A comparison of polyethylene wear in hips with cobalt-chrome or zirconia heads. A prospective, randomised study

We have reviewed 70 patients with bilateral simultaneous total hip arthroplasties to determine the rate of failure and to compare polyethylene wear and osteolysis between an implant with a cobalt-chrome head and Hylamer liner with that of a zirconia head and Hylamer liner. The mean thickness of the polyethylene liner was 11.0 mm (8.8 to 12.2) in the hip with a zirconia head and 10.7 mm (8.8 to 12.2) in that with a cobalt-chrome head. At follow-up at 6.4 years no acetabular or femoral component had been revised for aseptic loosening and no acetabular or femoral component was loose according to radiological criteria in both the cemented and cementless groups. The mean rate of linear wear and annual wear rate were highest in the 22 mm zirconia femoral head (1.25 mm (SD 1.05) and 0.21 mm (SD 0.18), respectively) and lowest in the 22 mm cobalt-chrome femoral head (0.70 mm (SD 0.39) and 0.12 mm (SD 0.07), respectively). The mean volumetric wear was highest in the 28 mm zirconia femoral head (730.79 mm ) and lowest in the 22 mm cobalt-chrome femoral head (264.67 mm3), but if the results were compared by size of the femoral head and type of material there was no statistical difference (p > 0.05). Sequential measurements of annual wear showed that the zirconia femoral head had a relatively higher rate of penetration than the cobalt-chrome head over the first three years; thereafter the rate of wear was reduced and compared favourably with that of cobalt-chrome heads. There was a statistically significant relationship between the wear of the polyethylene liner and the age of the patient, male gender and the degree of abduction angle of the cup, but not diagnosis, weight, hip score, range of movement, or amount of anteversion. Osteolysis was identified on both sides of the acetabulum in six patients (9%). Of 12 hips with acetabular osteolysis, six had a 28 mm cobalt-chrome femoral head and the remaining six a 28 mm zirconia head. Osteolysis was observed in zones 1A and 7A of the femur in two hips (3%) with a 28 mm zirconia head (cemented hip) and in four (6%) with a 28 mm cobalt-chrome femoral head (cementless hip). Our findings suggest that although the performance of a zirconia femoral head with a Hylamer liner was not statistically different from that of a cobalt-chrome femoral head and Hylamer liner, there was a trend for the zirconia head to be worse than the cobalt-chrome femoral head.     

Three-dimensional polyethylene wear of a press-fit titanium prosthesis: Factors influencing generation of polyethylene debris

Between 1985 and 1990, 108 consecutive Harris-Galante I (Zimmer, Warsaw, IN) total hip arthroplasties were performed by four surgeons at a single hospital. At the time of follow-up evaluation, 80 hips were available for review. The mean rate of linear wear was 0.15 mm/y, mean rate of three-dimensional femoral head displacement was 0.21 mm/y, and mean rate of volumetric wear was 121 mm³/y. Eight hips (10%) in this series had radiologic osteolysis around either the femoral or acetabular component. A significantly greater volumetric wear rate was found in patients who were younger, those with a higher activity level, those who received a 32-mm-diameter femoral head, and those with vertical orientation of their acetabular component. No relationship could be made with patient weight, gender, Harris hip score, or cup diameter.     

Adaptiive finite element modeling of long-term polyethylene wear in total hip arthroplasty

Adaptive remeshing capability was addded to an existing sliding-distance-coupled finite element model of polyethylene wear in total hip arthroplasty. This augmentation allowed earlier postoperative wear simulation to be extended to the clinically more significant long-term regimen (as long as 20 years). Loads and femoral head excursions were taken from a physically validated gait analysis model of a patient with an instrumented total hip replacement. For otherwise identical 22, 28, and 32 mm components, the least volumetric wear but the most linear wear occurred for the 22 mm head. When the polyethylene thickness in a 22 mm component was reduced to the same as that in a 32 mm component, the volumetric wear rate for the 22 mm component was still much less than that for the larger component, indicating that sliding distance (head size). rather than polyethylene liner thickness, was primarily responsible for the difference in rates, A “28 mm” series, for which head sizes were varied across the range of currently accepted industrial tolerances, showed that although initial wear rates were greatest for the least congruent articulations, the long-term volumetric wear was nearly the same, regardless of initial clearance.     

