Human microvascular endothelial cell growth and migration on biomimetic surfactant polymers

Successful engineering of a tissue-incorporated vascular prosthesis requires cells to proliferate and migrate on the scaffold. Here, we report on a series of "ECM-like" biomimetic surfactant polymers that exhibit quantitative control over the proliferation and migrational properties of human microvascular endothelial cells (HMVEC). The biomimetic polymers consist of a poly(vinyl amine) (PVAm) backbone with hexanal branches and varying ratios of cell binding peptide (RGD) to carbohydrate (maltose). Proliferation and migration behavior of HMVEC was investigated using polymers containing RGD: maltose ratios of 100:0, 75:25 and 50:50, and compared with fibronectin (FN) coated glass (1 microg/cm2). A radial Teflon fence migration assay was used to examine HMVEC migration at 12 h intervals over a 48 h period. Migration was quantified using an inverted optical microscope, and HMVEC were examined by confocal microscopy for actin and focal adhesion organization/ arrangement. Over the range of RGD ligand density studied (approximately 0.19-0.6 peptides/nm2), our results show HMVEC migration decreases with increasing RGD density in the polymer. HMVEC were least motile on the 100% RGD polymer (approximately 0.38-0.6 peptides/nm2) with an average migration of 0.20 mm2/h in area covered, whereas HMVEC showed the fastest migration of 0.48+/-0.06 mm2/h on the 50% RGD surface ( approximately 0.19-0.30 peptides/nm2). In contrast, cell proliferation increased with increasing surface peptide density; proliferation on the 50% RGD surface was 1.5%+/-0.06/h compared with 2.2%+/-0.07/h on the 100% RGD surface. Our results show that surface peptide density affects cellular functions such as growth and migration, with the highest peptide density supporting the most proliferation but the slowest migration.     

Human endothelial cell interaction with biomimetic surfactant polymers containing Peptide ligands from the heparin binding domain of fibronectin

Biomimetic materials that mimic the extracellular matrix (ECM) provide a means to control cellular functions such as adhesion and growth, which are vital to successful engineering of tissue-incorporated biomaterials. Novel "ECM-like" biomimetic surfactant polymers consisting of a poly(vinyl amine) backbone with pendant cell-adhesive peptides derived from one of the heparin-binding domains of fibronectin were developed to improve endothelial cell adhesion and growth on vascular biomaterials. Heparin-binding peptide (HBP) sequences, alone and in combination with RGD peptides, were examined for their ability to promote human pulmonary artery endothelial cell (HPAEC) adhesion and growth (HBP1, WQPPRARI; HBP2, SPPRRARVT; HBP1:RGD; and HBP2:RGD) and compared with cell adhesion and growth on fibronectin and on negative control polymer surfaces in which alanines were substituted for the positively charged arginine residues in the two peptides. The results showed that HPAECs adhered and spread equally well on all HBP-containing polymers and the positive fibronectin control, showing similar stress fiber and focal adhesion formation. However, the HBP alone was unable to support long-term HPAEC growth and survival, showing a loss of focal adhesions and cytoskeletal disorganization by 24 h after seeding. With the addition of RGD, the surfaces behaved similarly or better than fibronectin. The negative control polymers showed little to no initial cell attachment, and the addition of soluble heparin to the medium reduced initial cell adhesion on both the HBP2 and HBP2:RGD surfaces. These results indicate that the HBP surfaces promote initial HPAEC adhesion and spreading, but not long-term survival.     

Endothelial cell attachment and shear response on biomimetic polymer-coated vascular grafts

Endothelial cell (EC) adhesion, shear retention, morphology, and hemostatic gene expression on fibronectin (FN) and RGD fluorosurfactant polymer (FSP)-coated expanded polytetrafluoroethylene grafts were investigated using an in vitro perfusion system. ECs were sodded on both types of grafts and exposed to 8 dyn/cm(2) of shear stress. After 24 h, the EC retention on RGD-FSP-coated grafts was 59 ± 14%, which is statistically higher than the 36 ± 11% retention measured on FN grafts (p < 0.02). Additionally, ECs on RGD-FSP exhibited a more spread morphology and oriented in the direction of shear stress, as demonstrated by actin fiber staining. This spread morphology has been observed earlier in cells that are adapting to shear stress. Real-time PCR for vascular cell adhesion molecule 1, tissue factor, tissue plasminogen activator, and inducible nitric oxide synthase indicated that the RGD-FSP material did not activate the cells and that shear stress appears to induce a more vasoprotective phenotype, as shown by a significant decrease in VCAM-1 expression, compared with sodded grafts. RGD-FSP-coating allows for a cell layer that is more resistant to physiological shear stress, as shown by the increased cell retention over FN. This shear stable EC layer is necessary for in vivo endothelialization of the graft material, which shows promise to increase the patency of synthetic small diameter vascular grafts.     

