaffolds dramatically enhanced the efficiency of new bone formation, especially at the initial stage after implantation. In long term (more than 12 weeks implantation), however, the pure scaffolds show as good biocompatibility and osteogenesis as the hybrid ones. All these results indicate that the scaffolds fulfill the basic requirements of bone tissue engineering scaffold, and have the potential to be applied in orthopedic, reconstructive and maxillofacial surgery.     

Silver/hydroxyapatite composite coatings on porous titanium surfaces by sol-gel method

Hydroxyapatite (HA) coatings loaded with nanosilver particles is an attractive method to impart the HA coating with antibacterial properties. Producing Ag/HA coatings on porous Ti substrates have been an arduous job since commonly used line-of-sight techniques are not able to deposit uniform coatings on the inner pore surfaces of the porous Ti. In this study, porous Ti scaffolds with high porosity and interconnected structures were prepared by polymer impregnating method. A sol-gel process was used to produce uniform Ag/HA composite coatings on the surfaces of porous Ti substrates. Ca(NO(3) )(2) ·4H(2) O and P(2) O(5) in an ethyl alcohol based system was selected to prepare the sol, which ensured the homogeneous distribution of Ag in the sol. The characterization revealed that silver particles uniformly distributed in the coatings without agglomeration. High antibacterial ratio (>95%), against E. coli and S. albus was expressed by the silver-containing coatings (Ag/HA 0.8 and 1.6 wt %). The biocompatibility of the Ag/HA 0.8 surfaces was as good as that of pure HA surface, as revealed by culturing osteoblasts on them. The results indicated that Ag/HA 0.8 had the good balance between the biocompatibility and antibacterial properties of the coatings.     

透明质酸/壳聚糖复合支架的制备及其力学性能评价

目的　模拟天然骨组织的结构和成分,寻找适合骨组织工程的新型支架材料。 方法 以透明质酸、壳聚糖为基质材料,在微酸性环境中以一定配比与氯化钙和磷酸二氢钠混合,冷冻干燥得到多孔复合支架材料。然后在乙醇/水/尿素环境中分别陈化0、2、4、8、12和24 h,以生成产物钙磷盐前驱体转变为羟基磷灰石,最终制备出一种深度矿化的透明质酸/壳聚糖复合支架。并通过SEM、EDS等对支架进行表征,研究支架的形貌、成分及力学强度等性能。 结果 SEM观察显示,支架材料具有比较均匀的多孔结构,孔径大小为100~200 μm。EDS结果表明,复合支架在一次冻干之后形成的是磷酸氢钙（DCPD）,随着陈化时间的延长,DCPD逐渐向羟基磷灰石（HAP）转化。而压缩强度则表明经过原位矿化的支架力学性能显著提高。 结论 通过该法得到的透明质酸/壳聚糖复合支架可作为骨组织工程的新型支架材料。     

In vitro and in vivo evaluation of a novel nanosize hydroxyapatite particles/poly(ester-urethane) composite scaffold for bone tissue engineering

Scaffolds for bone tissue engineering should provide an osteoconductive surface to promote the ingrowth of new bone after implantation into bone defects. This may be achieved by hydroxyapatite loading of distinct scaffold biomaterials. Herein, we analyzed the in vitro and in vivo properties of a novel nanosize hydroxyapatite particles/poly(ester-urethane) (nHA/PU) composite scaffold which was prepared by a salt leaching–phase inverse process. Microtomography, scanning electron microscopy and X-ray spectroscopy analyses demonstrated the capability of the material processing to create a three-dimensional porous PU scaffold with nHA on the surface. Compared to nHA-free PU scaffolds (control), this modified scaffold type induced a significant increase in in vitro adsorption of model proteins. In vivo analysis of the inflammatory and angiogenic host tissue response to implanted nHA/PU scaffolds in the dorsal skinfold chamber model indicated that the incorporation of nHA particles into the scaffold material did not affect biocompatibility and vascularization when compared to control scaffolds. Thus, nHA/PU composite scaffolds represent a promising new type of scaffold for bone tissue engineering, combining the flexible material properties of PU with the advantage of an osteoconductive surface.     