The effect of femoral component head size on posterior dislocation of the artificial hip joint

BACKGROUND: Posterior dislocation continues to be a relatively common complication following total hip arthroplasty. In addition to technical and patient-associated factors, prosthetic features have also been shown to influence stability of the artificial hip joint. In this study, a dynamic model of the artificial hip joint was used to examine the influence of the size of the head of the femoral component on the range of motion prior to impingement and posterior dislocation following total hip replacement. METHODS: Six fresh cadaveric specimens were dissected, and an uncemented total hip prosthesis was implanted in each. Each specimen was mounted in a mechanical testing machine and loaded with use of a system of seven cables attached to the femur and pelvis that simulated the action of the major muscle groups crossing the hip joint. The hip was taken through a range of motion similar to that experienced when rising from a seated position. The three-dimensional position of the femur at the points of impingement and dislocation was recorded electronically. The range of joint motion was tested with prosthetic femoral heads of four different diameters (twenty-two, twenty-six, twenty-eight, and thirty-two millimeters). RESULTS: Significant associations were noted between the femoral head size and the degree of flexion at dislocation in ten (p = 0.001), twenty (p < 0.001), and thirty (p = 0.003) degrees of adduction. Increasing the femoral head size from twenty-two to twenty-eight millimeters increased the range of flexion by an average of 5.6 degrees prior to impingement and by an average of 7.6 degrees prior to posterior dislocation; however, increasing the head size from twenty-eight to thirty-two millimeters did not lead to more significant improvement in the range of joint motion. The site of impingement prior to dislocation varied with the size of the femoral head. With a twenty-two-millimeter head, impingement occurred between the neck of the femoral prosthesis and the acetabular liner, whereas with a thirty-two-millimeter head, impingement most frequently occurred between the osseous femur and the pelvis. CONCLUSIONS: With the particular prosthesis that was tested, increasing the diameter of the femoral head component increased the range of motion prior to impingement and dislocation, decreased the prevalence of prosthetic impingement, and increased the prevalence of osseous impingement. CLINICAL RELEVANCE: These results suggest that femoral heads with a twenty-eight-millimeter diameter increase the range of motion after total hip replacement. This may be beneficial when additional factors compromising joint stability are encountered.     

Clinical implications of anatomical wear characteristics in slipped capital femoral epiphysis and primary osteoarthritis

BACKGROUND: This study compares the wear characteristics in slipped capital femoral epiphysis (SCFE) with those of primary osteoarthritis (OA) in adult patients with advanced arthritis. METHODS: One hundred femoral heads and proximal neck specimens were studied from SCFE patients (16 hips) and from primary OA (84 hips) patients undergoing total hip arthroplasties (THA). Grade 4 chondromalacia was plotted on a 2-dimensional (2-D) paper grid. Computer tomographic scans were used to create 3-D models of the femoral head and neck to trace the wear patterns. RESULTS: The SCFE group was characterized by (1) loss of neck-head offset, (2) acetabular neck impingement, and (3) loss of superior peripheral articular cartilage adjacent to superior neck. Whereas the primary OA group showed (1) preservation of head-neck offset, (2) absence of acetabular neck impingement, and (3) preservation of superior peripheral articular cartilage. The 3-D modeling in SCFE specimens demonstrated acetabular impingement on the superior lateral femoral neck causing the femur to externally rotate with flexion. The SCFE patients undergoing THA on average were 11 years younger than those with primary OA. The study strongly suggests that the abnormal rotation of the femoral head in SCFE patients causes thinner superior lateral articular cartilage on the femoral head to articulate with the acetabulum. The pistol-grip deformity of the proximal femur in the SCFE group results in hip impingement, which explains why hip flexion and internal rotation can be restricted. CONCLUSIONS: There was a premature development of advanced OA of the adult hip joint in SCFE patients. This was associated with hip impingement caused by loss of the head-neck offset and reorientation of the articular cartilage of the femoral head. Unless the femoral head is redirected in patients with SCFE, the benefits of limited hip preservation debridement procedures are not expected to delay the onset and progression of arthritis. LEVEL OF EVIDENCE: Prognostic study.     