Enhanced endothelial cell retention on shear-stressed synthetic vascular grafts precoated with RGD-cross-linked fibrin

Clinical in vitro endothelialization has been shown to increase the patency of synthetic vascular grafts. The shear stress resistance of the cultured autologous endothelium represents a crucial cornerstone of the concept. We investigated whether an enrichment of the precoating matrix with adhesion sites can augment endothelial cell attachment. Adult human saphenous vein endothelial cells (AHSVECs) were seeded confluently ([58 +/- 11] x 10(3) AHSVECs/cm2) onto 10-cm-long ePTFE (expanded polytetrafluorethylene) vascular grafts (n = 24) precoated with commercial clinically approved fibrin gel (Tisseal) containing various concentrations of cross-linked RGD peptide (0.0, 4.0, 8.0, or 16.0 mg of RGD per milliliter of Tisseal fibrinogen component). Endothelialized grafts were postcultivated for 9 days before they were exposed to a pulsatile circulation model mimicking peak physiological shear stress conditions of the femoral artery (12 dyn/cm2; min/max, -60/+28 dyn/cm2). Cell loss after 24 h was quantitatively determined by image analysis of vital stains. Initial 24-h cell loss was 27.2 +/- 1.7% in grafts precoated with the non-RGD-enriched fibrin matrix. In contrast, cell loss was significantly less on fibrin containing 4.0 mg of RGD peptide per milliliter of Tisseal fibrinogen component (13.3 +/- 7.9%; p < 0.05). Cell loss on fibrin containing 8 and 16 mg of RGD per milliliter of Tisseal fibrinogen component was 41.0 +/- 27.4 and 43.0 +/- 23.2% (p > 0.05), respectively. We conclude that low concentrations of RGD peptide cross-linked into commercial fibrin matrices used for clinical in vitro lining of vascular grafts led to significantly increased endothelial cell retention. The failure of higher RGD concentrations to enhance endothelial cell attachment may be explained by competitive binding of endothelial cells to non-cross-linked RGD.     

The effect of RGD fluorosurfactant polymer modification of ePTFE on endothelial cell adhesion, growth, and function.

We have synthesized and characterized a novel peptide fluorosurfactant polymer (PFSP) modification that facilitates the adhesion and growth of endothelial cells on expanded polytetrafluoroetheylene (ePTFE) vascular graft material. This PFSP consists of a poly(vinyl amine) (PVAm) backbone with integrin binding Arg-Gly-Asp (RGD) peptides and perfluorocarbon pendant branches for adsorption and stable adhesion to underlying ePTFE. Aqueous PFSP solution was used to modify the surface of fluorocarbon substrates. Following subconfluent seeding, endothelial cell (EC) adhesion and growth on PFSP was assessed by determining cell population at different time points. Spectroscopic results indicated successful synthesis of PFSP. PFSP modification of ePTFE reduced the receding water contact angle measurement from 120 degrees to 6 degrees , indicating successful surface modification. Quantification of cell population demonstrated reduced EC attachment efficiency but increased growth rate on RGD PFSP compared with fibronectin (FN). Actin staining revealed a well-developed cytoskeleton for ECs on RGD PFSP indicative of stable adhesion. Uptake of acetylated low-density lipoprotein and positive staining for VE-Cadherin confirm EC phenotype for adherent cells. Production of prostacyclin, a potent antiplatelet agent, was equivalent between ECs on FN and RGD PFSP surfaces. Our results indicate successful synthesis and surface modification with PFSP; this is a simple, quantitative, and effective approach to modifying ePTFE to encourage endothelial cell attachment, growth, and function.     