Preparation,characterization and bioactivities of nano anhydrous calcium phosphate added gelatin–chitosan scaffolds for bone tissue engineering

Abstract

Gelatin, chitosan and nano calcium phosphate based composite scaffold with tailored architectures and properties has great potential for bone regeneration. Herein, we aimed to improve the physico chemical, mechanical and osteogenic properties of 3D porous scaffold by incorporation of dihydrogen calcium phosphate anhydrous (DCPA) nanoparticles into biopolymer matrix with variation in composition in the prepared scaffolds. Scaffolds were prepared from the slurry containing gelatin, chitosan and synthesized nano DCPA particle using lyophilization technique. DCPA nano particles were synthesized using calcium carbonate and phosphoric acid in water–ethanol medium. XRD pattern showed phase pure DCPA in synthesized nanopowder. Scaffolds were prepared by addition of DCPA nanoparticles to the extent of 5–10?wt% of total polymer into gelatin–chitosan solution with solid loading varying between 2.5 and 2.75?wt%. The prepared scaffold showed interconnected porosity with pore size varying between 110 and 200 micrometer. With addition of DCPA nanoparticles, average pore size of the prepared scaffolds decreased. With increase in nano ceramic phase content from 5?wt% to 10?wt% of total polymer, the compressive strength of the scaffold increased. Scaffold containing 10?wt% DCPA showed the highest average compressive strength of 2.2?MPa. Higher cellular activities were observed in DCPA containing scaffolds as compared to pure gelatin chitosan scaffold suggesting the fact that nano DCPA addition into the scaffold promoted better osteoblast adhesion and proliferation as evident from MTT assay and scanning electron microscopic (SEM) investigation of osteoblast cultured scaffolds. A higher degree of lamellopodia and filopodia extensions and better spreading behavior of osteoblasts were observed in FESEM micrographs of MG 63 cultured DCPA containing scaffold. The results demonstrated that both mechanical strength and osteogenic properties of gelatin–chitosan scaffold could be improved by addition of anhydrous dihydrogen calcium phosphate nanoparticles into it.     

胶原多糖基纳米羟基磷灰石仿生骨支架材料的研制

目的依据仿生原理制备新型的胶原多糖基纳米羟基磷灰石（HA）复合骨支架材料,并与成骨细胞复合培养,检测其细胞相容性。方法以胶原分子与透明质酸钠的交联产物为模板,调制钙磷盐在液相中沉积其上,得到矿化胶原多糖基复合材料;采用液相分离法与少量聚乳酸复合进一步制备成为三维多孔支架,使用成骨细胞（Mc3T3-E1）接种于该支架上培养。用X—ray衍射、扫描电镜、万能材料测试机等对材料进行观察和测试分析;并用倒置相差显微镜、荧光显微镜、扫描电镜、CCK-8细胞计数试剂盒、碱性磷酸酶（ALP）活性测定等观察和分析细胞在支架材料中的生长、分化情况。结果胶原多糖基纳米HA仿生复合材料的晶粒度较低,晶体极为细小,与天然骨中羟基磷灰石的组装结构类似;该复合支架为多孔状,孔隙率约82％,孔径大小为200～650μm;抗压性能好,成骨细胞可在其上贴附、生长和繁殖,并表现出较高的成骨活性。结论所制备的胶原多糖基纳米HA仿生骨支架材料,无论从组分和结构上均与天然松质骨类似,与成骨细胞相容性好,可望成为较理想的骨组织工程支架材料。     

Amorphous hydroxyapatite-sintered polymeric scaffolds for bone tissue regeneration: physical characterization studies

Given the inherent shortcomings of autografts and allografts, donor-site morbidity and risk of disease transmission, respectively, alternatives to traditional bone grafting options are warranted. To this end, poly(lactide-co-glycolide) (PLAGA) and in situ-synthesized amorphous hydroxyapatite (HA) were used to construct three-dimensional microsphere-based composite scaffolds of varying HA content for bone regeneration. In the current study, the effect of adding amorphous HA to the PLAGA scaffolds on their physical characteristics and in vitro degradation mechanism was investigated. Porosimetry and uniaxial compression testing were used to analyze the internal structure and elastic modulus of the scaffolds, respectively. Additionally, gel permeation chromatography (GPC) was performed to assess the polymer molecular weight over the course of an 8-week degradation study. HA content (17% or 27%) of the composite scaffolds was found to increase scaffold pore volume from 33.86% for pure polymer scaffolds, to 40.49% or 46.29%, depending on the amount of incorporated HA. This increased pore volume provided the composite scaffolds with a greater surface area and a corresponding decrease in elastic modulus. Scaffold degradation studies conducted over 8 weeks showed PLAGA to degrade in a first-order mechanism, with the rate of polymer degradation for the 27% HA composite scaffold being significantly slower than that of the pure PLAGA scaffold (degradation constants of 0.0324 and 0.0232 week(-1), respectively). These results suggest that the addition of amorphous HA to PLAGA microspheres resulted in porous, bioactive scaffolds that offer potential as alternative bone grafting materials for the field of regenerative medicine.