Short-term wear of Japanese highly cross-linked polyethylene in cementless THA

INTRODUCTION: Production of polyethylene wear from acetabular liners is thought, in part, to mediate the periprosthetic osteolysis. This study examined the in vivo wear performance of Japanese highly cross-linked polyethylene (Aeonian) in cementless total hip arthroplasty. MATHERIALS AND METHODS: Ninety-five hips received a highly cross-linked polyethylene liner, while 20 hips were implanted with conventional polyethylene. Two-dimensional linear wear was measured on radiographs and volumetric wear was then calculated. Both linear and volumetric wear rates were examined for the 1-year postoperative period as well as for the time frame beginning after 1 year ending with the final follow-up. RESULTS: The amount of linear wear was significantly lower in the cross-linked group at 3 and 5 years postoperatively (P < 0.01 and < 0.001, respectively). Linear and volumetric wear rates after 1 year postoperatively for hips with the cross-linked polyethylene were significantly reduced by 57 and 59%, respectively, when compared to rates for those who received conventional polyethylene (P < 0.01). A multiple logistic regression analysis revealed that cross-linking was a significant factor influencing linear wear rate after 1 year postoperatively with an odds ratio, exp(ss) = 10.033 (P < 0.001). CONCLUSION: These results suggest that the highly cross-linked polyethylene reduces penetration of the femoral head and may be an optimal bearing surface for patients receiving total hip arthroplasty.     

The influence of weight-bearing on the measurement of polyethylene wear in THA

We have studied the influence of weight-bearing on the measurement of wear of the polyethylene acetabular component in total hip arthroplasty using two techniques. The measured vertical wear was significantly greater when radiographs were taken weight-bearing rather than with the patient supine (p = 0.001, method 1; p = 0.007, method 2). Calculations of rates of linear wear of the acetabular component were significantly underestimated (p < 0.05) when radiographs were taken supine. There are two reasons for this. First, a change in pelvic orientation when bearing weight ensures that the thinnest polyethylene is brought into relief, and secondly, the head of the femoral component assumes the position of maximal displacement along its wear path. Interpretation of previous studies on both linear and volumetric polyethylene wear in total hip arthroplasty should be reassessed in the light of these findings.     

Hip joint deformity caused by osteochondrosis in the course of treatment of congenital dysplasia of the hip]

A series of 73 patients with avascular necrosis complicating surgical or nonsurgical treatment for congenital hip dysplasia is presented. The femoral head, neck and subcapital growth plate has been damaged in all cases. A-P radiographs of proximal femur revealed three types of growth disturbances: lateral, medial and total one. Localization of growth plate damage determined the type of growth disturbances. Mutual features for all types were: shortening of the femoral neck and growth disproportion between femoral head and greater trochanter. In 43 hips the greater trochanter grew over the femoral head and constituted the most proximal part of the femur (trochanter altus). Growth disturbances of the acetabulum coexisted (primary and secondary acetabular dysplasia). Radiological parameters of deformed hips have been compared with normal values.     

Femoroacetabular impingement and the cam-effect. A MRI-based quantitative anatomical study of the femoral head-neck offset

We have observed damage to the labrum as a result of repetitive acetabular impingement in non-dysplastic hips, in which the femoral neck appears to abut against the acetabular labrum and a non-spherical femoral head to press against the labrum and adjacent cartilage. In both mechanisms anatomical variations of the proximal femur may be a factor. We have measured the orientation of the femoral neck and the offset of the head at various circumferential positions, using MRI data from volunteers with no osteoarthritic changes on standard radiographs. Compared with the control subjects, paired for gender and age, patients showed a significant reduction in mean femoral anteversion and mean head-neck offset on the anterior aspect of the neck. This was consistent with the site of symptomatic impingement in flexion and internal rotation, and with lesions of the adjacent rim. Furthermore, when stratified for gender and age, and compared with the control group, the mean femoral head-neck offset was significantly reduced in the lateral-to-anterior aspect of the neck for young men, and in the anterolateral-to-anterior aspect of the neck for older women. For patients suspected of having impingement of the rim, anatomical variations in the proximal femur should be considered as a possible cause.     