人脐静脉内皮细胞在RGD肽聚酯材料表面的黏附稳定性研究

研究RGD肽对内皮细胞(Endothelialcell,EC)在生物材料表面黏附稳定性的影响。实验材料(聚酯)分为三组:RGD组(表面共价接枝人工合成的RGD三肽)、对照组(表面预衬纤维粘连蛋白)和空白组(表面未作任何处理),然后在三组材料表面种植体外培养的人脐静脉内皮细胞,并在定常流条件下观察比较RGD肽和纤维粘连蛋白对材料表面细胞黏附稳定性的影响。结果显示随着剪切力作用时间延长和剪切力加大,三组材料表面黏附的细胞脱落逐渐增多。空白组PET表面细胞脱落最为明显,8.19dyne/cm2作用4h后,材料表面细胞残留率仅为13.73%。PET表面结合RGD或纤维粘连蛋白后,细胞残留率明显增加,同样剪切力作用下细胞残留率分别为43.33%和40.75%,两组之间无显著性差异。由此得出结论,RGD可以提高EC在材料表面的黏附稳定性。本结果仅是一个体外实验的初步结果,需要进一步的体内实验加以证实。     

Bio-mimetic composite matrix that promotes endothelial cell growth for modification of biomaterial surface

The incidence of thrombogenesis and occlusion of cardiovascular implants is likely to be reduced by endothelial cell (EC) growth promotion on biomaterials used for device fabrication. However, proper signaling between the matrix proteins deposited on the device surface and the cells grown on it is a prime requirement for growth and function. It was demonstrated earlier that a composition of matrix proteins that include fibrin, fibronectin, gelatin, and growth factors maintain a steady proliferation potential and prolong the survival of endothelial cells in vitro. In this study, assessment of the same matrix to prevent EC from dedifferentiation during in vitro culture and to promote endothelialization of biomaterials used for fabrication of cardiovascular implants is carried out. Up/down regulation of m-RNA expression for a prothrombotic molecule-plasminogen activator inhibitor (PAI), and two antithrombotic molecules- nitric oxide synthetase (eNOS) and tissue plasminogen activator (t-PA) are chosen as the indicators of cell dedifferentiation during cell culture and passaging. Immunostaining for vinculin and actin demonstrated that composite coating on biomaterials improves focal adhesion and cytoskeletal organization that increases the quality of EC grown on it. EC proliferation, measured by (3)H-thymidine uptake, on all bare materials was poor and high incidence of cell apoptosis was noticed within 72 h in culture, whereas once coated with composite all materials showed good proliferation and survival. The results suggest that the designed composition of biomimetic adhesive proteins and growth factors is suitable for EC growth, survival, and functional integrity, thus making it suitable for cardiovascular tissue engineering that requires in vitro EC culture.     

Extracellular matrix production by human osteoblasts cultured on biodegradable polymers applicable for tissue engineering

The nature of the extracellular matrix (ECM) is crucial in regulating cell functions via cell-matrix interactions, cytoskeletal organization, and integrin-mediated signaling. In bone, the ECM is composed of proteins such as collagen (CO), fibronectin (FN), laminin (LM), vitronectin (VN), osteopontin (OP) and osteonectin (ON). For bone tissue engineering, the ECM should also be considered in terms of its function in mediating cell adhesion to biomaterials. This study examined ECM production, cytoskeletal organization, and adhesion of primary human osteoblastic cells on biodegradable matrices applicable for tissue engineering, namely polylactic-co-glycolic acid 50:50 (PLAGA) and polylactic acid (PLA). We hypothesized that the osteocompatible, biodegradable polymer surfaces promote the production of bone-specific ECM proteins in a manner dependent on polymer composition.We first examined whether the PLAGA and PLA matrices could support human osteoblastic cell growth by measuring cell adhesion at 3, 6 and 12h post-plating. Adhesion on PLAGA was consistently higher than on PLA throughout the duration of the experiment, and comparable to tissue culture polystyrene (TCPS). ECM components, including CO, FN, LM, ON, OP and VN, produced on the surface of the polymers were quantified by ELISA and localized by immunofluorescence staining. All of these proteins were present at significantly higher levels on PLAGA compared to PLA or TCPS surfaces. On PLAGA, OP and ON were the most abundant ECM components, followed by CO, FN, VN and LN. Immunofluorescence revealed an extracellular distribution for CO and FN, whereas OP and ON were found both intracellularly as well as extracellularly on the polymer. In addition, the actin cytoskeletal network was more extensive in osteoblasts cultured on PLAGA than on PLA or TCPS.In summary, we found that osteoblasts plated on PLAGA adhered better to the substrate, produced higher levels of ECM molecules, and showed greater cytoskeletal organization than on PLA and TCPS. We propose that this difference in ECM composition is functionally related to the enhanced cell adhesion observed on PLAGA. There is initial evidence that specific composition of the PLAGA polymer favors the ECM. Future studies will seek to optimize ECM production on these matrices for bone tissue engineering applications.     

Model surfaces engineered with nanoscale roughness and RGD tripeptides promote osteoblast activity

Cell adhesion to biomaterials is a prerequisite for tissue integration with the implant surface. Herein, we show that we can generate a model silica surface that contains a minimal-length arginine-glycine-aspartic acid (RGD) peptide that maintains its biological activity. In the first part of this study, attachment of MC3T3-E1 osteoblast-like cells was investigated on silicon oxide, amine terminated substrates [i.e., 3-aminopropyl triethoxysilane (APTS)], grafted RGD, and physisorbed RGD control. The APTS layer exhibited nanoscale roughness and presented amine functional groups for grafting a minimal RGD tripeptide devoid of any flanking groups or spacers. Contact angle measurements indicated that the hydrophobicity of the APTS surface was significantly lower than that of the surface with grafted RGD (RGD-APTS). Atomic force microscopy showed that surfaces covered with RGD-APTS were smoother (Ra = 0.71 nm) than those covered with APTS alone (Ra = 1.59 nm). Focusing mainly on cell morphology, experiments showed that the RGD-APTS hybrid provided an optimum surface for cell adhesion, spreading, and cytoskeletal organization. Discrete focal adhesion plaques were also observed consistent with successful cell signaling events. In a second set of experiments, smooth, monolayers of APTS (Ra = 0.1 nm) were used to prepare arginine-glycine-aspartic acid-serine (RGDS)-APTS and arginine-glycine-glutamic acid-serine (RGES)-APTS (control) substrates. Focusing mainly on cell function, integrin and gene expression were all enhanced for rate osteosarcoma cells on surfaces containing grafted RGDS. Both sets of studies demonstrated that grafted molecules of RGD(S) enhance both osteoblast-like cell adhesion and function.     

The use of mild trypsinization conditions in the detachment of endothelial cells to promote subsequent endothelialization on synthetic surfaces

A necessary condition for endothelialization of small diameter grafts is rapid and firm adhesion of endothelial cells upon exposure to flow. To retain integrins on the cell surface, we assessed the effects of trypsin concentration, the duration of trypsin incubation, and trypsin neutralization methods on endothelial cell adhesion. Human umbilical vein endothelial cells which were detached using 0.025% trypsin for 5 min and seeded onto glass pretreated with fibronectin had close to 100% cell retention when shear stresses as high as 200 dyn/cm2 were applied for 2 min. An equivalent level of cell retention was observed on fibronectin coated Teflon-AF for shear stresses up to 60 dyn/cm2 applied for 4h. Using 0.025% trypsin, initial cell spreading and cell surface alpha5beta1 integrins were increased relative to cells treated with 0.5% trypsin. After 1h of attachment, focal adhesions formed when low trypsin concentrations were used but were less evident with high trypsin concentrations. These results showed that low trypsin concentrations produced faster spreading, a higher number of intact integrins, and rapid focal adhesion formation.     