Changes in the bone mineral density in the acetabulum and proximal femur after cementless total hip replacement: alumina-on-alumina versus alumina-on-polyethylene articulation

Our aim in this prospective study was to compare the bone mineral density (BMD) around cementless acetabular and femoral components which were identical in geometry and had the same alumina modular femoral head, but differed in regard to the material of the acetabular liners (alumina ceramic or polyethylene) in 50 patients (100 hips) who had undergone bilateral simultaneous primary total hip replacement. Dual energy X-ray absorptiometry scans of the pelvis and proximal femur were obtained at one week, at one year, and annually thereafter during the five-year period of the study. At the final follow-up, the mean BMD had increased significantly in each group in acetabular zone I of DeLee and Charnley (20% (15% to 26%), p=0.003), but had decreased in acetabular zone II (24% (18% to 36%) in the alumina group and 25% (17% to 31%) in the polyethylene group, p=0.001). There was an increase in the mean BMD in zone III of 2% (0.8% to 3.2%) in the alumina group and 1% (0.6% to 2.2%) in the polyethylene group (p=0.315). There was a decrease in the mean BMD in the calcar region (femoral zone 7) of 15% (8% to 24%) in the alumina group and 14% (6% to 23%) in the polyethylene group (p<0.001). The mean bone loss in femoral zone 1 of Gruen et al was 2% (1.1% to 3.1%) in the alumina group and 3% (1.3% to 4.3%) in the polyethylene group (p=0.03), and in femoral zone 6, the mean bone loss was 15% (9% to 27%) in the alumina group and 14% (11% to 29%) in the polyethylene group compared with baseline values. There was an increase in the mean BMD on the final scans in femoral zones 2 (p=0.04), 3 (p=0.04), 4 (p=0.12) and 5 (p=0.049) in both groups. There was thus no significant difference in the bone remodelling of the acetabulum and femur five years after total hip replacement in those two groups where the only difference was in the acetabular liner.     

Proximal femoral replacement for the treatment of periprosthetic fractures

BACKGROUND: A periprosthetic fracture around the femoral component is a rare but potentially problematic complication after total hip arthroplasty. Reconstruction can be challenging, especially when severe bone stock deficiency is encountered. Proximal femoral replacement is one method of treating the severely deficient proximal part of the femur. The present report describes the outcomes of revision total hip arthroplasty with use of a proximal femoral replacement in a cohort of patients who had a Vancouver type-B3 periprosthetic fracture. METHODS: With use of a computerized institutional database, all patients in whom a Vancouver type-B3 fracture (characterized by severe proximal bone deficiency and a loose femoral stem) had been treated with a proximal femoral replacement were identified. A modular femoral replacement with proximal porous coating had been used in all cases. The twenty-one patients who were identified had had a mean age of 78.3 years (range, fifty-two to ninety years) at the time of the index operation. The clinical and radiographic records of these patients were reviewed. RESULTS: At the time of the latest follow-up (mean, 3.2 years), all but one of the patients were able to walk and had minimal to no pain. Complications included persistent wound drainage that was treated with incision and drainage (two hips), dislocation (two hips), refracture of the femur distal to the stem (one hip), and acetabular cage failure (one hip). CONCLUSIONS: Despite a relatively high complication rate, we believe that proximal femoral replacement is a viable option for the treatment of periprosthetic fractures in older patients with severe bone deficiency. If a proximal femoral replacement is used, the stability of the hip must be tested diligently intraoperatively and a constrained acetabular liner should be utilized if instability is encountered. In order to enhance the bone stock, the proximal part of the femur, however poor in quality, should be retained for reapproximation onto the implant.     