RGD-Functionalized polymer brushes as substrates for the integrin specific adhesion of human umbilical vein endothelial cells

This report demonstrates the feasibility of surface-initiated atom transfer radical polymerization to prepare thin polymer layers ("brushes") that can be functionalized with short peptide ligands and which may be of use as coatings to promote endothelialization of blood-contacting biomaterials. The brushes are composed of poly(2-hydroxyethyl methacrylate) (PHEMA) or poly(poly(ethylene glycol) methacrylate) (PPEGMA), which do not only suppress non-specific adhesion of proteins and cells but also contain hydroxyl groups that can be used to introduce small peptide ligands. A protocol has been developed that allows functionalization of the brushes with RGD containing peptide ligands resulting in surface concentrations ranging from approximately 0.5-12 pmol/cm(2). At peptide surface concentrations >1-5.3 pmol/cm(2), human umbilical vascular endothelial cells (HUVECs) were found to adhere and spread rapidly. A difference in size and morphology of focal adhesions between HUVECs immobilized on PHEMA and PPEGMA brushes was observed. It is proposed that this is due to the increased ethylene glycol spacer length and hydrophilicity of the PPEGMA brushes, which may lead to increased ligand mobility and reduced ligand-integrin affinity. HUVECs immobilized on the polymer brushes were also found to be able to retain homeostasis when exposed to shear stresses that simulated arterial blood flow.     

Platelet and endothelial adhesion on fluorosurfactant polymers designed for vascular graft modification

A prominent failure mechanism of small diameter expanded polytetrafluoroethylene (ePTFE) vascular grafts is platelet-mediated thrombosis. We have designed a surface modification for ePTFE consisting of a self-assembling fluorosurfactant polymer (FSP) bearing biologically active ligands, including adhesive peptides and polysaccharide moieties. The goal of this biomimetic construct is to improve graft hemocompatibility by promoting rapid surface endothelialization, whereas minimizing platelet adhesion. Here we present a direct comparison of platelet and endothelial cell (EC) adhesion to FSPs containing one of three cell-adhesion peptides: cyclic Arg-Gly-Asp-D-Phe-Glu (cRGD), cyclic *Cys-Arg-Arg-Glu-Thr-Ala-Trp-Ala-Cys* (cRRE, *denotes disulfide bond cyclization), linear Gly-Arg-Gly-Asp-Ser-Pro-Ala (RGD), or a polysaccharide moiety: oligomaltose (M-7), later designed to prevent nonspecific protein adhesion. Measurements of soluble peptide-integrin binding indicated that cRRE exhibits very low affinity for the alpha(IIb)beta(3) platelet fibrinogen receptor. Static and dynamic adhesion of washed, activated platelets on FSP-modified surfaces revealed that M-7 and cRRE promote significantly less platelet adhesion compared to RGD and cRGD FSPs, whereas EC adhesion was similar on all peptide FSPs and minimal on M-7 FSP. These results illustrate the potential for ligands presented in a FSP surface modification to selectively adhere ECs with limited platelet attachment.     

Acrylic Acid-RGD as a Biomimetic Surface Modifier for Poly(ethylene terephthalate)

INTRODUCTION　Biomaterials play an importantrole in human disease- treatmentand healing〔1,2〕.Due to the good mechanical property,PET is used to the coating of artificial heartvalve,the film of mending hearts and artificial vessel etc〔3〕.But the imperfection isthe low capability of surface hydrophile leading to the high static and low water ad-sorption〔4〕.In the application,traditional artificial cardiovascular materials( e.g.PET) have blood coagulation,alexin- activation and other…     

Regulation of mesenchymal stem cell attachment and spreading on hydroxyapatite by RGD peptides and adsorbed serum proteins

The successful development of biomaterials must take into consideration how those surfaces will interact with in vivo processes such as adsorption of endogenous proteins. In this study, we examined whether modifying highly adsorbent materials like hydroxyapatite (HA) with RGD peptides would improve mesenchymal stem cell (MSC) adhesion. We found that RGD, alone, was not sufficient to promote full cell spreading. However, given that RGD-modified HA will likely adsorb osteogenic serum proteins in vivo, we evaluated MSC behavior on HA pre-coated with RGD, then over-coated with serum (RGD/FBS). Interestingly, RGD/FBS coatings additively stimulated MSC attachment and spreading compared to either coating alone, but only at low RGD coating concentrations. High RGD concentrations inhibited cell attachment, and completely eliminated cell spreading on RGD/FBS surfaces. To better understand the mechanism by which RGD and adsorbed serum proteins interactively regulate cell behavior, we monitored the deposition of fibronectin (FN) from serum onto HA pre-coated with increasing RGD concentrations. These studies showed that high RGD concentrations did not inhibit FN adsorption, therefore cell spreading is attenuated by mechanisms other than lack of FN availability. Collectively, our results suggest a potential therapeutic benefit for functionalizing HA with RGD, however such a benefit will likely depend upon the RGD density.     

Biomimetic materials for tissue engineering

The development of biomaterials for tissue engineering applications has recently focused on the design of biomimetic materials that are capable of eliciting specific cellular responses and directing new tissue formation mediated by biomolecular recognition, which can be manipulated by altering design parameters of the material. Biomolecular recognition of materials by cells has been achieved by surface and bulk modification of biomaterials via chemical or physical methods with bioactive molecules such as a native long chain of extracellular matrix (ECM) proteins as well as short peptide sequences derived from intact ECM proteins that can incur specific interactions with cell receptors. The biomimetic materials potentially mimic many roles of ECM in tissues. For example, biomimetic scaffolds can provide biological cues for cell-matrix interactions to promote tissue growth, and the incorporation of peptide sequences into materials can also make the material degradable by specific protease enzymes. This review discusses the surface and bulk modification of biomaterials with cell recognition molecules to design biomimetic materials for tissue engineering. The criteria to design biomimetic materials such as the concentration and spatial distribution of modified bioactive molecules are addressed. Recent advances for the development of biomimetic materials in bone, nerve, and cardiovascular tissue engineering are also summarized.     

The selective modulation of endothelial cell mobility on RGD peptide containing surfaces by YIGSR peptides

The ability of the biomimetic peptides YIGSR, PHSRN and RGD to selectively affect adhesion and migration of human microvascular endothelial cells (MVEC) and vascular smooth muscle cells (HVSMC) was evaluated. Cell mobility was quantified by time-lapse video microscopy of single cells migrating on peptide modified surfaces. Polyethylene glycol (PEG) hydrogels modified with YIGSR or PHSRN allowed only limited adhesion and no spreading of MVEC and HVSMC. However, when these peptides were individually combined with the strong cell binding peptide RGD in PEG hydrogels, the YIGSR peptide was found to selectively enhance the migration of MVEC by 25% over that of MVEC on RGD alone (p<0.05). No corresponding effect was observed for HVSMC. This suggests that the desired response of specific cell types to tissue engineering scaffolds could be optimized through a combinatory approach to the use of biomimetic peptides.     

The effect of the addition of a polyglutamate motif to RGD on peptide tethering to hydroxyapatite and the promotion of mesenchymal stem cell adhesion

Mimicking endogenous bone-binding proteins, RGD peptides have been synthesized with polyacidic amino acid domains in order to ionically tether the peptides to bone-like synthetic biomaterials, including hydroxyapatite (HA). However, a direct comparison of unmodified RGD with polyacidic-conjugated RGD has not been performed, and thus a benefit for the acidic domain has not been established. We evaluated the peptide/HA bond of RGD peptides with and without an attached polyglutamate sequence (E(7)), as well as examined mesenchymal stem cell (MSC) adhesion and morphology as they were affected by the conjugated peptide. We found that significantly more E(7)RGD was bound to HA than RGD at all coating concentrations tested, and moreover, more E(7)RGD was retained on the HA surface even after extended washing in serum-free media. Consistent with in vitro results, higher levels of E(7)RGD than RGD remained on HA that had been implanted in vivo for 24 h, indicating that the polyacidic domain improved peptide-binding efficiency. At several peptide concentrations, E(7)RGD increased cell adhesion compared to RGD surfaces, establishing a biological benefit for the E(7) modification. In addition, HA pre-coated sequentially with low-density E(7)RGD (1-10 microg/ml) and serum (FBS) stimulated cell adhesion and spreading, compared to either coating alone, suggesting that an ionic linkage allows for the potential adsorption of serum proteins to unoccupied sites, which may be important for bone formation in vivo. Collectively, these results suggest that tethering peptides to HA via a polyglutamate domain is an effective method for improving the peptide/HA bond, as well as for enhancing MSC adhesion.     