Total hip replacement in the congenitally dysplastic hip

Total hip replacement arthroplasty can relieve pain and improve function for many patients with end-stage arthritis.Patients with congenital hip dysplasia, however, present special problems because of the deformities of the acetabulum and femur.Noncemented porous-coated hemispheric acetabular components available in small sizes, and small, straight-stemmed, cemented, femoral components can be used to deal with the bony deformities and have considerably expanded the success of total hip replacement in such patients.The acetabular dysplasia can be managed in most cases by reaming to the medial wall, inserting small-diameter, porous-coated, acetabular components and stabilizing them with screws to provide rigid initial stability. Small portions of the components can be covered with bone graft chips. If necessary, the acetabular component can be placed more proximal than normal, thus increasing the height of the prosthetic hip center, while restoring the limb length with a longer neck prosthesis. a high total dislocation without the development of an adequate false acetabulum, however, requires trochanteric osteotomy, femoral shortening, placement of the acetabular component in the true acetabulum, and the use of straight-stem femoral components.     

The 22-mm vs the 32-mm femoral head in cemented primary hip arthroplasty long-term clinical and radiological follow-up study

A retrospective clinical and radiological analysis was performed on 117 patients (138 hips) with a mean age of 75 years and a mean follow-up of 11 years. The prostheses used were 2 similar monoblock femoral components with 22- and 32-mm head sizes; their effects on the wear of the high-density polyethylene cup were studied. Wear of component was determined by evaluating the standardized initial and follow-up radiographs. The mean rate of linear wear was higher in the 22-mm femoral head, whereas the volumetric wear was higher in the 32-mm femoral head. In both groups, volumetric wear was significantly correlated with cup lysis. Increasing body weight in both groups was associated with more volumetric wear. The radiological evidence of prosthetic loosening did not correlate well with clinical evaluation of the hip.     

Cementless total hip arthroplasty in patients with high congenital hip dislocation

BACKGROUND: The optimal surgical treatment for patients with high congenital dislocation of the hip remains controversial. The purpose of our study was to evaluate the mid-term to long-term results of cementless total hip arthroplasty in such patients. METHODS: The study included sixty-eight total hip replacements performed between 1989 and 1994 in fifty-six consecutive patients with high congenital hip dislocation at our hospital. The cup was placed at the level of the true acetabulum, and a shortening osteotomy of the proximal part of the femur and distal advancement of the greater trochanter were performed in 90% of the hips. At the time of final follow-up, at a mean of 12.3 years postoperatively, fifty-two patients (sixty-four hips) were evaluated by us with a physical examination, determination of Harris hip scores, and radiographs. RESULTS: The mean Harris hip score increased from 54 points preoperatively to 84 points at the time of final follow-up (p < 0.001). There was a negative Trendelenburg sign in fifty-nine (92%) of the sixty-four hips. There were thirteen perioperative complications (19%): three peroneal nerve palsies, one femoral nerve palsy, one superior gluteal nerve palsy, four nondisplaced fractures of the proximal part of the femur, one malpositioned stem perforating the posteromedial cortex of the femur, one superficial wound infection, and two early dislocations. With revision because of aseptic loosening as the end point, the ten-year survival rate for press-fit, porous-coated acetabular components was 94.9% (95% confidence interval, 89.3% to 100%). Eight of nine threaded acetabular components were revised, and the ninth was radiographically loose at the time of the last follow-up examination. The rate of survival for the CDH femoral components, with revision because of aseptic loosening as the end point, was 98.4% (95% confidence interval, 96.8% to 100%) at ten years. CONCLUSIONS: Total hip arthroplasty, with placement of the cup at the level of the true acetabulum, distal advancement of the greater trochanter, and femoral shortening osteotomy, can be recommended for patients with high congenital hip dislocation. Complications such as wear, osteolysis, and cup revision were secondary to the suboptimal design of the acetabular components used in this series.     