Effects of adhesive proteins on endothelialization of PC crosslinking yak pericardial materials--an experimental study]

To investigate the conditions of endothelialization of biomaterials, we examined in vitro the growth properties of endothelial cells on PC treated yak pericardial materials. After rinsed in normal saline (0.9%), the surface of PC crosslinking yak pericardial materials was precoated with three kinds of adhesive proteins--Laminin (La), Fibronectin(FN) and Collagen-I(CL-I). Ednothelial cells(EC) from the canine were seeded on the precoated materials, and on the uncoated materials as control. The result showed that in the La and FN groups the seeded EC survived and grew on the patches, while in the CL-I group and uncoated group the seeded EC on and around the patches did not continue to live. Conclusively, in this experiment, PC yak pericardial materials had cytotoxicity; the cytotoxicity of PC crosslinking yak pericardial materials could be decreased by La and FN precoating; La and FN promoted the adhesion and growth of EC on the PC yak pericardial materials patches; the materials met the needs of endothelialization in vitro, prominently in the La group; there was significant difference in endothelialization between La and FN groups (P < 0.05); CL-I had no part in promoting EC adhesion and growth.     

Mylar and Teflon-AF as cell culture substrates for studying endothelial cell adhesion

The textured and opaque nature of Dacron and ePTFE has prevented the use of these fabrics in conventional cell culture techniques normally employed to optimize cell attachment and retention. This lack of optimization has led, in part, to the poor performance of endothelialization strategies for improving vascular graft patency. Here we show that thin, transparent films of Mylar and Teflon-AF are viable in vitro cell culture mimics of Dacron and ePTFE vascular graft materials, particularly for the study of protein mediated endothelial cell (EC) attachment, spreading and adhesion. Glass substrates were used as controls. X-ray photoelectron spectroscopy (XPS) and contact angle analysis showed that Mylar and Teflon-AF have surface chemistries that closely match Dacron and ePTFE. (125)I radiolabeling was used to quantify fibronectin (FN) adsorption, and FN and biotinylated-BSA "dual ligand" co-adsorption onto glass, Mylar and Teflon-AF substrates. Native human umbilical vein endothelial cells (HUVEC) and streptavidin-incubated biotinylated-HUVEC (SA-b-HUVEC) spreading was measured using phase contrast microscopy. Cell retention and adhesion was determined using phase contrast microscopy under laminar flow. All surfaces lacking protein pre-treatment, regardless of surface type, showed the lowest degree of cell spreading and retention. Dual ligand treated Mylar films showed significantly greater SA-b-HUVEC spreading up to 2 h, but were similar to HUVEC on FN treated Mylar at longer times; whereas SA-b-HUVEC spreading on dual ligand treated Teflon-AF was never significantly different from HUVEC on FN treated Teflon-AF at any time point. SA-b-HUVEC retention was significantly greater on dual ligand treated Mylar compared to HUVEC on FN treated Mylar over the entire range of shear stresses tested (3.54-28.3 dynes/cm(2)); whereas SA-b-HUVEC retention to dual ligand and HUVEC retention to FN treated Teflon-AF gave similar results at each shear stress, with only the mid-range of stresses showing significant difference in cell retention to Teflon-AF.     

The effect of integrin-specific bioactive coatings on tissue healing and implant osseointegration

Implant osseointegration, defined as bone apposition and functional fixation, is a requisite for clinical success in orthopaedic and dental applications, many of which are restricted by implant loosening. Modification of implants to present bioactive motifs such as the RGD cell-adhesive sequence from fibronectin (FN) represents a promising approach in regenerative medicine. However, these biomimetic strategies have yielded only marginal enhancements in tissue healing in vivo. In this study, clinical-grade titanium implants were grafted with a non-fouling oligo(ethylene glycol)-substituted polymer coating functionalized with controlled densities of ligands of varying specificity for target integrin receptors. Biomaterials presenting the alpha5beta1-integrin-specific FN fragment FNIII 7-10 enhanced osteoblastic differentiation in bone marrow stromal cells compared to unmodified titanium and RGD-presenting surfaces. Importantly, FNIII 7-10-functionalized titanium significantly improved functional implant osseointegration compared to RGD-functionalized and unmodified titanium in vivo. This study demonstrates that bioactive coatings that promote integrin binding specificity regulate marrow-derived progenitor osteoblastic differentiation and enhance healing responses and functional integration of biomedical implants. This work identifies an innovative strategy for the rational design of biomaterials for regenerative medicine.