Contemporary total hip arthroplasty with and without cement in patients with osteonecrosis of the femoral head

BACKGROUND: The rate of failure of primary total hip arthroplasty in patients with osteonecrosis of the femoral head is higher than that in patients with osteoarthritis. The purpose of this prospective study was to document the clinical and radiographic results of arthroplasty with so-called third-generation cementing and the results of second-generation cementless total hip arthroplasty in ninety-eight consecutive patients with osteonecrosis of the femoral head. METHODS: Fifty patients who had had simultaneous bilateral total hip arthroplasty with a cemented stem in one hip and a cementless stem in the other and forty-eight patients who had had a unilateral total hip arthroplasty with a cementless stem were included in the study. A cementless acetabular component was used in all hips. The presumed cause of the osteonecrosis was ethanol abuse in fifty-seven patients, unknown in twenty-seven, fracture of the femoral neck in nine, and steroid use in five. There were eighty men and eighteen women. The mean age at the time of the arthroplasty was 47.3 years (range, twenty-six to fifty-eight years). Clinical and radiographic evaluations were performed preoperatively; at six weeks; at three, six, and twelve months; and yearly thereafter. The average duration of follow-up was 9.3 years. RESULTS: The average Harris hip scores in the group treated with unilateral arthroplasty (97 points) and the group treated with bilateral arthroplasty (94 points) were similar at the time of final follow-up. They were also similar between the group treated with cement (mean, 96 points) and that treated without cement (95 points). No component had aseptic loosening in either group. In one hip, a cemented femoral stem (2%) and a cementless cup were revised because of infection. Two cementless stems (2%) were revised because of fracture of the proximal part of the femur with loosening of the stem. Annual wear of the polyethylene liner averaged 0.22 mm in the group treated with cement (a zirconia head) and 0.14 mm in the group treated without cement (a cobalt-chromium head). The prevalence of osteolysis in zones 1 and 7 of the femur was 16% in the group treated with cement and 24% in the group treated without cement. CONCLUSIONS: Advancements in surgical technique and better designs have greatly improved the long-term survival of cemented and cementless implants in young patients with osteonecrosis of the femoral head. Although there was no aseptic loosening of the components, a high rate of linear wear of the polyethylene liner and a high rate of osteolysis in these high-risk young patients remain challenging problems.     

Retrieval analysis of 240 metal-on-metal hip components, comparing modular total hip replacement with hip resurfacing

This study compared component wear rates and pre-revision blood metal ions levels in two groups of failed metal-on-metal hip arthroplasties: hip resurfacing and modular total hip replacement (THR). There was no significant difference in the median rate of linear wear between the groups for both acetabular (p = 0.4633) and femoral (p = 0.0872) components. There was also no significant difference in the median linear wear rates when failed hip resurfacing and modular THR hips of the same type (ASR and Birmingham hip resurfacing (BHR)) were compared. Unlike other studies of well-functioning hips, there was no significant difference in pre-revision blood metal ion levels between hip resurfacing and modular THR. Edge loading was common in both groups, but more common in the resurfacing group (67%) than in the modular group (57%). However, this was not significant (p = 0.3479). We attribute this difference to retention of the neck in resurfacing of the hip, leading to impingement-type edge loading. This was supported by visual evidence of impingement on the femur. These findings show that failed metal-on-metal hip resurfacing and modular THRs have similar component wear rates and are both associated with raised pre-revision blood levels of metal ions.     

Relationship between polyethylene wear and osteolysis in hips with a second-generation porous-coated cementless cup after seven years of follow-up

BACKGROUND: The development of osteolysis, a commonly reported complication after total hip arthroplasty without cement, is perceived to be related to the amount of polyethylene particles generated from the bearing surfaces. Although the literature has suggested that the prevalence of osteolysis increases with increasing rates of polyethylene wear, this relationship has never been quantified. The goals of this study were to quantify the relationship between the prevalence of osteolysis and both linear and volumetric wear and to evaluate the risk of osteolysis as a function of wear in a currently used, porous-coated cup design. METHODS: Polyethylene wear and osteolysis were examined in fifty-six hips with a Duraloc-100 acetabular cup articulating with a 28-mm femoral head. Penetration of the prosthetic head into the polyethylene liner was measured, with use of a validated computer-assisted technique, from anteroposterior pelvic radiographs of each patient. From these measurements, linear and volumetric wear rates were calculated. Each patient's series of radiographs was examined independently for the presence of osteolysis. A logistic regression analysis was performed to determine the risk of osteolysis associated with a given change in linear or volumetric wear rate. RESULTS: Osteolysis was found in twenty-three of the fifty-six hips. The hips with osteolysis had significantly higher linear (p < 0.001) and volumetric (p = 0.003) wear rates than the hips without osteolysis. Logistic regression revealed that every 0.1-mm/yr increase in the linear wear rate increased the likelihood of the development of osteolysis by a factor of four. Each 40-mm (3) /yr increase in volumetric wear raised the risk of osteolysis by about three times. CONCLUSIONS: To our knowledge, this study represents the first time that the relationship between polyethylene wear, as determined by both linear wear and volumetric wear, and the prevalence of osteolysis has been quantified. The use of the linear wear rate as a predictor of osteolysis can be a valuable tool in assessing the longevity of a particular implant. The results of our analysis provide quantitative support to the observation that a wear rate of 0.2 mm/yr seems to represent a "critical threshold" for the development of osteolysis. Close radiographic monitoring with the determination of linear wear rates to assess the risk of osteolysis is recommended for all patients after total hip arthroplasty.     

Effect of femoral head size on polyethylene wear and synovitis after total hip arthroplasty: A sonographic and radiographic study of 39 patients

Background and purpose?The role of synovitis and high fluid pressure in the loosening process after total hip arthroplasty has gained increasing attention. We investigated the correlation between head size, polyethylene wear, and capsular distention.

Patients and methods?We analyzed 39 unrevised, radiographically stable hips that had been operated with 28 or 32 mm femoral heads 10 years earlier because of osteoarthritis. We evaluated radiographic signs of loosening, linear and volumetric polyethylene wear, body mass index, activity level, and age. Sonographic examination was performed to measure capsular distance i.e. the distance between the prosthetic femoral neck and the anterior capsule.

Results?Linear wear was 0.09 mm/year and 0.18 mm/year in the 28 mm and 32 mm groups, respectively (p < 0.001). The volumetric wear was 51 mm³/year and 136 mm³/year (p < 0.001) and the capsular distance was 13 mm and 17 mm, respectively (p < 0.001). There was a correlation between linear wear (r = 0.54), volumetric wear (r = 0.62), and capsular distance (p < 0.001).

Interpretation?Wear was greater for the larger femoral head and was correlated to capsular distension.     

Alarming wear of the first-generation polyethylene liner of the cementless porous-coated Biomet Universal cup: 107 hips followed for mean 6 years

Wear of the socket liner and resulting osteolysis are the major causes of failure in cementless hip arthroplasties. We report alarming wear of the first-generation polyethylene liner of the cementless porous-coated Biomet Universal cup. Radiographs of 107 primary hip arthroplasties were analyzed retrospectively. The mean follow-up time was 74 (47-91) months. The linear wear of the polyethylene liners was assessed using a modification of the Livermore method. The median linear wear was 1.0 (0-6.2) and the median linear wear rate was 0.17 mm/year. There was a statistically significant difference between the 28 mm and 32 mm femoral head groups both in the volumetric wear and in the volumetric wear rate. The median linear wear was 0.28 mm/year and 0.14 mm/year for the 32 mm and 28 mm heads, respectively. So far, 14 revisions have been performed or have been scheduled because of excessive wear of the polyethylene liner. In regression analysis, the factors related to the wear rate were the 32 mm size of the femoral head and screw fixation of acetabular shell. We found that the cases with calcar rounding were associated with significantly greater wear. Possible reasons for increased wear of the Hexloc liner may be the cylindrical design, thin polyethylene, and poor quality of the polyethylene. Regular clinical and radiographic follow-ups are recommended especially for hips with 32 mm femoral heads or with screw fixation. If progressive wear of the liner is observed, revision must be considered.